Early and 24-hour bond strength and degree of conversion of etch-and-rinse and self-etch adhesives

Purpose: To evaluate early and 24-hour microtensile bond strength (mu TBS) and the degree of conversion (DC) of one representative adhesive system from each of the four current bonding approaches. Methods: 40 human molars were sectioned occluso-gingivally into two halves. Resin composite was bonded incrementally to flat, mid-coronal dentin, using the adhesives Adper Scotchbond MP (MP); Adper Scotchbond 2 (SB); Clearfil SE Bond (SE); and Adper Prompt L-Pop (LP) according to the respective manufacturer`s instructions (n= 10). One half was immediately sectioned into sticks and subjected to mu TBS test. As the sectioning process took approximately 1 hour, the results were designated as 1-hour bond strengths. The other half was stored in distilled water at 37 degrees C for 24 hours before being sectioned and tested. The DC of these systems was measured using Fourier Transform-Raman spectroscopy in three periods: immediately, 1 and 24 hours after polymerization. Data were analyzed with ANOVA and Tukey`s tests. Results: There were no significant differences between the 1-hour and 24-hour bond strengths (P> 0.05), or among the DC measured immediately, 1 hour and 24 hours after polymerization (P> 0.05). However, significant differences were observed among adhesives (P< 0.05). mu TBS values obtained, in MPa (1 hour/24 hour), were: SB (48.6 + 1.3/48.4 + 3.5) = SE (51.9 + 4.7/53.3 +/- 2.9) > MP (35.3 +/- 10.9/38.6 + 6.7) > LP (25.5 + 1.1/26.0 + 1.5). The DC, in percentage (immediately/1 hour/24 hour), were: SE (81/82/87) > MP (79/77/81) > SB (60/63/65) > LP (39/37/42).

Effect of Test Environment and Microstructure on the Flexural Strength of Dental Porcelains

Purpose: The objective of this study was to verify the influence of test environment on the flexural strength of dental porcelains with distinct microstructures. Material and Methods: Disk-shaped specimens from three dental porcelains with distinct leucite content (VM: zero; CE: 12; NS: 22 vol%) were manufactured and tested for biaxial flexural strength in air and immersed in artificial saliva. The results were analyzed by means of two-way ANOVA and Tukey`s test (alpha = 0.05). Results: The flexural strength (MPa) obtained for ambient air and artificial saliva environments, respectively, were: 110.0 +/- 16.0 and 81.5 +/- 10.8 for VM; 51.9 +/- 4.0 and 42.0 +/- 4.7 for CE; 72.0 +/- 11.5 and 63.6 +/- 5.8 for NS. A numerical decrease in the mean flexural strength was observed for all groups when specimens were tested under artificial saliva; however, the difference was only statistically significant for VM. Conclusions: The results indicate that the effect of water immersion on the flexural strength of dental porcelains varies according to their leucite content, as only the material without leucite in its microstructure (VM) showed significant strength degradation when tested under water.

Adhesive Temperature: Effects on Adhesive Properties and Resin-Dentin Bond Strength

Objectives: To evaluate the effect of adhesive temperature on the resin-dentin bond strength (mu TBS), nanoleakage (NL), adhesive layer thickness (AL), and degree of conversion (DC) of ethanol/water- (SB) and acetone-based (PB) etch-and-rinse adhesive systems. Methods: The bottles of the two adhesives were kept at each temperature (5 degrees C, 20 degrees C, 37 degrees C, and 50 degrees C) for 2 hours before application to demineralized dentin surfaces of 40 molars. Specimens were prepared for mu TBS testing. Bonded sticks (0.8 mm(2)) were tested under tension (0.5 mm/min). Three bonded sticks from each tooth were immersed in silver nitrate and analyzed by scanning electron microscopy. The DC of the adhesives was evaluated by Fourier transformed infrared spectroscopy. Results: Lower mu TBS was observed for PB at 50 degrees C. For SB, the mu TBS values were similar for all temperatures. DC was higher at 50 degrees C for PB. Higher NL and thicker AL were observed for both adhesives in the 5 degrees C and 20 degrees C groups compared to the 37 degrees C and 50 degrees C groups. The higher temperatures (37 degrees C or 50 degrees C) reduced the number of pores within the adhesive layer of both adhesive systems. Conclusions: It could be useful to use an ethanol/water-based adhesive at 37 degrees C or 50 degrees C and an acetone-based adhesive at 37 degrees C to improve adhesive performance.

Bone repair and augmentation using block of sintered bovine-derived anorganic bone graft in cranial bone defect model

To histomorphometrically investigate the repair of critical size defects (CSDs) and bone augmentation in cranial walls using block of sintered bovine-derived anorganic bone (sBDAB) graft. Forty guinea-pigs were divided into test (n=20) and CSD control (n=20) groups. In each animal, a full-thickness bone defect with 9.5 mm diameter was made in the frontal bone. The defects were filled with an sBDAB block soaked in blood in the test group and with blood clot in the CSD control group. The skulls were collected at 0 h (n=2) and 30, 90 and 180 days (n=6/group and period) postoperatively. The volume density and total volume of newly formed bone, sBDAB, blood vessels and connective tissue, vertical thickness of removed bone plug, sBDAB block and graft area were evaluated. The vertical thickness of the adapted sBDAB block was 3.8 times higher than that of the removed bone plug and did not show significant difference between periods, filling in average 29.8% of the total graft region. The sBDAB block exhibited complete osseointegration with the borders of the defect at 90 days. At 90 and 180 days, the vertical thickness of the graft was 279% in the average, and the total volume of bone augmentation was, respectively, 78.8% and 148.5% higher compared with the removed bone plug. The defects of the CDS control group showed limited osteogenesis and filling by connective tissue plus tegument. The sBDAB block can be used to promote repair of CSDs and bone augmentation in the craniomaxillofacial region, due to its good osteoconductive and slow resorptive properties. To cite this article:Cestari TM, Granjeiro JM, de Assis GF, Garlet GP, Taga R. Bone repair and augmentation using block of sintered bovine-derived anorganic bone graft in cranial bone defect model.Clin. Oral Impl. Res. 20, 2009; 340-350.doi: 10.1111/j.1600-0501.2008.01659.x.

The Potential Role of Suppressors of Cytokine Signaling in the Attenuation of Inflammatory Reaction and Alveolar Bone Loss Associated with Apical Periodontitis

Inflammatory cytokines contribute to periapical tissue destruction. Their activity is potentially regulated by suppressors of cytokine signaling (SOCS), which down-regulate signal transduction as part of an inhibitory feedback loop. We investigated the expression of the cytokines tumor necrosis factor alpha (TNF-alpha); interleukin (IL)-10 and RANKL; and SOCS-1, -2, and -3 by real-time polymerase chain reaction in 57 periapical granulomas and 38 healthy periapical tissues. Periapical granulomas exhibited significantly higher SOCS-1, -2, and -3, TNF-alpha, IL-10, and RANKL messenger RNA levels when compared with healthy controls. Significant positive correlations were found between SOCS1 and IL-10 and between SOCS3 and IL-10. Significant inverse correlations were observed between SOCS1 and TNF-alpha, SOCS1 and RANKL, and SOCS3 and TNF-alpha. Increased SOCS-1, -2, and -3 messenger RNA levels in periapical granulomas may be related to the downregulation of inflammatory cytokines in these lesions; therefore, SOCS molecules may play a role in the dynamics of periapical granulomas development. (J Endod 2008;34:1480-1484)

Fluoride effects on ectopic bone formation in young and old rats

This study evaluated the effect of fluoride oil bone fluoride levels and on ectopic bone formation in young and old rats. Eighty male Wistar rats were assigned to four groups (n = 20/g), which differed according to the fluoride concentration in their drinking water (0, 5, 15 and 50 mg/l). When half of the rats were 90 days old, demineralized bone matrix (DBM) was implanted. The other rats received DBM implants when they were 365 day`s old. The animals were killed 28 days after. Fluoride in the femur surface, whole femur and plasma was analyzed with an electrode, The implants were analyzed histomorphometrically. Data were tested for statistically, significant differences by ANOVA, Tukey`s test, t-test and linear regression (p < 0.05). Increases in plasma, femur surface and whole femur fluoride concentrations were observed cis water fluoride levels increased. There was also a trend for increase in plasina and femur fluoride concentrations cis age increased. Significant positive correlations were found between plasma and femur surface, plasina and femur and femur surface and femur fluoride, concentrations. The morphometric analyses indicated all increase in bone formation for younger rats that received 5 mg/l of fluoride in the drinking water. However, this was not statistically, significant. The younger rats that received 50 mg/l of fluoride showed impairment in bone formation. Bone formation was not significantly affected among the older rats. The results suggest that lower doses of fluoride in the drinking water, which slightly increase plasma fluoride levels, may have an anabolic effect oil bone formation in younger rats. Copyright 2008 Prous Science, S.A.U. or its licensors. All rights reserved.

Healing of critical-size cranial defects in guinea pigs using a bovine bone-derived resorbable membrane

Purpose: To investigate the healing of critical-size cranial bone defects (9-mm-diameter) in guinea pigs treated with a bovine bone-derived resorbable membrane. Materials and Methods: A sample of 42 guinea pigs was divided into test (n = 20), control (n = 20), and standard (n = 2) groups. A full-thickness trephine defect was made in the fronto-parietal bone of each animal. In the test group, the internal and external openings of the defect were each closed with a separate membrane, and the space between them was filled with blood clot and a central spacer. In the control group, the defect was filled only with the blood clot and spacer. At 1, 3, 6, and 9 months later, the calvarias (5 per period) for both the test and control groups were collected, fixed, radiographed, and histologically processed. The Standard-group animals were sacrificed immediately after surgery and used to determine the initial size of defect radiographically. The areas of defects in the radiographs were measured with image-analysis software and were compared between groups and periods by multiple regression analysis with the Bonferroni correction. Results: At 1 and 3 months, newly formed woven bone was histologically observed in both test and control groups. Radiographically, this new bone occupied an average of 32% of the defect area at 1 month and 60% at 3 months in the test group. In the control group, 21% of the defect was filled at 1 month and 39% at 3 months. However, the differences between treatments were not statistically significant (P > .05). At 6 and 9 months, a significant increase in newly formed lamellar bone was seen histologically in both groups. Radiographically, for the test group, the new bone occupied an average of 82% of the defect area at 6 months and 96% at 9 months. For the control group, new bone composed an average of 45% of the defect area at 6 months and 40% at 9 months. The differences between the test and control groups were statistically significant at 6 and 9 months (P < .05). Complete or almost complete filling of the defect was observed in several cases. Conclusion: It was concluded that the bovine bone-derived membrane is highly biocompatible and is able to promote good healing of critical-size defects in calvaria of guinea pig.

Influence of nicotine on healing process of autogenous bone block grafts in the mandible: A histomorphometric study in rats

Purpose: The aim of this study was to perform qualitative and quantitative analyses of the effect of nicotine on autogenous bone block grafts and to describe events in the initial healing phase and the differences in the repair processes between animals exposed to nicotine and controls. Materials and Methods: Forty-eight female Wistar rats were randomly divided into 2 groups, the nicotine group and the saline group. All animals received either nicotine (3 mg/kg) or saline 4 weeks before the surgical procedure and continued to receive nicotine from surgery to sacrifice at 7, 14, or 28 days. The autogenous bone block graft was harvested from the calvaria and stabilized on the external cortical area near the angle of the mandible. Results: The histologic analyses of the nicotine group depicted a delay in osteogenic activity at the bed-graft interface, as well as impairment of the organization of the granulation tissue that developed instead of blood clot. Nicotine-group specimens exhibited less bone neoformation, and the newly formed bone was poorly cellularized and vascularized. The histometric analysis revealed significantly less bone formation in the nicotine group at both 14 days (23.75% +/- 6.18% versus 51.31% +/- 8.31%) and 28 days (42.44% +/- 8.70% versus 73.00% +/- 4.99%). Conclusion: Nicotine did jeopardize the early healing process of autogenous bone block grafts in rats but did not prevent it.

Kinetics of fluoride removal from plasma and bone of rats after chronic intake of fluoride

This study evaluated the kinetics of fluoride in plasma, femur surface and the whole femur of rats, after chronic exposure to different water fluoride levels was interrupted. Four groups of Wistar rats received drinking water containing 0, 5, 15 or 50 mu g F/ml for 60 days (n = 50/group). The animals were euthanized immediately after exposure to fluoride or after 7, 30, 90 or 180 days (n = 10/subgroup). Plasma and femurs were collected. Fluoride on the femur surface, whole femur and plasma was analyzed with an electrode. Data were analyzed using ANOVA and Tukey`s test (p < 0.05). The increase in plasma fluoride levels was significant only for the 50 mu g F/ml group at 0 and 7 days. Regarding bone surface and whole bone, for most groups, significant increases in fluoride concentrations were observed with the increase in water fluoride concentrations at each time of euthanasia. For fluoride doses up to 15 mu g F/ml, femur surface fluoride levels were reestablished 180 days after the exposure was discontinued, which Was not valid for whole femur or for higher fluoride doses. We found a different kinetics of fluoride in plasma,femur surface and the whole femur of rats after chronic exposure to fluoride is interrupted. Copyright 2008 Prous Science, S.A.U. or its licensors. All rights reserved.

Compromised Bond Strength after Root Dentin Deproteinization Reversed with Ascorbic Acid

Introduction: The present study evaluated the effect of a reducing agent on the bond strength of deproteinized root canal dentin surfaces when using a self-adhesive versus dual-cured cement. Regional differences were also evaluated. Methods: A total of 45 bovine incisor roots were divided into 3 groups: irrigation with physiologic solution (control), 10-minute deproteinization with 5% NaOCl, and 10-minute deproteinization with 5% NaOCl followed by 10 minutes of 10% ascorbic acid. Fiber posts were cemented with either RelyX 0100 or RelyX ARC (with SingleBond 2 or Clearfil SE Bond). The push-out bond strength was evaluated after 24 hours of storage. Data were submitted to three-way analyses of variance and Dunnett 13 tests (alpha = 0.05). Results: No differences between cements were observed within the testing conditions, regardless of the adhesive (P < .05). Deproteinization reduced bond strengths. Subsequent treatment with ascorbic acid was capable of reversing bond strength value changes to levels similar to those of controls. Regional radicular differences were also found, where coronal > middle > apical. Conclusions: The reducing agent was capable. of reversing the effect of dentin deproteinization, and RelyX U100 behaved similarly to RelyX ARC. (J Endod 2010;36:130-134)

The influence of cone-beam computed tomography and periapical radiographic evaluation on the assessment of periapical bone destruction in dog`s teeth

Objective. The aim of this study was to determine the influence of periapical radiographs, cone beam computed tomography (CBCT) sections, and cone beam volumetric data on the determination of periapical bone destruction in endodontically treated distal root canals of premolar canine teeth. Nontreated mesial roots were used as controls. Study design. Enterococcus faecalis strain (ATCC 29212) was inoculated into 30 root canals of 2 mongrel dogs to induce apical periodontitis. After 60 days, the root canals of the distal roots of the 11 mandibular and 4 maxillary premolars were endodontically treated (n = 15). The mesial root canals were used as controls (no treatment). The bone destruction was evaluated after 6 months by 5 evaluators using periapical radiographs and by CBCT (coronal and sagittal sections). After the experimental period, the area of the lesions in periapical radiographs and CBCT sections were measured in mm(2) using the ImageTool software. A single evaluator measured the volumetric data using the OsiriX software. The comparison between the diagnosis methods in treated root canals and controls was performed using parametric and nonparametric criteria. The Pearson correlation coefficient was computed between radiographic values and CBCT volumetric data in treated root canals and controls. Results. The results showed the presence of chronic apical periodontitis in every inoculated tooth. After 6 months, periapical radiographs, coronal CBCT sections, and volumetric data showed lower bone destruction in endodontically treated teeth in comparison with the control group (P < .05). The 5 evaluators found no differences between the apical periodontitis area of treated teeth and controls when CBCT sagittal sections were used (P > .05). No correlation was found between x-ray and CBCT volumetric values in treated root canals. Conclusions. Although selected CBCT sagittal sections showed similar values of bone destruction in endodontically and nontreated root canals, volumetric CBCT data showed that periapical lesions of endodontically treated root canals had half of the volume of periapical lesions in nontreated root canals. No relationship could be found between the periapical values of bone destruction and volumetric data found in CBCT of treated rood canals. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011; 112: 272-279)

Influence of glutaraldehyde priming on bond strength of an experimental adhesive system applied to wet and dry dentine

Objectives: This study tested the following null hypotheses: (1) there is no difference in resin-dentine bond strength when an experimental glutaraldehyde primer solution is added prior to bonding procedures and (2) there is no difference in resin-dentine bond strength when experimental glutaraldehyde/adhesive system is applied under dry or wet demineralized dentine conditions. Methods: Extracted human maxillary third molars were selected. Flat, mid-coronal dentine was exposed for bonding and four groups were formed. Two groups were designated for the dry and two for the wet dentine technique: DRY: (1) Group GD: acid etching + glutaraldehyde primer (primer A) + HEMA/ethanol primer (primer B)-under dried dentine + unfilled resin; (2) Group D: the same as GD, except for primer A application; WET: (3) Group GW: the same as GD, but primer B was applied under wet dentine condition; (4) Group W: the same as GW, except for primer A application. The bonding resin was light-cured and a resin core was built up on the adhesive layer. Teeth were then prepared for microtensile bond testing to evaluate bond strength. The data obtained were submitted to ANOVA and Tukey`s test (alpha = 0.05). Results: Glutaraldehyde primer application significantly improved resin-dentine bond strength. No significant difference was observed when the same experimental adhesive system was applied under either dry or wet dentine conditions. These results allow the first null hypothesis to be rejected and the second to be accepted. Conclusion: Glutaraldehyde may affect demineralized dentine properties leading to improved resin bonding to wet and dry substrates. (C) 2008 Elsevier Ltd. All rights reserved.

Effect of different surface treatments on the repair bond strength of indirect composites

Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surface treatments and direct composites. Methods: 180 specimens were prepared with Targis, belleGlass HP and Sculpture indirect composites, light-activated and post-cured according to the manufacturers` recommendations. The specimens were stored in distilled water for 24 hours at 37 degrees C. The bonding surfaces were prepared with air abrasion, hydrofluoric acid or hydrofluoric acid followed by a neutralizing solution. All the treated surfaces were subject to the application of a silane and a bonding agent before the repair procedures with Tetric Ceram and Tetric Flow for the Targis specimens, Herculite XRV and Revolution for the belleGlass HP specimens and Sculp-It and Flow-It for Sculpture specimens. The tensile bond strength tests were carried out using a universal testing machine at cross-head speed of 0.5 mm/minute. The type of fracture was observed under a light microscope at x40 magnification. Data were analyzed by a two-way ANOVA and Tukey`s post-hoc tests (P<0.05). Results: Targis showed a statistically higher repair bond strength than belleGlass HP and Sculpture, which were not significantly different from each other. Air abrasion increased the repair bond strength of belleGlass HP and Sculpture. For Targis, all the surface treatments resulted in similar repair bond strength. The different viscosity of repair composites did not affect the repair of indirect composites. Fractured surfaces showed mostly adhesive failures, mainly with hydrofluoric acid treatment.

Influence of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and bond strength

Statement of the Problem: Adhesive systems can spread differently onto a substrate and, consequently, influence bonding. Purpose: The purpose of this study was to evaluate the effect of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and microtensile bond strength (MTBS). Materials and Methods: Twenty-four molars were sectioned mesiodistally to expose flat buccal and lingual halves. Standardized drop volumes of adhesive systems (Single Bond [SB] and Prime & Bond 2.1 [PB2.1]) were applied to dentin according to the manufacturer`s instructions. Teeth halves were randomly divided into groups: 1A-SB/parallel to gravity; 1B-SB/perpendicular to gravity; 2A-PB2.1/parallel to gravity; and 2B-PB2.1/perpendicular to gravity. The bonded assemblies were stored in 37 degrees C distilled water for 24 hours and then sectioned to obtain dentin sticks (0.8 mm(2)). The adhesive layer thickness was determined in a light microscope (x200), and after 48 hours the specimens were subjected to MTBS test. Data were analyzed by one-way and two-way analysis of variance and Student-Newman-Keuls tests. Results: Mean values (MPa +/- SD) of MTBS were: 39.1 +/- 12.9 (1A); 32.9 +/- 12.4 (1B); 52.9 +/- 15.2 (2A); and 52.3 +/- 16.5 (2B). The adhesive systems` thicknesses (mu m +/- SD) were: 11.2 +/- 2.9 (1A); 18.1 +/- 7.3 (1B); 4.2 +/- 1.8 (2A); and 3.9 +/- 1.3 (2B). No correlation between bond strength and adhesive layer thickness for both SB and PB2.1 (r = -0.224, p = 0.112 and r = 0.099, p = 0.491, respectively) was observed. Conclusions: The differently oriented dentin surfaces and the regional variation of specimens on the adhesive layer thickness are material-dependent. These variables do not influence the adhesive systems` bond strength to dentin. CLINICAL SIGNIFICANCE Adhesive systems have different viscosities and spread differently onto a substrate, influencing the bond strength and also the adhesive layer thickness. Adhesive thickness does not influence dentin bond strength, but it may impair adequate solvent evaporation, polymer conversion, and may also determine water sorption and adhesive degradation over time. In the literature, many studies have shown that the adhesive layer is a permeable membrane and can fail over timebecause ofits continuous plasticizing and degradation when in contact with water. Therefore, avoiding thick adhesive layers may minimize these problems and provide long-term success for adhesive restorations.

Enamel Wetness Effects on Bond Strength Using Different Adhesive Systems

Objective: To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. Methods: This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive systems (Clearfil SE Bond; and Xeno IV). Flat bovine enamel surfaces were either air-dried for 30 seconds or blotted with absorbent paper after acid-etching for the conventional bonding agents or before the application of self-etching bonding agents. The resin composite EsthetX was bonded to flat surfaces that had been treated with one of the adhesives, following the manufacturer`s instructions. After being stored in water at 37 degrees C for one week, bonded specimens were broken in shear. Data were evaluated with two-way analysis of variance (ANOVA) and Student-Newman-Keuls tests (alpha=0.05). For comparing each condition individually, regardless of the adhesive or wetness condition, a one-way ANOVA and a Student-Newman-Keuls test (alpha=0.05) were applied. Results: The two-way ANOVA showed significant differences among adhesive systems. An interaction effect was also observed (p < 0.05), but wetness did not influence shear bond strength (p=0.98). The one-way ANOVA showed that the all-in-one adhesive was the only material influenced by the presence of water at the enamel`s surface. Conclusion: The all-in-one adhesive behaved differently depending on whether the enamel surface was dry or wet.