The effect of long-term disinfection procedures on hardness property of resin denture teeth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Flexural strength of acrylic resin repairs processed by different methods: water bath, microwave energy and chemical polymerization

Denture fractures are common in daily practice, causing inconvenience to the patient and to the dentists. Denture repairs should have adequate strength, dimensional stability and color match, and should be easily and quickly performed as well as relatively inexpensive. Objective: The aim of this study was to evaluate the flexural strength of acrylic resin repairs processed by different methods: warm water-bath, microwave energy, and chemical polymerization. Material and methods: Sixty rectangular specimens (31x10x2.5 mm) were made with warm water-bath acrylic resin (Lucitone 550) and grouped (15 specimens per group) according to the resin type used to make repair procedure: 1) specimens of warm water-bath resin (Lucitone 550) without repair (control group); 2) specimens of warm water-bath resin repaired with warm water-bath; 3) specimens of warm water-bath resin repaired with microwave resin (Acron MC); 4) specimens of warm water-bath resin repaired with autopolymerized acrylic resin (Simplex). Flexural strength was measured with the three-point bending in a universal testing machine (MTS 810 Material Test System) with load cell of 100 kgf under constant speed of 5 mm/min. Data were analyzed statistically by Kruskal-Wallis test (p<0.05). Results: The control group showed the best result (156.04 +/- 1.82 MPa). Significant differences were found among repaired specimens and the results were decreasing as follows: group 3 (43.02 +/- 2.25 MPa), group 2 (36.21 +/- 1.20 MPa) and group 4 (6.74 +/- 0.85 MPa). Conclusion: All repaired specimens demonstrated lower flexural strength than the control group. Repairs with autopolymerized acrylic resin showed the lowest flexural strength.

Measurement of Interfacial Porosity at the Acrylic Resin/Denture Tooth Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of water storage on the shear strength and fatigue limit of the reline resin bond to denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of an acrylic resin combined with an antimicrobial polymer on biofilm formation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of Candida albicans adhesion and biofilm formation on a denture base acrylic resin containing silver nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efficacy of Air-abrasion Technique and Additional Surface Treatment at Titanium/Resin Cement Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling.Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05).Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps.Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

Effect of incorporation of 2-tert-butylaminoethyl methacrylate on flexural strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Adhesive Bonding of Resin Composite to Various Ni-Cr Alloy Surfaces Using Different Metal Conditioners and a Surface Modification System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Assessing the surface roughness of a posterior resin composite: effect of surface sealing

This study assessed the in vitro influence of surface sealing on the surface roughness of a posterior resin composite before and after tooth-brushing. Thirty. specimens (13 nun diameter x 1 mm high) were fabricated from Filtek-P60 resin composite and randomly assigned to three groups (n=10): a non-sealed control and two groups sealed with one of the tested materials-a surface-penetrating sealant (Protect-it!-PI) and a one bottle adhesive system (Single Bond-SB). The samples were subjected to a surface roughness reading to determine the initial roughness, then submitted to simulated toothbrushing with 35,600 cycles for 100 minutes. Specimens were then cleaned and a post-abrasion surface roughness reading accomplished. Means (pm), recorded before (B) and after (A) toothbrushing, and standard deviations were: Control-(B): 0.032 (+/-0.005), (A): 0.054 (+/-0.005); PI-(B): 0.034 (+/-0.005), (A): 0.060 (+/-0.034); SB (B): 0.031 (+/-0.004), (A): 0.047 (+/-0.007). Data were tabulated and submitted to two-way ANOVA. No statistically significant difference was observed when the control and experimental groups were compared. However, a significant difference (p<0.05) was found between the measurements performed before and after toothbrushing. Based on these results, it may be concluded that using either a surface penetrating sealant or a one bottle adhesive system did not provide the optimization of superficial integrity. The use of a dentifrice and toothbrush resulted in significant alterations to the surface smoothness of the resin composite.

Analysis of surface roughness of glass-ionomer cements and compomer

The purpose of this study was to evaluate the surface roughness of two glass-ionomer cements (Vitremer and Chelon-Fil), and one compomer (Dyract) when submitted to different finishing/polishing procedures at different times. A hundred 80-sample discs were made of each material and randomly divided into six finishing/polishing groups: mylar strip (control); Sof-Lex discs; diamond burs; diamond burs/Sof-Lex discs; 30-fluted carbide bur; 30-fluted carbide bur/Sof-Lex discs. These procedures were carried out immediately after preparation of the samples, after 24 and 168 h. Average surface roughness (Ra) was measured with a profilometer and the values were compared using anova (P < 0.05). The smoothest surface for all materials was obtained when cured in contact with the mylar strip. All other tested products increased surface roughness of restorative materials, but Sof-lex discs lead to better results. The worst results were verified with diamond burs. The finishing/polishing procedures, when performed immediately, can improve the roughness of glass-ionomer cements but not of the compomer tested.

Deposition of Lead and Cadmium Released by Cigarette Smoke in Dental Structures and Resin Composite

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)