Synthesis and electrical characterization of tungsten doped Pb(Zr0.53Ti0.47)O-3 ceramics obtained from a hybrid process

Pure and W-doped PZT ceramics (PZT and PZTW) were prepared by a hybrid process consisting in the association of polymeric precursor and partial oxalate methods. The phase formation was investigated by simultaneous thermal analysis (TG/DSC) and X-ray diffraction (XRD). The effect of W doping PZT and their electrical properties was evaluated. Substitution of W by Ti leads to an increase of Curie temperature and broadening of dielectric constant. A typical hysteresis loop was observed at room temperature and the remnant polarization was increased with the content of W. (c) 2007 Elsevier B.V. All rights reserved.

Spectroscopic and thermal characterization in poly(p-phenylene vinylene)/sol-gel silica sample

The absorption and luminescence spectra for the poly(p-phenylene vinylene)/sol-gel silica with different thermal treatments were measured. A considerable increase in the luminescence was observed for the polymer introduced into SiO2 matrix with thermal treatment at 120 degreesC. The thermal diffusivity of these samples was measured using the thermal lens technique, and the obtained value 3.3 x 10(-5) cm(2)/s (sample treated at 37 degreesC) is practically independent of the thermal treatment (37-150 degreesC). (C) 2003 Elsevier B.V. All rights reserved.

Electrical characterization of in situ polymerized polyaniline thin films

The alternating conductivity, sigma*(f) = sigma'(f) + i sigma ''(f), of in situ polymerized polyaniline thin films doped with hydrochloric acid, deposited on top of an interdigitated gold line array previously deposited on glass substrates, were measured in the frequency (f) range between 0.1 Hz to 10 MHz and in the temperature range from 100 to 430 K. The results for sigma'(f) are typical of a disordered solid material: for frequencies lower than a certain hopping frequency gamma(hop), log[sigma'(f)] is frequency-independent rising almost linearly for in logf > gamma(hop). A master curve was thus obtained by plotting the real component of the conductivity using normalized scales sigma'(f)/sigma(dc) and f/gamma(hop) which is indicative of a single process operating in the whole frequency range. An expression encompassing the conduction through a disordered structure taken from previous random free energy barrier model for hopping carriers, as well a dielectric function to represent the capacitive behavior of the PAni was employed to fit the experimental results. The dielectric constant and activation energy for hopping carriers were obtained as function of the polymer doping level. (c) 2007 Elsevier B.V. All rights reserved.

Structural and phenomenological characterization of the thermoreversible sol-gel transition of a zirconyl aqueous precursor modified by sulfuric acid

The thermoreversible sol-gel transition is well-known in biological and organic polymeric systems but has not been reported for inorganic systems. In this paper we put in evidence a thermoreversible sol-gel transition for zirconyl chloride aqueous solutions modified by sulfuric acid in the ratio 3:1 Zr:SO4. The synthesis conditions are detailed and a variety of experimental techniques (turbidimetry, dynamic rheology, and EXAFS) have been employed for investigating the thermal reversibility and the chemical structure of this new material. Turbidimetric measurements performed for solutions containing different concentrations of precursor have evidenced that the sol-gel transformation temperature increases from 50 to 80 degrees C as the concentration of zirconyl chloride decreases from 0.22 to 0.018 mol L-1. A more detailed study has been done for the sample with [Zr] = 0.156 mol L-1, in which the sol-gel-sol transformation has been repeated several times by a cyclic variation of the temperature. The mechanical properties of this sample, evaluated by measuring the storage and the loss moduli, show a change from liquid like to viscoelastic to elastic behavior during the sol-gel transition and vice versa during the gel-sol one. In situ EXAFS measurements performed at the Zr K-edge show that no change of the local order around Zr occurs during the sol-gel-sol transition, in agreement with the concept of physical gel formation. We have proposed for the structure of the precursor an inner core made of hydroxyl and oxo groups bridging together zirconium atoms surrounded in surface by complexing sulfate ligands, the sulfate groups act as a protective layer, playing a key role in the linking propagation among primary particles during sol-gel-sol transition.

Synthesis and characterization of 9.5/65/35 PLZT prepared from the polymeric precursors

The 9.5/65/35 PLZT was prepared from the polymeric precursors (the Pechini and partial oxalate process) and by sintering in two stages in an oxygen atmosphere. After thermal treatment at 400 degreesC, the powders were calcinated and sintered at 1200 degreesC with slow heating and cooling rates. The second stage of sintering consisted of hot pressing at the same temperature in oxygen atmosphere. After calcination of PLZT powders obtained by both methods, as well as after sintering of PLZT obtained by Pechini process, the paraelectric cubic phase was formed. After sintering of PLZT obtained by partial oxalate procedure, small tetragonality of crystal structure was observed. After hot pressing PLZT was pseudocubic. SEM microstructural analyses were carried out of the sintering and hot pressed samples and indicated the small grain size less than 2 mum. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Structural characterization of blends containing both PVDF and natural rubber latex

Films containing different volumes of latex of natural rubber (NR) in a fixed mass of poly (vinylidene fluoride) (PVDF) powder were fabricated by compressing under annealing a mixture of both materials without using any solvent. This is an important issue keeping in mind that these films have to be used in the future as biomaterials in different applications once the solvents that are used to dissolve the PVDF become toxic to human. The films with different percentage of latex in PVDF were characterized using microRaman scattering and Fourier transform infrared absorption (FTIR) spectroscopies, thermomechanical techniques using thermogravimetry (TG), differential scanning calorimetry (DSC), dynamical-mechanical analysis (DMA) and scanning electron microscopy (SEM). The results showed that the latex of NR and PVDF do not interact chemically, leading to the formation of a polymeric blend with high thermal stability and mechanical properties suitable for applications involving bone (prostheses, for instance). Besides, the results recorded using the micro-Raman technique revealed that for a fixed amount of PVDF the higher the amount of latex in the blend, the better the miscibility between both materials. Copyright (c) 2005 John Wiley & Sons, Ltd.

Electrochemical impedance spectroscopy characterization of passive film formed on implant Ti-6Al-7Nb alloy in Hank's solution

The influence of potential on electrochemical behavior of Ti-6Al-7Nb alloy under simulate physiological conditions was investigated by electrochemical impedance spectroscopy (EIS). The experimental results were compared with those obtained by potentiodynamic polarization curves. All measurements were carried out in Hank's aerated solution at 25degreesC, at pH 7.8 and at different potentials (corrosion potential, 0 mV(SCE), 1000 mV(SCE), and 2000 mV(SCE)). The EIS spectra exhibited a two-step or a two-time constant system, suggesting the formation of a two-layer oxide film on the metal surface. The high corrosion resistance, displayed by this alloy in electrochemical polarization tests, is due to the dense inner layer, while its osseointegration ability can be ascribed to the presence of the outer porous layer. (C) 2004 Kluwer Academic Publishers.

Synthesis, characterization and electrochemical study of layered double hydroxides intercalated with 2-thiophenecarboxylate anions

The synthesis, characterization, and electrochemical study of the Zn(II)-Al(III) and Zn(II)-Cr(III) Layered Double Hydroxides (LDHs) containing 2-thiopenecarboxylate as the interlayer anions are described. The LDHs were prepared by the constant pH coprecipitation technique followed by hydrothermal treatment for 72 h. The materials were analyzed by PXRD, FT-IR, C-13 CP-MAS, EDX, TEM, and CV. The presence of the organic heterocyclic anions was confirmed by FT-IR and the related solid-state C-13 NMR data strongly suggested that these were dimerised during coprecipitation. Accordingly, the basal spacing found by the X-ray technique was similar to 15.3 Angstrom, a distance coincident with the formation of bilayers of the intercalated anions. The structural organization of all the new materials was greatly enhanced by hydrothermal treatment, as shown by PXRD. The improved organization of the bilayered structures had a strong influence in the electrochemical behaviour of clay-modified electrodes produced with these materials, such as the diminished resistance to the ionic flow through the LDHs films. (C) 2003 Elsevier Ltd. All rights reserved.

Synthesis and electrical characterization of CaBi2Nb2O9 thin films deposited on Pt/Ti/SiO2/Si substrates by polymeric precursor method

We report the successful deposition of CaBi2Nb2O9 (CBN) thin films on platinum coated silicon substrates by polymeric precursor method. The CBN thin films exhibited good structural, dielectric and CBN/Pt interface characteristics. The leakage current of the capacitor structure was around 0.15 A cm(-2) at an applied electric field of 30 kV cm(-1). The capacitance-voltage measurements indicated good ferroelectric polarization switching characteristics. The typical measured small signal dielectric constant and the dissipation factor at a frequency of 100 kHz were 90 and 0.053, respectively. The remanent polarization and the drive voltage values were 4.2 C cm(-2) and 1.7 V at an applied voltage of 10 V. No significant fatigue was observed at least up to 10(8) switching cycles. (c) 2005 Elsevier B.V. All rights reserved.

Development of Ti-Mo alloys for biomedical applications: Microstructure and electrochemical characterization

Ti-Mo alloys from 4 to 20 Mo wt.% were arc-melted. Their compositions and surfaces were analyzed by EDX, XRF and SEM. The Mo mapping shows a homogeneous distribution for all alloys. The XRD analysis showed that the crystal structure of the alloys is sensitive to the Mo concentration; a mixture of the hexagonal alpha' and orthorhombic alpha '' phases was observed for the Ti-4Mo alloy, and the alpha '' phase is observed almost exclusively when the concentration of Mo added to the Ti reaches 6%. A significant retention of the beta phase is observed for the alloy containing 10% Mo, while at higher Mo concentrations (15% and 20%), retention of phase beta is only verified. Preliminary electrochemical studies have indicated a valve-metal behavior and good corrosion resistance in aerated Ringer solution for all alloys. (c) 2006 Published by Elsevier B.V.

Characterization of an all sol-gel electrochromic device WO3/Ormolyte/CeO2-TiO2

Electrochemical lithium intercalation in thin films of CeO2-TiO2 and WO3, prepared by the sol-gel technique was investigated with cyclic voltammetry and spectroelectrochemical techniques in propylene carbonate solutions. A solid state system having the configuration WO3/Ormolyte/CeO2-TiO2 has been assembled. The solid electrolyte, an organically modified electrolyte (ormolyte), was prepared with different [O]/[Li] ratios. The transmittance variation of this system during a potentiostatic step from -0.7 V to 0.8 V was about 35% at 550 nm.

Preparation and characterization of erbium and ytterbium co-doped sol-gel SiO2 : HfO2 films for planar waveguides

This work reports on the preparation of erbium and ytterbium co-doped SiO2:HfO2 single mode planar waveguides using the sol-gel method. Silica nanoparticles were prepared from tetraethylorthosilicate in basic media and the films were characterized by transmission electron microscopy, scanning electron microscopy, mechanical profilometry, M-lines spectroscopy based on prism coupling technique, X-ray diffractometry, infrared spectroscopy and photoluminescence spectroscopy. The film thicknesses and the refractive indexes were adjusted in order to satisfy a future efficient coupling to single mode optical fiber. Films suitable for both weak and strong light confinement were prepared varying hafnia concentration into the silica matrix. The lifetime values of erbium I-4(13/2) state were measured in order to investigate the influence of clustering and hydroxyl groups on the fluorescence quantum efficiency of the I-4(13/2) level, responsible for the emission at 1.55 mu m attributed to the I-4(13/2) -> I-4(15/2) transition. The high lifetime values suggest the absence of erbium clusters and the elimination of hydroxyl groups by rapid thermal process. (c) 2007 Elsevier B.V. All rights reserved.

Preparation and characterization of nanosized SrBi2Nb2O9 powder by the combustion synthesis

This work presents the preparation of SrBi2Nb2O9 (SBN) directly by the combustion synthesis. Strontium nitrate, niobium ammonium oxalate (NH4H2[NbO-(C2O4)(3)].3H(2)O) and bismuth oxide were used as oxidant reactants and urea as fuel. The influence of the fuel was evaluated by the addition of different fuel amounts (50%, 100%, 200% and 300%), 100% being the stoichiometric proportion. The XRD patterns showed that the SBN perovskite crystallized as the majority phase. The as-synthesized stoichiometric powder presented a specific surface area of around 13 m(2)/g and a mean grain size of around 16 nm. Dilatometric measurements showed that the maximum sintering rate occurs at 1275degreesC. The determination of the ferroparaelectric transition showed a Curie temperature (T-c) of 429degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Microstructural and optical characterization of CaWO4 and SrWO4 thin films prepared by a chemical solution method

Stoichiometric CaWO4 and SrWO4 thin films were synthesized using a chemical solution processing, the so-called polymeric precursor method. In this soft chemical method, soluble precursors such as strontium carbonate, calcium carbonate and tungstic acid, as starting materials, were mixed in an aqueous solution. The thin films were deposited on glass substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Nucleation stages and surface morphology evolution of the thin films on glass substrates were studied by atomic force microscopy. The films nucleate at 300 degreesC, after the coalescence of small nuclei into larger grains yielding a homogeneous dense surface. XRD characterization of these films showed that the CaWO4 and SrWO4 phases crystallize at 400 degreesC from an inorganic amorphous phase. No intermediate crystalline phase was identified. The optical properties were also studied. It was found that CaWO4 and SrWO4 thin films have an optical band gap, E-gap=5.27 and 5.78 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity confirmed that this soft solution processing provides an inexpensive and environmentally friendly route for the preparation of CaWO4 and SrWO4 thin films. (C) 2003 Elsevier B.V. All rights reserved.

Pyrosol preparation and structural characterization of SnO2 thin films

Polycrystalline tin oxide thin films were prepared from ethanol solution of SnCl2.H2O (concentrations: 0.05, 0.1, 0.2 and 0.4 mol/dm(3)) at different substrate temperatures ranging from 300 to 450 degreesC. The kinetic deposition processes were studied in terms of various process parameters. The crystal phases, crystalline structure, grain size and surface morphology are revealed in accordance to X-ray diffractometry and scanning electron microscopy (SEM). Texture coefficients (TCs) for (110), (2 0 0), (2 11) and (3 0 1) reflections of the tetragonal SnO2 were calculated. Structural characteristics of deposited films with respect to varying precursor chemistry and substrate temperature are presented and discussed. (C) 2003 Published by Elsevier B.V.