Barium titanate screen-printed thick films

Barium titanate (BT) thick films were prepared from mechanically activated powders based on BaCO(3) and TiO(2). After homogenization and milling in a high-energy vibro mill, the powders were calcined at 700 degreesC for 2 h by slow heating and cooling rates. A thick film paste was prepared by mixing BT fine powders with small amount of low temperature sintering aid and organic binder. The thick films were screen-printed on alumina substrates electroded with Ag-Pd. The BT films were sintered at 850 degreesC for 1 h. The thickness was 25-75 mum depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate were investigated by SEM Results of dielectric property measurements are also reported. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Strontium titanate films prepared by spray pyrolysis

Strontium titanate thin films were prepared by spray pyrolysis technique. Deposition parameters, such as solution concentration, time and temperature of deposition, and flow rate of carrier gas were optimized to obtain dense films without cracks. Films with different thicknesses were prepared through the control of deposition time. Prepared thin films were homogeneous, well crystallized, with uniform grain size. (C) 2003 Elsevier Ltd. All rights reserved.

Low temperature synthesis and electrical properties of PbTiO3 thin films prepared by the polymeric precursor method

Ferroelectric PbTiO3 thin films were successfully prepared on a Pt(111)Ti/SiO2/Si(100) substrate for the first time by spin coating, using the polymeric precursor method. X-ray diffraction patterns of the films indicate that they are polycrystalline in nature. This method allows low temperature (500 degrees C) synthesis and high electrical properties. The multilayer PbTiO3 thin films were granular in structure with a grain size of approximately 110-120 nm. A 380-nm-thick film was obtained by carrying out four cycles of the spin-coating/heating process. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness (=3.4 nm). At room temperature and at a frequency of 100 kHz, the dielectric constant and the dissipation factor were, respectively, 570 and 0.016. The C-V characteristics of perovskite thin film prepared at low temperature show normal ferrolectric behavior. The remanent polarization and coercive field for the films deposited were 13.62 mu C/cm(2) and 121.43 kV/cm, respectively. The high electrical property values are attributed to the excellent microstrutural quality and chemical homogeneity of thin films obtained by the polymeric precursor method. (C) 2000 Elsevier B.V. S.A. All rights reserved.

Evolution of CaCu3Ti4O12 varistor properties during heat treatment in vacuum

Calcium copper titanate (CaCu3Ti4O12) ceramic varistors were prepared by solid-state method. The samples were several times heat treated in vacuum and the evolution of electrical characteristics were monitored by current density versus electric field measurements and impedance spectroscopy. Repeated heat treatments in vacuum (900 degrees C for 1 h, 0.01 Torr) lead to a desorption of oxygen adsorbed at the grain boundaries and consequently to a degradation of the varistor properties. During further successive heat treatments some oxygen from the grain interior moves to the grain boundary thereby partially restoring the varistor properties. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Structural and ferroelectric properties of Pb1-xSrxTiO3 thin films

Strontium-modified lead titanate (PST) thin films with composition Pb1-xSrxTiO3 (0.10 < x &LE; 0.60) were grown on Pt/Ti/SiO2/Si substrates using a soft chemical process. The crystallization of the PST thin films was achieved by heat treatment at 600&DEG;C. The structural and microstructural modifications in the films were studied using X-ray diffraction (XRD) and atomic force microscopy, respectively. The XRD study shows that the lattice parameters of polycrystalline PST thin films calculated from X-ray data indicate a decrease in lattice tetragonality with the increase in strontium content in these films. This indicates a gradual change from tetragonal to cubic structure. By atomic force microscopy analysis, the average grain size of the thin films was systematically reduced with the increase in Sr content. The dielectric property of the thin films was found to be strongly dependent on the Sr concentration. With 60 at.% Sr content, a ferroelectric to paraelectric phase transition was observed at room temperature.

Ionic medium effects on equilibrium constants .1. Proton, copper(II), cadmium(II), lead(II) and acetate activity coefficients in aqueous solution

The molar single ion activity coefficients associated with hydrogen, copper(II), cadmium(II) and lead(II) ions were determined at 25 degrees C and ionic strengths between 0.100 and 3.00 M (NaClO4), whereas for acetate the ionic strengths were fixed between 0.300 and 2.00 M, held with the same inert electrolyte. The investigation was carried out potentiometrically by using proton-sensitive glass, copper, cadmium and lead ion-selective electrodes and a second-class Hg\Hg-2(CH3COO)(2) electrode. It was found that the activity coefficients of these ions (y(i)) can be assessed through the following empirical equations:log y(H) = -0.542I(0.5) + 0.451I; log y(Cu) = -1.249I(0.5) + 0.912I; log y(Cd) = -0.829I(0.5) + 0.448I(1.5);log y(Pb) = -0.404I(0.5) + 0.117I(2); and log y(Ac) = 0.0370I .

Effect of additives and powder preparation techniques on PTCR properties of barium titanate

PTCR barium titanate has been prepared following two different powder preparation techniques: the solid-state reaction route and co-precipitation route for the comparison of results. The co-precipitation route produces better PTCR characteristics with low room temperature resistivity and better reproducibility of prepared samples. The effects of different concentrations of additives like donors, acceptors and excess titanium have been optimized to get good quality PTCR samples. (C) 2002 Elsevier B.V. B.V. All rights reserved.

In vitro biocompatibility of poly(vinylidene fluoride-trifluoroethylene)/barium titanate composite using cultures of human periodontal ligament fibroblasts and keratinocytes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lead poisoning in cattle grazing pasture contaminated by industrial waste

Lead poisoning is described in a herd of 120 Nelore cows of which 35 were affected. All affected cows died after a clinical course of 2-7 d with clinical signs related to cortical neurological disturbances. The source of Pb was fumes from a car battery recycling plant which has had a failure in its filtering system. Lead concentrations in liver and kidneys of 2 cows, in soil;and in grass where the cows were held were respective 39 to 431 ppm, 147 to 431 ppm,and 245ppm. No significant gross changes were observed. Histopathology revealed of neuronal necrosis, vacuolation of the neuropil and hypertrophy of the vascular endothelium inthecerebral cortices, degeneration of the epithelial cellsofrenal proximal tubules, and hemosiderosis of kidney, spleen and liver.

Developmental lead exposure induces depressive-like behavior in female rats

The involvement of neurotoxicants in the etiology of emotional pathologies is becoming an issue in neurotoxicology. Lead (Pb) exposure during childhood has been associated with increased impulsivity, aggressivity, and delinquency. Considering the paucity of experimental studies investigating the involvement of developmental Pb exposure in emotional disorders, our objective was to investigate whether Pb exposure during pregnancy and/or lactation could be related to depressive symptoms in adult male and female rats. Wistar dams received 10 mg of Pb, as Pb acetate, or 13.4 mg of Na acetate, by gavage, daily, during pregnancy and lactation. By cross-fostering at the time of birth, pups were either exposed to Ph or Na acetate during pregnancy only, lactation only, or during both pregnancy and lactation. At 70 days of age, animals were submitted to the open-field test followed by the forced swimming test. Ph levels were measured in the blood of dams (weaning) and pups (after behavioral evaluation). The results demonstrated that exposure to Ph during both pregnancy and lactation induced, in males, an increased emotionality state detected in the open-field test, and in females, depressive-like behavior detected in the forced swimming test. These alterations were observed at residual blood Pb levels (i.e., around 5 mug/dL).

Influence of temperature on the dielectric and ferroelectric properties of bismuth titanate thin films obtained by the polymeric precursor method

The (1 1 7) and (0 0 1 0)-oriented Bi4Ti3O12 thin films were fabricated on Pt/Ti/SiO2/Si substrates by using a polymeric precursor solution under appropriate crystallization conditions. Atomic force microscopy and scanning electron microscopy showed relatively large grains, which is typical for this system. The capacitance dependence on voltage is strongly non-linear, confirming the ferroelectric properties of the films resulting from the domain switching. The (1 1 7)-oriented films exhibited a higher remanent polarization (23.7 μ C cm(-2)) than the (0 0 1 0)-oriented films (11.8 μ C cm(-2)). Fatigue tests revealed that the temperature of thermal treatment and degree of orientation affect the performance of the device. © 2005 Elsevier B.V. All rights reserved.

An insight into the theoretical investigation of possible piezoelectric effect in samarium titanate (SmTiO3)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.