Influence of spraying parameters on the electrochemical behaviour of HVOF thermally sprayed stainless steel coatings in 3.4% NaCl

Stainless steel coatings obtained by High Velocity Oxygen Fuel (HVOF) were characterized using optical (OM) and scanning electron microscopy (SEM), electron probe micro-analysis, X-ray diffraction (XRD), open-circuit potential (E-OC) measurements, electrochemical impedance spectroscopy (EIS) and polarisation tests. Differences among coated steels were mainly related with the gun-substrate distance parameter (310 nm for samples A and B and 260 min for C and D). The open-circuit potential values measured for all the samples after 18 h of immersion in aerated and unstirred 3.4% NaCl solution were: - 0.334, - 0.360, - 0.379 and - 0.412 V vs. Ag/AgCl,KClsat. for samples A to D, respectively. For EIS measurements, Nyquist plots showed higher capacitive semi-circle for samples sprayed at longer distance, indicating higher corrosion resistance in NaCl solution. (c) 2005 Elsevier B.V. All rights reserved.

Electrochemical behavior of thermally sprayed stainless steel coatings in 3.4% NaCl solution

Four types of stainless steel coatings prepared by a high velocity oxy-fuel spraying system (HVOF) were studied. Differences among coated steels were related to the spraying parameters, which influenced the behavior of the samples against the corrosion. The electrochemical behavior of the stainless steel coatings was strongly influenced by porosity, the presence of micro- and macro-cracks, and also of un-melted particles. Once the electrolyte reached the steel substrate via these defects, the galvanic pair formed between the coating and substrate-accelerated corrosion, leading to the depletion of the coating. (C) 2004 Elsevier Ltd. All rights reserved.

Effect of hydrogen charging on the stability of SAE 10B22 steel surface in alkaline solutions

The influence of hydrogen charging into a quenched and tempered boron steel membrane electrode (SAE 10B22) was studied using borate buffer (pH 8.4) and NaOH solutions (pH 12.7), with or without the addition of 0.01 M EDTA. At the hydrogen input side, hydrogen charging influenced cyclic voltammograms increasing the anodic charge of iron(II) hydroxide formation, and decreasing the donor density of passive films. These results suggest that the hydrogen ingress caused instability of metallic surface, increasing the surface area activity. (C) 2005 Elsevier Ltd. All rights reserved.

Austenite decomposition of C-Mn steel containing boron by continuous cooling

The austenite decomposition in C-Mn steel containing boron was studied by continuous cooling from 1100 and 845 degreesC using the Jominy test. The results indicate that the different cooling speeds and the presence of boron refine and change the percentage of ferrite microstructure, martensite, and fine pearlite. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrochemical study of TEOS, TEOS/MPTS, MPTS/MMA and TEOS/MPTS/MMA films on tin coated steel in 3.5% NaCl solution

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Photo-electrochemical investigation of anodic oxide films on cast Ti-Mo alloys I. Anodic behaviour and effect of alloy composition

The anodic behaviour of cast Ti-Mo alloys, having different Mo contents (6-20 wt.%), was investigated in acidic and neutral aerated aqueous solutions. All sample showed a valve-metal behaviour, owing to formation and thickening of barrier-type anodic oxides displaying interference colours Growth kinetics. of passive films is influenced by both anodizing electrolyte and composition of the starting alloy. This last parameter was found to change also the solid-state properties of the films, explored by photoelectrochemical and impedance spectroscopy experiments. Thicker films (U(f) = 8 V/MSE) grown on alloys richer in Mo showed more resistive character and a photocurrent sign inversion under negative bias, that revealed an insulating character, whereas corresponding films grown on alloys with lower Mo content, as well as thinner films, behaved as n-type semiconductors. Results are discussed in terms of formation of a mixed Ti-Mo oxide phase. (C) 2008 Elsevier Ltd. All rights reserved

Mini-implant and Nance button for initial retraction of maxillary canines: a prospective study in cast models

OBJETIVO: a ancoragem óssea é fundamental para o sucesso do tratamento de algumas más oclusões, pois permite a aplicação de forças contínuas, diminui o tempo de tratamento e independe da colaboração do paciente. MÉTODOS: o propósito desse trabalho foi comparar, por meio de modelos dentários, a perda de ancoragem após a retração inicial de caninos superiores entre dois grupos. O grupo A utilizou o mini-implante enquanto o grupo B utilizou o Botão de Nance. Para todos os pacientes foram realizados dois modelos (M1 e M2). Os primeiros modelos foram realizados ao início (M1), e os outros ao final da retração inicial de canino (M2). RESULTADOS: todas as medidas foram tabuladas e submetidas à análise estatística. Para verificar o erro sistemático intraexaminador foi utilizado o teste t pareado. Na determinação do erro casual utilizou-se o cálculo de erro proposto por Dahlberg. Para comparação entre as fases Início e Após, foi utilizado o teste t pareado. Para a comparação entre os grupos de mini-implante e Botão de Nance, foi utilizado o teste t de Student para medidas independentes. em todos os testes foi adotado nível de significância de 5% (p<0,05). CONCLUSÃO: ao se medir e comparar em modelos dentários a perda de ancoragem dos molares após a retração inicial de canino utilizando-se dois sistemas de ancoragem distintos (Mini-implante e Botão de Nance), pôde-se observar a inexistência de diferença estatisticamente significativa entre os dois grupos.

The influence of soil and landfill leachate microorganisms in the degradation of PVC/PCL films cast from DMF

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The use of ultrasound for cleaning the surface of stainless steel and nickel-titanium endodontic instruments

Aim the aim of this study was to evaluate the efficacy of ultrasound in cleaning the surface of stainless steel and Ni-Ti endodontic instruments.Methodology Twenty nickel-titanium instruments (10 Quantec files and 10 Nitiflex) and 20 stainless steel K-files (10 Maillefer-Dentsply and 10 Moyco Union Broach) were removed from their original packages and evaluated using a scanning electron microscope. Scores were given for the presence of residues on the surface or the instruments. The instruments were then cleaned in an ultrasonic bath containing only distilled water or detergent solution for 15 min, and re-evaluated, using scanning electron microscopy.Results Before cleaning, a greater amount of metallic debris was observed on the nickel-titanium Quantec instruments (P < 0.05), when compared to those made of stainless steel. Statistical analysis showed that the use of ultrasound was effective for cleaning the instruments, regardless of the irrigating solution or the instruments type (P < 0.05).Conclusions the use of ultrasound proved to be an efficient method for the removal of metallic particles from the surface of stainless steel and Ni-Ti endodontic instruments.

Plasma immersion ion implantation of nitrogen into H13 steel under moderate temperatures

Ion implantation of nitrogen into samples of tempered and quenched H13 steel was carried out by plasma immersion technique. A glow discharge plasma of nitrogen species was the ion source and the negative high voltage pulser provided 10-12 kV, 60 mu s duration and 1.0-2.0 kHz frequency, flat voltage pulses. The temperatures of the samples remained between 300 and 450 degrees C, sustained solely by the ion bombardment. In some of the discharges, we used a N-2 + H-2 gas mixture with 1:1 ratio. PIII treatments as long as 3, 6, 9 and up to 12 h were carried out to achieve as thickest treated layer as possible, and we were able to reach over 20 mu m treated layers, as a result of ion implantation and thermal (and possibly radiation enhanced) diffusion. The nitrogen depth profiles were obtained by GDOS (Glow Discharge Optical Spectroscopy) and the exact composition profiles by AES (Auger Electron Spectroscopy). The hardness of the treated surface was increased by more than 250%, reaching 18.8 GPa. No white layer was seen in this case. A hardness profile was obtained which corroborated a deep hardened layer, confirming the high efficacy of the moderate temperature PIII treatment of steels. (c) 2005 Elsevier B.V. All rights reserved.

Force-versus-time curves during collisions between two identical steel balls

We describe a numerical procedure for plotting the force-versus-time curves in elastic collisions between identical conducting balls. A system of parametric equations relating the force and the time to a dimensionless parameter is derived from the assumption of a force compatible with Hertz's theory of collision. A simple experimental arrangement consisting of a mechanical system of colliding balls and an electrical circuit containing a crystal oscillator and an electronic counter is used to measure the collision time as a function of the energy of impact. From the data we can determine the relevant parameters. The calculated results agree very well with the expected values and are consistent with the assumption that the collisions are elastic. (C) 2006 American Association of Physics Teachers.

Bactericidal stainless steel

Coatings are largely used in industries. However the development of new materials with improved properties still feeds a continuous need for performance, cost or endurance, the coatings are obtained by a hybrid material, organic-inorganic, and this polymer is applied on metallic, ceramic and glassy surfaces. The material generated in-situ on the desired surface has a nanometric structure. Results in abrasion loss (according ASTM standards) showed that the coatings improve the abrasion resistance of stainless steel by 30%, and also, diminish oxidization and surface rugosity.

Analyses of fatigue data in 4340 high strength steel after cadmium electroplating

Bending fatigue tests were carried out to clarify the effects of heat treatment parameters: temperature and time after cadmium electroplating on a high strength steel, to avoid hydrogen embrittlement. Temperatures heat of 190 degrees C, 230 degrees C, 250 degrees C and 300 degrees C at 3, 8 and 24 hours together with the base material electroplated, with and without heat treatment, resulted in 14 conditions studied with respect to fatigue behaviour. Statistical data analysis was performed to identify the best combination temperature/time regarding fatigue strength of the ABNT 4340 steel and the results obtained revealed that the fatigue strength depend on temperature/time conditions.