White Light and Multicolor Emission Tuning in Triply Doped Yb3+/Tm3+/Er3+ Novel Fluoro-phosphate Transparent Glass-ceramics

New Yb3+, Er3+ and Tm3+ doped fluoro-phosphate glasses belonging to the system NaPO3–YF3–BaF2–CaF2 and containing up to 10 wt% of rare-earth ion fluorides were prepared and characterized by differential scanning calorimetry, absorption spectroscopy and up-conversion emission spectroscopy under excitation with a 975 nm laser diode. Transparent and homogeneous glass-ceramics have been reproducibly obtained with a view to manage the red, green and blue emission bands and generate white light. X-ray diffraction as well as electron microscopy techniques have confirmed the formation of fluorite-type cubic nanocrystals at the beginning of the crystallization process while complex nanocrystalline phases are formed after a longer heat-treatment. The prepared glass-ceramics exhibit high optical transparency even after 170 h of thermal treatment. An improvement of up-conversion emission intensity – from 10 to 160 times larger – was measured in the glass-ceramics when compared to the parent glass, suggesting an important incorporation of the rare-earth ions into the crystalline phase(s). The involved mechanisms and lifetime were described in detail as a function of heat-treatment time. Finally, a large range of designable color rendering (from orange to turquoise through white) can be observed in these materials by controlling the laser excitation power and the crystallization rate.

Effect of oxidizing and reducing atmospheres on Ba(Ti0.90 Zr0.10)O3:2V ceramics as characterized by piezoresponse force microscopy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dielectric response of tungsten modified Ba(Ti0.90Zr0.10)O3 ceramics obtained by mixed oxide method

The electrical response of Ba(Ti0.90Zr0.10)O3 (BZT) ceramics obtained by the mixed oxide method as a functionof tungsten content was investigated. According to X-ray diffraction analysis the single phase BZT1W (1wt.% W doped BZT) and BZT2W (2 wt.% W doped BZT) ceramics, crystallized in a perovskite structure, wereobtained. It is also shown that tungsten substituted ceramics can be sintered at a reduced temperature whencompared to the undoped BZT. Electron paramagnetic resonance (EPR) analyses reveals that substitution ofTi4+ by W6+ causes distortion in the crystal structure changing lattice parameter. Substitution of W6+ on B-siteof ABO3 perovskite BZT ceramics shifted the phase transition to lower temperatures up to a tungsten contentof 2 wt.% leading to a relaxor-like behaviour.Keywords: donor dopant; ceramics; dielectric response; mixed oxide method

Surface roughness analysis of dental ceramics treated with hydrofl uoric acid and aluminum oxide jet

The aim of this study was to evaluate the surface roughness of 5 indirect restorative materials treated with hydrofluoric acid to 10%, with aluminum oxide jet and a combination of both. The specimens was prepared with 10 mm in diameter and 2 mm thickness, divided into fi ve groups: (1) Ceromer (CeseadII-Kuraray), (2) Leucite crystals ceramics (IPS EmpressIIIvoclarforcasket), (3) glass ceramic with fluorapatite (IPS D. Sign-Ivoclar), (4) lithium disilicate ceramic (IPS Empress II-Ivoclar restorations), (5) ceramics (Cergogold-Degussa). For all groups were performed the controls, and the surfaces with the 3 types of treatment. For testing roughness used the rugosimeter Taylor/Hobson-Precision, model form tracerSV-C525 high sensitivity. After confi rmation of variance analysis with a signifi cance level of 1% (p < 0.01), there was equality between the average roughness of materials from groups 1, 3 and 5, and the group 2 was different from the others. It was also found that the ceramics of the group 5 behaved similar to group 4. However the lowest average roughness was observed in group 2 ceramic. In the evaluation between the types of treatment, the aluminum oxide jet and associations and blasting with hydrofl uoric acid were similar, and different isolated hydrofl uoric acid, and 3 types of treatment signifi cantly higher than the control group. All treatments promoted superfi cial alterations in all tested materials.

Reabilitação estética do sorriso por meio do sistema cerâmico dissilicato de lítio: relato de caso

The reestablishment of a harmonious smile through dental ceramics, when properly conducted and with specific indications, can achieve extremely predictable results. For aesthetic and functional rehabilitation, many ceramic materials can be used such as zirconia, leucite, alumina, feldspar, and lithium disilicate. Among these materials the lithium disilicate stands out due to the following characteristics: its resistance to wear, to chemical attack, high temperatures and oxidation; low electrical conductivity; near zero thermal expansion; good optical properties and biocompatibility with periodontal; excellent esthetics; color stability and reinforcement of tooth structure. The indications for the use of lithium disilicate are not limited to multiple facets of teeth in cases where there was no favorable response to tooth whitening, and also comprehend teeth with multiple restorations, diastema closure, shape alteration, and dental contouring, replacement of missing or fractured teeth, among others. The versatility of lithium disilicate ceramics allows its utilization in several clinical situations. The concomitant use of lithium disilicate for veneers and over metal has satisfactory aesthetic results, as reported in the present studying cases that require both aesthetics and resistance.

Characterization of aluminum hydroxide (Al(OH)(3)) for use as a porogenic agent in castable ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Análise do acabamento superficial e força de corte no torneamento de alumina a verde

In experimental conditions, cutting forces were studied during turning of green alumina billets, including their correlation with surface aspects of the workpiece. The correlation between cutting power and the removal rate are important parameters for defining the design of ceramic products, since inadequate parameters can produce excessive surface damage to the workpiece. This study examined the forces obtained during turning of alumina workpieces with 99.8% purity in their green state, by means of a three-point dynamometer, evaluating the cutting, feed and depth forces, using a cermet tool under constant machining conditions. Variables were compared with the forces, including surface finish, tool wear and temperature during machining. In the study, it was found that the depth of cut had no significant effect on the surface quality, and the cutting speed and feed influencing the finish. However, preliminary tests for selecting the cutting conditions showed that unsuitables cutting speeds and feeds generate severe damage to the workpiece surface. The best condition was 1.00 mm depth of cut, and the forces increasedfor with each pass performed, with the feed force the variable with greatest increases in relation to the cutting and depth forces, and wear of the cutting tool directly influenced the surface finish, generated by the highly abrasive nature of the alumina particles of the green compact. It is emphasized that the alumina in its green state showed high abrasive effect on the cutting tool during the turning process and the surface finishing of the green workpiece had a direct influence on the sintered workpiece.

Surface analysis of alumina ceramic exposed to shock waves produced by plasma expander

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Pigments based on Cr and Sb doped TiO2 prepared by microemulsion-mediated solvothermal synthesis for inkjet printing on ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Correlation between structural and catalytic properties of copper supported on porous alumina for the ethanol dehydrogenation reaction

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Titanium K-edge XAS study on local structure of Pb1-xCaxTiO3 ferroelectric ceramics

In order to characterize the local structure of Pb1-xCaxTiO3 (PCT) samples, Ti K-edge XANES measurements were performed and showed that Ca incorporation to PbTiO3 structure leads to a decreasing of local distortion of Ti atoms in relation to oxygen atoms at the TiO6 octahedra. Moreover, according to EXAFS measurements, the local structure around Ti atoms exhibits tetragonal symmetry with P4mm space group for samples with x <= 0.475, whereas orthorhombic symmetry with Pbnm space group was observed for x equals to 0.50 and 0.55.

Properties of glass-ceramics obtained from crystallization of the SiO2-Al2O3-MgO-Li2O system with addition of ZrO2

This paper presents the study results with glass-ceramics obtained from base glass (MgO-Al2O3- SiO2-Li2O system) with addition of ZrO2 as nucleating agent. The glass was melted at 1650 degrees C for 3 h and at a heating rate of 10 degrees C/min. The molten glass was poured into a graphite mold to obtain monolithic samples and also in water in order to obtain particulate material. Such material was grinded and then pressed by both uniaxial and isostatic pressing methods before being sintered. Both the monolithic and pressed samples were performed under two different conditions of heat treatment so that their nucleation and crystallization occurred. In the first one, the samples were heated to 1100 degrees C with a heating rate of 10 degrees C/min. In the second one, there was an initial heating rate of 10 degrees C/min up to 780 degrees C, which was kept for 5 minutes. After that, the samples were heated to 1100 degrees C at a heating rate of 1 degrees C/min. Microhardness analyses showed that base glass presented values around 7.0 GPa. The glass-ceramics obtained from the powder sintering showed microhardness values lower than those obtained from monolithic samples. The highest hardness values were observed in the samples which were treated with two heating rates, whose values were around 9.2 +/- 0.5 GPa. Moreover, the glass-ceramics which were produced with an only heating rate, presented values around 7.1 +/- 0.2 GPa, very close to those observed in the base glass.

Innovative low temperature plasma approach for deposition of alumina films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

X-ray photoelectron spectroscopy study on sintered Pb1-xLaxTiO3 ferroelectric ceramics

The Pb1-xLaxTiO3 sintered ferroelectric ceramics with x equal to 0, 0.10, 0.15, 0.20, and 0.30 were studied by X-ray photoelectron spectroscopy (XPS). The binding energy of the Ti 2p lines is consistent with only one chemical state, Ti4+. on the other hand, in the case of Pb 4f and 0 Is XPS spectra, apart from the main peaks attributed to the lattice ions, minor peaks related to the surface states were also observed. The presence of Pb-0 state on the surface of all samples was due to the reduction of lead ions caused by the preferential removal of the oxygen ions after sputtering. The non observation of Ti3+ ions confirms that the mechanism of charge compensation that should occurs owing to the substitution of Ph2+ by La3+ is due to the preferential formation of Pb site vacancies, and not to a reduction from Ti4+ to Ti3+ states. Within the limits of the present experiment, there is no evidence of the existence of non-equivalent Pb, Ti, and La sites as the Pb1-xLaxTiO3 ceramic changes from a normal to a relaxor ferroelectric state. (c) 2006 Elsevier B.V. All rights reserved.

Avaliação da tenacidade à fratura de diferentes sistemas cerâmicos

Although ceramics present high compressive strength, they are brittle materials due to their low tensile strength so they have lower capacity to absorb shocks. This study evaluated the fracture toughness of different ceramic systems, which refers to the ability of a friable material to absorb defformation energy. Three ceramic systems were investigated. Ten cylindrical samples (5,0mm x 3,0mm), were obtained from each ceramic material as follows: G1- 10 samples of Vitadur Alpha (Vita-Zahnfabrik); G2- 10 samples of IPS Empress2 (Ivoclar-Vivadent); G3- 10 samples of In-Ceram Alumina (Vita-Zahnfabrik). Fracture toughness values were collected upon indentation tests that were performed under a heavy load. A microhardness tester (Digital Microhardness Tester FM) utilized a 500gf load cell during 10seconds to perform four impressions on each sample. Statistically significant results were observed (ANOVA and Kruskal-Wallis tests). In-Ceram Alumina presented the highest median toughness values (2,96N/m3/2), followed by Vitadur Alpha (2,08N/m3/2) and IPS Empress2 (1,05N/m3/2). It may be concluded that different ceramic systems present distinct fracture toughness values, thus In-Ceram is capable of absorbing superior stress when compared to Vitadur Alpha and IPS Empress2.