Cytotoxicity of denture base acrylic resins: A literature review

Acrylic resins are widely used in the fabrication of denture bases and have been shown to be cytotoxic as a result of substances that leach from the resin. The primary eluate is residual monomer. Numerous reports suggest that residual monomer may be responsible for mucosal irritation and sensitization of tissues. This information is important, not only to assess the biologic effects of such materials, but also to enable a comparison among the different polymerization methods, thus assisting the clinician in selecting a material with minimal cytotoxicity. This article reviews the literature published from 1973 to 2000, selected by use of a Medline search, associated with cytotoxic effects usually ascribed to acrylic denture base materials.

Penetration of a light-cured glass ionomer and a resin sealant into occlusal fissures and etched enamel.

PURPOSE: To evaluate the penetration of a light-cured glass ionomer and a resin sealant into occlusal fissures and etched enamel. MATERIALS AND METHODS: Forty-eight maxillary and mandibular caries-free premolars scheduled for extraction for orthodontic reasons were isolated, the occlusal surfaces subjected to prophylaxis and acid-etched with orthophosphoric acid prior to the application of the VariGlass VLC glass ionomer and Concise resin sealants. The teeth were extracted, two longitudinal median sectiors from each tooth were ground to a thickness of 80-100 microns, and the sealant penetration into the fissures evaluated. The sections were placed in nitric acid to dissolve the enamel so the lengths of the tags which had penetrated into the etched enamel could be measured at different sites on the walls of the fissures. RESULTS: Both sealants adapted well to the fissures but penetrated deeper into shallow, open fissures than into deep, constricted fissures. The VariGlass VLC tags into etched enamel were generally longer than the Concise projections.

Effect of post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins

Introduction: Most denture base acrylic resins have polymethylmethacrylate in their composition. Several authors have discussed the polymerization process involved in converting monomer into polymer because adequate polymerization is a crucial factor in optimizing the physical properties and biocompatibility of denture base acrylic resins. To ensure the safety of these materials, in vitro cytotoxicity assays have been developed as preliminary screening tests to evaluate material biocompatibility. 3H-thymidine incorporation test, which measures the number of cells synthesizing DNA, is one of the biological assays suggested for cytotoxicity testing. Aim: The purpose of this study was to investigate, using 3H-thymidine incorporation test, the effect of microwave and water-bath post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins. Materials and Methods: Nine disc-shaped specimens (10 x 1 mm) of each denture base resin (Lucitone 550 and QC 20) were prepared according to the manufacturers' recommendations and stored in distilled water at 37°C for 48 h. The specimens were assigned to 3 groups: 1) post-polymerization in a microwave oven for 3 min at 500 W; 2) post-polymerization in water-bath at 55°C for 60 min; and 3) without post-polymerization. For preparation of eluates, 3 discs were placed into a sterile glass vial with 9 mL of Eagle's medium and incubated at 37°C for 24 h. The cytotoxic effect of the eluates was evaluated by 3H-thymidine incorporation. Results: The results showed that the components leached from the resins were cytotoxic to L929 cells, except for the specimens heat treated in water bath (p<0.05). Compared to the group with no heat treatment, water-bath decreased the cytotoxicity of the denture base acrylic resins. Conclusion: The in vitro cytotoxicity of the tested denture base materials was not influenced by microwave post-polymerization heat treatment.

Bond strength of hard chairside reline resins to a rapid polymerizing denture base resin before and after thermal cycling

Purpose: This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling. Materials and Methods: Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerized using cycle A (boiling water-20 minutes) or B (boiling water; remove heat-20 minutes; boiling water-20 minutes). For each reline resin/polymerization cycle combination, 10 specimens (groups CAt e CBt) were thermally cycled (5 and 55°C; dwell time 30 seconds; 2,000 cycles); the other 10 were tested without thermal cycling (groups CAwt ad CBwt). Shear bond tests (0.5 mm/min) were performed on the specimens and the failure mode was assessed. Data were analyzed by 3-way ANOVA and Newman-Keuls post-hoc test (α=.05). Results: QC-20 resin demonstrated the lowest bond strengths among the reline materials (P<.05) and mainly failed cohesively. Overall, the bond strength of the hard chairside reline resins were similar (10.09±1.40 to 15.17±1.73 MPa) and most of the failures were adhesive/cohesive (mixed mode). However, Ufi Gel Hard bonded to QC-20 polymerized using cycle A and not thermally cycled showed the highest bond strength (P<.001). When Tokuso Rebase Fast and Duraliner II were bonded to QC-20 resin polymerized using cycle A, the bond strength was increased (P=.043) after thermal cycling. Conclusions: QC-20 displayed the lowest bond strength values in all groups. In general, the bond strengths of the hard chairside reline resins were comparable and not affected by polymerization cycle of QC-20 resin and thermal cycling.

Influence of cavity preparation and curing method on the marginal seal of resin composite restorations: an in vitro evaluation.

OBJECTIVE: To evaluate the influence of cavity design and photocuring method on the marginal seal of resin composite restorations. METHOD AND MATERIALS: Seventy-two bovine teeth were divided into 2 groups: group 1 received box-type cavity preparations, and group 2 received plate-type preparations. Each group was divided into 3 subgroups. After etching and bonding, Z250 resin composite (3M Espe) was applied in 2 equal increments and cured with 1 of 3 techniques: (1) conventional curing for 30 seconds at 650 mW/cm2; (2) 2-step photocuring, in which the first step was performed 14 mm from the restoration for 10 seconds at 180 mW/cm2 and the second step was performed in direct contact for 20 seconds at 650 mW/cm2; or (3) progressive curing using Jetlite 4000 (J. Morita) for 8 seconds at 125 mW/cm2 and then 22 seconds at 125 mW/cm2 up to 500 mW/cm2. The specimens were thermocycled for 500 cycles and then submitted to dye penetration with a 50% silver nitrate solution. Microleakage was assessed using a stereomicroscope. Data were analyzed using analysis of variance and Tukey test (5% level of significance). RESULTS: A statistically significant difference was found between groups when a double interaction between photocuring and cavity preparation was considered (P = .029). CONCLUSIONS: No one type of cavity preparation or photocuring method prevented micro-leakage. The plate-type preparation showed the worst dye penetration when conventional and progressive photocuring methods were used. The best results were found using the 2-step photocuring with the plate-type preparation.

In vitro evaluation of surface roughness of 4 resin composites after the toothbrushing process and methods to recover superficial smoothness.

OBJECTIVE: This study evaluated the efficiency of repolishing, sealing with surface sealant, and the joining of both in decreasing the surface roughness of resin-based composites after a toothbrushing process. METHOD AND MATERIALS: Ten specimens of each composite (Alert, Z100, Definite, and Prodigy Condensable), measuring 2 mm in thickness and 4 mm in diameter, were made and submitted to finishing and polishing processes on both sides of the specimens using the Sof-Lex system. The specimens were then subjected to toothbrushing (30,000 cycles), and surface roughness (Ra) was analyzed with a Surfcorder SE 1700 profilometer. The upper surface of each composite was etched with 37% phosphoric acid, and the surface-penetrating sealant Protect-it was applied on 1 surface. The roughness of these surfaces was again measured. On the other side, the surface of the specimen was repolished, and the efficiency of this procedure was measured using the profilometer. The surface roughness resulting from the joining of the 2 methods was verified by applying, in the final stage, the surface-penetrating sealant on the repolished surface. Data were analyzed with analysis of variance and Tukey test (P <.05). RESULTS: Results showed that the lowest surface roughness values were obtained for Definite, Z100, and Prodigy Condensable after the repolishing process and after the repolishing plus sealing. For Alert, the joining of repolishing plus sealing promoted the lowest values of surface roughness. CONCLUSION: Of the resin-based composites, Alert demonstrated the highest values of surface roughness in all the techniques tested.

Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins

This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (mTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artifcial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm 2 were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4°C and 60°C). mTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (a=0.05). There was no statisti-caly signifcant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean mTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The mTBS of Biotone artifcial teeth to the denture base acrylic resins was not infuenced by the polymer type, surface treatment or thermocycling.

Effects of five carbamide peroxide bleaching gels on composite resin microhardness.

The purpose of this study was to evaluate the effects of five home bleaching products containing 15-16% carbamide peroxide on the microhardness of microhybrid composite resin Z-250 (3M/Espe). A total of 72 specimens were fabricated in cylindrical acrylic matrices (4 x 2 mm), filled with composite resin and photo-activated for 40 seconds. They were divided in 6 study groups (n = 12), according to the bleaching product: Review (SS White), Magic Bleaching (Vigodent), Opalescence (Ultradent), Whiteness Perfect (FGM), Claridex (Biodinâmica), and a control group (not bleached). Specimens were exposed to 1 cc of bleaching gel for 6 hours daily for 2 weeks. The control group specimens were kept in artificial saliva throughout this time. All the specimens were then analyzed in a microhardness tester. Knoop hardness measurements were performed, and the results were submitted to parametric statistical analysis (analysis of variance and Tukey's test). Mean Knoop values and standard deviation were: baseline, 68.52a (4.28); control, 63.42b (7.16); Whiteness Perfect, 57.57c (1.81); Magic Bleaching, 57.22c (3.84); Opalescence, 57.03cd (4.00); Claridex, 53.64de (3.33); Review 51.45e (2.82). Identical letters mean statistical equality according to Tukey's test at the 5% significance level. The products significantly decreased Z-250 (3M/Espe) microhardness.

Impact strength of denture base and reline acrylic resins subjected to long-term water immersion

Water may influence the mechanical properties of the acrylic resins. Thus, the effect of water storage on the impact strength (IS) of one denture base (Lucitone 550 - L) and four reline resins (Tokuyama Rebase II - T; UfiGel Hard - U; Kooliner - K; New Truliner - NT) was evaluated. Bars of L were made (60 x 6 x 2 mm) and relined (2 mm) with T, U, K, NT and L. Intact specimens of each material (60 x 6 x 4 mm) were also fabricated for comparative purposes. Specimens were submitted to Charpy impact tests without water storage (control) and after immersion in water for 7, 90 and 180 days. Data (kJ/m 2) analyzed by two-way ANOVA and Tukey's test (p=0.05) revealed that after 90 days, U exhibited an increase in the IS (0.93) compared to 7 days (0.58). K (1.48) and L/K (7.21) exhibited a decrease at the 7-day period (1.01 and 3.23, respectively). NT (0.60) showed an increase in the IS after 180 days (1.52), whereas L/ NT (7.70) showed a decrease (3.17). Water immersion improved the IS of U and NT, and decreased the IS of K, L/K, and L/NT. Water may affect differently the IS of acrylic resins and, consequently, the resistance to fracture of relined denture bases.

Impact strength of denture base and reline acrylic resins: An in vitro study

This study evaluated the impact strength of a denture base resin (Lucitone 550-L) and four reline resins (Tokuyama Rebase II-T; Ufi Gel Hard-U; New Truliner-NT, and Kooliner-K), both intact and in a reline combination (L/L, L/T, L/U, L/NT, and L/K). For each group (n = 20), half of the specimens were thermocycled before testing. Charpy tests were performed, and the impact strengths were calculated. Data were analyzed by two-way analyses of variance and Tukey's test (p = 0.05). For the intact groups, mean impact strength values for L (1.65 and 1.50) were significantly higher than those of the reline resins (0.38-1.17). For the relined groups, the highest mean impact strength values were produced by L/T (5.76 and 5.12), L/NT (6.20 and 6.03), and L/K (5.60 and 5.31) and the lowest by L/U (0.76 and 0.78). There were no significant differences between L and L/L. Thermocycling reduced the impact strength of T (from 0.73 to 0.38) and L/L (from 1.82 to 1.56). © The Author(s) 2012.

Effect of different disinfectants on the microhardness and roughness of acrylic resins for ocular prosthesis

Background: Ocular prosthesis materials should have specific properties for their indication and durability; therefore, it is important to investigate their physical behaviour when affected by several disinfectants. Objectives: This study evaluated the influence of different disinfecting solutions on the microhardness and surface roughness of acrylic resins for ocular prosthesis. Materials and Methods: Fifty samples simulating ocular prostheses were fabricated with N1 resin and colourless resin and divided (n = 10) according to the disinfectant used: neutral soap, Opti-free, Efferdent, 1% hypochlorite (HYC) and 4% chlorhexidine (CHX). Samples were stored in saline solution at 37°C and disinfected during 120 days. Both microhardness and roughness were investigated before, after 60 days and 120 days of disinfection and storage. Microhardness was measured using a microhardner and the roughness with a roughness device. Results: N1 resin showed lower microhardness when compared with colourless resin (p < 0.05). HYC and CHX groups exhibited the highest change of microhardness and roughness values (p < 0.05). An increase in roughness and reduction in microhardness of ocular acrylic resins were observed after both periods of disinfection and storage (p < 0.05). Conclusion: Both disinfection/storage periods affected the microhardness and roughness values of the samples. © 2012 The Gerodontology Society and John Wiley & Sons A/S.

Effect of Surface Conditioning Modalities on the Repair Bond Strength of Resin Composite to the Zirconia Core / Veneering Ceramic Complex

Purpose: This study evaluated the effect of different surface conditioning protocols on the repair strength of resin composite to the zirconia core / veneering ceramic complex, simulating the clinical chipping phenomenon.Materials and Methods: Forty disk-shaped zirconia core (Lava Zirconia, 3M ESPE) (diameter: 3 mm) specimens were veneered circumferentially with a feldspathic veneering ceramic (VM7, Vita Zahnfabrik) (thickness: 2 mm) using a split metal mold. They were then embedded in autopolymerizing acrylic with the bonding surfaces exposed. Specimens were randomly assigned to one of the following surface conditioning protocols (n = 10 per group): group 1, veneer: 4% hydrofluoric acid (HF) (Porcelain Etch) + core: aluminum trioxide (50-mu m Al2O3) + core + veneer: silane (ESPE-Sil); group 2: core: Al2O3 (50 mu m) + veneer: HF + core + veneer: silane; group 3: veneer: HF + core: 30 mu m aluminum trioxide particles coated with silica (30 mu m SiO2) + core + veneer: silane; group 4: core: 30 mu m SiO2 + veneer: HF + core + veneer: silane. Core and veneer ceramic were conditioned individually but no attempt was made to avoid cross contamination of conditioning, simulating the clinical intraoral repair situation. Adhesive resin (VisioBond) was applied to both the core and the veneer ceramic, and resin composite (Quadrant Posterior) was bonded onto both substrates using polyethylene molds and photopolymerized. After thermocycling (6000 cycles, 5 degrees C-55 degrees C), the specimens were subjected to shear bond testing using a universal testing machine (1 mm/min). Failure modes were identified using an optical microscope, and scanning electron microscope images were obtained. Bond strength data (MPa) were analyzed statistically using the non-parametric Kruskal-Wallis test followed by the Wilcoxon rank-sum test and the Bonferroni Holm correction (alpha = 0.05).Results: Group 3 demonstrated significantly higher values (MPa) (8.6 +/- 2.7) than those of the other groups (3.2 +/- 3.1, 3.2 +/- 3, and 3.1 +/- 3.5 for groups 1, 2, and 4, respectively) (p < 0.001). All groups showed exclusively adhesive failure between the repair resin and the core zirconia. The incidence of cohesive failure in the ceramic was highest in group 3 (8 out of 10) compared to the other groups (0/10, 2/10, and 2/10, in groups 1, 2, and 4, respectively). SEM images showed that air abrasion on the zirconia core only also impinged on the veneering ceramic where the etching pattern was affected.Conclusion: Etching the veneer ceramic with HF gel and silica coating of the zirconia core followed by silanization of both substrates could be advised for the repair of the zirconia core / veneering ceramic complex.

Polymerization kinetics and polymerization stress in resin composites after accelerated aging as a function of the expiration date

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Shear bond strength of resin cements to human dentin

OBJECTIVES: The objectives of this in vitro study were (1) to assess the bond strength of the universal cement RelyX Unicem to dentin and to compare it with three conventional resin cements, (2) to test the influence of aging on their bonding capacity and (3) to test the influence of the operator on bonding quality by performing the same test in two different centers. METHODS: 160 third molars, divided into 80 for tests at the University of Zurich (Z) and 80 for tests at the University of Berne (B), were assigned to 2 x 8 subgroups of 10 teeth each. The specimens were prepared with the corresponding bonding agents and acrylic rods were luted either with RelyX Unicem (U), RelyX ARC (A), Multilink (M) or Panavia 21 (P). All specimens were stored in water for 24h (W) and half of the specimens were subjected to 1500 cycles of thermocycling (5 degrees C and 55 degrees C) (T). Bond strength was measured by means of a shear test. RESULTS: After water storage RelyX Unicem exhibited lowest bond strength (UWZ: 9.2+/-1.6 MPa, UWB: 9.9+/-1.2 MPa, AWZ: 15.3+/-6.0 MPa, AWB: 12.2+/-4.3 MPa, MWZ: 15.6+/-3.3 MPa, MWB: 12.4 MPa+/-2.4, PWZ: 13.4+/-2.9 MPa, PWB: 14.9+/-2.6 MPa). Thermocycling affected the bonding performance of all four cements. However, bond strength of RelyX Unicem was least influenced by thermocycling (UTZ: 9.4+/-2.9 MPa, UTB: 8.6+/-1.3 MPa, ATZ: 11.4+/-6.3 MPa, ATB: 13.3+/-3.7 MPa, MTZ: 15.4+/-3.1 MPa, MTB: 10.3+/-2.4 MPa, PTZ: 11.1+/-2.8 MPa, PTB: 11.3+/-2.8 MPa). SIGNIFICANCE: Although the bond strength of RelyX Unicem to dentin was lower in comparison to RelyX ARC, Multilink and Panavia 21, its bond strength was less sensitive to variations in handling and aging.

Effect Of 4-(n,n-dimethylamino)phenethyl Alcohol On Degree Of Conversion And Cytotoxicity Of Photo-polymerized Cq-based Resin Composites.

The aim of this study was to evaluate the degree of conversion (DC) and the cytotoxicity of photo-cured experimental resin composites containing 4-(N,N-dimethylamino)phenethyl alcohol (DMPOH) combined to the camphorquinone (CQ) compared with ethylamine benzoate (EDAB). The resin composites were mechanically blended using 35 wt% of an organic matrix and 65 wt% of filler loading. To this matrix was added 0.2 wt% of CQ and 0.2 wt% of one of the reducing agents tested. 5x1 mm samples (n=5) were previously submitted to DC measurement and then pre-immersed in complete culture medium without 10% (v/v) bovine serum for 1 h or 24 h at 37 °C in a humidifier incubator with 5% CO2 and 95% humidity to evaluate the cytotoxic effects of experimental resin composites using the MTT assay on immortalized human keratinocytes cells. As a result of absence of normal distribution, the statistical analysis was performed using the nonparametric Kruskal-Wallis to evaluate the cytotoxicity and one-way analysis of variance to evaluate the DC. For multiple comparisons, cytotoxicity statistical analyses were submitted to Student-Newman-Keuls and DC analysis to Tukey's HSD post-hoc test (=0.05). No significant differences were found between the DC of DMPOH (49.9%) and EDAB (50.7%). 1 h outcomes showed no significant difference of the cell viability between EDAB (99.26%), DMPOH (94.85%) and the control group (100%). After 24 h no significant difference were found between EDAB (48.44%) and DMPOH (38.06%), but significant difference was found compared with the control group (p>0.05). DMPOH presented similar DC and cytotoxicity compared with EDAB when associated with CQ.