Study of fibre distribution and orientations in UHPFRC by electrical resistivity and mechanical tests

This paper presents experimental tests carried out on steel fibre reinforced concrete samples, including mechanical tests as well as non-destructive technique (electrical resistivity) and non destructive technique on cores (X-ray). Electrical resistivity measurements are done as a blind test, to characterise the electrical anisotropy and deduce the distribution and the orientation of fibres. These results are compared to X-ray imaging to check the quality of the non destructive evaluation. Then, flexural and compressive strength are measured on specimens to assess the influence of fibre distribution on the concrete properties.

Assessment of fibre orientation in ultra high performance fibre reinforced concrete and its effect on flexural strength

Fibre distribution and orientation in a series of round panel specimens of ultra high performance fibre reinforced concrete (UHPFRC) was investigated using electrical resistivity measurements and confirmed by X-ray CT imaging. By pouring specimens in different ways, the orientation of steel fibres was influenced and the sensitivity of the electrical resistivity technique was investigated. The round panels were tested in flexure and the results are discussed in relation to the observed orientation of fibres in the panels. It was found that the fibres tended to align perpendicular to the direction of flow. As a result, panels poured from the centre were significantly stronger than panels poured by other methods because the alignment of fibres led to more fibres bridging the radial cracks formed during mechanical testing.

Influence of aggregate and curing regime on the mechanical properties of ultra-high performance fibre reinforced concrete (UHPFRC)

A new generation of concrete, Ultra-high performance fibre reinforced concrete (UHPFRC) has been developed for its outstanding mechanical performance and shows a very promising future in construction applications. In this paper, several possibilities are examined for reducing the price of producing UHPFRC and for bringing UHPFRC away from solely precast applications and onto the construction site as an in situ material. Recycled glass cullet and two types of local natural sand were examined as replacement materials for the more expensive silica sand normally used to produce UHPFRC. In addition, curing of UHPFRC cubes and prisms at 20 degrees C and 90 degrees C has been investigated to determine differences in both mechanical and ductility.

Fast-track construction with slag cement concrete: Adiabatic strength development and strength prediction

The early-age strength development of concrete containing slag cement has been investigated to give guidance for its use in fast-track construction. Measurements of temperature rise under adiabatic conditions have shown that high levels of slag cement-for example, 70% of the total binder-are required to obtain a significant reduction in the peak temperature rise. Despite these temperature rises being lower than those for portland cement mixtures, however the early-age strength under adiabatic conditions of slag cement concrete can be as high as 250% of the strength of companion cubes cured at 20 degrees C (68 degrees F). The maturity and, hence, strength development were calculated from the adiabatic temperature histories based on several Maturity functions available in the literature. The predicted strength development with age was compared with the experimental results. Maturity functions that take into account the lower ultimate strengths obtained at elevated curing temperatures were found to be better at predicting the strength development.

Strength development of mortars containing ground granulated blast-furnace slag: Effect of curing temperature and determination of apparent activation energies

The strength development of mortars containing ground granulated blast-furnace slag (ggbs) and portland cement was investigated. Variables were the level of ggbs in the binder, water-binder ratio and curing temperature. All mortars gain strength more rapidly at higher temperatures and have a lower calculated ultimate strength. The early age strength is much more sensitive to temperature for higher levels of ground granulated blast-furnace slag. The calculated ultimate strength is affected to a similar degree for all ggbs levels and water-binder ratios, with only the curing temperature having a significant effect. Apparent activation energies were determined according to ASTM C1074 and were found to vary approximately linearly with ggbs level from 34 kJ/mol for portland cement mortars to around 60 kJ/mol for mortars containing 70% ggbs. The water-binder ratio appears to have little or no effect oil the apparent activation energy. (c) 2005 Elsevier Ltd. All rights reserved.