Crystallization in poly(L-lactide)-b-poly(epsilon-caprolactone) double crystalline diblock copolymers: a study using X-ray scattering, differential scanning calorimetry, and polarized optical microscopy

The crystallization of well-defined poly(L-lactide)-b-poly(epsilon-caprolactone) diblock copolymers, PLLA-b-PCL, was investigated by time-resolved X-ray techniques, polarized optical microscopy (POM), and differential scanning calorimetry (DSC). Two compositions were studied that contained 44 and 60 wt % poly(L-lactide), PLLA (they are referred to as (L44C5614)-C-11 and (L60C409)-C-12, respectively, with the molecular weight of each block in kg/mol as superscript). The copolymers were found to be initially miscible in the melt according to small-angle X-ray scattering measurements (SAXS). Their thermal behavior was also indicative of samples whose crystallization proceeds from a mixed melt. Sequential isothermal crystallization from the melt at 100 degreesC (for 30 min) and then at 30 degreesC (for 15 min) was measured. At 100 degreesC only the PLLA block is capable of crystallization, and its crystallization kinetics was followed by both WAXS and DSC; comparable results were obtained that indicated an instantaneous nucleation with three-dimensional superstructures (Avrami index of approximately 3). The spherulitic nature of the superstructure was confirmed by POM. When the temperature was decreased to 30 degreesC, the PCL block was able to crystallize within the PLLA negative spherulites (with an Avrami index of 2, as opposed to 3 in homo-PCL), and its crystallization rate was much slower than an equivalent homo-PCL. Time-resolved SAXS experiments in (L60C409)-C-12 revealed an initial melt mixed morphology at 165 degreesC that upon cooling transformed into a transient microphase-separated lamellar structure prior to crystallization at 100 degreesC.

Self-nucleation and crystallization kinetics of double crystalline poly(p-dioxanone)-b-poly(epsilon-caprolactone) diblock copolymers

The crystallization kinetics of each constituent of poly(p-dioxanone)-b-poly(epsilon-caprolactone) diblock copolymers (PPDX-b-PCL) has been determined in a wide composition range by differential scanning calorimetry and compared to that of the equivalent homopolymers. Spherulitic growth rates were also measured by polarized optical microscopy while atomic force microscopy was employed to reveal the morphology of one selected diblock copolymer. It was found that crystallization drives structure formation and both components form lamellae within mixed spherulitic superstructures. The overall isothermal crystallization kinetics of the PPDX block at high temperatures, where the PCL is molten, was determined by accelerating the kinetics through a previous self-nucleation procedure. The application of the Lauritzen and Ho. man theory to overall growth rate data yielded successful results for PPDX and the diblock copolymers. The theory was applied to isothermal overall crystallization of previously self-nucleated PPDX ( where growth should be the dominant factor if self-nucleation was effective) and the energetic parameters obtained were perfectly matched with those obtained from spherulitic growth rate data of neat PPDX. A quantitative estimate of the increase in the energy barrier for crystallization of the PPDX block, caused by the covalently bonded molten PCL as compared to homo-PPDX, was thus determined. This energy increase can dramatically reduce the crystallization rate of the PPDX block as compared to homo-PPDX. In the case of the PCL block, both the crystallization kinetics and the self-nucleation results indicate that the PPDX is able to nucleate the PCL within the copolymers and heterogeneous nucleation is always present regardless of composition. Finally, preliminary results on hydrolytic degradation showed that the presence of relatively small amounts of PCL within PPDX-bPCL copolymers substantially retards hydrolytic degradation of the material in comparison to homo-PPDX. This increased resistance to hydrolysis is a complex function of composition and its knowledge may allow future prediction of the lifetime of the material for biomedical applications.

Multi-scale structural description of siloxane-PPO hybrid ionic conductors doped by sodium salts

Alkaline metal doped organic - inorganic hybrids have potential applications in the field of portable energy sources. Attractive sol - gel derived urea cross-linked polyether, siloxane - PPO ( poly( propylene oxide)) hybrids doped with sodium salts ( NaClO4 and NaBF4) were examined by multi-spectroscopic approach that includes complex impedance, X-ray powder diffraction (XRPD), small angle X-ray scattering (SAXS), Si-29 and Na-23 magic-angle spinning nuclear magnetic resonance (NMR/MAS), Na K-edge X-ray absorption near edge structure (XANES) and Raman spectroscopies. The goals of this work were to determine which cation coordinating site of the host matrix ( ether oxygen atoms or carbonyl oxygen atoms) is active in each of the materials analyzed, its influence on the nanostructure of the samples and its relation with the thermal and electrical properties. The main conclusion derived from this study is that the NaBF4 salt has a much lower solubility in the hybrid matrix than the NaClO4 salt. Furthermore, the addition of a large amount of salt plays a major role in the hybrid nanostructure and electrical properties, modifying the PPO chain conformation, weakening or breaking the hydrogen bond of the polyether - urea associations and changing the polycondensation and aggregation processes involving the siloxane species.

Solid-state NMR, ionic conductivity, and thermal studies of lithium-doped siloxane-poly(propylene glycol) organic-inorganic nanocomposites

Hybrid organic-inorganic ionic conductors, also called ormolytes (organically modified electrolytes), were obtained by dissolution of LiClO 4 in siloxane-poly(propylene glycol) matrixes. The dynamic features of these nanocomposites were studied and correlated to their electrical properties. Solid-state nuclear magnetic resonance (NMR) spectroscopy was used to probe the effects of the temperature and nanocomposite composition on the dynamic behaviors of both the ionic species ( 7Li) and the polymer chains ( 13C). NMR, dc ionic conductivity, and DSC results demonstrate that the Li + mobility is strongly assisted by the segmental motion of the polymer chain above its glass transition temperature. The ac ionic conductivity in such composites is explained by use of the random free energy barrier (RFEB) model, which is agreement with their disordered and heterogenous structures. These solid ormolytes are transparent and flexible, and they exhibit good ionic conductivity at room temperature (up to 10 -4 S/cm). Consequently, they are very promising candidates for use in several applications such as batteries, sensors, and electrochromic and photoelectro-chemical devices.

Synthesis and preliminary characterization of Poly(Propylene)Imine hexadecylamine dendrimer (DAB-Am-16) modified with methyl acrylate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nano- and macroscale structural and mechanical properties of in situ synthesized bacterial cellulose/PEO-b-PPO-b-PEO biocomposites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Biodegradable nanosize particles of poly(L,L-lactide)-b-poly(ethylene glycol)-b-poly(L,L-lactide)

Two series of poly(L,L-lactide-b-ethylene glycol-b-L,L-lactide) copolymers, PLA-PEO-PLA, were synthesized by polymerization Of L,L-lactide using a dihydroxy-terminated poly(ethylene glycol) (PEG) (M-n = 4000 or 600 g/mol) as coinitiator and stannous 2-ethylhexanoate, Sn(Oct)(2), as initiator. The synthesized copolymers have shown high stereoregularity as observed by C-13 NMR analyses. The nanoparticles were prepared by using a solvent diffusion method and the self-assemblage process and were characterized by NMR and SEM. It was possible to conclude that the self-assembled particles presented a core-shell structure characterized by a hydrophobic PLA core and a hydrophilic PEG shell, thus the NMR of the aqueous solutions indicated a quasi-solid behavior for the particles` interior. The diameters of the spherical particles as observed by SEM were in the 50-250 nm range, depending on the copolymer composition and the preparation procedure.

PEG-b-PPS diblock copolymer aggregates for hydrophobic drug solubilization and release: cyclosporin A as an example

Micelles formed from amphiphilic block copolymers have been explored in recent years as carriers for hydrophobic drugs. In an aqueous environment, the hydrophobic blocks form the core of the micelle, which can host lipophilic drugs, while the hydrophilic blocks form the corona or outer shell and stabilize the interface between the hydrophobic core and the external medium. In the present work, mesophase behavior and drug encapsulation were explored in the AB block copolymeric amphiphile composed of poly(ethylene glycol) (PEG) as a hydrophile and poly(propylene sulfide) PPS as a hydrophobe, using the immunosuppressive drug cyclosporin A (CsA) as an example of a highly hydrophobic drug. Block copolymers with a degree of polymerization of 44 on the PEG and of 10, 20 and 40 on the PPS respectively (abbreviated as PEG44-b-PPS10, PEG44-b-PPS20, PEG44-b-PPS40) were synthesized and characterized. Drug-loaded polymeric micelles were obtained by the cosolvent displacement method as well as the remarkably simple method of dispersing the warm polymer melt, with drug dissolved therein, in warm water. Effective drug solubility up to 2 mg/mL in aqueous media was facilitated by the PEG- b-PPS micelles, with loading levels up to 19% w/w being achieved. Release was burst-free and sustained over periods of 9-12 days. These micelles demonstrate interesting solubilization characteristics, due to the low glass transition temperature, highly hydrophobic nature, and good solvent properties of the PPS block

Immobilization of glucose oxidase enzyme (GOD) in large pore ordered mesoporous cage-like FDU-1 silica

Large pore ordered mesoporous silica FDU-1 with three-dimensional (3D) face-centered cubic, Fm3m arrangement of rnesopores, was synthesized under strong acid media using B-50-6600 poly(ethylene oxide)-poly(butylene oxide)-poly(ethylene oxide) triblock copolymer (EO(39)BO(47)EO(39)), tetraethyl orthosilicate (TEOS) and trimethyl-benzene (TMB). Large pore FDU-1 silica was obtained by using the following gel composition 1TEOS:0.00735B50-6600:0.00735TMB:6HCl:155H(2)O. The pristine material exhibited a BET specific surface area of 684 m(2) g(-1), total pore volume of 0.89 cm(3) g(-1), external surface area of 49 m(2) g(-1) and microporous volume of 0.09 cm(3) g(-1). The enzyme activity was determined by the Flow Injection Analysis-Chemiluminescence (FIA-CL) method. For GOD immobilized on the FDU-1 silica, GOD supernatant and GOD solution, the FIA-CL results were 9.0, 18.6 and 34.0 U, respectively. The value obtained for the activity of the GOD solution with FIA-CL method is in agreement with the 35 U, obtained by spectrophotometry. (C) 2011 Elsevier B.V. All rights reserved.

Adsorption of Pb(2+), Cu(2+) and Cd(2+) in FDU-1 silica and FDU-1 silica modified with humic acid

Ordered mesoporous silica with cubic structure, type FDU-1, was synthesized under strong acid media using B-50-6600 poly(ethylene oxide)-poly(butilene oxide)-poly(ethylene oxide) triblock copolymer (EO(39)BO(47)EO(39)) and tetraethyl orthosilicate (TEOS). Humic acid (HA) was modified to the synthesis process at a concentration of 1.5 mmol per gram of SiO(2). Thermogravimetry, small angle X-ray diffraction, nitrogen adsorption and high resolution transmission electron microscopy were used to characterize the samples. The pristine FDU-1 and FDU-1 with incorporated 1.5 mmol of HA were tested for adsorption of Pb(2+), Cu(2+) and Cd(2+) in aqueous solution. Incorporation of humic acid into the FDU-1 silica afforded an adsorbent with strong affinity for Cd(2+), Cu(2+) and Pb(2+) from single ion solutions. Adsorption of Cu(2+) was significantly enhanced after incorporation of humic acid, a fact that can be explained by the formation of complexes with carboxylic and phenolic groups at low concentrations of the metal cation. The results demonstrated the potential applicability of FDU-1 with incorporated HA in the removal of low concentrations of heavy metal cations from aqueous solution, such as wastewaters, after usual precipitation of metal hydroxides in alkaline medium and proper pH conditioning in the range between 6 and 7. (C) 2007 Elsevier Inc. All rights reserved.

Interaction between Pluronic F127 and Dioctadecyldimethylammonium Bromide (DODAB) Vesicles Studied by Differential Scanning Calorimetry

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Methodische Entwicklung der MALDI-TOF-Massenspektrometrie für Grenzbereiche der Polymeranalytik

Zusammenfassung der DoktorarbeitDie MALDI-TOF-Massenspektrometrie (Matrix Assisted Laser Desorption and Ionisation–Time Of Flight) ist in der Lage, Moleküle mit einem Molekulargewicht bis zu mehreren Hunderttausend Da intakt in die Gasphase zu überführen. Dabei wird die Fragmentierung des Analyten stark eingeschränkt bzw. gänzlich vermieden. Diese Methode findet daher zunehmend Verwendung für die Charakterisierung von Biopolymeren und synthetischen Polymeren. Ziel dieser Arbeit war, die MALDI-TOF-Massenspektrometrie zur Charakterisierung von Makromolekülen einzusetzen, bei denen die konventionellen polymeranalytischen Methoden nur unzureichende Informationen oder gar falsche bzw. gar keine Ergebnisse liefern. Mittels einer methodischen Entwicklung der MALDI-TOF-Massenspektrometrie gelang es, die bisherigen Grenzen der Methode zu erweitern und neue Anwendungsbereiche der Polymeranalytik aufzuzeigen. Anhand der erzielten Ergebnisse wurden darüber hinaus neue Erklärungsansätze formuliert, die zu einem besseren Verständnis des noch immer ungeklärten MALDI-Prozesses beitragen können. Besonders vielversprechend sind zum einen die Ergebnisse der Fragmentionenanalyse synthetischer Polymere und zum anderen die Charakterisierung von unlöslichen PAHs (Polycyclic Aromatic Hydrocarbons). Die Möglichkeiten und Aussagekraft der Fragmentionenanalyse wurde an synthetischen Polymeren getestet. Mit Hilfe dieser neuen Technik konnte die komplizierte Endgruppenverteilung einer Polycarbonat-Probe sowie die Zusammensetzung eines Poly-para-phenylenethynylen-b-Polyethylenoxid-Diblock-Copolymers eindeutig bestimmen werden, während die konventionellen MALDI-Massenspektren nur über einen wesentlich geringeren Informationsgehalt verfügten. Auf dem Gebiet der Analytik von unlöslichen PAHs wurde mit der Entwicklung einer neuen MALDI-Probenvorbereitung eine Methode gefunden, die über die PAH Analytik hinaus von großem Nutzen ist. Diese erstmalig angewendete Probenvorbereitung unterscheidet sich von den üblichen MALDI-Probenpräparationen, indem sie auf die Beteiligung eines Lösungsmittels vollkommen verzichtet. Damit konnte speziell ein unlöslicher, zuvor nicht nachweisbarer PAH von ca. 2700 Da mit MALDI eindeutig charakterisiert werden.

Thin nanostructured crystalline TiO 2 films and their applications in solar cells

Research on thin nanostructured crystalline TiO2 films has attracted considerable interests because of their intriguing physical properties and potential applications in photovoltaics. Nanostructured TiO2 film plays an important role in the TiO2 based dye-sensitized solar cells because they act as a substrate for the adsorption of dye molecules and a matrix for the transportation of electrons as well. Thus they can influence the solar cell performance significantly. Consequently, the control of the morphology including the shape, size and size distribution of the TiO2 nanostructures is critical to tune and optimize the performance of the solar cells. To control the TiO2 morphology, a strategy using amphiphilic block copolymer as templating agent coupled with sol-gel chemistry has been applied. Especially, a good-poor solvent pair induced phase separation process has been developed to guide the microphase separation behavior of the block copolymers. The amphiphilic block copolymers used include polystyrene-block-poly (ethylene oxide) (PS-b-PEO), poly (methyl methacrylate)-block-poly (ethylene oxide) (PMMA-b-PEO), and poly (ethylene oxide)-block-polystyrene-block-poly (ethylene oxide) (PEO-b-PS-b-PEO). The block copolymer undergoes a good-poor-solvent pair induced phase separation in a mixed solution of 1, 4-dioxane or N, N’-dimethyl formamide (DMF), concentrated hydrochloric acid (HCl) and Titanium tetraisopropoxide (TTIP). Specifically, in the system of PS-b-PEO, a morphology phase diagram of the inorganic-copolymer composite films was mapped by adjusting the weight fractions among 1, 4-dioxane, HCl, and TTIP in solution. The amorphous TiO2 within the titania-block copolymer composite films was crystallized by calcination at temperatures above 400C, where the organic block copolymer was simultaneously burned away. This strategy is further extended to other amphiphilic block copolymers of PMMA-b-PEO and PEO-b-PS-b-PEO, where the morphology of TiO2 films can also be controlled. The local and long range structures of the titania films were investigated by the combination of imaging techniques (AFM, SEM) and x-ray scattering techniques (x-ray reflectivity and grazing incidence small-angle x-ray scattering). Based on the knowledge of the morphology control, the crystalline TiO2 nanostructured films with different morphologies were introduced into solid state dye-sensitized solar cells. It has been found that all of the morphologies help to improve the performance of the solar cells. Especially, clustered nanoparticles, worm-like structures, foam-like structures, large collapsed nanovesicles show more pronounced performance improvement than other morphologies such as nanowires, flakes, and nanogranulars.

A rheology study of high-energy radiolysis of a semicrystalline ethylene-propylene copolymer containing DOP mobilizer

The ractiolysis of a poly(ethylene-co-propylene), Elpro grade P 750 J, marketed by Thai Polypropylene Co. Ltd. for the manufacture of medical goods, was investigated at ambient temperature and melt rheology measured. The roles of calcium stearate, blended with the Elpro as a processing aid, and dioctyl phthalate (DOP), added in various amounts as a radical scavenger, were assessed. Following radiolysis, G' and the viscosity of the polymer melts at 453 K both decreased with increasing radiation dose, even when the mobilizer was present. The results indicated that although the DOP did scavenge radicals, it did not protect the polymer from net chain scission in a low-dose regimen. The value of (G(S) - 4G(X)) was approximately 0.6-0.7. (c) 2006 Wiley Periodicals, Inc.