Effect of Nd on the microstructure, mechanical properties and corrosion behavior of die-cast Mg-4Al-based alloy

Die-cast Mg-4Al-0.4Mn-xNd(x = 0, 1, 2, 4 and 6 wt.%) magnesium alloys were prepared successfully and influences of Nd on the microstructure, mechanical properties and corrosion behavior of the Mg-4Al-0.4Mn alloy have been investigated. The results showed that with the addition of Nd binary Al2Nd phase and Al11Nd3 phase. which mainly aggregated along the grain boundaries, were formed, and the relative ratio of above two phases was in correlation with the Nd content in the alloy. Meanwhile, the grain sizes were greatly reduced with the increasing Nd content. It was found that due to the addition of Nd both the tensile properties and corrosion resistance were improved substantially.

Structure and mechanical properties of extruded Mg-Gd based alloy sheet

The Mg-8Gd-2Y-1Nd-0.3Zn-0.6Zr (wt.%) alloy sheet was prepared by hot extrusion technique, and the structure and mechanical properties of the extruded alloy were investigated. The results show that the alloy in different states is mainly composed of alpha-Mg solid solution and secondary phases of Mg5RE and Mg24RE5 (RE = Gd, Y and Nd). At aging temperatures from 200 degrees C to 300 degrees C the alloy exhibits obvious age-hardening response. Great improvement of mechanical properties is observed in the peak-aged state alloy (aged at 200 degrees C for 60 h), the ultimate tensile strength (sigma(b)), tensile yield strength (sigma(0.2)) and elongation (epsilon) are 376 MPa, 270 MPa and 14.2% at room temperature (RT), and 206 MPa. 153 MPa and 25.4% at 300 degrees C, respectively, the alloy exhibits high thermal stability.

Effect of La-Mg-based alloy addition on structure and electrochemical characteristics of Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy

Effect of La-Mg-based alloy (AB(5)) addition on Structure and electrochemical characteristics of Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy has been investigated systematically. XRD shows that the matrix phase structure is not changed after adding AB(5) alloy, however, the amount of the secondary phase increases with increasing AB(5) alloy content. The electrochemical measurements show that the plateau pressure Ti0.10Zr0.15V0.35Cr0.10Ni0.30 + x% La0.85Mg0.25Ni4.5Co0.35Al0.15 (X = 0, 1, 5, 10, 20) hydrogen storage alloys increase with increasing x, and the width of the pressure plateau first increases when x increases from 0 to 5 and then decreases as x increases further, and the maximum discharge capacity changes in the same trend.

Structure stability and strengthening mechanism of die-cast Mg-Gd-Dy based alloy

Mg-8Gd-1Dy-0.3Zn (wt.%) alloy was prepared by high-pressure die-casting technique. The thermal stability, mechanical properties at temperature range from room temperature to 573 K and strengthening mechanism was investigated. The results showed that the die-cast state alloy was mainly composed of fine cellular equiaxed grain. The fine porosity-free skin region was related to the aggregation of rare earth elements. The long lamellar-shaped stacking compound containing Zn and polygon-shaped precipitate were observed along the grain boundaries. The die-cast sample exhibited high mechanical properties and good thermal stability until 523 K.

In situ study of carbon nanotube formation by C2H2 decomposition on an iron-based catalyst

The properties and formation of nanotubes have been extensively studied, but very few deal with the catalytic production mechanism of nanotubes. Two different techniques, thermogravimetric analysis and UV-Raman, have been applied to analyse the carbon deposition by catalysed decomposition of acetylene over an iron-based catalyst. The nature of the produced carbon materials depends on reaction temperature. Also, TEM allows identification of carbon nanotubes, encapsulated particles, and other nanostructures, while UV-Raman confirms its graphitic and graphite-like nature. (C) 2000 Elsevier Science Ltd. All rights reserved.

Experimental and Modelling Studies of the Thermodynamics and Kinetics of Phase and Structural Transformations in a Gamma TiAl-based Alloy

This work combines microscopy, synchrotron radiation X-ray diffraction, differential scanning calorimetry and thermodynamic calculations in the characterisation of phase transformation behaviour of a Ti–46Al–1.9Cr–3Nb alloy upon continuous heating at constant rates. It has been found that the Ti–46Al–1.9Cr–3Nb alloy after being forged at 1200 °C without further treatment has a duplex microstructure consisting of fine equiaxed and lamellar ? grains with a small amount of a2 plates and particles and about 1 wt.% B2 phase. Differential scanning calorimetry revealed reproducibly several thermal effects upon heating of the as-forged alloy. These thermal effects are related to the equilibration and homogenisation of the sample, change of phase ratios between a2, ? and B2 phases in particular the increase of B2 in respect to a2 and ?, and the following five phase transformations: a2 + ? + B2 a + ? + B2, a + ? + B2 a + ?, ? + a a, a a + ß, a + ß a + ß + L. The observation of these transformations by differential scanning calorimetry is largely in agreement with literature phase diagrams and thermodynamic calculations, though care is needed to consider the different alloy compositions. Kinetics of the ? + a a phase transformation in the Ti–46Al–1.9Cr–3Nb alloy has been quantitatively derived from the calorimetry data, giving phase compositions at any point during the transformation upon continuous heating.