Resumo:
Potassium fluorrichterite (KNaCaMg5Si8O22F2) glass-ceramics were modified by either increasing the concentration of calcium (GC5) or by the addition of P2O5 (GP2). Rods (2 x 4 mm) of stoichiometric fluorrichterite (GST), modified compositions (GC5 and GP2) and 45S5 bioglass, which was used as the reference material, were prepared using a conventional lost-wax technique. Osteoconductivity was investigated by implantation into healing defects in the midshaft of rabbit femora. Specimens were harvested at 4 and 12 weeks following implantation and tissue response was investigated using computed microtomography (mu CT) and histological analyses. The results showed greatest bone to implant contact in the 45S5 bioglass reference material at 4 and 12 weeks following implantation, however, GST, GC5 and GP2 all showed direct bone tissue contact with evidence of new bone formation and cell proliferation along the implant surface into the medullary space. There was no evidence of bone necrosis or fibrous tissue encapsulation around the test specimens. Of the modified potassium fluorrichterite compositions, GP2 showed the greatest promise as a bone substitute material due to its osteoconductive potential and superior mechanical properties.
Resumo:
Das Gebiet der drahtlosen Kommunikationsanwendungen befindet sich in einem permanenten Entwicklungsprozess (Mobilfunkstandards: GSM/UMTS/LTE/5G, glo-bale Navigationssatellitensysteme (GNSS): GPS, GLONASS, Galileo, Beidou) zu immer höheren Datenraten und zunehmender Miniaturisierung, woraus ein hoher Bedarf für neue, optimierte Hochfrequenzmaterialien resultiert. Diese Entwicklung zeigt sich besonders in den letzten Jahren in der zunehmenden Entwicklung und Anzahl von Smartphones, welche verschiedene Technologien mit unterschiedlichen Arbeitsfrequenzen innerhalb eines Geräts kombinieren (data: 1G-4G, GPS, WLAN, Bluetooth). Die für zukünftige Technologien (z.B. 5G) benötigte Performance-steigerung kann durch die Verwendung von auf MIMO basierenden Antennensystemen realisiert werden (multiple-input & multiple-output, gesteuerte Kombination von mehreren Antennen) für welche auf dielectric Loading basierende Technologien als eine der vielversprechendsten Implementierungslösungen angesehen werden. rnDas Ziel dieser Arbeit war die Entwicklung einer geeigneten paraelektrischen Glaskeramik ($varepsilon_{r}$ > 20, $Qf$ > 5000 GHz, |$tau_f$| < 20 ppm/K; im GHz Frequenzbe-reich) im $mathrm{La_{2}O_{3}}$-$mathrm{TiO_{2}}$-$mathrm{SiO_{2}}$-$mathrm{B_{2}O_{3}}$-System für auf dielectric Loading basierende Mobilfunkkommunikationstechnologien als Alternative zu existierenden kommerziell genutzten Sinterkeramiken. Der Fokus lag hierbei auf der Frage, wie die makroskopi-schen dielektrischen Eigenschaften der Glaskeramik mit ihrer Mikrostruktur korreliert bzw. modifiziert werden können. Es konnte gezeigt werden, dass die dielektrischen Materialanforderungen durch das untersuchte System erfüllt werden und dass auf Glaskeramik basierende Dielektrika weitere vorteilhafte nichtelektro-nische Eigenschaften gegenüber gesinterten Keramiken besitzen, womit dielektrische Glaskeramiken durchaus als geeignete Alternative angesehen werden können. rnEin stabiles Grünglas mit minimalen Glasbildneranteil wurde entwickelt und die chemische Zusammensetzung bezüglich Entglasung und Redoxinstabilitäten optimiert. Geeignete Dotierungen für dielektrisch verlustarme $mathrm{TiO_{2}}$-haltige Glaskeramiken wurden identifiziert.rnDer Einfluss der Schmelzbedingungen auf die Keimbildung wurde untersucht und der Keramisierungsprozess auf einen maximalen Anteil der gewünschten Kristallphasen optimiert um optimale dielektrische Eigenschaften zu erhalten. Die mikroskopische Struktur der Glaskeramiken wurde analysiert und ihr Einfluss auf die makroskopischen dielektrischen Eigenschaften bestimmt. Die Hochfrequenzverlustmechanismen wurden untersucht und Antennen-Prototypenserien wurden analysiert um die Eignung von auf Glaskeramik basierenden Dielektrika für die Verwendung in dielectric Loading Anwendungen zu zeigen.
Resumo:
OBJECTIVES The aim of this study was to investigate micromechanical properties of five dual-curing resin cements after different curing modes including light curing through glass ceramic materials. MATERIALS AND METHODS Vickers hardness (VH) and indentation modulus (Y HU) of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA were measured after 1 week of storage (37 °C, 100 % humidity). The resin cements were tested following self-curing or light curing with the second-generation light-emitting diode (LED) curing unit Elipar FreeLight 2 in Standard Mode (1,545 mW/cm(2)) or with the third-generation LED curing unit VALO in High Power Mode (1,869 mW/cm(2)) or in XtraPower Mode (3,505 mW/cm(2)). Light curing was performed directly or through glass ceramic discs of 1.5 or 3 mm thickness of IPS Empress CAD or IPS e.max CAD. VH and Y HU were analysed with Kruskal-Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). RESULTS RelyX Unicem 2 Automix resulted in the highest VH and Y HU followed by BeautiCem SA, BisCem, SpeedCEM, and finally Panavia F2.0. Self-curing of RelyX Unicem 2 Automix and SpeedCEM lowered VH and Y HU compared to light curing whereas self-curing of Panavia F2.0, BisCem, and BeautiCem SA led to similar or significantly higher VH and Y HU compared to light curing. Generally, direct light curing resulted in similar or lower VH and Y HU compared to light curing through 1.5-mm-thick ceramic discs. Light curing through 3-mm-thick discs of IPS e.max CAD generally reduced VH and Y HU for all resin cements except SpeedCEM, which was the least affected by light curing through ceramic discs. CONCLUSIONS The resin cements responded heterogeneously to changes in curing mode. The applied irradiances and light curing times adequately cured the resin cements even through 1.5-mm-thick ceramic discs. CLINICAL RELEVANCE When light curing resin cements through thick glass ceramic restorations, clinicians should consider to prolong the light curing times even with LED curing units providing high irradiances.
Resumo:
Objectives The aim of this study was to measure the degree of conversion (DC) of five dual-curing resin cements after different curing modes with a second- and a third-generation light-emitting diode (LED) curing unit. Additionally, irradiance of both light curing units was measured at increasing distances and through discs of two glass ceramics for computer-aided design/manufacturing (CAD/CAM). Materials and methods Irradiance and spectra of the Elipar FreeLight 2 (Standard Mode (SM)) and of the VALO light curing unit (High Power Mode (HPM) and Xtra Power Mode (XPM)) were measured with a MARC radiometer. Irradiance was measured at increasing distances (control) and through discs (1.5 to 6 mm thickness) of IPS Empress CAD and IPS e.max CAD. DC of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA was measured with an attenuated total reflectance–Fourier transform infrared spectrometer when self-cured (negative control) or light cured in SM for 40 s, HPM for 32 s, or XPM for 18 s. Light curing was performed directly (positive control) or through discs of either 1.5- or 3-mm thickness of IPS Empress CAD or IPS e.max CAD. DC was analysed with Kruskal–Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). Results Maximum irradiances were 1,545 mW/cm2 (SM), 2,179 mW/cm2 (HPM), and 4,156 mW/cm2 (XPM), and all irradiances decreased by >80 % through discs of 1.5 mm, ≥95 % through 3 mm, and up to >99 % through 6 mm. Generally, self-curing resulted in the lowest DC. For some cements, direct light curing did not result in higher DC compared to when light cured through ceramic discs. For other cements, light curing through ceramic discs of 3 mm generally reduced DC. Conclusions Light curing was favourable for dual-curing cements. Some cements were more susceptible to variations in curing mode than others. Clinical relevance When light curing a given cement, the higher irradiances of the third-generation LED curing unit resulted in similar DC compared to the second-generation one, though at shorter light curing times.
Resumo:
Mode of access: Internet.
Resumo:
Cover title.
Resumo:
Femtosecond-pulsed laser writing of waveguides, a few mm long, is demonstrated; waveguides were written orthogonally to the writing beam inside the bulk of ErIII-doped oxyfluoride glasses at a depth of 160 mum. The writing beam was 795 nm wavelength, 54 fs pulse duration and 11 MHz repetition rate. Tracks were written at pulse energies of 13.1 nJ to 26.1 nJ and sample translational velocity of 10 mmmiddot.s-1 to 28 mmmiddots-1. The influence of translational velocity and pulse energy on the cross-sectional shape and integrity of the written tracks is reported. Tracks tend to be narrower as the pulse energy is lowered or translational velocity decreased. Above 22.9 nJ, pulse energy, tracks tend to crack. The estimated refractive index profile of one track has a maximum increase of refractive index of 0.003 at the centre. These glasses normally form nano-glass-ceramics on heat treatment just above the glass transformation temperature (Tg). Here, a post-fs-writing heat-treatment just above Tg causes nano-ceramming of the glass sample and removes a light-guiding peripheral region of the fs-written tracks suggesting that this region may have been fs-modified by stress alone. Waveguiding at 651 nm and 973 nm wavelengths, and upconversion, are demonstrated in optimally written tracks.
Resumo:
Femtosecond-pulsed laser writing of waveguides, a few mm long, is demonstrated; waveguides were written orthogonally to the writing beam inside the bulk of ErIII-doped oxyfluoride glasses at a depth of 160 mum. The writing beam was 795 nm wavelength, 54 fs pulse duration and 11 MHz repetition rate. Tracks were written at pulse energies of 13.1 nJ to 26.1 nJ and sample translational velocity of 10 mmmiddot.s-1 to 28 mmmiddots-1. The influence of translational velocity and pulse energy on the cross-sectional shape and integrity of the written tracks is reported. Tracks tend to be narrower as the pulse energy is lowered or translational velocity decreased. Above 22.9 nJ, pulse energy, tracks tend to crack. The estimated refractive index profile of one track has a maximum increase of refractive index of 0.003 at the centre. These glasses normally form nano-glass-ceramics on heat treatment just above the glass transformation temperature (Tg). Here, a post-fs-writing heat-treatment just above Tg causes nano-ceramming of the glass sample and removes a light-guiding peripheral region of the fs-written tracks suggesting that this region may have been fs-modified by stress alone. Waveguiding at 651 nm and 973 nm wavelengths, and upconversion, are demonstrated in optimally written tracks.
Resumo:
Poster presented at the 24th Annual Meeting of the Portuguese Dental Association, Lisbon, 12-14 November 2015.
Resumo:
In this paper we present some result on sol-gel derived silica-hafnia systems. In particular we focus on fabrication, morphological and spectroscopic assessment of Er(3+)-activated thin films. Two examples of silica-hafnia-derived waveguiding glass ceramics, prepared by top-down and bottom-up techniques are reported, and the main optical properties are discussed. Finally, some properties of activated microspherical resonators, having a silica core, obtained by melting the end of a telecom fiber, coated with an Er(3+)-doped 70SiO(2)-30HfO(2) film, are presented. (C) 2009 Elsevier B.V. All rights reserved.
Resumo:
The biological and therapeutic responses to hyperthermia, when it is envisaged as an anti-tumor treatment modality, are complex and variable. Heat delivery plays a critical role and is counteracted by more or less efficient body cooling, which is largely mediated by blood flow. In the case of magnetically mediated modality, the delivery of the magnetic particles, most often superparamagnetic iron oxide nanoparticles (SPIONs), is also critically involved. We focus here on the magnetic characterization of two injectable formulations able to gel in situ and entrap silica microparticles embedding SPIONs. These formulations have previously shown suitable syringeability and intratumoral distribution in vivo. The first formulation is based on alginate, and the second on a poly(ethylene-co-vinyl alcohol) (EVAL). Here we investigated the magnetic properties and heating capacities in an alternating magnetic field (141 kHz, 12 mT) for implants with increasing concentrations of magnetic microparticles. We found that the magnetic properties of the magnetic microparticles were preserved using the formulation and in the wet implant at 37 degrees C, as in vivo. Using two orthogonal methods, a common SLP (20 Wg(-1)) was found after weighting by magnetic microparticle fraction, suggesting that both formulations are able to properly carry the magnetic microparticles in situ while preserving their magnetic properties and heating capacities. (C) 2010 Elsevier B.V. All rights reserved.
Resumo:
Purpose: To compare the flexural strength of two glass-infiltrated high-strength ceramics and two veneering glass-ceramics.Materials and Methods: Four ceramic materials were tested: two glass-infiltrated high-strength ceramics used as framework in metal-free restorations [In-Ceram Zirconia IZ (Gr1) and In-Ceram Alumina IA (Gr2)], and two glass-ceramics used as veneering material in metal-free restorations [Vita VM7 (Gr3) and Vitadur-alpha (Gr4)]. Bar specimens (25 x 5 x 2 mm(3)) made from core ceramics, alumina, and zirconia/alumina composites were prepared and applied to a silicone mold, which rested on a base from a gypsum die material. The IZ and IA specimens were partially sintered in an In-Ceram furnace according to the firing cycle of each material, and then were infiltrated with a low-viscosity glass to yield bar specimens of high density and strength. The Vita VM7 and Vitadur-alpha specimens were made from veneering materials, by vibration of slurry porcelain powder and condensation into a two-part brass Teflon matrix (25 x 5 x 2 mm(3)). Excess water was removed with absorbent paper. The veneering ceramic specimens were then removed from the matrix and were fired as recommended by the manufacturer. Another ceramic application and sintering were performed to compensate the contraction of the feldspar ceramic. The bar specimens were then tested in a three-point bending test.Results: The core materials (Gr1: 436.1 +/- 54.8; Gr2: 419.4 +/- 83.8) presented significantly higher flexural strength (MPa) than the veneer ceramics (Gr3: 63.5 +/- 9.9; Gr4: 57.8 +/- 12.7).Conclusion: In-Ceram Alumina and Zirconia were similar statistically and more resistant than VM7 and Vitadur-alpha.
Resumo: