Tribological characteristics of A356 Al alloy-SiC(P) composite discs

The dry sliding wear and friction behaviour of A356 Al alloy and its composites containing 10 and 20 vol.% SiC(P) have been studied using pin-on-disc set up. In these tests, A356 Al alloy and its composites are used as disc whereas brake pad was used in the form of pins. Wear tests were carried out at a load of 192 N and the sliding speed was varied from 1 to 5 m/s. Tests were done for a sliding distance of 15 km. The effects of sliding velocity on the wear rate, coefficient of friction and nature of tribolayers formed on discs have been studied. Wear rates of composites as calculated by weight loss method, found to be negative at sliding speed of more than 2 m/s. Worn surfaces of pins and discs have been analyzed using scanning electron microscope. SEM and EDAX analysis of worn surfaces of composite discs showed formation of tribolayers, consisting of mixture of oxides of Al, Si, Cu, Ca, Ba, Mg, and Fe. In these layers, copper and barium content found to be increase with sliding speed in the case of composites. (C) 2011 Elsevier B.V. All rights reserved.

Análise tribológica na interface aço carbono SAE 1020 e poliamida 11 em sistemas de deslizamento automotivos

Sistemas deslizantes com interface formada com aços baixa liga e polímeros variados são vastamente utilizados na indústria automotiva em sistemas de transmissão de torque submetidas à carregamento axial. Geralmente esses sistemas são acoplados aos sistemas de direção e interagem quase diretamente com o usuário final do veículo. Para conhecer as condições de desgaste mais severas as quais esses sistemas são submetidos e tentar minimiza-las, foi proposta a análise tribológica, em tribômetro do tipo pino-no-disco, da interface aço SAE 1020 com poliamida 11 em água destilada, solução aquosa com 5% em massa de cloreto de sódio e solução aquosa com 184,21 g/l. de areia natural, de acordo com as normas técnicas automotivas VW PV1210:2010-02 e VW PV2982:2013-07. Os ensaios foram realizados em frequências de 3,0 Hz e 1,5 Hz com quantidade fixada em 10.000 ciclos de rotação. O potencial de corrosão em circuito aberto foi monitorado ao longo dos ensaios e a taxa de desgaste foi calculada. Foram evidenciados maiores coeficientes de atrito, maiores taxas de desgaste e maiores amplitudes de potencial de corrosão nas amostras ensaiadas em solução de areia; com valores mais brandos para as amostras ensaiadas em água destilada e valores intermediários para as amostras ensaiadas em solução de cloreto de sódio.

Tribological properties of mems materials measured on a small-scale device

Micro-electro-mechanical systems, MEMS, is a rapidly growing interdisciplinary technology within the general field of Micro-Systems Technology which deals with the design and manufacture of miniaturised machines with major dimensions at the scale of tens, to perhaps hundreds, of microns. Because they depend on the cube of a representative dimension, component masses and inertias rapidly become small as size decreases whereas surface and tribological effects, which often depend on area, become increasingly important. Although MEMS components and their areas of contact are small, tribological conditions, measured by contact pressures or acceptable wear rates, are demanding and technical and commercial success will require careful measurement and precise control of surface topography and properties. Fabrication of small numbers of MEMS devices designed to test potential material combinations can be prohibitively expensive and thus there is a need for small scale test facilities which mimic the contact conditions within a micro-machine without themselves requiring processing within a full semiconductor foundry. The talk will illustrate some initial experimental results from a small-scale experimental device which meets these requirements, examining in particular the performance of Diamond-Like-Carbon coatings on a silicon substrate. Copyright © 2005 by ASME.

Microabrasion : A novel method to assess surface degradation of UHMWPE following sterilisation and ageing

The ageing behaviour of ultra-high molecular weight polyethylene (UHMWPE) has been studied following gamma irradiation (25 or 40 kGy) in air. Accelerated ageing procedures used elevated temperature (70°C) and/or pressurised oxygen (5 bar). Shelf-aged UHMWPE was also studied. The variation in surface density and mechanical properties were determined following the various sterilisation and ageing treatments. Microabrasive wear testing was also performed. Wear rates were found to correlate well with stress at break for sterilised and aged UHMWPE but not with elongation to failure. It is proposed that the wear mechanism is fracture dominated and occurs following some disentanglement of the polymer chains. Wear also depends upon embrittlement of the surface layer due to its processing and ageing. Elongation to failure in a tensile test is not a good measure of this embrittlement whereas the microabrasion test provides more surface sensitive information concerning this property.

Micro-abrasion mechanisms of cast CoCrMo in simulated body fluids

The abrasion seen on some of the retrieved CoCrMo hip joints has been reported to be caused by entrained hard particles in vivo. However, little work has been reported on the abrasion mechanisms of CoCrMo alloy in simulated body environments. Therefore. this study covers the mapping of micro-abrasion wear mechanisms of cast CoCrMo induced by third body hard particles under a wide range of abrasive test conditions. This study has a specific focus on covering the possible in vivo wear modes seen on metal-on-metal (MoM) surfaces. Nano-indentation and nano-scratch tests were also employed to further investigate the secondary wear mechanisms-nano-scale material deformation that involved in micro-abrasion processes. This work addresses the potential detrimental effects of third body hard particles in vivo such as increased wear rates (debris generation) and corrosion (metal-ion release). The abrasive wear mechanisms of cast CoCrMo have been investigated under various wear-corrosion conditions employing two abrasives, SiC (similar to 4 mu m) and Al(2)O(3) (similar to 1 mu m), in two test solutions, 0.9% NaCl and 25% bovine serum. The specific wear rates, wear mechanisms and transitions between mechanisms are discussed in terms of the abrasive size, volume fraction and the test solutions deployed. The work shows that at high abrasive volume fractions, the presence of protein enhanced the wear loss due to the enhanced particle entrainment, whereas at much lower abrasive volume fractions, protein reduced the wear loss by acting as a boundary lubricant or rolling elements which reduced the abrasivity (load per particle) of the abrasive particles. The abrasive wear rate and wear mechanisms of the CoCrMo are dependent on the nature of the third body abrasives, their entrainment into the contact and the presence of the proteins. (C) 2009 Elsevier B.V. All rights reserved.

Interpretation of electrochemical measurements made during micro-scale abrasion-corrosion

This paper brings together and analyzes recent work based on the interpretation of the electrochemical measurements made on a modified micro-abrasion-corrosion tester used in several research programmes. These programmes investigated the role of abradant size, test solution pH in abrasion-corrosion of biomaterials, the abrasion-corrosion performance of sintered and thermally sprayed tungsten carbide surfaces under downhole drilling environments and the abrasion-corrosion of UNS S32205 duplex stainless steel. Various abrasion tests were conducted under two-body grooving, three-body rolling and mixed grooving-rolling abrasion conditions, with and without abrasives, on cast F75 cobalt-chromium-molybdenum (CoCrMo) alloy in simulated body fluids, 2205 in chloride containing solutions as well as sprayed and sintered tungsten carbide surfaces in simulated downhole fluids. Pre- and post-test inspections based on optical and scanning electron microscopy analysis are used to help interpret the electrochemical response and current noise measurements made in situ during micro-abrasion-corrosion tests. The complex wear and corrosion mechanisms and their dependence on the microstructure and surface composition as a function of the pH, abrasive concentration, size and type are detailed and linked to the electrochemical signals. The electrochemical versus mechanical processes are plotted for different test parameters and this new approach is used to interpret tribo-corrosion test data to give greater insights into different tribo-corrosion systems. Thus new approaches to interpreting in-situ electrochemical responses to surfaces under different abrasive wear rates, different abrasives and liquid environments (pH and NaCl levels) are made. This representation is directly related to the mechano-electrochemical processes on the surface and avoids quantification of numerous synergistic, antagonistic and additive terms associated with repeat experiments. (C) 2010 Elsevier Ltd. All rights reserved.

Micro-abrasion-corrosion of cast CoCrMo-Effects of micron and sub-micron sized abrasives

The abrasion damage on retrieved CoCrMo based hip joints is reported to be influenced by the entrainment of micron and sub-micron sized debris/hard particles. This paper represents the first attempt to look into the effects of relatively soft abrasives with micron and sub-micron dimensions on the abrasion mechanisms and the abrasion-corrosion performance of the cast CoCrMo in simulated hip joint environments. A modified micro-abrasion tester incorporating a liquid tank and a three-electrode electrochemical cell was used. Al O (300 nm and 1 μm) and sub-micron sized BaSO abrasives were chosen as being comparable in the size and hardness to the wear particles found in vivo. Results show that the specific wear rates of cast CoCrMo are dependent on the abrasive particle size, hardness and volume concentration. Larger particle size, higher hardness and greater abrasive volume fractions gave greater wear rates. The wear-induced corrosion current generally increases with increasing wear rates, and the presence of proteins seems to suppress the wear-induced corrosion current especially when abrasive volume fractions were high. This study shows that the nature of abrasives and the test solutions are both important in determining the wear mechanisms and the abrasion-corrosion response of cast CoCrMo. These findings provide new and important insights into the in vivo wear mechanisms of CoCrMo. © 2009 Elsevier B.V. All rights reserved.

Desgaste corrosivo-cavitativo-erosivo de um aço-carbono em meio aquoso com frações de sal (NaCl), CO2 e particulados sólidos (SiO2)

A batch of eighty-four coupons of low carbon steel were investigated at laboratory conditions under a corrosive, cavitative-corrosive (CO2) and corrosive-erosive (SiO2 + CO2) in an aqueous salt solution and two levels of temperature. The following measurements were made on Vickers (HV0,05, HV0,10, HV0,20) Microhardness tests at three levels of subsurface layer. A turbulent flow collided on the cylindrical sample, with and without mechanical stirring and gas bubbling, with and without fluid contamination by solid particles of SiO2, at two temperatures. Surface Roughness and Waviness, under two conditions "as received, after machining" and "after worn out", as well as gravimetric and electrochemical parameter were measured on the two opposite generatrices of each cylindrical sample, on the flow upstream (0°) and downstream (180°) by Profilometry, Mass Variation and Linear Polarization Resistance (LPR). The results of the Microhardness and Surface Texture of all coupons were subjected to statistical comparison, using the software Statgraphics® Centurion XVI, 95% statistical certainty, and significant differences were observed in some arrays of measurements. The corrosive wear rate measured by LPR and mass variation shown to be sensitive to the presence of bubbles and hydrodynamic fluctuations inside the cell, considering the temperature and contamination of corrosive fluid by solid particles. The main results of visual inspection relative to some topologies of the surface damages involving different mechanisms that were seen to give explanation for some fluctuations in wear rates of the steel experimentally investigated

Evaluation of the performance of α-SiAlON tool when turning Ti-6Al-4V alloy without coolant

Due to their high hardness and wear resistance, Si3N4 based ceramics are one of the most suitable cutting tool materials for machining cast iron, nickel alloys and hardened steels. However, their high degree of brittleness usually leads to inconsistent results and sudden catastrophic failures. This necessitates a process optimization when machining superalloys with Si3N4 based ceramic cutting tools. The tools are expected to withstand the heat and pressure developed when machining at higher cutting conditions because of their high hardness and melting point. This paper evaluates the performance of α-SiAlON tool in turning Ti-6Al-4V alloy at high cutting conditions, up to 250 m min-1, without coolant. Tool wear, failure modes and temperature were monitored to access the performance of the cutting tool. Test results showed that the performance of α-SiAl0N tool, in terms of tool life, at the cutting conditions investigated is relatively poor due probably to rapid notching and excessive chipping of the cutting edge. These facts are associated with adhesion and diffusion wear rate that tends to weaken the bond strength of the cutting tool.

Physicochemical analysis of Ti-Si-B powder aalloys

Titanium alloys of Ti-Si-B system were manufactured by blended elemental powder method using Ti, Si and B powders as starting materials. It was found that uniaxial and isostatic pressing followed by hot pressing at around 1000°C, for 20 minutes, provided good densification of such alloys. The physicochemical studies were performed by means of scanning electron microscopy, X-ray diffraction, atomic force microscopy and microindentation/wear tests. The investigations revealed a multiphase microstructure formed mainly by α-titanium, Ti6Si2B, Ti5Si3, TiB and Ti3Si phases. The phase transformations after pressureless sintering at 1200°C was also studied by X-ray diffraction for the Ti-18Si-6B composition. As stated in some other researches, these intermetallics in the α-titanium matrix provide high wear resistance and hardness, with the best wear rate of 0.2 mm3/N.m and the highest hardness of around 1300 HV. © (2012) Trans Tech Publications, Switzerland.

Avaliação do desempenho de compósitos de PPA/Fibra de vidro para aplicação em bombas de óleo de motores de motocicletas

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Effect of fluoride varnish supplemented with sodium trimetaphosphate on enamel erosion and abrasion

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito do oxigênio intersticial no módulo de elasticidade de Ligas Ti-15Mo-xZr(x=5,10,15%p)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tribocorrosion behaviour of hot pressed CoCrMo−Al2O3 composites for biomedical applications

Alumina/alumina wear couple can lower the wear rates and thus metallic ion releasing on load bearing metallic implant materials. However, the low fracture toughness of ceramics is still a major concern. Therefore, the present study aims to process and to triboelectrochemically characterise the 5 and 10 vol.-%Al2O3 reinforced CoCrMo matrix composites. Corrosion and tribocorrosion behaviour of the composites were investigated in 8 g L−1 NaCl solution at body temperature. Corroded and worn surfaces were investigated by a field emission gun scanning electron microscope equipped with energy dispersive X-ray spectroscopy. After tribocorrosion experiments, wear rates were calculated using a profilometer. Results suggest that Al2O3 particle addition decreased the tendency of CoCrMo alloy to corrosion under both static and tribocorrosion conditions. However, no significant influence on the corrosion and wear rates was observed in composites mainly due to increased porosity and insufficient matrix/reinforcement bonding.

Abrasão-corrosão em corpos moedores na moagem de minério de ferro.

O desgaste de corpos moedores constitui um custo importante na indústria mineral, que depende da operação de cominuição para promover a liberação das espécies minerais e produzir concentrados. Embora se conheça alguns dos mecanismos individuais que afetam o desgaste, a interação entre eles num sistema tão complexo quanto um moinho ainda precisa ser melhor entendido. Este trabalho avaliou o efeito da corrosão no desgaste de bolas de aço e de ferro fundido branco de alto cromo durante a moagem de minério de ferro, através de ensaios eletroquímicos e de desgaste em moinho de laboratório. Foi feita uma alteração no modo tradicional de realização do ensaio de polarização potenciodinâmica, utilizando polpa de minério de ferro a 70% de sólidos (em peso) como eletrólito. As curvas de polarização obtidas foram compatíveis com os resultados de desgaste, de modo que as curvas correspondentes aos metais na condição mais ativa estavam associadas às menores taxas de desgaste nos ensaios de moagem em laboratório, demonstrando que os ensaios de polarização realizados podem ser utilizados como indicativo do comportamento do metal na moagem de minério de ferro. Sobretudo, os testes demonstraram que o desgaste das bolas de aço é devido, principalmente, à abrasão, já que uma pequena diferença, de apenas 8%, foi observada nas taxas de desgaste nas condições avaliadas (polpa no pH 5 e pH 8). Por outro lado, as bolas de ferro fundido branco de alto cromo, que são mais caras, são mais propensas a resistir ao desgaste em polpa ácida, em que a taxa de desgaste foi 40% menor que a determinada em pH 8.