Electrokinetic and Rheological Properties of Nano Zirconia in the Presence of Rhamnolipid Biosurfactant

In this paper, the effect of rhamnolipid biosurfactant on the electrokinetic and rheological behavior of nanozirconia particles is reported. The effect of pH, concentration of biosurfactant, and solids loading on ζ-potential and rheological behavior was investigated. ζ-potential measurements showed that adsorption of biosurfactant shifted the iso-electric point of zirconia with increasing biosurfactant concentration. The surface of zirconia became more electronegative in the presence of biosurfactant indicating a strong interaction. Maximum charge was obtained in the presence of about 230 ppm of biosurfactant. Rheological tests at pH 7 revealed that the zirconia suspension is viscous at high solids loading and addition of biosurfactant decreased the viscosity substantially especially at high solids loading (>50 wt%). Sedimentation tests confirmed that the biosurfactant is a good dispersant for zirconia particles at pH values of 7 and above.

Electrical and structural properties of zirconia thin films prepared by reactive magnetron sputtering

Thin films of ZrO2 were prepared by reactive magnetron sputtering. Annealing of the films exhibited a drastic change in the properties due to improved crystallinity and packing density. The root mean square roughness of the sample observed from atomic force microscope is about 5.75 nm which is comparable to the average grain size of the thin film which is about 6 nm obtained from X-ray diffraction. The film annealed at 873 K exhibits an optical band gap of around 4.83 eV and shows +4 oxidation state of zirconium indicating fully oxidized zirconium, whereas higher annealing temperatures lead to oxygen deficiency in the films and this is reflected in their properties. A discontinuity in the imaginary part of the AC conductivity was observed in the frequency range of tens of thousands of Hz, where as, the real part does not show such behavior.

Pd and Pt ions as highly active sites for the water-gas shift reaction over combustion synthesized zirconia and zirconia-modified ceria

Noble metal substituted ionic catalysts were synthesized by solution combustion technique. The compounds were characterized by X-ray diffraction, FT-Raman spectroscopy, and X-ray photoelectron spectroscopy. Zirconia supported compounds crystallized in tetragonal phase. The solid solutions of ceria with zirconia crystallized in fluorite structure. The noble metals were substituted in ionic form.The water-gas shift reaction was carried out over the catalysts.Negligible conversions were observed with unsubstituted compounds. The substitution of a noble metal ion was found to enhance the reaction rate. Equilibrium conversion was obtained below 250 degrees C in the presence of Pt ion substituted compounds. The formation of Bronsted acid-Bronsted base pairs was proposed to explain the activity of zirconia catalysts. The effect of oxide ion vacancies on the reactions over substituted ceria-zirconia solid solutions was established. (c)2010 Elsevier B.V. All rights reserved.

The Influence of Titania on Creep in Superplastic Zirconia

Detailed high-temperature compression creep experiments on a pure 3 mol% yttria-stabilized tetragonal zirconia (3YTZ) and 3YTZ doped with 4.8 wt% TiO2 revealed that both materials exhibit a similar transition in stress exponents from n similar to 1 to n similar to 2 with a decrease in stress. The stress exponent of 1 and the inverse grain size dependence p of similar to 3 are consistent with the Coble diffusion creep at high stresses; the increase in stress exponent at low stresses is attributed to an interface-controlled diffusion creep process. Measurements revealed that grain-boundary sliding contributes to >similar to 50% of the total strain in both regions with n similar to 1 and n similar to 2, indicating the operation of the same fundamental deformation process in both regions. The creep data indicate that doping with TiO2 leads to an increase in the grain-boundary diffusion coefficients. The increase observed in the dihedral angle with doping is also consistent with the increase in grain boundary diffusion coefficient and the reported enhanced ductility in such materials.

Dispersion of Zirconia in the Presence of Dolapix PC75

The effect of Dolapix PC75 on the electrokinetic and rheological behavior of nano zirconia particles is presented here. The effect of pH, concentration of dispersant, and solids loading on zeta-potential and rheological behavior was studied. Upon interaction with the dispersant, the iso-electric point of zirconia changed and the surface became more negative with increasing concentration of dispersant, suggesting a strong interaction. Maximum charge was obtained in the presence of about 200ppm of Dolapix. Rheological tests at pH 7 showed that the zirconia suspension is viscous at high solids loading and addition of the dispersant decreased the viscosity substantially especially at high solids loading (50wt%). Sedimentation tests confirmed that Dolapix PC75 is a good dispersant for zirconia particles at pH values of 7 and above.

Phase Relations in the System CaO-Fe2O3-Y2O3 at 1273 K and Compatibility Between Y1-xCaxFeO3-0.5x and Stabilized Zirconia

Phase relations in the system CaO-Fe2O3-Y2O3 in air (P-O2/P-o = 0.21) were explored by equilibrating samples representing eleven compositions in the ternary at 1273 K, followed by quenching to room temperature and phase identification using XRD. Limited mutual solubility was observed between YFeO3 and Ca2Fe2O5. No quaternary oxide was identified. An isothermal section of the phase diagram at 1273 K was constructed from the results. Five three-phase regions and four extended two-phase regions were observed. The extended two-phase regions arise from the limited solid solutions based on the ternary oxides YFeO3 and Ca2Fe2O5. Activities of CaO, Fe2O3 and Y2O3 in the three-phase fields were computed using recently measured thermodynamic data on the ternary oxides. The experimental phase diagram is consistent with thermodynamic data. The computed activities of CaO indicate that compositions of CaO-doped YFeO3 exhibiting good electrical conductivity are not compatible with zirconia-based electrolytes; CaO will react with ZrO2 to form CaZrO3.

Effects of thermal annealing on the properties of zirconia films prepared by ion-assisted deposition

The effect of thermal annealing in the range 300–800 °C on the properties of zirconia films prepared by ion assisted deposition was studied. It was found that at low temperature the cubic phase is formed. This phase is stable up to 700 °C. All the films exhibit a monophasic monoclinic structure at 800 °C. The stress, estimated from X-ray patterns, shows a transition from tensile to compressive with increasing ion fluence. The refractive index and extinction coefficient do not seem to change appreciably up to 700 °C, showing a marked degradation thereafter. Single step annealing to the highest temperature was found to result in better stability than multistep annealing.

Hydrazine carboxylate precursors to fine particle titania, zirconia and zirconium titanate

Titanyl hydrazine carboxylate dihydrate, TiO(N2H3COO)2.2H2O, zirconyl hydrazine carboxylate dihydrate, ZrO(N2H3COO)2.2H2O and their solid solution, ZrTiO2(N2H3COO)4.4H2O have been prepared for the first time and investigated as precursors to fine particle TiO2, ZrO2 and ZrTiO4 respectively. Titania(anatase) formed has a very high surface area of 110 m2/g and zirconium titanate showed very low dielectric loss (4 x 10(-4)).

Phase Transformation Introduced by Mechanical and Chemical Surface Preparations of Tetragonal Zirconia Polycrystals

Cutting of Y2O3-doped TZP rods by a low-speed diamond saw introduces an unidentified, metastable phase X (x-ZrO2) coexisting with the tetragonal (t-ZrO2) and the monoclinic (m-ZrO2) phases initially present in the sample. Further mechanical deformation of the cut surface by indentation or polishing sustains the x-ZrO2. Chemical etching removes the x-ZrO2 and increases the m-ZrO2content.

Structural, mechanical and biocompatibility studies of hydroxyapatite-derived composites toughened by zirconia addition

Hydroxyapatite(OHAp)-based ceramic composites with added ZrO2 have been prepared both by sintering at 1400 °C and by hot isostatic pressing (HIP) at 1450 °C and 140 MPa pressure (argon atmosphere). The development of the crystalline phases and the microstructure of the composites have been examined using X-ray diffraction, electron microscopy, infrared and magic-angle spinning nuclear magnetic resonance (MASNMR) spectroscopic techniques. The fracture toughness and biocompatibility of the composites have also been studied. The effect of the addition of CeO2- and Y2O3-stabilized ZrO2 and of simple monoclinic ZrO2 to the initial physical mixture, on the structure and properties of the resulting composites has been investigated. In most of the sintered or HIP samples, the OHAp decomposes into tricalcium phosphate (β-TCP). CaO, which forms as a product of decomposition, dissolves completely in ZrO2 and stabilizes the latter in its cubic/tetragonal phase. Presence of the β-TCP phase in the product seems to be the result of a structural synergistic effect of hexagonal OHAp. Two structurally distinct orthophosphate groups have been identified in the composites by MASNMR of 31P and attributed to decomposition products of OHAp at higher temperatures. The composites possess high KIC values (2–3 times higher than that of pure OHAp). Decomposition of hydroxyapatite gives rise to differences in microstructure between HIP and simply sintered composites although fracture toughness values are similar in magnitude indicating the presence of several toughening mechanisms. The in vitro SP2-O cell test suggests that these composites possess good biocompatibility. The combination of good biocompatibility, desirable microstructure and easy availability of initial reactants indicates that the simply sintered composite of OHAp and monoclinic ZrO2(ZAP-30) appears to be the most suitable for prosthetic applications.

Cement stabilised rammed earth. Part A: compaction characteristics and physical properties of compacted cement stabilised soils

Rammed earth is used for load bearing walls of buildings and there is growing interest in this low carbon building material. This paper is focused on understanding the compaction characteristics and physical properties of compacted cement stabilised soil mixtures and cement stabilised rammed earth (CSRE). This experimental study addresses (a) influence of soil composition, cement content, time lag on compaction characteristics of stabilised soils and CSRE and (b) effect of moulding water content and density on compressive strength and water absorption of compacted cement stabilised soil mixes. Salient conclusions of the study are (a) compaction characteristics of soils are not affected by the addition of cement, (b) there is 50% fall in strength of CSRE for 10 h time lag, (c) compressive strength of compacted cement stabilised soil increases with increase in density irrespective of moulding moisture content and cement content, and (d) compressive strength increases with the increase in moulding water content and compaction of CSRE on the wet side of OMC is beneficial in terms of strength.

Cement stabilised rammed earth. Part B: compressive strength and stress-strain characteristics

Strength and behaviour of cement stabilised rammed earth (CSRE) is a scantily explored area. The present study is focused on the strength and elastic properties of CSRE. Characteristics of CSRE are influenced by soil composition, density of rammed earth, cement and moisture content. The study is focused on examining (a) role of clay content of the soil on strength of CSRE and arriving at optimum clay fraction of the soil mix, (b) influence of moisture content, cement content and density on strength and (c) stress-strain relationships and elastic properties for CSRE. Major conclusions are (a) there is considerable difference between dry and wet compressive strength of CSRE and the wet to dry strength ratio depends upon the clay fraction of soil mix and cement content, (b) optimum clay fraction yielding maximum compressive strength for CSRE is about 16%, (c) strength of CSRE is highly sensitive to density and for a 20% increase in density the strength increases by 300-500% and (d) in dry state the ultimate strain at failure for CSRE is as high as 1.5%, which is unusual for brittle materials.

Creep in TiO2 doped Zirconia: Implications for high strain rate superplasticity

In ceramics, dopants offer the possibility of higher creep rates by enhancing diffusion. The present study examines the potential for high strain rate superplasticity in a TiO2 doped zirconia, by conducting creep experiments together with microstructural characterization. It is shown that both pure and doped zirconia exhibit transitions in creep behaviour from Coble diffusion creep with n similar to 1 to an interface controlled process with n similar to 2. Doping with TiO2 enhances the creep rate by over an order of magnitude. There is evidence of substantial grain boundary sliding, consistent with diffusion creep.

Influence of grain boundary sliding on diffusion in yttria doped zirconia

Grain boundary sliding during high temperature deformation can lead to stress concentrations and an enhancement of diffusion in mobile boundaries. Experiments were conducted on a fine grained 3 mol% yttria stabilized tetragonal zirconia, under conditions associated with superplastic flow involving grain boundary sliding. Tracer diffusion studies under creep conditions and without load indicate that there is no enhancement in either the lattice or grain boundary diffusivities. The experimental creep data are consistent with an interface controlled diffusion creep mechanism. (C) 2011 Elsevier Ltd. All rights reserved.

Synthesis and properties of zirconia thin films

Thin films of zirconia have been synthesized using reactive DC magnetron sputtering. It has been found that films with good optical constants, high refractive index (1.9 at 600 nm) and low extinction coefficient can be prepared al ambient temperatures. The optical constants and band gnp and hence the composition nle dependent on the deposition parameters such as target power, rate of deposition and oxygen background pressure. Thermal annealing of the films revealed that tile films showed optical and crystalline inhomogeneity and also large variations in optical constants.