Effect of silica coating combined to a MDP-based primer on the resin bond to Y-TZP ceramic

The aim of this study was to evaluate the influence of silica coating and 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based primer applications upon the bonding durability of a MDP-based resin cement to a yttrium stabilized tetragonal zirconia (Y-TZP) ceramic. Ninety-six Y-TZP tabs were embedded in an acrylic resin (free surface for adhesion: 5 x 5 mm(2)), ground finished and randomly divided into four groups (N = 24) according to the ceramic surface conditioning: (1) cleaning with isopropanol (ALC); (2) ALC + phosphoric acid etching + MDP-based primer application (MDP-primer); (3) silica coating + 3-methacryloyloxypropyl trimethoxysilane (MPS)-based coupling agent application (SiO(2) + MPS-Sil); and (4) SiO(2) + MDP-primer. The MDP-based resin cement was applied on the treated surface using a cylindrical mold (diameter=3 mm). Half of the specimens from each surface conditioning were stored in distilled water (37 C, 24 h) before testing. Another half of the specimens were stored (90 days) and thermo-cycled (12,000x) during this period (90d/TC) before testing. A shear bond strength (SBS) test was performed at a crosshead speed of 0.5 mm/min. Two factors composed the experimental design: ceramic conditioning strategy (in four levels) and storage condition (in two levels), totaling eight groups. After 90d/TC (Tukey; p < 0.05), SiO(2) + MDP-primer (24.40 MPa) promoted the highest SBS. The ALC and MDP-primer groups debonded spontaneously during 90d/TC. Bonding values were higher and more stable in the SiO2 groups. The use of MDP-primer after silica coating increased the bond strength. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part 8: Appl Biomater 95B: 69-74, 2010.

Repair bond strength of a resin composite to alumina-reinforced feldspathic ceramic

This study compared the microtensile bond strength of a repair resin to an alumina-reinforced feldspathic ceramic (Vitadur-alpha, Vita) after 3 surface conditioning methods: Group 1, etching with 9.6% hydrofluoric acid for 1 minute plus rinsing and drying, followed by application of silane for 5 minutes; group 2, airborne particle abrasion with 110-mm aluminum oxide using a chairside air-abrasion device followed by silane application for 5 minutes; group 3, chairside tribochemical silica coating with 30-mu m SiOx followed by silane application for 5 minutes (N = 30). Group 1 presented the highest mean bond strength (19.7 +/- 3.8 MPa), which was significantly higher than those of groups 2 (10 +/- 2.6 MPa) and 3 (10.4 +/- 4 MPa) (P <.01). Scanning electron microscope analysis of the failure modes demonstrated predominantly mixed types of failures, with adhesive and/or cohesive failures in all experimental groups.

Adhesive Quality of Self-adhesive and Conventional Adhesive Resin Cement to Y-TZP Ceramic Before and After Aging Conditions

Purpose: This study evaluated the adhesive quality of simplified self-adhesive and conventional resin cements to Y-TZP in dry and aged conditions. Methods: Y-TZP ceramic blocks (N=192) (5 x 5 x 2 mm) were embedded in acrylic resin and randomly divided into two groups, based on surface conditioning: 96% isopropanol or chairside tribochemical silica coating and silanization. Conditioned ceramics were divided into four groups to receive the resin cements (Panavia F 2.0, Variolink II, RelyX U100 and Maxcem). After 24 hours, half of the specimens (n=12) from each group were submitted to shear bond strength testing (0.5 nun/minute). The remaining specimens were tested after 90 days of water storage at 37 degrees C and thermocycling (12,000x, 5 degrees C-55 degrees C). Failure types were then assessed. The data were analyzed using three-way ANOVA and the Tukey's test (alpha=0.05). Results: Significant effects of ceramic conditioning, cement type and storage conditions were observed (p<0.0001). The groups cleaned using alcohol only showed low bond strength values in dry conditions and the bond strength was reduced dramatically after aging. Groups conditioned using silica coating and silanization showed higher bond strengths both in dry and aged conditions. A high number of specimens failed prematurely prior to testing when they were cleaned using 96% isopropanol. Conclusion: Overall, silica coating and silanization showed higher, stable bond strengths with and without aging. The durability of resin-ceramic adhesion varied, depending on the adhesive cement type.

Fatigue resistance of the bond of a glass-infiltrated alumina ceramic to human dentin

Purpose: To evaluate the fatigue resistance of the bond between dentin and glass-infiltrated alumina ceramic, using different luting protocols. Materials and Methods: The null hypothesis is that the fatigue resistance varies with the luting strategy. Forty blocks of In-Ceram Alumina were prepared, and one surface of each block was abraded with 110-μm aluminum oxide particles. Then, the blocks were luted to flat dentin surfaces of 40 human third molars, using 4 different luting strategies (luting system [LS]/ceramic surface conditioning [CSC]) (n=10): (G1) [LS] RelyX-Unicem/[CSC] airborne abrasion with 110-μm Al2O3 particles; (G2) [LS] One-Step + Duo-Link (bis-GMA-based resin)/[CSC] etching with 4% hydrofluoric acid + silane agent; (G3) [LS] ED-Primer + Panavia F (MDP-based resin)/[CSC] Al2O 3; (G4) [LS] Scotchbond1+RelyX-ARC (bis-GMA-based resin)/[CSC] chairside tribochemical silica coating (air abrasion with 30-μm SiO x particles + silane). After 24 h of water storage at 37°C, the specimens were subjected to 106 fatigue cycles in shear with a sinusoidal load (0 to 21 N, 8 Hz frequency, 37°C water). A fatigue survivor score was given, considering the number of the fatigue cycles until fracture. The failure modes of failed specimens were observed in a SEM. Results: G3 (score = 5.9, 1 failure) and G4 (score = 6, no failures) were statistically similar (p = 0.33) and had significantly higher fatigue resistance than G1 (score = 3.9, 5 failures) and G2 (score = 3.7, 6 failures) (p < 0.03). SEM analysis of fractured specimens of G1 and G2 showed that almost all the failures were between ceramic and cement. Conclusion: The MDP-based resin cement + sandblasting with Al2O3 particles (G3) and bis-GMA-based resin cement + tribochemical silica coating (G4), both using the respective dentin bonding systems, were the best luting protocols for the alumina ceramic. The null hypothesis was confirmed.

Microtensile bond strength of a repair composite to leucite-reinforced feldspathic ceramic

The purpose of this study was to evaluate the microtensile bond strength of a repair composite resin to a leucite-reinforced feldspathic ceramic (Omega 900, VITA) submitted to two surface conditionings methods: 1) etching with hydrofluoric acid + silane application or 2) tribochemical silica coating. The null hypothesis is that both surface treatments can generate similar bond strengths. Ten ceramic blocks (6x6x6 mm) were fabricated and randomly assigned to 2 groups (n=5), according to the conditioning method: G1- 10% hydrofluoric acid application for 2 min plus rinsing and drying, followed by silane application for 30 s; G2- airborne particle abrasion with 30 μm silica oxide particles (CoJet-Sand) for 20 s using a chairside air-abrasion device (CoJet System), followed by silane application for 5 min. Single Bond adhesive system was applied to the surfaces and light cured (40 s). Z-250 composite resin was placed incrementally on the treated ceramic surface to build a 6x6x6 mm block. Bar specimens with an adhesive area of approximately 1 ± 0.1 mm2 were obtained from the composite-ceramic blocks (6 per block and 30 per group) for microtensile testing. No statistically significant difference was observed between G1 (10.19 ± 3.1 MPa) and G2 (10.17 ± 3.1 MPa) (p=0.982) (Student's t test; á = 0.05). The null hypothesis was, therefore, accepted. In conclusion, both surface conditioning methods provided similar microtensile bond strengths between the repair composite resin and the ceramic. Further studies using long-term aging procedures should be conducted.

Shear bond strength of resin cement bonded to alumina ceramic after treatment by aluminum oxide sandblasting or silica coating

Purpose: To evaluate the shear bond strength and bond durability between a dual-cured resin cement (RC) and a high alumina ceramic (In-Ceram Alumina), subjected to two surface treatments. Materials and Methods: Forty disc-shaped specimens (sp) (4-mm diameter, 5-mm thick) were fabricated from In-Ceram Alumina and divided into two groups (n = 20) in accordance with surface treatment: (1) sandblasting by aluminum oxide particles (50 μm Al 2O 3) (SB) and (2) silica coating (30 μm SiO x) using the CoJet system (SC). After the 40 sp were bonded to the dual-cured RC, they were stored in distilled water at 37°C for 24 hours. After this period, the sp from each group were divided into two conditions of storage (n = 10): (a) 24 h-shear bond test 24 hours after cementation; (b) Aging-thermocycling (TC) (12,000 times, 5 to 55°C) and water storage (150 days). The shear test was performed in a universal test machine (1 mm/min). Results: ANOVA and Tukey (5%) tests noted no statistically significant difference in the bond strength values between the two surface treatments (p= 0.7897). The bond strengths (MPa) for both surface treatments reduced significantly after aging (SB-24: 8.2 ± 4.6; SB-Aging: 3.7 ± 2.5; SC-24: 8.6 ± 2.2; SC-Aging: 3.5 ± 3.1). Conclusion: Surface conditioning using airborne particle abrasion with either 50 μm alumina or 30 μm silica particles exhibited similar bond strength values and decreased after long-term TC and water storage for both methods. © 2011 by The American College of Prosthodontists.

O efeito do fator de crescimento de fibroblastos básico aplicado em superfícies radiculares condicionadas com cloridrato de tetraciclina ou EDTA na morfologia e densidade de fibroblastos. Estudo in vitro

Pós-graduação em Odontologia - FOAR

Adesão de um cimento resinoso a uma cerâmica feldspática: avaliação da resistência adesiva, ângulo de contato e ph, em função de diferentes técnicas de condicionamento

Pós-graduação em Odontologia Restauradora - ICT

Efeito do condicionamento radicular na reparação periodontal de defeitos tipo deiscência: Estudo experimental em cães

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Filmes de SiOx crescidos em substrato de zircônia tetragonal policristalina estabilizada por ítria: influência na durabilidade da adesão a cimentos resinosos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união de reparos de resinas compostas nanoparticuladas e nanohíbridas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Adhesion of substrate-adherent combinations for early composite repairs: Effect of intermediate adhesive resin application

This study evaluated the effect of intermediate adhesive resin application (IAR) on tensile bond strength (TBS) for early composite repairs in situations where substrate and repair composite bonded together were once of the same kind with the substrate (similar) and once other than the substrate material (dissimilar). Specimens from three types of composites (TPH Spectrum (TPH), Charisma (CHA) and Filtek Z250 (Z250)) were fabricated. The specimens in each composite group (n=72) were randomly divided into six subgroups (n=12). In each composite group, the similar and two dissimilar composites were bonded onto the substrates once using an IAR (Adper Single Bond Plus) and once without. After water storage for I week at 37 degrees C, substrate-adherent combinations were submitted to tensile test. Data were analyzed with three-way ANOVA and Tukey's tests (alpha=0.05). The substrate-adherent combination (p=0.0001), adherent (repair) composite (p=0.0001), and application of IAR (p=0.0001) significantly affected the results. Utilization of IAR improved the repair bond strength for all composite combinations. (C) 2013 Elsevier Ltd. All rights reserved.

Silica-based Nano-coating on Zirconia Surfaces Using Reactive Magnetron Sputtering: Effect on Chemical Adhesion of Resin Cements

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação do tempo e da concentração do condicionamento com ácido fluorídrico sobre a resistência de união entre cerâmica e cimento resinoso

The aim of this study was to verify through microtensile test the influence of time and concentration of surface conditioning with hydrofluoric acid and its interference in the adhesion of dual resin cement to porcelain.We used 32 bodies of glass-ceramic lithium disilicate system IPS e.max Press LT with dimensions of 6mm thick, 8 mm in length and 8 mm in length, which will be molded to obtain composite resin blocks corresponding to blocks ceramics. Ceramic and resin blocks were divided into 16 groups (n = 4) and numbered according to the concentration of hydrofluoric acid (2.5%, 5%, 7.5% and 10%) and conditioning time (20 seconds, 40 seconds, 1 minute and 2 minutes). The blocks were cleaned in ultrasonic apparatus with distilled water and dried with compressed air, subjected to acid etching and air-jet washed with water, dried with compressed air and received application of silane agent Monobond-S, followed by adhesive Excite ( Ivoclar Vivaden). Each ceramic block was bonded to the corresponding block of resin through the resin cement Multilink Automix. The specimens were cut to obtain nine micro samples for each set of ceramic-resin with 1 mm X 1 mm X 12 mm in length, which were submitted to microtensile test. The results were analyzed with descriptive statistics and analysis of variance with significance level of 5%, revealing that there were statistically significant (p = 0.000001 <0.05). From the Tukey test can be concluded that etching with hydrofluoric acid and 2.5% for 120 seconds gave the best bond strength, however, no statistical difference between the conditioning with the same acid in the concentration of 5.0% for 20 to 40 seconds

Ceramic Primer Heat-Treatment Effect on Resin Cement/Y-TZP Bond Strength

The purpose of this study was to evaluate the effect of different heat-treatment strategies for a ceramic primer on the shear bond strength of a 10-methacryloyloxydecyl-dihydrogen-phosphate (MDP)-based resin cement to a yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic. Specimens measuring 4.5 x 3.5 x 4.5 mm(3) were produced from Y-TZP presintered cubes and embedded in polymethyl methacrylate (PMMA). Following finishing, the specimens were cleaned using an ultrasound device and distilled water and randomly divided into 10 experimental groups (n=14) according to the heat treatment of the ceramic primer and aging condition. The strategies used for the experimental groups were: GC (control), without primer; G20, primer application at ambient temperature (20 degrees C); G45, primer application + heat treatment at 45 degrees C; G79, primer application + heat treatment at 79 degrees C; and G100, primer application + heat treatment at 100 degrees C. The specimens from the aging groups were submitted to thermal cycling (6000 cycles, 5 degrees C/55 degrees C, 30 seconds per bath) after 24 hours. A cylinder of MDP-based resin cement (2.4 mm in diameter) was constructed on the ceramic surface of the specimens of each experimental group and stored for 24 hours at 37 degrees C. The specimens were submitted to a shear bond strength test (n=14). Thermal gravimetric analysis was performed on the ceramic primer. The data obtained were statistically analyzed by two-way analysis of variance and the Tukey test (alpha=0.05). The experimental group G79 without aging (7.23 +/- 2.87 MPa) presented a significantly higher mean than the other experimental groups without aging (GC: 2.81 +/- 1.5 MPa; G20: 3.38 +/- 2.21 MPa; G100: 3.96 +/- 1.57 MPa), showing no difference from G45 only (G45: 6 +/- 3.63 MPa). All specimens of the aging groups debonded during thermocycling and were considered to present zero bond strength for the statistical analyses. In conclusion, heat treatment of the metal/zirconia primer improved bond strength under the initial condition but did not promote stable bonding under the aging condition.