Adhesives bonded to erbium:yttrium-aluminum-garnet laser-irradiated dentin: transmission electron microscopy, scanning electron microscopy and tensile bond strength analyses

The aim of this in vitro study was to investigate the effect of erbium:yttrium-aluminum-garnet (Er:YAG) laser irradiation on dentinal collagen by transmission electron microscopy and to analyze the resin-dentin interface by scanning electron microscopy. A tensile bond strength test was also applied. Specimens from 69 sound human third molars were randomly divided into three groups: control (no laser), and two irradiated groups, laser 250 (250 mJ/2 Hz) and laser 400 (400 mJ/4 Hz). Then, specimens were restored with two adhesive systems, an etch-and-rinse or a self-etch system. Although ultrastructural examination showed a modified surface in the irradiated dentin, there was no statistical difference in bond strength values between the laser groups and controls (P < 0.05). In conclusion, the use of Er:YAG laser for ablating human dentin did not alter the main adhesion parameters when compared with those obtained by conventional methods, thus reinforcing its use in restorative dentistry.

Direct comparison of the bond strength results of the different test methods: A critical literature review

Objective. The goal of this paper is to undertake a literature search collecting all dentin bond strength data obtained for six adhesives with four tests ( shear, microshear, tensile and microtensile) and to critically analyze the results with respect to average bond strength, coefficient of variation, mode of failure and product ranking. Method. A PubMed search was carried out for the years between 1998 and 2009 identifying publications on bond strength measurements of resin composite to dentin using four tests: shear, tensile, microshear and microtensile. The six adhesive resins were selected covering three step systems ( OptiBond FL, Scotch Bond Multi-Purpose Plus), two-step (Prime & Bond NT, Single Bond, Clear. l SE Bond) and one step (Adper Prompt L Pop). Results. Pooling results from 147 references showed an ongoing high scatter in the bond strength data regardless which adhesive and which bond test was used. Coefficients of variation remained high (20-50%) even with the microbond test. The reported modes of failure for all tests still included high number of cohesive failures. The ranking seemed to be dependant on the test used. Significance. The scatter in dentin bond strength data remains regardless which test is used confirming Finite Element Analysis predicting non-uniform stress distributions due to a number of geometrical, loading, material properties and specimens preparation variables. This reopens the question whether, an interfacial fracture mechanics approach to analyze the dentin - adhesive bond is not more appropriate for obtaining better agreement among dentin bond related papers. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Does Adhesive Thickness Affect Resin-dentin Bond Strength After Thermal/Load Cycling?

This study evaluated the influence of adhesive layer thickness (ADL) on the resin-dentin bond strength of two adhesive systems (AS) after ther-mal and mechanical loading (TML). A flat superficial dentin surface was exposed with 600-grit SiC paper on 40 molars. After primer application, the adhesive layer of Scotchbond Multipurpose (SBMP) or Clearfil SE Bond (CSEB) was applied in one or two layers to a delimited area (52 mm(2)) and resin blocks (Filtek 2250) were built incrementally: Half of the sample was stored in distilled water (37 C, 24 hours) and submitted to thermal (1,000; 5 degrees-55 degrees C) and mechanical cycles (500,000; 10kgf) [TML]. The other half was stored in distilled water (72 hours). The teeth were then sectioned to obtain sticks (0.8 mm(2)) to be tested under tensile mode (1.0 mm/minute). The fracture mode was analyzed at 400x. The BS from all sticks from the same tooth was averaged for statistical purposes. The data was analyzed by three-way ANOVA. The x(2) test was used (p<0.05) to compare the frequency of pre-testing failure specimens. Higher BS values were observed for SBMP regardless of the ADL. The TML reduced the BS values irrespective of the adhesive employed and the ADL. A higher frequency of pre-testing failure specimens was observed for the cycled groups. A thicker adhesive layer, acting as an intermediate flexible layer, did not min-imize the damage caused by thermal/mechanical load cycling for a three-step etch-and-rinse and two-step self-etch system.

Differential bonds degradation of two resin-modified glass-ionomer cements in primary and permanent teeth

Objectives: To evaluate the effect of chemical degradation on bond strength of resin-modified glass-ionomer cements bonded to primary and permanent dentin. Methods: Class I cavities of permanent and primary extracted human molars were restored with two resin-modified glass-ionomer cements: Fuji 11 LC and Vitremer, and stored in water for 24 h. Half samples were immersed in 10% NaOCl aqueous solution for 5 h. Teeth were sectioned into beams and tested for microtensile bond strengths. Results were analyzed with multiple ANOVA and Tukey`s tests (p < 0.05). Analysis of debonded surfaces was performed by SEM. Results: 24 h bond strengths for Vitremer and Fuji 11 LC were similar. For Fuji 11, bond strength values were higher for primary than for permanent dentin. Vitremer bond strength was similar for both. Chemical degradation did not affect Fuji I] LC bond strength to dentin. However, decreases in bond strength were found for Vitremer groups after NaOCl immersion. Signs of glass ionomer-dentin interaction were evident by SEM analysis for Fuji 11 LC specimens. Conclusions: Vitremer and Fuji II presented similar bond strength at 24. Vitremer dentin bonds were prone to chemical degradation. Fuji II LC-dentin bonds showed typical features of glass-ionomer dentin interaction at the bonded interfaces, and were resistant to in vitro degradation. (C) 2009 Elsevier Ltd. All rights reserved.

Effect of 2% Chlorhexidine Digluconate on the Bond Strength to Normal Versus Caries-affected Dentin

This study evaluated the effect of 2% chlorhexidine digluconate (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesives to normal (ND) and caries-affected (CAD) dentin. Forty extracted human molars with coronal carious lesions, surrounded by normal dentin, were selected for this study. The flat surfaces of two types of dentin (ND and CAD) were prepared with a water-cooled high-speed diamond disc, then acidetched, rinsed and air-dried. In the control groups, the dentin was re-hydrated with distilled water, blot-dried and bonded with a three-step (Scotchbond Multi-Purpose-MP) or two-step (Single Bond 2-SB) etch-and-rinse adhesive. In the experimental groups, the dentin was rehydrated with 2% CHX (60 seconds), blot-dried and bonded with the same adhesives. Resin composite build-ups were made. The specimens were prepared for microtensile bond testing in accordance with the non-trimming technique, then tested either immediately or after six-months storage in artificial saliva. The data were analyzed by ANOVA/Bonferroni tests (alpha=0.05). CHX did not affect the immediate bond strength to ND or CAD (p>0.05). CHX treatment significantly lowered the loss of bond strength after six months as seen in the control bonds for ND (p<0.05), but it did not alter the bond strength of CAD (p>0.05). The application of NIP on CHX-treated ND or CAD produced bonds that did not change over six months of storage.

Physicochemical Properties of Methacrylate Resin-based Root Canal Sealers

Introduction: This study assessed in vitro the physicochemical properties of 2 methacrylate resin-based sealers (Epiphany SE and Hybrid Root SEAL), comparing the results with a well-established epoxy resin-based sealer (AH Plus). Methods: Five samples of each material were used for each test (setting time, flow, radiopacity, dimensional change after setting, and solubility) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. The samples were assigned to 3 groups: I, AH Plus; II, Epiphany SE; and III, Hybrid Root SEAL. The distilled and deionized water used at the solubility test was submitted to atomic absorption spectrometry to observe the presence of Ca2+, K+, Ni2+, and Zn2+ ions. In addition, the surface morphology of the specimens was analyzed by means of scanning electron microscopy (SEM). Statistical analysis was performed by using one-way analysis of variance and Tukey-Kramer test (P < .05). Results: Flow, radiopacity, and solubility of all sealers were in accordance with ANSI/ADA. The setting time of Hybrid Root SEAL did not agree with ANSUADA requirements. The dimensional change of all sealers was greater than the values considered acceptable by ANSI/ADA. The spectrometry analysis showed significant Ca2+ ions release for AH Plus. In SEM analysis, Hybrid Root SEAL presented spherical monomers with inferior size than AH Plus and Epiphany SE. Conclusions: It might be concluded that physicochemical properties of the tested sealers conformed to ANSI/ADA (2000) standardization, except for the setting time of Hybrid Root SEAL and the dimensional change of all sealers, which did not fulfill the ANSI/ADA requirements. (J Endod 2010;36:1531-1536)

Assessment of the biocompatibility of Epiphany root canal sealer in rat subcutaneous tissues

Objective. The aim of this study was to evaluate the biocompatibility of the root canal sealer Epiphany in rat subcutaneous tissues. Study design. Polyethylene tubes were filled with the sealer (I: Epiphany; II: photoactivated Epiphany; III: Epiphany associated with self-etch primer; IV: photoactivated Epiphany associated with primer; and V: control group) and later implanted into 4 different regions of the dorsum of 15 adult male rats (Rattus novergicus, Albinus Wistar). After 7, 21, and 42 days, 5 animals were killed, obtaining 4 samples per group, in addition to the control group, at each analyzed time. Results. In all periods, Epiphany induced a mild inflammatory reaction. However, in group II, in which the primer was not used, extensive necrosis and a moderate to intense inflammatory reaction were observed, mainly after 7 and 21 days. Conclusion. Epiphany sealer appears biocompatible when tested on rat subcutaneous tissues.

Biocompatibility Evaluation of Epiphany/Resilon Root Canal Filling System in Subcutaneous Tissue of Rats

Introduction: The purpose of this study was to evaluate the biocompatibility of the root canal filling system Epiphany/Resilon in connective tissue of rats. Methods: Fifteen rats were used, separated into 3 groups in accordance with its period of death (7, 21, 42 days). Four filled dentin tubes were implanted with the tested materials as follows: ERSP group, Epiphany/Resilon with Self-etch Primer; ER group, Epiphany/Resilon without primer; EG group, Endofill/gutta-percha points; and ET group, empty tube. After 7, 21, and 42 days, animals were killed, obtaining 5 samples per group. A grade from I-IV was used to graduate the inflammatory reaction. Results: Results showed that Epiphany/Resilon (ERSP and ER groups) induced a slight (II) inflammatory reaction after 42 days. However, in ER group, in which the self-etch primer was not applied, severe (IV) to moderate (III) inflammatory reactions were observed between 7 and 21 days. When compared with the EG and ET groups, it was observed that these groups presented tissue reaction ranging from slight (II, 7 and 21 days) to no inflammation (I, 42 days). Conclusions: Epiphany/Resilon root canal filling system presented satisfactory tissue reaction. It was biocompatible when tested in connective tissue of rats. (J Endod 2010;36:110-114)

Influence of dentin cavity surface finishing on micro-tensile bond strength of adhesives

The current trend toward minimal-invasive dentistry has introduced innovative techniques for cavity preparation. Chemical vapor deposition (CVD) and laser-irradiation technology have been employed as an alternative to the common use of regular burs in high-speed turbines. Objectives. The purpose of this study was to assess the influence of alternative techniques for cavity preparation on the bonding effectiveness of different adhesives to dentin, and to evaluate the morphological characteristics of dentin prepared with those techniques. Methods. One etch&rinse adhesive (OptiBond FL, Kerr) and three self-etch systems (Adper Prompt L-Pop, 3M ESPE; Clearfil SE Bond, Kuraray; Clearfil S3 Bond, Kuraray) were applied on dentin prepared with a regular bur in a turbine, with a CVD bur in a turbine, with a CVD tip in ultrasound and with an ErCr:YSGG laser. The micro-tensile bond strength (mu TBS) was determined after storage in water for 24 h at 37 degrees C, and morphological evaluation was performed by means of field -emission -gun scanning electron microscopy (Feg-SEM). Results. Feg-SEM evaluation revealed different morphological features on the dentin surface after the usage of both the conventional and alternative techniques for cavity preparation, more specifically regarding smear-layer thickness and surface roughness. CVD bur-cut, CVD ultra-sonoabraded and laser-irradiated dentin resulted in lower mu TBSs than conventionally bur-cut dentin, irrespective of the adhesive employed. Significance. The techniques, such as CVD diamond-bur cutting, CVD diamond ultra-sonoabrasion and laser-irradiation, used for cavity preparation may affect the bonding effectiveness of adhesives to dentin, irrespective of their acidity or approach. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bond Strength of Dental Adhesive Systems Irradiated with Ionizing Radiation

Purpose: The aim of the present paper was to determine the effect of different types of ionizing radiation on the bond strength of three different dentin adhesive systems. Materials and Methods: One hundred twenty specimens of 60 human teeth (protocol number: 032/2007) sectioned mesiodistally were divided into 3 groups according to the adhesives systems used: SB (Adper Single Bond Plus), CB (Clearfil SE Bond) and AP (Adper Prompt Self-Etch). The adhesives were applied on dentin and photo-activated using LED (Lec 1000, MMoptics, 1000 mW/cm(2)). Customized elastomer molds (0.5 mm thickness) with three orifices of 1.2 mm diameter were placed onto the bonding areas and filled with composite resin (Filtek Z-250), which was photo-activated for 20 s. Each group was subdivided into 4 Subgroups for application of the different types of ionizing radiation: ultraviolet radiation (UV), diagnostic x-ray radiation (DX), therapeutic x-ray radiation (TX) and without irradiation (control group, CG). Microshear tests were carried out (Instron, model 4411), and afterwards the modes of failure were evaluated by optical and scanning electron microscope and classified using 5 scores: adhesive failure, mixed failures with 3 significance levels, and cohesive failure. The results of the shear bond strength test were submitted to ANOVA with Tukey`s test and Dunnett`s test, and the data from the failure pattern evaluation were analyzed with the Mann Whitney test (p = 0.05). Results: No change in bond strength of CB and AP was observed after application of the different radiation types, only SB showed increase in bond strength after UV (p = 0.0267) irradiation. The UV also changed the failure patterns of SB (p = 0.0001). Conclusion: The radio-induced changes did not cause degradation of the restorations, which means that they can be exposed to these types of ionizing radiation without weakening the bond strength.

Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm(2), respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey`s test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements.

Bond Strength and Etching Pattern of Adhesive Systems to Enamel: Effects of Conditioning Time and Enamel Preparation

Statement of the problem: The performance of self-etch systems on enamel is controversial and seems to be dependent on the application technique and the enamel preparation. Purpose of the Study: To examine the effects of conditioning time and enamel surface preparation on bond strength and etching pattern of adhesive systems to enamel. Materials and Methods: Ninety-six teeth were divided into 16 conditions (N = 6) in function of enamel preparation and conditioning time for bond strength test. The adhesive systems OptiBond FL (Kerr, Orange, CA, USA), OptiBond SOLO Plus (Kerr), Clearfil SE Bond (Kuraray, Osaka, Japan), and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA) were applied on unground or ground enamel following the manufacturers` directions or doubling the conditioning time. Cylinders of Filtek Flow (0.5-mm height) were applied to each bonded enamel surface using a Tygon tube (0.7 mm in diameter; Saint-Gobain Corp., Aurora, OH, USA). After storage (24 h/37 degrees C), the specimens were subjected to shear force (0.5 mm/min). The data were treated by a three-way analysis of variance and Tukey`s test (alpha = 0.05). The failure modes of the debonded interfaces and the etching pattern of adhesives were observed using scanning electron microscopy. Results: Only the main factor ""adhesive"" was statistically significant (p < 0.001). The lowest bond strength value was observed for OptiBond FL. The most defined etching pattern was observed for 35% phosphoric acid and for Adper Prompt L-Pop. Mixed failures were observed for all adhesives, but OptiBond FL showed cohesive failures in resin predominantly. Conclusions: The increase in the conditioning time as well as the enamel pretreatment did not provide an increase in the resin-enamel bond strength values for the studied adhesives. CLINICAL SIGNIFICANCE The surface enamel preparation and the conditioning time do not affect the performance of self-etch systems to enamel. (J Esthet Restor Dent 20:322-336, 2008)

Effect of dentin conditioning time on nanoleakage

Objectives: To study the nanoleakage pattern in the dentin hybrid layer by using different dentin adhesives. The null hypotheses tested in this study were: 1) dentin conditioning time does not affect nanoleakage within the hybrid layer; 2) the type of dentin adhesive used does not affect nanoleakage. Methods: Standardized Class V cavities were prepared in 30 intact human molars on the buccal and lingual surfaces. The specimens were randomly assigned to 2 total-etch dentin adhesives (OptiBond SOLO Plus [OPS, Kerr] and One-Step [ONS, BISCO Inc]) and 2 self-etch dentin adhesives (Clearfil SE Bond [CSE, Kuraray] and Adper Prompt L-Pop [APL, 3M ESPE]). The specimens were etched or conditioned for 15 seconds, 30 seconds or 60 seconds. Upon restoration of the Class V cavities with the proprietary resin composite, the specimens were isolated with nail polish except for a 2.0-mm rim around the restoration, and they were immersed in 50 wt% ammoniacal silver nitrate solution (pH=9.5) for 24 hours followed by 8 hours of immersion in photo-developing solution to reduce the silver ions to metallic silver. The specimens were fixed, dehydrated and processed for FESEM and TEM. Silver penetration was measured along the cervical wall, and data were analyzed with Kruskal-Wallis non-parametric tests at a significance level of 95%. Results: There were no statistically significant differences among the experimental groups for the factor conditioning time (p>0.926). There were significant differences for the variable dentin adhesive (p<0.0001). The least amount of nanoleakage within the hybrid layer occurred with CSE, while ONS resulted in the greatest penetration of silver ions. The adhesives OPS and APL ranked in the intermediary subset. Under TEM, all adhesives resulted in some degree of nanoleakage within the hybrid layer. Both spotted/reticular and water-tree nanoleakage patterns were observed. Significance: Longer conditioning times did not increase nanoleakage within the hybrid layer. Nanoleakage varied with the type of adhesive used.

Fracture resistance of bleached teeth restored with different procedures

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different non-metallic post. Eighty mandibular incisors were endodontically treated and randomly divided in 10 groups (n = 8): G1- restored with composite resin (CR), G2- CR + fiber-reinforced composite post (FRC, Everstick post, Sticktech) cemented with resin cement self-etch adhesive (RCS, Panavia F 2.0, Kuraray), G3- CR + FRC + self-adhesive resin cement (SRC, Breeze, Pentral Clinical), G4- CR+ glass fiber post (GF, Exacto Post, Angelus) + RCS, G5- CR + GF + SRC. The G6 to G10 were bleached with hydrogen peroxide (HP) and restored with the same restorative procedures used for G1 to G5, respectively. After 7 days storage in artificial saliva, the specimens were submitted to the compressive strength test (N) at 0.5 mm/min cross-head speed and the failure pattern was identified as either reparable (failure showed until 2 mm below the cement-enamel junction) or irreparable (the failure showed <2 mm or more below the cement-enamel). Data were analyzed by ANOVA and Tukey test (α = 0.05). No significant difference (p < 0.05) was found among G1 to G10. The results suggest that intracoronal bleaching did not significantly weaken the teeth and the failure patterns were predominately reparable for all groups. The non-metallic posts in these teeth did not improve fracture resistance.

Effect of Resin Cement System and Root Region on the Push-out Bond Strength of a Translucent Fiber Post

Objectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etch-and-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dual-cured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Push-out bond strength was evaluated at three different radicular levels: cervical, middle, and apical. The interface between resinous cement and the post was observed using a stereoscopic microscope.Results: Analysis of variance showed a statistically significant difference among the cements (p<0.05) and the root canal thirds (p<0.05). The self-adhesive resinous cement had lower values of retention.Conclusions: The resin cements used with etch-and-rinse and self-etch adhesive systems seem to be adequate for glass fiber post cementation.