Preparation of CaTiO3 fine powders by the hydrothermal method

Fine powders consisting of 0.1–0.5 μm size crystallites of CaTiO3 are prepared at 150–200°C by the hydrothermal method starting from hydrated titania gel and reactive calcium oxide suspended as an aqueous slurry in an autoclave. The resulting high-purity CaTiO3 is characterised by TEM, X-ray powder diffraction, chemical analyses and sintering characteristics. The hydrothermally prepared CaTiO3 powders are sinterable to high-density ceramics below 1400°C. The dc conductivity behaviour of the chemically reduced ceramics is presented.

Hydrothermal preparation of Ba(Ti,Zr)O3 fine powders

Fine powders consisting of aggregated submicron crystallites of Ba(Ti,Zr)O3 in the complete range of Ti/Zr ratios are prepared at 85–130°C by hydrothermal method, starting from TiO2 + ZrO2 · xH2O mixed gel and Ba(OH)2 solution. The products obtained below 110°C incorporate considerable amounts of H2O and OH− within the lattice. As-prepared BaTiO3 is cubic and converts to tetragonal phase after the heat treatment at 1200°C, accompanied by the loss of residual hydroxyl ions. TEM investgations of the growth features show a transformation of the gel to the crystallite. Ba2+ ions entering the gel produce chemical changes within the gel, followed by dehydration, resulting in a cubic perovskite phase irrespective of Ti/Zr. The sintering properties of these powders to fine-grained, high density ceramics and their dielectric properties are presented.

Preparation and properties of rare earth hydroxides and oxides ultrafine powders in alcohol

A series of rare earth hydroxides and oxides ultrafine powders have been prepared by precipitation method using alcohol as dispersive and protective reagent. It was first to find that the crystallite size of cubic rare earth oxides had Lanthanide shrinking effect,but average crystal lattice distortion rate possessed lanthanide swelling effect;the change of diffraction intensity with atomic number presented an inverted W type, and double peaks structure was formed.

Preparation of pyrochlore-free PMN by an alternative chemical method

This work reports the synthesis of the MgNb(2)O(6) and the ferroelectric lead magnesium niobate Pb(Mg(1/3)Nb(2/3))O(3) (PMN) using fine precursor powders obtained from a chemical Oxide Precursor Method (OPM). To obtain pyrochlore-free PMN ceramics, the synthesis of the precursor MgNb(2)O(6) powders was studied for 2-25 mol% excess of MgO and 10 mol% excess of PbO. Structural and microstructural properties of the sintered ceramics obtained by the cited method and by the classical columbite method were studied and compared. Results lead to good quality, pyrochlore-free PMN ceramic prepared by OPM, presenting greater grain size if compared with ceramic prepared by columbite method.

Preparation of 9.5/65/35 PLZT powders by organic precursor method

In this study the preparation of 9.5/65/35 PLZT ceramic powders were investigated. The powders with the formula Pb0.905La0.095(Zr0.65 Ti0.35)0.976O3 + 3.5 w% PbO were prepared using Pechini process and partial oxalate method. The powder phase formation, powder morphology, and green density of PLZT were shown.

Ultrafine powders of SrTiO3 from the hydrothermal preparation and their catalytic activity in the photolysis of water

Ultrafine powders of SrTiO3 are prepared at 100–150°C by the hydrothermal method, starting from TiO2·xH2O gel and Sr(OH)2 and H2O-isopropanol mixed solvent as the medium, The X-ray diffractograms of the powder show line broadening. The minimum crystallite size obtained ranges from 5 to 20nm with 20% H2O-80% C3H7OH as the reaction medium, as estimated from X-ray half-peak widths and TEM studies. The electron diffraction results indicate high concentration of lattice defects in these crystallites. The optical spectra of the particle suspensions in water show that the absorption around the band gap is considerably broadened, together with the appearance of maxima in the far ultraviolet. Aqueous suspensions of SrTiO3 powders, as such, do not produce H2 or O2 on UV irradiation. After coating with rhodium, H2 and O2 are evolved on illumination. However, the turn over number of O2 is lower than the stoichiometrically expected values from the corresponding values of H2. No correlation of the photocatalytic activity with surface area is observed. The activity of Rh-SrTiO3 slowly deteriorates with extended period of irradiation.

Wet chemical syntheses of ultrafine multicomponent ceramic powders through gel to crystallite conversion

Coarse (BOn/2)-O-n+/xH(2)O (10

A simple method for the preparation of plasma-sprayable powders based on ZrO2

Plasma-sprayable powders of calcia, magnesia and yttria-stabilized zirconia have been prepared by using polyvinyl alcohol binders. The powders have been characterized for sprayability by spray coating on steer plates previously coated with an NiAl bond coat. The suitability of these coatings for thermal barrier applications have been examined. Thermal barrier and related properties, along with phase stability and mechanical properties, have been found to be good. Failure of the thermal barrier coating has been observed to occur at the interface between the bond coat and the substrate, due to the formation of a pile-up layer consisting of Fe-Zr-Al-O compound.

Photocatalysis on Fine Powders of Perovskite Oxides

Fine powders of semiconductor oxides have been widely used as photocatalysts for many reactions. Among the various photocatalytic reactions, water splitting has been given much importance, since it is a promising chemical route for solar energy conversion. Perovskite oxides, in particular SrTiO, have been commonly used as photocatalysts because some of them can decompose H,O into H, and 0, without an external bias potential (1). In turn, this is because the conduction band (CB) edges of some of the perovskite oxides are more negative than the H+/H, energy level. Since the catalytic activity is related to the surface properties of the solids, fine powders rather than single crystals are used. Photocatalysis on fine powers can be conveniently discussed in three parts, viz. preparation, characterization and their catalytic activity. Presently, photo-decomposition of water using SrTiO, fine powders is discussed in greater detail, although other photocatalytic reactions on various perovskite oxides are also briefly dealt with.

Preparation and characterization of nanocrystalline powders of bismuth vanadate

The influence of mechanical activation on the formation of Bi2VO5.5 bismuth vanadate (BiV) phase, was investigated by ball-milling a stoichiometric mixture of bismuth oxide and vanadium pentoxide. The structural evolution of the desired BN phase, via an intermediate BiVO4,phase, was investigated using X-ray powder diffraction; (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM). Milling for 54h. yielded monophasic gamma-BiV powders with an average crystallite size of 30 nm. The electron paramagnetic resonance (EPR) peaks associated with the V4+ ions are stronger and broader in nanocrystalline (n) BN than in the conventionally prepared microcrystalline (m) BN, suggesting theta significant portion of V5+ has been transformed to V4+ during milling. The optical bandgap of n-BiV was found to be higher than that of m-BiV. High density (97% of the theoretical density), fine-grained (average grain-size of 2 tun) ceramics with uniform grain-size distribution could be fabricated using n-BiV powders. These fine-grained ceramics exhibit improved dielectric, pyre and ferroelectric properties. (C) 1999 Elsevier Science S.A. All rights reserved.