Effects of plasticizing and crosslinking on the mechanical and barrier properties of coatings based on blends of starch and poly(vinyl alcohol)

In the last decades, intensive research has been carried out in order to replace oil-based polymers with bio-based polymers due to growing environmental concerns. So far, most of the barrier materials used in food packaging are petroleum-based materials. The purpose of the barrier is to protect the packaged food from oxygen, water vapour, water and fat. The mechanical and barrier properties of coatings based on starch-plasticizer and starch-poly(vinyl alcohol) (PVOH)-plasticizer blends have been studied in the work described in this thesis. The plasticizers used were glycerol, polyethylene glycol and citric acid. In a second step, polyethylene coatings were extruded onto paperboard pre-coated with a starch-PVOH-plasticizer blend. The addition of PVOH to the starch increased the flexibility of the film. Curing of the film led to a decrease in flexibility and an increase in tensile strength. The flexibility of the starch-PVOH films was increased more when glycerol or polyethylene glycol was added than citric acid. The storage modulus of the starch-PVOH films containing citric acid increased substantially at high temperature. It was seen that the addition of polyethylene glycol or citric acid to the starch-PVOH blend resulted in an enrichment of PVOH at the surface of the films. Tensile tests on the films indicated that citric acid acted as a compatibilizer and increased the compatibility of the starch and PVOH in the blend. The addition of citric acid to the coating recipe substantially decreased the water vapour transmission rate through the starch-PVOH coated paperboard, which indicated that citric acid acts as a cross-linker for starch and/or PVOH. The starch-PVOH coatings containing citric acid showed oxygen-barrier properties similar to those of pure PVOH or of a starch-PVOH blend without plasticizer when four coating layers were applied on a paperboard. The oxygen-barrier properties of coatings based on a starch-PVOH blend containing citric acid indicated a cross-linking and increase in compatibility of the starch-PVOH blends. Polyethylene extrusion coating on a pre-coated paperboard resulted in a clear reduction in the oxygen transmission rate for all the pre-coating formulations containing plasticizers. The addition of a plasticizer to the pre-coating reduced the adhesion of polyethylene to pre-coated board. Polyethylene extrusion coating gave a board with a lower oxygen transmission rate when the paperboard was pre-coated with a polyethylene-glycol-containing formulation than with a citric-acid-containing formulation. The addition of polyethylene glycol to pre-coatings indicated an increase in wetting of the pre-coated paperboard by the polyethylene melt, and this may have sealed the small defects in the pre-coating leading to low oxygen transmission rate. The increase in brittleness of starch-PVOH films containing citric acid at a high temperature seemed to have a dominating effect on the barrier properties developed by the extrusion coating process. 

An experimental and finite element poroelastic creep response analysis of an intervertebral hydrogel disc model in axial compression

A hydrogel intervertebral disc (lVD) model consisting of an inner nucleus core and an outer anulus ring was manufactured from 30 and 35% by weight Poly(vinyl alcohol) hydrogel (PVA-H) concentrations and subjected to axial compression in between saturated porous endplates at 200 N for 11 h, 30 min. Repeat experiments (n = 4) on different samples (N = 2) show good reproducibility of fluid loss and axial deformation. An axisymmetric nonlinear poroelastic finite element model with variable permeability was developed using commercial finite element software to compare axial deformation and predicted fluid loss with experimental data. The FE predictions indicate differential fluid loss similar to that of biological IVDs, with the nucleus losing more water than the anulus, and there is overall good agreement between experimental and finite element predicted fluid loss. The stress distribution pattern indicates important similarities with the biological lVD that includes stress transference from the nucleus to the anulus upon sustained loading and renders it suitable as a model that can be used in future studies to better understand the role of fluid and stress in biological IVDs. (C) 2005 Springer Science + Business Media, Inc.

NMR characterization of blends of poly(hydroxybutyrate-co-hydroxyvalerate) with poly(vinyl acetate)

The extent of mixing in blends of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) (27% HV) and poly(vinyl acetate) (PVAc) has been measured using a number of different techniques, principally solid-state NMR. Differential scanning calorimetry DSC measurements indicated effective mixing of the polymer chains on a scale of several nanometres. The results of H-1 T-1 and H-1 T-1rho. measurements confirm intimate mixing of the chains. A change on blending in the H-1 T-1rho, and the H-1 NMR line width of the signal from the protons of PVAc was consistent with an increase in the amplitude and frequency of motion of this component. The PVAc chains reside within the inter-lamellar space, as confirmed by spin diffusion measurements after H-1 T-1rho preparation. (C) 2003 Society of Chemical Industry.

Viscoelasticity of radiation-formed PVA/PVP hydrogel

The dynamic theological behaviour of gamma-irradiated 12.8 wt% poly(vinyl alcohol) (PVA), 12.8 wt% poly(vinyl pyrrolidone) (PVP), and a blend of 8 wt% PVA and 4.8 wt% PVP aqueous solutions have been studied pre- and post-gelation. The non-irradiated solutions displayed theological behaviour typical of dilute to semi-dilute polymer solutions, with the complex viscosity being independent of the frequency and shear rate (i.e. Newtonian behaviour) over the range of frequencies tested and the loss modulus G(omega) and storage modulus G(omega) being nearly proportional to omega and omega(2) respectively. After a set of doses of gamma-radiation, the magnitudes of the dynamic moduli G'(omega) and G(omega) increased as the absorbed dose increased, with notable differences between the two homopolymers and the blend. The stages of gelation were effectively monitored by means of dynamic theological measurements, allowing the possible mechanisms of network formation to be elucidated. The doses required for gelation of the PVA, PVP, and blend samples, determined on the basis of the Winter and Chambon criteria for gelation, were found to be 12 kGy for the 12.8 wt% PVA, 4 kGy for the 12.8 wt% PVP, and 5 kGy for the 8 wt% PVA/4.8 wt% PVP solutions. The unexpected lower gelation dose demonstrated by the blend sample, compared with predictions based on the blend composition, and the associated gelation mechanism are also discussed.

Microwave-assisted hydrogel synthesis: a new method for crosslinking polymers in aqueous solutions

It has been found that hydrogels may be formed by microwave irradiation of aqueous solutions containing appropriate combinations of polymers. This new method of hydrogel synthesis yields sterile hydrogels without the use of monomers, eliminating the need for the removal of unreacted species from the final product. Results for two particularly successful combinations, poly(vinyl alcohol) with either poly(acrylic acid) or poly(methylvinylether-alt-maleic anhydride), are presented. Irradiation using temperatures of 100–150 °C was found to yield hydrogels with large equilibrium swelling degrees of 500–1000 g g−1. Material leached from both types of hydrogel shows little cytotoxicity towards HT29 cells.

Pt/TiO(2)/poly(vinyl sulfonic acid) Layer-by-Layer Films for Methanol Electrocatalytic Oxidation

One major challenge for the widespread application of direct methanol fuel cells (DMFCs) is to decrease the amount of platinum used in the electrodes, which has motivated a search for novel electrodes containing platinum nanoparticles. In this study, platinum nanoparticles were electrodeposited on layer-by-layer (LbL) films from TiO(2) and poly(vinyl sulfonic) (PVS), by immersing the films into a H(2)PtCl(6) solution and applying a 100 mu A current during different electrode position times. Scanning tunnel microscopy (STM) and atomic force microscopy (AFM) images showed increased platinum particle size and electrode roughness for increasing electrodeposition times. The potentiodynamic profile of the electrodes indicated that oxygen-like species in 0.5 mol L(-1) H(2)SO(4) were formed at less positive potentials for the smallest platinum particles. Electrochemical impedance spectroscopy measurements confirmed the high reactivity for the water dissociation and the large amount of oxygen-like species adsorbed on the smallest platinum nanoparticles. This high oxophilicity of the smallest nanoparticles was responsible for the electrocatalytic activity of Pt-TiO(2)/PVS systems for methanol electrooxidation, according to the Langmuir-Hinshelwood bifunctional mechanism. Significantly, the approach used here combining platinum electrodeposition and LbL matrices allows one to both control the particle size and optimize methanol electrooxidation, being therefore promising for producing membrane-electrode assemblies of DMFCs.

The states, diffusion, and concentration distribution of water in radiation-formed PVA/PVP hydrogels

Hydrogels with various compositions of polyvinyl alcohol (PVA) and poly(1-vinyl-2-pyrrolidinone) (PVP) were prepared by irradiating mixtures of PVA and PVP in aqueous solutions with gamma-rays from Co-60 sources at room temperature. The states of water in the hydrogels were characterized using DSC and NMR T-2 relaxation measurements and the kinetics of water diffusion in the hydrogels were studied by sorption experiments and NMR imaging. The DSC endothermic peaks in the temperature range -10 to +10 degrees C implied that there are at least two kinds of freezable water present in the matrix. The difference between the total water content and the freezable water content was refer-red to as bound water, which is not freezable. The weight fraction of water at which only nonfreezable water is present in a hydrogel with F-VP = 0.19 has been estimated to be g(H2O)/g(Polymer) = 0.375. From water sorption experiments, it was demonstrated that the early stage of the diffusion of water into the hydrogels was Fickian. A curve-fit of the early-stage experimental data to the Fickian model allowed determination of the water diffusion coefficient, which was found to lie between 1.5 x 10(-11) m(2) s(-1) and 4.5 x 10(-11) m(2) s(-1), depending on the polymer composition, the cross-link density, and the temperature. It was also found that the energy barrier for diffusion of water molecules into PVA/PVP hydrogels was approximate to 24 kJ mol(-1). Additionally, the diffusion coefficients determined from NMR imaging of the volumetric swelling of the gels agreed well with the results obtained by the mass sorption method.

In vivo study of an injectable poly(acrylonitrile)-based hydrogel paste as a bulking agent for the treatment of urinary incontinence.

Urinary incontinence can be treated by endoscopic injection of bulking agents, however, no optimal therapeutic effect has been achieved upon this treatment yet. In the present study, the development of a injectable poly(acrylonitrile) hydrogel paste is described, and its efficacy and histological behavior, once injected into the submucosal space of the minipig bladder, are evaluated. A device was developed to mix poly(acrylonitrile) hydrogel powder with glycerin, used as carrier, prior to injection into the submucosal space of the bladder. Several paste deposits, depending on the size of the bladder, were injected per animal. The implants were harvested at days 7, 14, 21, 28, 84 and 168 and analyzed morphologically and by histology. The persistence of the implants was demonstrated. However, at later time points the implants were split up and surrounded by granulomatous tissue, which was gradually replaced by histiocytes and adipocytes. Transitory focal urothelial metaplasia was observed only at day 7 and moderate foreign body reaction was detected predominantly between the second and fifth week. This study demonstrated the feasibility to develop an injectable paste of poly(acrylonitrile) hydrogel thought to provide the expected bulking effect, necessary for the treatment of urinary incontinence.

Électrofilage de fibres à partir de mélanges polystyrène/poly(vinyl méthyl éther)

L’électrofilage est un procédé permettant de préparer des fibres possédant un diamètre de l’ordre du micromètre ou de quelques centaines de nanomètres. Son utilisation est toutefois limitée par le manque de contrôle sur la structure et les propriétés des fibres ainsi produites. Dans ce travail, des fibres électrofilées à partir de mélanges de polystyrène (PS) et de poly(vinyl méthyl éther) (PVME) ont été caractérisées. La calorimétrie différentielle à balayage (DSC) a montré que les fibres du mélange PS/PVME sont miscibles (une seule transition vitreuse) lorsque préparées dans le benzène, alors qu'une séparation de phases a lieu lorsque le chloroforme est utilisé. Les fibres immiscibles sont néanmoins malléables, contrairement à un film préparé par évaporation du chloroforme qui a des propriétés mécaniques médiocres. Des clichés en microscopies optique et électronique à balayage (MEB) ont permis d’étudier l'effet de la composition et du solvant sur le diamètre et la morphologie des fibres. Des mesures d’angles de contact ont permis d’évaluer l’hydrophobicité des fibres, qui diminue avec l’ajout de PVME (hydrophile); les valeurs sont de 60° supérieures à celles des films de composition équivalente. Un retrait sélectif du PVME a été réalisé par l’immersion des fibres dans l’eau. La spectroscopie infrarouge a montré que la composition passe de 70 à 95% de PS pour une fibre immiscible mais seulement à 75% pour une fibre miscible. Ces résultats indiquent que la phase riche en PVME se situe presque uniquement à la surface des fibres immiscibles, ce qui a été confirmé par microscopie à force atomique (AFM) et MEB. Finalement, l’effet du mélange des deux solvants, lors de l’électrofilage du mélange PS/PVME, a été étudié. La présence du chloroforme, même en quantité réduite, provoque une séparation de phases similaire à celle observée avec ce solvant pur.

Development and characterization of polymeric nanoparticles(NPs) made from functionalized poly (D,L- lactide) (PLA)polymers

Les nanoparticules polymériques biodégradable (NPs) sont apparues ces dernières années comme des systèmes prometteurs pour le ciblage et la libération contrôlée de médicaments. La première partie de cette étude visait à développer des NPs biodégradables préparées à partir de copolymères fonctionnalisés de l’acide lactique (poly (D,L)lactide ou PLA). Les polymères ont été étudiés comme systèmes de libération de médicaments dans le but d'améliorer les performances des NPs de PLA conventionnelles. L'effet de la fonctionnalisation du PLA par insertion de groupements chimiques dans la chaîne du polymère sur les propriétés physico-chimiques des NPs a été étudié. En outre, l'effet de l'architecture du polymère (mode d'organisation des chaînes de polymère dans le copolymère obtenu) sur divers aspects de l’administration de médicament a également été étudié. Pour atteindre ces objectifs, divers copolymères à base de PLA ont été synthétisés. Plus précisément il s’agit de 1) copolymères du poly (éthylène glycol) (PEG) greffées sur la chaîne de PLA à 2.5% et 7% mol. / mol. de monomères d'acide lactique (PEG2.5%-g-PLA et PEG7%-g-PLA, respectivement), 2) des groupements d’acide palmitique greffés sur le squelette de PLA à une densité de greffage de 2,5% (palmitique acid2.5%-g-PLA), 3) de copolymère « multibloc » de PLA et de PEG, (PLA-PEG-PLA)n. Dans la deuxième partie, l'effet des différentes densités de greffage sur les propriétés des NPs de PEG-g-PLA (propriétés physico-chimiques et biologiques) a été étudié pour déterminer la densité optimale de greffage PEG nécessaire pour développer la furtivité (« long circulating NPs »). Enfin, les copolymères de PLA fonctionnalisé avec du PEG ayant montré les résultats les plus satisfaisants en regard des divers aspects d’administration de médicaments, (tels que taille et de distribution de taille, charge de surface, chargement de drogue, libération contrôlée de médicaments) ont été sélectionnés pour l'encapsulation de l'itraconazole (ITZ). Le but est dans ce cas d’améliorer sa solubilité dans l'eau, sa biodisponibilité et donc son activité antifongique. Les NPs ont d'abord été préparées à partir de copolymères fonctionnalisés de PLA, puis ensuite analysés pour leurs paramètres physico-chimiques majeurs tels que l'efficacité d'encapsulation, la taille et distribution de taille, la charge de surface, les propriétés thermiques, la chimie de surface, le pourcentage de poly (alcool vinylique) (PVA) adsorbé à la surface, et le profil de libération de médicament. L'analyse de la chimie de surface par la spectroscopie de photoélectrons rayon X (XPS) et la microscopie à force atomique (AFM) ont été utilisés pour étudier l'organisation des chaînes de copolymère dans la formulation des NPs. De manière générale, les copolymères de PLA fonctionnalisés avec le PEG ont montré une amélioration du comportement de libération de médicaments en termes de taille et distribution de taille étroite, d’amélioration de l'efficacité de chargement, de diminution de l'adsorption des protéines plasmatiques sur leurs surfaces, de diminution de l’internalisation par les cellules de type macrophages, et enfin une meilleure activité antifongique des NPs chargées avec ITZ. En ce qui concerne l'analyse de la chimie de surface, l'imagerie de phase en AFM et les résultats de l’XPS ont montré la possibilité de la présence de davantage de chaînes de PEG à la surface des NPs faites de PEG-g-PLA que de NPS faites à partie de (PLA-PEG-PLA)n. Nos résultats démontrent que les propriétés des NPs peuvent être modifiées à la fois par le choix approprié de la composition en polymère mais aussi par l'architecture de ceux-ci. Les résultats suggèrent également que les copolymères de PEG-g-PLA pourraient être utilisés efficacement pour préparer des transporteurs nanométriques améliorant les propriétés de certains médicaments,notamment la solubilité, la stabilité et la biodisponibilité.

Enhancement of Diffraction Efficiency and Storage Life of Poly (Vinyl Chloride) Based Optical Recording Medium with the Incorporation of an Electron Donor

The differaction efficiency,sensitivity and storage life of Methylene Blue sencitized poly (vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days.

Optimization of pH and Direct Imaging Conditions of Complexed Methylene Blue Sensitized Poly(vinyl chloride) Films

Significant results of our experimental investigations on the dependence of pH on real time transmission characteristics on recording media fabricated by doping PVC with complexed methylene blue are presented. The optimum pH value for faster bleaching was found to be 4×5. In typical applications, the illumination from one side, normal to the surface of this material, initiates a chemical sequence that records the incident light pattern in the polymer. Thus direct imaging can be successfully done on this sample. The recorded letters were very legible with good contrast and no scattering centres. Diffraction efficiency measurements were also carried out on this material.