Estudo da resistência à corrosão de ligas Ni-Cr-Mo-Ta E Ni-Cr-Mo-W em solução NaF 0,08 mol/L, pH 4,7 para aplicações odontológicas

A large number of metal alloys are used in Dentistry for the manufacture of fixed and removable dentures. In the oral cavity, these structures are exposed to a chemically aggressive medium, like saliva and mechanical efforts, like mastication. In addition, acidic solutions containing fluoride ions are also frequently used in dental treatments to prevent dental plates and decays development. In this context, it was considered important to investigate the influence that a fourth element could exert when added to the ternary alloy Ni-Cr-Mo, largely used in Brazil. Therefore, electrochemical tests were done to evaluate the resistance to corrosion of quaternary alloy 65Ni-25Cr-5Mo-5Ta and 65Ni-25Cr-5Mo-5W in NaF solution 0,08mol / L, pH = 4.7. For greater understanding the microstructure and morphology of alloys were studied, through metallographic analysis, using optics microscopy and electron microscopy scanning. For the electrochemical tests were applied techniques traditionally used in corrosion researches, such as: potential measures in open circuit (OCP) and cyclic polarization (CP). It was found that both quaternary alloys showed very similar results. Comparing these quaternary alloys with the ternary 65Ni-25Cr-10Mo, it was found that the quaternary alloys exhibit greater resistance to corrosion, in other words, less passivation current density than the ternary alloy, showing that it is advantageous to add a fourth element in the alloy

Estudo do comportamento eletroquímico da liga UNS N07090 em diferentes concentrações de ácido sulfúrico.

Ligas de níquel têm atualmente uma vasta gama de aplicações, sendo a agressividade do meio e as elevadas temperaturas que estas ligas suportam, um diferencial excepcional. A liga UNS N07090, objeto deste trabalho, encontra aplicações muito diversas, entre elas turbocompressores, sistemas de exaustão e de pós-tratamento de motores a diesel. Nestas aplicações a liga está exposta a gases, que ao condensarem formam ácido sulfúrico (H2SO4). Torna-se, assim, importante, o conhecimento da resistência à corrosão da liga nesse meio. O presente trabalho tem como objetivo caracterizar o comportamento eletroquímico da liga através de curvas de polarização potenciodinâmica em diferentes concentrações de ácido sulfúrico. Observou-se que quanto maior a concentração de ácido, maior é a corrosão da liga. Este fato pode ser discutido pela adsorção do íon sulfato (SO42-), que prejudica tanto a formação quanto a cinética de crescimento da película passiva do níquel. Em contrapartida, a presença de Cr na liga UNS N07090 apresentou um benefício sobre a resistência à corrosão desta muito acima do esperado, influenciando de forma direta as curvas de polarização da liga e mantendo-a em condição de elevada resistência à corrosão em detrimento do pior desempenho observado em outros elementos pertecentes à liga, como Co, Al e Ti. Tempos de imersão de 24h em ácido sulfúrico elevam discretamente os parâmetros de corrosão da liga, mantendo-os, no entanto em patamares bastante baixos, permitindo finalmente concluir que a liga UNS N07090, quando exposta a concentrações que variam de 1M a 4M H2SO4, a 25°C, apresenta boa resistência à corrosão e que esta não se altera com o tempo de exposição. A análise dos resultados mostrou que o processo corrosivo é controlado por reações catódicas de sulfato e hidrogênio, as quais podem ter diferentes contribuições dependendo da concentração do ácido e do tempo de imersão da liga UNS N07090 no meio corrosivo.

The corrosion of monel and 70-30 cupronickel in hydrofluoric acid /

"Contract No. W-7405-eng-92."

The processing and properties of Hastelloy C /

"May 1964."

The Nicrosil versus Nisil thermocouple : properties and thermoelectric reference data /

Mode of access: Internet.

Redução in situ de NIO durante a sinterização de misturas NI/NIO produzidas por metalurgia do pó

The nickel alloys are widely used in the production of various materials, especially those that require mechanical strength characteristics associated with resistance to corrosion, for example, the stainless steel. Another use is the production of nickel alloy sintered from powder of metallic nickel. A promising alternative for the production of sintered components of nickel with an important reduction in costs of starting material is the use of mixtures of powders of Ni-NiO. This work aimed to study in situ reduction of NiO during sintering mixtures of Ni / NiO produced by powder metallurgy. The nickel mixtures have been processed by the technique of powder metallurgy and were pre-sintered in an oven under plasma reducing atmosphere of hydrogen. Mixtures Ni +15%NiO, Ni +25%NiO and Ni +35%NiO were studied and compared with samples consisting only of metallic Ni. Dilatometric tests were performed to study the sintering conditions of the mixtures. The consolidated material was analyzed for their microstructure and microhardness. Dilatometry graphs showed that the addition of nickel oxide in all compositions the active sintering the mixtures studied. In tests of microhardness indentations were made at different points of the sample surface. All compositions showed microhardness values close to the consolidated material from metallic nickel. However, sample containing Ni+35% NiO, showed a large dispersion of the values of microhardness tests performed at different points of the sample surface. Microstructural analysis of the material showed a higher concentration of voids and the presence of oxides in the waste composition of the mixtures Ni 35% NiO. The samples containing Ni+15%NiO showed microstructural characteristics and mechanical properties similar to metallic nickel consolidated under the same conditions of the compositions studied in this work and therefore had great potential for production of sintered nickel alloys

Desenvolvimento de eletrocatalisadores de PdM (M= Ni, Cu, Ag) para reação de redução de oxigênio em meio básico na ausência e presença de álcool

Tese (Doutorado em Tecnologia Nuclear)

Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita

Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carriers for such were used in this study SiC, Si3N4 or Si metal with graphite. Carbonyl Ni powder with mean particle size of 11 mM were mixed with 3 wt% of SiC powders with an average particle size of 15, 30 and 50 μm and further samples were obtained containing 4 to 5% by mass of SiC with average particle size of 15 μm. Samples were also obtained by varying the carrier alloy, these being Si3N4 powder with graphite, with average particle size of 1.5 and 5 μm, respectively. As a metallic Si graphite with average particle size of 12.5 and 5 μm, respectively. The reference material used was nickel carbonyl sintered without adding carriers. Microstructural characterization of the alloys was made by optical microscopy and scanning electron microscopy with semi-quantitative chemical analysis. We determined the densities of the samples and measurement of microhardness. We studied the dissociation of carriers alloy after sintering at 1200 ° C for 60 minutes. Was evaluated also in the same sintering conditions, the influence of the variation of average particle size of the SiC carrier to the proportion of 3% by mass. Finally, we studied the influence of variation of the temperatures of sintering at 950, 1080 and 1200 ° C without landing and also with heights of 30, 60, 120 and 240 minutes for sintering where the temperature was 950 °C. Dilatometry curves showed that the SiC sintered Ni favors more effectively than other carriers alloy analyzed. SiC with average particle size of 15 μm active sintering the alloy more effectively than other SiC used. However, with the chemical and morphological analyzes for all leagues, it was observed that there was dissociation of SiC and Si3N4, as well as diffusion of Si in Ni matrix and carbon cluster and dispersed in the matrix, which also occurred for the alloys with Si carriers and metallic graphite. So the league that was presented better results containing Si Ni with graphite metallic alloy as carriers, since this had dispersed graphite best in the league, reaching the microstructural model proposed, which is necessary for material characteristic of solid lubricant, so how we got the best results when the density and hardness of the alloy

Extraordinary high strain rate superplasticity in electrodeposited nano-nickel and alloys

Superplastic materials exhibit very large elongations to failure,typically >500%, and this enables commercial forming of complex shaped components at slow strain rates of similar to 10(-4) s(-1). We report extraordinary record superplastic elongations to failure of up to 5300% at both high strain rates and low temperature in electrodeposited nanocrystalline Ni and some Ni alloys. Superplasticity is not related to the presence of sulfur or a low melting phase at grain boundaries. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Directional solidification of aluminum-nickel eutectic alloys using electroslag remelting

Attempts were made to produce directionally solidified, specifically grain aligned Al-6 wt pct Ni eutectic alloy using a laboratory scale ESR unit. For this purpose sand cast alloy electrodes were electroslag remelted under different mold conditions. The grain structure of the ingots obtained from these meltings showed that insulated silica molds gave the best vertical alignment of grains along the length of the ingot. The NiAl3 fibers within the grains tended to fan out and there was only a preferred alignment of fibers along the growth direction under the conditions of our experiments. The ESR parameters most suitable for vertical alignment of eutectic grains have been identified. In some electroslag remelting trials ingots were grown on a seed ingot. This resulted in a fewer vertical grains compared to the case when no seed ingot was used. The sand cast specimen of the eutectic exhibited a maximum tensile strength of around 88.2 MN/m2 (9.0 kg/mm2) whereas conventional ESR using water cooled mold gave strength value of 98.0 MN/m2 (10 kg/mm2). The directionally solidified ESR material showed longitudinal tensile strength as high as 213.7 MN/m2 (21.8 kg/mm2) which could be further increased to 220.6 MN/m2 (22.5 kg/mm2) by using the seed ingot. The average growth rate was varied between 5 to 25 mm/min during electroslag remelting in this study. The flow stresses, tangent modulus and ultimate tensile strength of directionally solidified eutectic increased with increasing growth rates.

Processing maps for hot working of Cu-Ni-Zn alloys. Part I - Alpha-nickel silver

The constitutive behaviour of agr — nickel silver in the temperature range 700–950 °C and strain rate range 0.001–100 s–1 was characterized with the help of a processing map generated on the basis of the principles of the ldquodynamic materials modelrdquo of Prasadet al Using the flow stress data, processing maps showing the variation of the efficiency of power dissipation (given by 2m/(m+1) wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-nickel silver exhibits a single domain at temperatures greater than 750 °C and at strain rates lower than 1s–1, with a maximum efficiency of 38% occurring at about 950 °C and at a strain rate of 0.1 s–1. In the domain the material undergoes dynamic recrystallization (DRX). On the basis of a model, it is shown that the DRX is controlled by the rate of interface formation (nucleation) which depends on the diffusion-controlled process of thermal recovery by climb. At high strain rates (10 and 100s–1) the material undergoes microstructural instabilities, the manifestations of which are in the form of adiabatic shear bands and strain markings.

Processing maps for hot working of Cu-Ni-Zn alloys Part II Alpha-Beta nickel silver

The constitutive behaviour of agr-beta nickel silver in the temperature range 600�850 °C and strainrate range 0.001�100s�1 was characterized with the help of a processing map generated on the principles of the dynamic materials model. On the basis of the flow-stress data, processing maps showing the variation of the efficiency of power dissipation (given by [2m/(m+1)], wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-beta nickel silver exhibits a single domain at temperatures greater than 700 °C and at strain rates lower than 1 s�1 with a maximum efficiency of power dissipation of about 42% occurring at about 850 °C and at 0.1 s�1. In the domain, the agr phase undergoes dynamic recrystallization and controls the deformation of the alloy, while the beta phase deforms superplastically. Optimum conditions for the processing of agr-beta nickel silver are 850 °C and 0.1 s�1. The material undergoes unstable flow at strain rates of 10 and 100 s�1 and in the temperature range 600�750 °C, manifestated in the form of adiabatic shear bands.

The Determination of the Surface Tensions of Nickel Sulfur Alloys using the Electromagnetic Oscillating Droplet Technique

An oscillating droplet method combined with electromagnetic levitation technique has been applied to determine the surface tensions of liquid nickel sulphur alloys as a function of the temperature and composition. The natural frequency of the oscillating droplet is evaluated using a Fourier analyser, and the influence of magnetic field strength on the surface tension was considered. Furthermore, the applicability of Butler's equation and subregular solution model for the surface was shown to predict the surface tension of the systems containing the surface active elements.