Photoluminescent multilayer films based on polyoxometalates

Ultrathin multilayer films consisting of the polyoxotungstoeuropate cluster K-12[EuP5W30O110] (EuP5W30) and poly( allylamine hydrochloride) (PAH) have been prepared by the layer-by-layer self-assembly method. The (EuP5W30 /PAH) multilayer films have been characterized by small-angle X-ray reflectivity measurements, X-ray photoelectron spectra, and atomic force microscopy (AFM). From the AFM images, the thickness of the {PEI/PSS/PAH(EuW30/PAH)} multilayer film was estimated to be 6.5 nm, corresponding to an average thickness of ca. 1.1 nm for a EuW30/PAH layer pair. The photoluminescent behavior of the film at room temperature was investigated to show the characteristic Eu3+ emission pattern of D-5(0)-->F-7(J). The fluorescence behavior of the multilayer film is essentially identical to that of H-n[EuP5W30O110]((12-n)-) in a concentrated aqueous solution, except for the relative intensities and peak bandwidths. The occurence of photoluminescent activity confirms the potential for creating luminescent multilayers with polyoxometalates (see ref. 23).

Covalent modification of a glassy carbon surface by 4-aminobenzoic acid and its application in fabrication of a polyoxometalates-consisting monolayer and multilayer films

4-Aminobenzoic acid (4-ABA) was covalently grafted on a glassy carbon electrode (GCE) by amine cation radical formation in the electrooxidation process of the amino-containing compound. X-ray photoelectron spectroscopy measurement proves the presence of 4-carboxylphenylamine monolayer on the GCE. The redox responses of various electroactive probes were investigated on the 4-ABA-modified GCE. Electron transfer to Fe(CN)(6)(3-) in solutions of various pHs was studied by both cyclic voltammetry and electrochemical impedance analysis on the modified electrode. Changes in the solution pH value result in the variation of the terminal group charge state, based on which surface pK(a) values are estimated. The 4-ABA-modified GCE was used as a suitable charged substrate to fabricate polyoxometalates-consisting (POM-consisting) monolayer and multilayer films through layer-by-layer assembly based on electrostatic attraction. Cyclic voltammetry shows the uniform growth of these three-dimensional multilayer films. Taking K10H3[Pr-(SiMo7W4O39)(2)]. H2O (abbreviated as Pr(SiMo7W4)(2)), for example, the preparation and electrochemical behavior of its monolayer and multilayer film had been investigated in detail. This modification strategy is proven to be a general one suitable for anchoring many kinds of POMs on the 4-ABA-modified GCE.

Layer-by-layer assembly of multilayer films consisting of silicotungstate and a cationic redox polymer on 4-aminobenzoic acid modified glassy carbon electrode and their electrocatalytic effects

A novel 4-aminobenzoic acid (4-ABA) monolayer film is formed on glassy carbon electrode (GCE) by amino cation radical method. Silicotungstic heteropolyanion (SiW12O404-, denoted as SiW12)-containing multilayer films have been fabricated on the 4-ABA modified GCE surface by alternate deposition with a quaternized poly(4-vinylpyridine) partially complexed with [Os(bpy)(2)Cl](2+/+) (denoted as QPVP-Os). Cyclic voltammetry (CV), X-ray photoelectron spectroscopy (XPS) and X-ray reflectivity (XR) have been used to characterise the as-prepared multilayer films. It is proved that the multilayer films are uniform and stable. The average thickness for a bilayer of QPVP-Os/SiW12 in the multilayer film is 30.2 Angstrom. The electrocatalytic activities of the multilayer films have been investigated on the reduction of three substrates of important analytical interests, HNO2, BrO3- and H2O2. Especially, the influence of layer number of the multilayer films on the electrocatalytic reduction of HNO2 has been investigated in detail. (C) 2000 Elsevier Science B.V. All rights reserved.

Comparative studies on electrochemical behavior and electrocatalytic properties of heteropolyanion-containing multilayer films prepared by two methods

Two modification methods for multilayer formation, i.e. immersion growth and electrochemical growth, were studied comparatively for their influence on the electrochemical behavior and the electrocatalytic properties of the thus-fabricated SiMo11V-containing multilayer films. Electrochemical growth was proven to be a more suitable method than immersion growth in preparing uniform ultrathin multilayer self-assemblies with good functions. We investigated the effects of scan rate and pH on the electrochemical behavior of the monolayer and multilayer films. We also compared the electrocatalytic effects on the reduction of BrO3- and HNO2 by the multilayer films prepared by the two methods. Moreover, the influence of multilayer thickness and the identity of the outermost layer on the electrocatalytic properties were studied. Much higher catalytic currents appeared on the thicker multilayer films than those on the thinner ones. On the other hand, the catalytic currents became smaller when the multilayer films with SiMo11V as the outermost layer were covered with an additional quarternized poly(4-vinylpyridine) layer partially complexed with osmium bis(2,2'-bypyridine) chloride (QPVP-Os layer). These influences were believed to be due to the different quantities of electrocatalyst loaded in the multilayer films and the blocking effect of the QPVP-Os outermost layer. (C) 2000 Elsevier Science S.A. All rights reserved.

Assembly of alternating polycation and DNA multilayer films by electrostatic layer-by-layer adsorption

The assembly of alternating DNA and positively charged poly(dimethyldiallylammonium chloride) (PDDA) multilayer films by electrostatic layer-by-layer adsorption has been studied. The real-time surface plasmon resonance (BIAcore) technique was used to characterize and monitor the formation of multilayer films in solution in real time continuously. Electrochemical impedance spectroscopy (EIS) and UV-vis absorbance measurements were also used to study the film assembly, and linear film growth was observed. All the results indicate that the uniform multilayer can be obtained on the poly(ethylenimine)- (PEI-) coated substrate surface. The kinetics of the adsorption of DNA on PDDA surface was also studied by the real-time BIAcore technique; the observed rate constant was calculated using a Langmuir model (k(obs) = (1.28 +/- 0.08) x 10(-2) s(-1).

Fabrication of layer-by-layer deposited multilayer films containing DNA and its interaction with methyl green

Multilayer films were fabricated by layer-by-layer electrostatic deposition techniques between poly(diallyIdimethylammonium chloride) (PDDA) and calf thymus DNA (CT DNA) on glassy carbon and quartz substrates. Electrochemical impedance spectroscopy (EIS), Fourier transform infrared (FTIR) spectroscopy and UV-vis spectroscopy demonstrated the uniform assembly of PDDA/DNA multilayer films, and X-ray photoelectron spectroscopy confirmed the elemental composition of the films. Moreover, the interaction of DNA in PDDA/DNA films with methyl green was investigated by UV-vis spectroscopy and circular dichroism (CD). (C) 2001 Elsevier Science B.V. All rights reserved.

Ultrathin multilayer films incorporating Keggin-type heteropolyanion clusters

Two new ultrathin multiplayer films have been successfully prepared fi-om Keggin-type heteropoly acids H-4[SiW12O40] and H-3[PMo12O40] with polyelectrolytes PEI, PSS, and PAH, using the electrostatic layer-by-layer self-assembly, technique. The XR results reveal their film thickness at nanoscale (similar to 20 nm). According to the AFM images, it is believed that the surface roughness (rough degree of film surface) of the polyelectrolyte-polyoxometalate film greatly depends on the kind of polyoxometalates.

Electrostatic layer-by-layer assembly of polycation and DNA multilayer films by real-time surface plasmon resonance technique

The assembly of alternating DNA and positively charged poly(dimethyldiallylammonium chloride) (PDDA) multilayer films by electrostatic layer-by-layer adsorption has been studied. Real time surface plasmon resonance (BIAcore) technique was used to characterize and monitor the formation of multilayer films in solution in real time continuously. The results indicate that the uniform multilayer can be obtained on the poly(ethylenimine) (PEI) coated substrate surface. The kinetics of the adsorption of DNA on PDDA surface was also studied by real-time BIAcore technique, and the observed rate constant was calculated using a Langmuir model (k(obs) = (1.28 +/- 0.08) x 10(-2) s(-1)).

Formation and characterization of heteropolyacid/polycation multilayer films on gold electrode

Ultrathin multilayer films of a polybasic lanthanide heteropoly tungstate-molybdate complex and a cationic polymer of quaternized poly(4-vinylpyridine) partially complexed with osmium bis(2,2'-bipyridine) have been fabricated on a gold electrode precoated with a cysteamine self-assembled monolayer. The multilayer films have been characterized by optical spectroscopy, small-angle X-ray diffraction, and electrochemical methods (cyclic voltammetry and electrochemical impedance). Especially, the electrochemical impedance spectroscopy is developed to monitor the layer deposition processes. It provides important information such as double-layer capacitance and charge-transfer resistance. All obtained results reveal regular film growth with each layer adsorption. (C) 2001 The Electrochemical Society.

Surface roughness characterization of soft x-ray multilayer films on the nanometer scale

The soft x-ray reflectivity of multilayer films is affected by the surface roughness on the transverse nanometer scale. Scanning tunneling microscopy (STM) is an ideal instrument for providing high-lateral-resolution roughness measurements for soft x-ray multilayer films that cannot be obtained with other types of instruments on the transverse nanometer scale. The surface roughnesses of Mo/Si, Mo/C, and W/Si soft x-ray multilayer films prepared by an ion-beam-sputtering technique were measured with a STM on the vertical and transverse attributes. The film roughnesses and average spatial wavelengths added to the substrates depend on the multilayer film fabrication conditions, i.e., material combinations, number of layers, and individual layer thickness. These were estimated to lead to a loss of specular reflectivity and variations of the soft x-ray scattering angle distribution. This method points the way to further studies of soft x-ray multilayer film functional properties and can be used as basic guidance for selecting the best coating conditions in the fabrications of soft x-ray multilayer films. (C) 1996 American Vacuum Society.

Immobilization of Poly(propylene imine) Dendrimer/Nickel Phtalocyanine as Nanostructured Multilayer Films To Be Used as Gate Membranes for SEGFET pH Sensors

We describe the assembly of layer-by-layer films based on the poly(propylene imine) dendrimer (PPID) generation 3 and nickel tetrasulfonated phthalocyanine (NiTsPc) for application as chemically sensitive membranes in sepal alive extended-gate field effect transistor (SEGFET) pH sensors PPID/NiTsPc films wet e adsorbed on quartz, glass. indium tin oxide. or gold (Au)-covered glass substrates Multilayer formation was monitored via UV-vis absorption upon following the increment in the Q-band intensity (615 nm) of NiTsPc The nanostructured membranes were very stable in a pH range of 4-10 and displayed a good sensitivity toward H(+), ca 30 mV/pH for PPID/N(1)TsPc films deposited on Au-covered substrates For films deposited on ITO, the sensitivity was ca 52 4 mV/pH. close to the expected theoretical value for ton-sensitive membranes. The use of chemically stable PPID/NiTsPc films as gate membranes in SEGFETs, as introduced here, may represent an alternative for the fabrication of nanostructured, porous platforms for enzyme immobilization to be used in enzymatic biosensors.

Electrochromic Properties of a Metallo-supramolecular Polymer Derived from Tetra(2-pyridyl-1,4-pyrazine) Ligands Integrated in Thin Multilayer Films

The electrochromic behavior of iron complexes derived from tetra-2-pyridyl-1,4-pyrazine (TPPZ) and a hexacyanoferrate species in polyelectrolytic multilayer adsorbed films is described for the first time. This complex macromolecule was deposited onto indium-tin oxide (ITO) substrates via self-assembly, and the morphology of the modified electrodes was studied using atomic force microscopy (AFM), which indicated that the hybrid film containing the polyelectrolyte multilayer and the iron complex was highly homogeneous and was approximately 50 nm thick. The modified electrodes exhibited excellent electrochromic behavior with both intense and persistent coloration as well as a chromatic contrast of approximately 70%. In addition, this system achieved high electrochromic efficiency (over 70 cm(2) C-1 at 630 nm) and a response time that could be measured in milliseconds. The electrode was cycled more than 10(3) times, indicating excellent stability.

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO2/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 degrees C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications. (C) 2010 Elsevier B.V. All rights reserved.

Buildup of gold nanoparticle multilayer thin films based on the covalent-bonding interaction between boronic acids and polyols

A novel method for the fabrication of gold nanoparticle multilayer films based on the covalent-bonding interaction between boronic acid and polyols, poly(vinyl alcohol) (PVA), was developed. The multilayer buildup was monitored by UV-vis absorbance, spectroscopy, which showed a linear increase of the film absorbance with the number of adsorbed Au layers and indicated the stepwise and uniform assembling process. The atomic force microscopy (AFM) image showed that a compact gold multilayer thin film was successfully assembled. The residual boronic acid group on the surface of thin film Could incorporate glycosylated-protein horseradish peroxidase (HRP), and good catalytic activity for H2O2 could be observed.