Thermal Decomposition and Combustion Studies on Potassium Perchlorat e/Polystyrene Propellant Systems

STUDIES on potassium perchlorate/polystyrene (KP/PS) propellant systems have been carried out by using such techniques as thermogravimetry (TG), differential thermal analysis (DTA), and mass spectrometry (MS). It has been found that the thermal decomposition (TD) behavior of the KP/PS propellant is similar to that of the AP/PS propellant studied earlier.! It has also been observed that the TD of KP in the melt has a correlation with the burning rate (r) of KP/PS propellant at atmospheric pressure.

Curing reactions in plastic prepolymers and propellants. I. Polystyrene

Curing reactions of the viscous PS prepolymer and PS/AP propellant slurry have been studied. The molecular weight of the binder (separated from the propellant) and the prepolymer was found to increase to a maximum value, remain constant for some time, and then fall off between 50–125°C. The molecular weight of the binder was found to be less than corresponding prepolymer between 100–150°C but at lower temperatures (50–75°C) the reverse was found to be true. The increase in the molecular weight during curing at lower temperatures has been explained on the basis of Trommsdorff effect which gets support from the estimated activation energy (9 kcal mole−1) for the curing process. Curing was recognized as chain extension where the rate of polymerization becomes diffusion controlled below 75° C.

Characterization, electrical percolation and magnetization studies of polystyrene/multiwall carbon nanotube composite films

Polystyrene/multiwall carbon nanotube composite films are prepared with loading up to 7 weight percent (wt%) of multiwall carbon nanotubes by solution processing and casting technique. In the formation of these composite films, iron filled carbon nanotubes with high aspect ratio (similar to 4000) were used. Scanning electron microscopy study shows that the nanotubes are uniformly dispersed within the polymer matrix. At high magnification, bending of carbon nanotubes is noticed which can be attributed to their elastic properties. The electrical conductivity measurements show that the percolation threshold is rather low at 0.21 wt%. Hysteresis loop measurements on the bulk multiwall carbon nanotube and composite samples are done at 10, 150 and 300 K and the coercivity values are found to be largest at all the temperatures, for 1 wt% composite sample. (C) 2010 Elsevier B.V. All rights reserved.

Second harmonic generation in poled molecularly doped polymer films : Push-pull butadienes in poly(methyl methacrylate) and polystyrene

We report second harmonic generation in a new class of organic materials, namely donor-acceptor substituted all-trans butadienes doped in poly(methyl methacrylate) or polystyrene and oriented by corona poling at elevated temperatures. Second harmonic measurements were made at room temperature. The observed d33 coefficients are greater than those of potassium dihydrogen phosphate or 4-dimethylamino-4'-nitrostilbene doped in similar polymer matrices. Rotational diffusion coefficients estimated from the decay characteristics of the second harmonic intensity in the polymer films indicate that the polymer matrix plays a major role in stabilizing the dopants in a nonlinear optics conducive environment.

Comparison of the miscibility strategies in poly(benzyl methacrylate)-polystyrene blends

Exothermic interactions like hydrogen bonding, ionic and charge transfer, etc., and ''copolymer effect'' are commonly used to induce miscibility in immiscible blends. The efficacy of these methods in promoting miscibility in poly(benzyl methacrylate) (PBMA)-polystyrene (PS) immiscible blends has been studied by suitably modifying the structure of the component polymers. It has been found that hydrogen bonding approach is most advantageous among these approaches as it involves the need for minimum interacting sites. It has also been shown that these results can be extended to the blends of poly(acrylate)s or poly(methacrylate)s with PS. (C) 1996 John Wiley & Sons, Inc.

Synthesis of two designed hairpin peptides on a newly developed 1,6-hexanediol diacrylate (HDODA)-crosslinked polystyrene resin

Synthesis of two designed hairpin peptides on 1,6-hexanediol diacrylate crosslinked polystyrene support using the standard solid phase methodology is described. Both the peptides are obtained in high yield and purity. The new polymeric system is an ideal support for the synthesis of hairpin peptides, which is a very difficult task by the solid phase method.

Grafting of m-isopropenyl-alpha, alpha-dimethylbenzyl-isocyanate (m-TMI) onto isotactic polypropylene: Synthesis and characterization

A novel vinyl monomer with an isocyanate functional group, m-isopropenyl-alpha,alpha-dimethylbenzyl-isocyanate (m-TMI), was grafted onto isotactic polypropylene (i-PP) using dicumyl peroxide (DCP) as the initiator. This would open up the possibility of using the grafted polymer with the reactive isocyanate group as compatibilizer for blending carbohydrates such as cellulose with. polypropylene. The grafting was carried out in a Brabender Plasticoder at 180degreesC. The effects of monomer and initiator concentrations on the yield of grafting were investigated by performing statistical analysis. While the grafting yield increased with the concentration of DCP at any given concentration of m-TMI, the variation of the grafting yield with m-TMI concentration, for a given concentration of DCP, went through a maximum, the optimum yield of 7.8% (w/w) being obtained at 10 wt.% concentration of both DCP and m-TMI. The grafting reaction is. accompanied by considerable chain scission of I-PP, resulting in a decrease in the molecular weight of the grafted polymer. While the molecular weight drops sharply even at a low concentration of DCP, there occurs no further significant change in the molecular weight even at much higher concentrations of the initiator.

Nanoparticle-Driven Intermolecular Cooperativity and Miscibility in Polystyrene/Poly(vinyl methyl ether) Blends

The effect of silver nanoparticles (nAg) in PS/PVME polystyrene/poly(vinyl methyl ether)] blends was studied with respect to the evolution of morphology, demixing temperature, and segmental dynamics. In the early stage of demixing, PVME developed an interconnected network that coarsened in the late stage. The nAg induced miscibility in the blends as supported by shear rheological measurements. The physicochemical processes that drive phase separation in blends also led to migration of nAg to the PVME phase as supported by AFM. The segmental dynamics was greatly influenced by the presence of nAg due to the specific interaction of nAg with PVME. Slower dynamics and an increase in intermolecular cooperativity in the presence of nAg further supported the role of nAg in delaying the phase separation processes and augmenting the demixing temperature in the blends. Different theoretical models were assessed to gain insight into the dynamic heterogeneity in PS/PVME blends at different length scales.

Magnetic field induced delocalization in multi-wall carbon nanotube-polystyrene composite at high fields

In well dispersed multi-wall carbon nanotube-polystyrene composite of 15 wt%, with room temperature conductivity of similar to 5 S/cm and resistivity ratio R-2K/R-200K] of similar to 1.4, the temperature dependence of conductivity follows a power-law behavior. The conductivity increases with magnetic field for a wide range of temperature (2-200 K), and power-law fits to conductivity data show that localization length (xi) increases with magnetic field, resulting in a large negative magnetoresistance (MR). At 50T, the negative MR at 8 K is similar to 13% and it shows a maximum at 90K (similar to 25%). This unusually large negative MR indicates that the field is delocalizing the charge carriers even at higher temperatures, apart from the smaller weak localization contribution at T < 20 K. This field-induced delocalization mechanism of MR can provide insight into the intra and inter tube transport. (C) 2013 Elsevier Ltd. All rights reserved.

Reduced graphene oxide induced phase miscibility in polystyrene-poly(vinyl methyl ether) blends

Graphene oxide and reduced graphene oxide (r-GO) were synthesized by wet chemistry and the effect of r-GO in PS-PVME blends was investigated here with respect to phase miscibility, intermolecular cooperativity in the glass transition region and concentration fluctuation variance by shear rheology and dielectric spectroscopy. The spinodal decomposition temperature (T-s) and correlation length were evaluated from isochronal temperature scans in shear rheology. The r-GO is shown to induce miscibility in the blends, which may lead to increased local heterogeneity in the blends, though the length of cooperatively re-arranged regions (xi) at T-g is more or less unaltered. The evolution of the phase morphology as a function of temperature was assessed using polarized optical microscopy (POM). In the case of the 60/40 PS-PVME blends with 0.25 wt% r-GO, apart from significant refinement in the morphology, retention of the interconnected ligaments of PVME was observed, even in the late stages of phase separation suggesting that the coarsening of the phase morphology has been slowed down in the presence of r-GO. This phenomenon was also supported by AFM. Surface enrichment of PVME, owing to its lower surface tension, in the demixed samples was supported by XPS scans. The interconnected network of PVME has resulted in significantly higher permittivity in the bi-phasic blends, although the concentration of r-GO is below the percolation threshold.

Electromagnetic Interference Shielding Materials Derived from Gelation of Multiwall Carbon Nanotubes in Polystyrene/Poly(methyl methacrylate) Blends

Blends of polystyrene (PS) and poly(methyl methacrylate) (PMMA) with different surface-functionalized multiwall carbon nanotubes (MWNTs) were prepared by solution blending to design materials with tunable EMI (electromagnetic interference) shielding. Different MWNTs like pristine, amine (similar to NH2), and carboxyl acid (similar to COOH) functionalized were incorporated in the polymer by solution blending. The specific interaction driven localization of MWNTs in the blend during annealing was monitored using contact mode AFM (atomic force microscopy) on thin films. Surface composition of the phase separated blends was further evaluated using X-ray photoelectron spectroscopy (XPS). The localization of MWNTs in a given phase in the bulk was further supported by selective dissolution experiments. Solution-casted PS/PMMA (50/50, wt/wt) blend exhibited a cocontinuous morphology on annealing for 30 min, whereas on longer annealing times it coarsened into matrix-droplet type of morphology. Interestingly, both pristine MWNTs and NH2-MWNTs resulted in interconnected structures of PMMA in PS matrix upon annealing, whereas COOH-MWNTs were localized in the PMMA droplets. Room-temperature electrical conductivity and electromagnetic shielding effectiveness (SE) were measured in a broad range of frequency. It was observed that both electrical conductivity and SE were strongly contingent on the type of surface functional groups on the MWNTs. The thermal conductivity of the blends was measured with laser flash technique at different temperatures. Interestingly, the SE for blends with pristine and NH2-MWNTs was >-24 dB at room temperature, which is commercially important, and with very marginal variation in thermal conductivity in the temperature range of 303-343 K. The gelation of MWNTs in the blends resulted in a higher SE than those obtained using the composites.

Kinetic and Size Control of Polystyrene and Polyacrylic Octadecyl Ester Lattices Via Polymerization in O/W Microemulsions

The kinetic studies of the acrylic octadecyl ester and styrene polymerization in microemulsion systems, (1) cetyl pyridine bromide (CPDB)/t-butanol/styrene/water; (2) CPDB/t-butanol/toluene + acrylic octadecyl ester (1:1, w/v)/ water; (3) cetyl pyridine bromide/styrene/formamide, were made by using dynamic laser light scattering techniques (DLS). The mechanisms of nucleation of latex particles were discussed. The most possible nucleation location of the styrene and acrylic octadecyl ester microlatex particles in aqueous microemulsion system is in aqueous phase via homogeneous nucleation. Meanwhile, parts of microlatex particles are possibly produced via swollen micelles (microemulsions) and monomer droplets nucleation. On the other hand, the most possible nucleation location of the styrene microlatex particles in nonaqueous microemulsion system is inside monomer droplets. The relationship between the amount of monomer and the size of microlatex was also investigated. It has been found that the size of microlatex particles could be controlled by changing the amount of monomer. (C) 2002 Elsevier Science B.V. All rights reserved.

Improving Nucleation in the Fabrication of High-Quality 3D Macro-Porous Copper Film through The Surface-Modification of A Polystyrene Colloid-Assembled Template

A new approach is developed to the fabrication of high-quality three-dimensional macro-porous copper films. A highly-ordered macroporous copper film is successfully produced on a polystyrene sphere (PS) template that has been modified by sodium dodecyl sulfate (SDS). It is shown that this procedure can change a hydrophobic surface of PS template into a hydrophilic surface. The present study is devoted to the influence of the electrolyte solution transport on the nucleation process. It is demonstrated that the permeability of the electrolyte solution in the nanochannels of the PS template plays an important role in the chemical electrodeposition of high-quality macroporous copper film. The permeability is drastically enhanced in our experiment through the surface modi. cation of the PS templates. The method could be used to homogeneously produce a large number of nucleations on a substrate, which is a key factor for the fabrication of the high-quality macroporous copper film.