Evaluation of two mineral trioxide aggregate compounds as pulp-capping agents in human teeth

The present randomized, controlled prospective study evaluated the histomorphological response of human dental pulps capped with two grey mineral trioxide aggregate (MTA) compounds. Pulp exposures were performed on the occlusal floor of 40 human permanent pre-molars. The pulp was capped either with ProRoot (Dentsply) or MTA-Angelus (Angelus) and restored with zinc oxide eugenol cement. After 30 and 60 days, teeth were extracted and processed for histological examination and the effects on the pulp were scored. The data were subjected to Kruskal-Wallis and Conover tests (alpha = 0.05). In five out of the 40 teeth bacteria were present in pulp tissue. No significant difference was observed between the two materials (P > 0.05) in terms of overall histological features (hard tissue bridge, inflammatory response, giant cells and particles of capping materials). Overall, 94% and 88% of the specimens capped with MTA-Angelus and ProRoot, respectively, showed either total or partial hard tissue bridge formation (P > 0.05). Both commercial materials ProRoot (Dentsply) and MTA-Angelus (Angelus) produced similar responses in the pulp when used for pulp capping in intact, caries-free teeth.

Response of human dental pulp capped with MTA and calcium hydroxide powder

Objectives: To compare the response of human dental pulp capped with a mineral trioxide aggregate (MTA) and Ca(OH)(2) powder. Methods and Material: Pulp exposures were performed on the occlusal floor of 40 permanent premolars. The pulp was then capped with either Ca(OH)(2) powder (CH) or MTA and restored with resin composite. After 30 days (groups CH30 and MTA30) and 60 days (groups CH60 and MTA60), the teeth were extracted and processed for HE and categorized in a histological score system. The data were subjected to Kruskal-Wallis and Conover tests (alpha=0.05). Results: In regard to dentin bridge formation, CH30 showed a tendency towards superior performance compared to MTA30 (p>0.05), although the products showed comparable results at day 60. In the item ""Inflammation"" and ""General State of the Pulp"" (p>0.05), CH showed a tendency towards presenting a higher inflammatory response. In the item ""Other Pulpal Findings,"" MTA and Ca(OH)(2) showed equal and excellent performance after 30 and 60 days (p>0.05). Conclusion: After 30 days, Ca(OH)(2) powder covered with calcium hydroxide cement showed faster hard tissue bridge formation compared to MTA. After 60 days, Ca(OH)(2) powder or NITA materials showed a similar and excellent histological response with the formation of a hard tissue bridge in almost all cases with low inflammatory infiltrate.

Heat-killed Enterococcus faecalis Alters Nitric Oxide and CXCL12 Production but not CXCL8 and CCL3 Production by Cultured Human Dental Pulp Fibroblasts

Introduction: Fibroblasts are the most abundant cells in dental pulp. To investigate their capacity to produce the chemokines CCL3, CXCL8, and CXCL12 as well as nitric oxide (NO), we evaluated the production of these mediators in supernatants of cultured human dental pulp fibroblasts (HDPF) stimulated by heat-killed Enterococcus faecalis (HKEF). Methods: Primary cultures of HDPF were stimulated with medium alone or HKEF (1:1, 10:1, or 100:1 bacteria:fibroblast) for 1, 6, and 24 hours. Chemokines and NO were assessed through enzyme-linked immunosorbent assay and Griess reaction, respectively. Statistical analysis was performed by using analysis of variance and Tukey post test. Results: CCL3 was not detected, whereas constitutive CXCL8 was not affected. Production of CXCL12 was increased at 1 and 6 hours, and NO was increased at the concentration of 1:1 bacteria:fibroblast at 24 hours. Viability and proliferation assays did not reveal cell number differences. Conclusions: These findings demonstrate that heat-killed E. faecalis is able to increase production of CXCL12 and NO by HDPF. (J Endod 2010;36:91-94)

In vitro analysis of human tooth pulp chamber temperature after low-intensity laser therapy at different power outputs

In vitro studies have provided conflicting evidence of temperature changes in the tooth pulp chamber after low-level laser irradiation of the tooth surface. The present study was an in vitro evaluation of temperature increases in the human tooth pulp chamber after diode laser irradiation (GaAlAs, lambda = 808 nm) using different power densities. Twelve human teeth (three incisors, three canines, three premolars and three molars) were sectioned in the cervical third of the root and enlarged for the introduction of a thermocouple into the pulp chamber. The teeth were irradiated with 417 mW, 207 mW and 78 mW power outputs for 30 s on the vestibular surface approximately 2 mm from the cervical line of the crown. The highest average increase in temperature (5.6A degrees C) was observed in incisors irradiated with 417 mW. None of the teeth (incisors, canines, premolars or molars) irradiated with 207 mW showed temperature increases higher than 5.5A degrees C that could potentially be harmful to pulp tissue. Teeth irradiated with 78 mW showed lower temperature increases. The study showed that diode laser irradiation with a wavelength of 808 nm at 417 mW power output increased the pulp chamber temperature of certain groups of teeth, especially incisors and premolars, to critical threshold values for the dental pulp (5.5A degrees C). Thus, this study serves as a warning to clinicians that ""more"" is not necessarily ""better"".

Effect of a calcium hydroxide/chlorhexidine paste as intracanal dressing in human primary teeth with necrotic pulp against Porphyromonas gingivalis and Enterococcus faecalis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Hypoxia Enhances the Angiogenic Potential of Human Dental Pulp Cells

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Penetration of 38% hydrogen peroxide into the pulp chamber in bovine and human teeth submitted to office bleach technique

This study evaluated the pulp chamber penetration of peroxide bleaching agent in human and bovine teeth after office bleach technique. All the teeth were sectioned 3 mm apical of the cement-enamel junction and were divided into 2 groups, A (70 third human molars) and B (70 bovine lateral incisors), that were subdivided into A1 and B1 restored by using composite resin, A2 and B2 by using glass ionomer cement, and A3 and B3 by using resin-modified glass ionomer cement; A4, A5, B4, and B5 were not restored. Acetate buffer was placed in the pulp chamber, and the bleaching agent was applied for 40 minutes as follows: A1-A4 and B1-B4, 38% hydrogen peroxide exposure and A5 and B5, immersion into distilled water. The buffer solution was transferred to a glass tube in which leuco crystal violet and horseradish peroxidase were added, producing a blue solution. The optical density of the blue solution was determined by spectrophotometer and converted into microgram equivalents of hydrogen peroxide. Data were submitted to analysis of variance and Dunnett, Kruskal-Wallis, and Tukey tests (5%). A higher level of hydrogen peroxide penetrated into the pulp chamber in resin-modified glass ionomer cements in bovine (0.79 +/- 0.61 mu g) and human (2.27 +/- 0.41 mu g) groups. The bleaching agent penetration into the pulp chamber was higher in human teeth for any experimental situation. The penetration of the hydrogen peroxide depends on restorative materials, and under the conditions of this study human teeth are more susceptible to penetration of bleaching agent into the pulp chamber than bovine teeth.

Heat-killed Enterococcus faecalis Alters Nitric Oxide and CXCL12 Production but not CXCL8 and CCL3 Production by Cultured Human Dental Pulp Fibroblasts

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Response of human dental pulp capped with MTA and calcium hydroxide powder

Objectives: To compare the response of human dental pulp capped with a mineral trioxide aggregate (MTA) and Ca(OH) 2 powder. Methods and Material: Pulp exposures were performed on the occlusal floor of 40 permanent premolars. The pulp was then capped with either Ca(OH) 2 powder (CH) or MTA and restored with resin composite. After 30 days (groups CH30 and MTA30) and 60 days (groups CH60 and MTA60), the teeth were extracted and processed for HE and categorized in a histological score system. The data were subjected to Kruskal-Wallis and Conover tests (α=0.05). Results: In regard to dentin bridge formation, CH30 showed a tendency towards superior performance compared to MTA30 (p>0.05), although the products showed comparable results at day 60. In the item Inflammation and General State of the Pulp (p>0.05), CH showed a tendency towards presenting a higher inflammatory response. In the item Other Pulpal Findings, MTA and Ca(OH) 2 showed equal and excellent performance after 30 and 60 days (p>0.05). Conclusion: After 30 days, Ca(OH) 2 powder covered with calcium hydroxide cement showed faster hard tissue bridge formation compared to MTA. After 60 days, Ca(OH) 2 powder or MTA materials showed a similar and excellent histological response with the formation of a hard tissue bridge in almost all cases with low inflammatory infiltrate. © Operative Dentistry, 2008.

Evaluation of two mineral trioxide aggregate compounds as pulp-capping agents in human teeth

Aim: The present randomized, controlled prospective study evaluated the histomorphological response of human dental pulps capped with two grey mineral trioxide aggregate (MTA) compounds. Methodology: Pulp exposures were performed on the occlusal floor of 40 human permanent pre-molars. The pulp was capped either with ProRoot (Dentsply) or MTA-Angelus (Angelus) and restored with zinc oxide eugenol cement. After 30 and 60 days, teeth were extracted and processed for histological examination and the effects on the pulp were scored. The data were subjected to Kruskal-Wallis and Conover tests (α = 0.05). Results: In five out of the 40 teeth bacteria were present in pulp tissue. No significant difference was observed between the two materials (P > 0.05) in terms of overall histological features (hard tissue bridge, inflammatory response, giant cells and particles of capping materials). Overall, 94% and 88% of the specimens capped with MTA-Angelus and ProRoot, respectively, showed either total or partial hard tissue bridge formation (P > 0.05). Conclusions: Both commercial materials ProRoot (Dentsply) and MTA-Angelus (Angelus) produced similar responses in the pulp when used for pulp capping in intact, caries-free teeth. © 2009 International Endodontic Journal.

Response of human dental pulp to calcium hydroxide paste preceded by a corticosteroid/antibiotic dressing agent

Aim: To evaluate the treatment with corticosteroid/antibiotic dressing in pulpotomy with calcium hydroxide. Methods: Forty-six premolars were pulpotomized and randomly assigned into 3 groups. In Group I pulpal wound was directly capped with calcium hydroxide, and Group II and Group III received corticosteroid/antibiotic dressing for 10 min or 48 h, respectively, before pulp capping. Teeth were processed for histological analysis after 7, 30 or 60 days to determine inflammatory cell response, tissue disorganization, dentin bridge formation and presence of bacteria. Attributed scores were analyzed by Kruskal-Wallis and Mann-Whitney tests (α=0.05). Results: On the 7th day, all groups exhibited dilated and congested blood vessels in the tissue adjacent to pulpal wound. The inflammatory cell response was significantly greater in Group III (p<0.05). On the 30th day, in all groups, a thin dentin matrix layer was deposited adjacent to the pulpal wound and a continuous odontoblast-like cell layer underlying the dentin matrix was observed. On the 60th day, all groups presented a thick hard barrier characterized by an outer zone of dystrophic calcification and an inner zone of tubular dentin matrix underlined by a defined odontoblast-like cell layer. Conclusions: Within the limitations of present study, considering that the treatment was performed in healthy teeth, it may be concluded that the use of a corticosteroid/antibiotic dressing before remaining tissue protection with calcium hydroxide had no influence on pulp tissue healing.

LED light attenuation through human dentin: A first step toward pulp photobiomodulation after cavity preparation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Infrared LED irradiation photobiomodulation of oxidative stress in human dental pulp cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)