Heat capacity enhancement and thermodynamic properties of nanostructured amorphous SiO2

The heat capacity of nanostructured amorphous SiO2 (na-SiO2) has been measured by adiabatic calorimetric method over the temperature range 9-354 K. TG and differential scanning calorimeter (DSC) were also employed to determine the thermal stability. Glass transition temperature (T-g) for the two same grain sizes with different specific surface of naSiO(2) samples and one coarse-grained amorphous SiO2 (ca-SiO2) sample were determined to be 1377, 1397 and 1320 K, respectively. The low temperature experimental results show that there are significant heat capacity (C-P) enhancements among na-SiO2 samples and ca-SiO2. Entropy, enthalpy, Gibbs free energy and Debye temperature (theta (D)) were obtained based on the low temperature heat capacity measurement of na-SiO2. The Cp enhancements of na-SiO2 were discussed in terms of configurational and vibrational entropy. (C) 2001 Elsevier Science B.V. All rights reserved.

Enhancement of molar heat capacity of nanostructured Al2O3

The nanosized alumina prepared by the hydrolysis method with an average particle size of 20 nm was characterized by X-ray diffraction. The heat capacity measurements of the prepared sample were carried out using an adiabatic calorimeter in the temperature range from 78 to 370 K. Enhancement of heat capacity was observed in the nanostructured materials as the heat capacity data were compared with those of the corresponding coarse-grained materials. The enhanced heat capacity was discussed on the basis of experiments. Differential scanning calorimetry and thermogravimetry were used to determine the thermal stability of the nanostructured alumina.

Heat capacity and thermochemical study of trifluoroacetamide (C2H2F3NO)

The low-temperature heat capacities of trifluoroacetamide were precisely determined with a small sample precision automated adiabatic calorimeter over the temperature range from 78 to 404 K. A solid-to-solid phase transition, a fusion and a phase transition from a liquid crystalline phase to fully liquid phase have been observed at the temperatures of 336.911+/-0.102, 347.622+/-0.094 and 388.896+/-0.160 K, respectively. The molar enthalpies of these phase transitions as well as the chemical purity of the substance were determined to be 5.576+/-0.004, 11.496+/-0.007, 1.340+/-0.005 kJ mol(-1) and 99.30 mol%, respectively, on the basis of the heat capacity measurements. The molar entropies of the three phase transitions were calculated to be 16.550+/-0.012, 33.071+/-0.029 and 3.447+/-0.027 J mol(-1) K-1, respectively. Further researches of the thermochemical properties for this compound have been carried out by means of TG and DSC techniques. (C) 2000 Elsevier Science B.V. All rights reserved.

Low-temperature heat capacity and phase transition of n-hexatriacontane

The heat capacities of crystalline and liquid n-hexatriacontane were measured with an automatic adiabatic calorimeter over the temperature range of 80-370 K. Two solid-to-solid phase transitions at the temperatures of 345.397 and 346.836 K, and a fusion at the temperature of 348.959 K have been observed. The enthalpies and entropies of these phase transitions as well as the chemical purity of the substance were determined on the basis of the heat capacity measurements. Thermal decomposition temperatures of the compound were measured by thermogravimetric analysis. (C) 1999 Elsevier Science B.V. All rights reserved.

Heat capacity and thermodynamic properties of N-(2-cyanoethyl) aniline (C9H10N2)

The low temperature heat capacities of N-(2-cyanoethyl)aniline were measured with an automated adiabatic calorimeter over the temperature range from 83 to 353 K. The temperature corresponding to the maximum value of the apparent heat capacity in the fusion interval, molar enthalpy and entropy of fusion of this compound were determined to be 323.33 +/- 0.13 K, 19.4 +/- 0.1 kJ mol(-1) and 60.1 +/- 0.1 J K-1 mol(-1), respectively. Using the fractional melting technique, the purity of the sample was determined to be 99.0 mol% and the melting temperature for the tested sample and the absolutely pure compound were determined to be 323.50 and 323.99 K, respectively. A solid-to-solid phase transition occurred at 310.63 +/- 0.15 K. The molar enthalpy and molar entropy of the transition were determined to be 980 +/- 5 J mol(-1) and 3.16 +/- 0.02 J K-1 mol(-1), respectively. The thermodynamic functions of the compound [H-T - H-298.15] and [S-T - S-298.(15)] were calculated based on the heat capacity measurements in the temperature range of 83-353 K with an interval of 5 K. (c) 2004 Elsevier B.V. All rights reserved.