Influence of normal and radial contributions of local current density on local electrochemical impedance spectroscopy

A new tri-electrode probe is presented and applied to local electrochemical impedance spectroscopy (LEIS) measurements. As opposed to two-probe systems, the three-probe one allows measurement not only of normal, but also of radial contributions of local current densities to the local impedance values. The results concerning the cases of the blocking electrode and the electrode with faradaic reaction are discussed from the theoretical point of view for a disk electrode. Numerical simulations and experimental results are compared for the case of the ferri/ferrocyanide electrode reaction at the Pt working electrode disk. At the centre of the disk, the impedance taking into account both normal and radial contributions was in good agreement with the local impedance measured in terms of only the normal contribution. At the periphery of the electrode, the impedance taking into account both normal and radial contributions differed significantly from the local impedance measured in terms of only the normal contribution. The radial impedance results at the periphery of the electrode are in good agreement with the usual explanation that the associated larger current density is attributed to the geometry of the electrode, which exhibits a greater accessibility at the electrode edge. (C) 2011 Elsevier Ltd. All rights reserved.

Aluminum slurry coatings to replace cadmium for aeronautic applications

Cadmium has been widely used as a coating to provide protection against galvanic corrosion for steels and for its natural lubricity on threaded applications. However, it is a toxic metal and a known carcinogenic agent, which is plated from an aqueous bath containing cyanide salts. For these reasons, the use of cadmium has been banned in Europe for most industrial applications. However, the aerospace industry is still exempt due to the stringent technical and safety requirements associated with aeronautical applications, as an acceptable replacement is yet to be found. Al slurry coatings have been developed as an alternative to replace cadmium coatings. The coatings were deposited on AISI 4340 steel and have been characterized by optical and electron microscopy. Testing included salt fog corrosion exposure, fluid corrosion exposure (immersion), humidity resistance, coating-substrate and paint-coating adhesion, electric conductivity, galvanic corrosion, embrittlement and fatigue. The results indicated that Al slurry coatings are an excellent alternative for Cd replacement.

Evaluation of the BEASY program using linear and piecewise linear approaches for the boundary conditions

The boundary element method (BEM) was used to study galvanic corrosion using linear and logarithmic boundary conditions. The linear boundary condition was implemented by using the linear approach and the piecewise linear approach. The logarithmic boundary condition was implemented by the piecewise linear approach. The calculated potential and current density distribution were compared with the prior analytical results. For the linear boundary condition, the BEASY program using the linear approach and the piecewise linear approach gave accurate predictions of the potential and the galvanic current density distributions for varied electrolyte conditions, various film thicknesses, various electrolyte conductivities and various area ratio of anode/cathode. The 50-point piecewise linear method could be used with both linear and logarithmic polarization curves.

Hybrid CuTCNQ/AgTCNQ metal-organic charge transfer complexes via galvanic replacement vs. corrosion recrystallization

This study reports a hybrid of two metal-organic semiconductors that are based on organic charge transfer complexes of 7,7,8,8-tetracyanoquinodimethane (TCNQ). It is shown that the spontaneous reaction between semiconducting microrods of CuTCNQ with Ag+ ions leads to the formation of a CuTCNQ/AgTCNQ hybrid, both in aqueous solution and acetonitrile, albeit with completely different reaction mechanisms. In an aqueous environment, the reaction proceeds by a complex galvanic replacement (GR) mechanism, wherein in addition to AgTCNQ nanowires, Ag0 nanoparticles and Cu(OH)2 crystals decorate the surface of CuTCNQ microrods. Conversely, in acetonitrile, a GR mechanism is found to be thermodynamically unfavorable and instead a corrosion-recrystallization mechanism leads to the decoration of CuTCNQ microrods with AgTCNQ nanoplates, resulting in a pure CuTCNQ/AgTCNQ hybrid metal-organic charge transfer complex. While hybrids of two different inorganic semiconductors are regularly reported, this report pioneers the formation of a hybrid involving two metal-organic semiconductors that will expand the scope of TCNQ-based charge transfer complexes for improved catalysis, sensing, electronics and biological applications.

Cathodic corrosion of Cu substrates as a route to nanostructured Cu/M (M = Ag, Au, Pd) surfaces

The electrochemical formation of nanostructured materials is generally achieved by reduction of a metal salt onto a substrate that does not influence the composition of the deposit. In this work we report that Ag, Au and Pd electrodeposited onto Cu under conditions where galvanic replacement is not viable and hydrogen gas is evolved results in the formation of nanostructured surfaces that unexpectedly incorporate a high concentration of Cu in the final material. Under cathodic polarization conditions the electrodissolution/corrosion of Cu occurs which provides a source of ionic copper that is reduced at the surface-electrolyte interface. The nanostructured Cu/M (M = Ag, Au and Pd) surfaces are investigated for their catalytic activity for the reduction of 4 nitrophenol by NaBH4 where Cu/Ag was found to be extremely active. This work indicates that a substrate electrode can be utilized in an interesting manner t make bimetallic nanostructures with enhanced catalytic activity.

Polyaniline for corrosion prevention of mild steel coupled with copper

Polyaniline emeraldine base/epoxy resin (EB/ER) coating was investigated for corrosion protection of mild steel coupled with copper in 3.5% NaCl solution. EB/ER coating with 5-10 wt% EB had long-term corrosion resistance on both uncoupled steel and copper due to the passivation effect of EB on the metal surfaces. During the 150 immersion days, the impedance at 0.1 Hz for the coating increased in the first 1-40 days and subsequently remained constant above 10(9) Omega cm(2), whereas that for pure ER coating fell below 10(6) Omega cm(2) after only 30 or 40 days. Immersion tests on coated steel-copper galvanic couple showed that EB/ER coating offered 100 times more protection than ER coating against steel dissolution and coating delamination on copper, which was mainly attributed to the passive metal oxide films formed by EB blocking both the anodic and cathodic reactions. Salt spray tests showed that 100 mu m EB/ER coating protected steel-copper couple for at least 2000 h.

Grey interrelation analysis to assess the influence of elements on the galvanic efficiency of Al sacrificial anode

Grey interrelation analysis method was used to study the correlation of Al-anode elements and its galvanic efficiency at 20 degreesC, 40 degreesC and 60 degreesC. Twenty-eight kinds of Al-anodes were made for experiments by the method given by Chinese National Standard GB4948-85 [1] and the correlation degree of elements added in the anodes were calculated. The results showed that the order of elements affecting galvanic efficiency at different temperature is basically the same, and the correlation degree can reflect the variation of Al-anode galvanic efficiency when changing temperature. It is suggested that the elements being added in Al-anode are Zn, In, Ga, Mg.

Corrosion behaviour of hot dip zinc and zinc-aluminium coatings on steel in seawater

A comparative investigation of hot dip Zn-25Al alloy, Zn-55Al-Si and Zn coatings on steel was performed with attention to their corrosion performance in seawater. The results of 2-year exposure testing of these at Zhoushan test site are reported here. In tidal and immersion environments, Zn-25Al alloy coating is several times more durable than zinc coating of double thickness. At long exposure times, corrosion rate for the Zn-25Al alloy coating remains indistinguishable from that for the Zn-55Al-Si coating of similar thickness in tidal zone, and is two to three times lower than the latter in immersion zone. The decrease in tensile strength suggested that galvanized and Zn-55Al-Si coated steel suffer intense pitting corrosion in immersion zone. The electrochemical tests showed that all these coatings provide cathodic protection to the substrate metal; the galvanic potentials are equal to - 1,050, - 1,025 and - 880 mV (SCE) for zinc, Zn-25Al alloy and Zn-55Al-Si coating, respectively, which are adequate to keep the steel inside the immunity region. It is believed that the superior performance of the Zn-25Al alloy coating is due to its optimal combination of the uniform corrosion resistance and pitting corrosion resistance. The inferior corrosion performance by comparison of the Zn coating mainly results from its larger dissolution rate, while the failure of the Zn-55Al-Si coating is probably related to its higher susceptibility to pitting corrosion in seawater.

Effect of sulfate-reducing bacteria on corrosion behavior of mild steel in sea mud

Microbiologically influenced corrosion (MIC) is very severe corrosion for constructions buried under sea mud environment. Therefore it is of great importance to carry out the investigation of the corrosion behavior of marine steel in sea mud. In this paper, the effect of sulfate-reducing bacteria (SRB) on corrosion behavior of mild steel in sea mud was studied by weight loss, dual-compartment cell, electronic probe microanalysis (EPMA), transmission electron microscopy (TEM).combined with energy dispersive X-ray analysis (EDX) and electrochemical impedance spectroscopy (EIS). The results showed that corrosion rate and galvanic current were influenced by the metabolic activity of SRB. In the environment of sea mud containing SRB, the original corrosion products, ferric (oxyhydr) oxide, transformed to iron sulfide. With the excess of the dissolved H2S, the composition of the protective layer formed of FeS transformed to FeS2 or other non-stoichiometric polysulphide, which changed the state of the former layer and accelerated the corrosion process.

Effect of post-weld heat-treatment on the oxide film and corrosion behaviour of laser-welded shape memory NiTi wires

Post-weld heat-treatment (PWHT) was applied to NiTi weldments to improve the corrosion behaviour by modifying the microstructure and surface composition. The surface oxide film on the weldments is principally TiO2, together with some Ti, TiO, and Ti2O3. The surface Ti/Ni ratio of the weldments after PWHT is increased. The oxide film formed in Hanks’ solution is thicker on the weldments after PWHT. The pitting resistance of the weldments is increased by PWHT. The galvanic effect in the weldments is very small. The weldment with PWHT at 350 °C shows the best corrosion resistance among other heat-treated weldments in this study.

Identification of MnCr2O4 nano-octahedron in catalysing pitting corrosion of austenitic stainless steels

Pitting corrosion of stainless steels, one of the classical problems in materials science and electrochemistry, is generally believed to originate from the local dissolution in MnS inclusions, which are more or less ubiquitous in stainless steels. However, the initial location where MnS dissolution preferentially occurs is known to be unpredictable, which makes pitting corrosion a major concern. In this work we show, at an atomic scale, the initial site where MnS starts to dissolve in the presence of salt water. Using in situ ex-environment transmission electron microscopy (TEM), we found a number of nano-sized octahedral MnCr2O4 crystals (with a spinel structure and a space group of Fd (3) over barm) embedded in the MnS medium, generating local MnCr2O4/MnS nano-galvanic cells. The TEM experiments combined with first-principles calculations clarified that the nano-octahedron, enclosed by eight {1 1 1} facets with metal terminations, is "malignant", and this acts as the reactive site and catalyses the dissolution of MnS. This work not only uncovers the origin of MnS dissolution in stainless steels, but also presents an atomic-scale evolution in a material's failure which may occur in a wide range of engineering alloys and biomedical instruments serving in wet environments. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

A novel electrochemical method for monitoring corrosion under insulation

Purpose - The objective of this work was to develop practical experimental techniques for monitoring corrosion in "difficult-to-test" conditions such as corrosion under insulation (CUI).

Design/methodology/approach - An electrochemically integrated multi-electrode array namely the wire beam electrode (WBE) method has been used in combination with noise signature analysis for the first time to monitor the penetration of corrosive species under simulated corrosion-under-insulation conditions. Corrosion of aluminium exposed under insulation materials such as rock wool, glass wool, cotton wool and tissue paper has been successfully monitored.

Findings - A typical potential noise signature of a major potential jump from AA1100 WBE was observed which corresponded to the corrosive species reaching the WBE surface in WBE current distribution map. A good correlation between the galvanic current maps and the corroded surface was also observed.

Originality/value - The preliminary results suggest that the proposed novel electrochemical method is capable of monitoring CUI.

A novel sensing technique for monitoring pitting corrosion of stainless steel type 316L

A novel electrochemically integrated multi-electrode array namely the wire beam electrode(WBE) in combination with noise signatures analysis has been designed to monitor pittingcorrosion of one of the best corrosion resistance ferrous alloys, stainless steel type 316L.From the direct correlation of electrochemical potential noise signatures and galvanic currentdistribution maps during pitting corrosion processes, two characteristic noise patterns wereobserved prior to stable pit formation: (i) the characteristic ‘peak’ of rapid potential transient,towards less negative direction, followed by recovery (termed noise signature I) was found tocorrelate with the disappearance of unstable anode; (ii) the characteristic noise pattern ofquick potential changes towards less negative direction followed by no recovery (termed noisesignature II) was found to correspond with the massive disappearance of minor anodes leadingto formation of highly localized major anodes in the galvanic current distribution maps.

An auto-switch for multisampling of a wire beam electrode corrosion monitoring system

An auto-switch device has been designed, constructed, and tested for multisensor corrosion measurements. The auto-switch is able to connect/disconnect the selected wire beam electrode and/or electrode pairs under computer control. A computer controlled analog switch-array consisting of 100 inputs has been used as an essential part of the switch bank. The switch-bank is an essential component of a corrosion-monitoring instrument that is expected to find wide application in industry. The performance of the switch-bank is discussed and its effect on the signals is illustrated.

Quantifying the efficiency and understanding the mechanism of localised corrosion inhibition using the wire beam electrode

Parameters extracted from the wire beam electrode (WBE) galvanic current maps have been used in conjunction with electrochemical noise patterns to directly quantify the degree of localised corrosion inhibition provided by inhibitors and to understand the mechanism of localised corrosion inhibition. The behaviour of two traditional localised corrosion inhibitors has been assessed by their effects on the maximum anodic current density (imax), total anodic current density (itot), the number of anodic sites (Na) and the localised corrosion intensity index (LCII). Typical experiments are presented to illustrate the application of these parameters in providing useful information on the efficiency and mechanism of localised corrosion inhibition.