The effect of microstructure on the fracture toughness of a metal-matrix composite

The fracture behaviour and plane strain fracture toughness, KIC, of four 8090-based metal-matrix composites containing 20 weight % SiC particles, 3, 6 and 23 μm in diameter, has been evaluated as a function of matrix ageing condition. Toughness values are found to be almost independent of reinforcement size. Ageing at 170°C results in a monotonic decrease in toughness with increasing strength up to the peak condition, with no subsequent recovery in toughness on overageing. However, unlike reinforced 8090, the composites are not found to be susceptible to intergranular embrittlement on overageing. The observed trends are found to be independent of reinforcement size. These findings are explained in terms of the strength, work hardening behaviour and nature and distribution of void-nucleating particles in the matrix. © 1993.

Effects of crack length and shape on the fracture toughness of a high strength steel 300m

The results of fracture toughness tests on a high strength steel 300m are presented. These results show (i) that in the presence of through-thickness cracks the toughness remains constant down to (a/W)-ratios as low as 0.01 and failure loads up to 0.85σy, and (ii) that the material is more resistant to crack growth when the cracks are semi-elliptical in shape, giving a toughness value which is almost 25 per cent higher than the through-thickness one. Three independent stress analyses are used to obtain stress intensity values for the semi-elliptical cracks and additional confirmation of the increase in toughness comes from stretch zone measurements.

Increasing the fracture toughness of silicon by ion implantation

Previous studies have shown that moderate doses of radiation can lead to increased fracture toughness in ceramics. An experimental investigation was conducted to determine the effects of ion implantation on fracture toughness in silicon. Specimens implanted with Ne showed increased fracture toughness, over the entire range of implantations tested. Using ions of various energies to better distribute implantation damage further increased the fracture toughness even though the region of amorphous damage was slightly decreased. The implantation damage accumulated in a predictable manner so that fracture toughness could be optimized.

Effect of dopants on the fracture toughness of silicon

Fracture experiments were conducted on p-type and n-type Si in the presence and absence of hydrogen. It was found that fracture toughness is slightly less than the fracture toughness of n-type silicon. Annealing silicon in an Ar/H atmosphere gave a hydrogen concentration of less than 0.1 ppm, which did not have any measurable effect on fracture toughness. Likewise, the exposure of pre-cracked specimens to H did not cause any measurable change in fracture toughness.

Fracture toughness characterization of aluminium-epoxy adhesive joints reinforced with electrospun Nylon 6,6 nanofibers

The use of adhesives to join two different substrates is an efficient replacement to classic joining technologies such as welding and soldering. One the one hand adhesion has different advantages over those techniques such as an improved stress distribution and the potential weight reduction of the structure; on the other hand, two of the most important drawbacks are a relatively low fracture toughness and the need of an accurate surface preparation. These two aspects will be accurately analysed in the present work: the use of Nylon nanofibers as reinforcement for the adhesive should increase fracture toughness, while a surface preparation method consisting of mechanical and chemical treatments will be developed. After the specimens are produced, they will be tested in mode I fracture using a DCB (Double Beam Cantilever) test, which allows to measure the fracture toughness during crack propagation. At the end of the test, the surfaces of the adherends will be visually observed and SEM (Scanning Electronic Microscope) analysed in order to evaluate if adhesive or cohesive fracture occurred, and thus if surface treatments has been well developed to allow a better adhesive-aluminium joining.

Computational evaluation of flexural toughness of FRC and fracture properties of plain concrete

In this paper, a computational tool concerning the computation of flexural and fracture toughness of cement based composites is presented. Firstly, RILEM`s (Reunion Internationale des Laboratoires d`Essais de Materiaux) recommendations related to the analysis of FRC in three-point bend tests are discussed in their relevant aspects regarding the computational implementations. The determination of other mechanical properties such as the Young modulus has been added to the program. Taking this into account, a new formulation based on displacements is used. In the second part of the paper, the determination of fracture properties of concrete, such as the fracture energy, G(F) , and the fracture toughness, K-IC(S), is discussed regarding the computational strategies used in the implementations. Several features whereby anterior data can be reanalyzed, obtained from other standards and recommendations, have been incorporated into the program, therefore allowing comparative studies and back analysis activities.

On the loading-rate dependence of the Al 7017-T73 fracture-initiation toughness

While static fracture toughness is a widely studied and standardised parameter, its dynamic counterpart has not been exhaustively examined. Therefore, in this research a series of quasi-static and different loading-rate dynamic tests were carried out to determine the evolution of fracture toughness with the velocity of the application of the load on aluminium 7017-T73 alloy. Three-point bending tests of pre-fatigued standard specimens (ASTM E399) at four loading-rates were carried out. The experiments were conducted by employing the subsequent apparatus ordered from lowest to highest load application velocity: a servo-hydraulic universal testing machine, a free-drop tower, a modified Split Hopkinson Pressure Bar and an explosive load testing device. In order to perform the dynamic fracture toughness tests, it was necessary to design and develop some experimental devices. The fracture-initiation toughness of the aluminium 7017-T73 alloy did not exhibit a significant variation for the studied cases. As a conclusion, the research showed that fracture-initiation toughness remained constant regardless of the velocity at which the load was applied.

A novel method for measuring the dynamic fracture-initiation toughness under impulsive loadings

The design and development of a new method for performing fracture toughness tests under impulsive loadings using explosives is presented. The experimental set-up was complemented with pressure transducers and strain gauges in order to measure, respectively, the blast wave that reached the specimen and the loading history. Fracture toughness tests on a 7017-T73 aluminium alloy were carried out by using this device under impulsive loadings. Previous studies reported that such aluminium alloy had very little strain rate sensitivity, which made it an ideal candidate for comparison at different loading rates. The fracture-initiation toughness values of the 7017-T73 aluminium alloy obtained at impulsive loadings did not exhibit a significant variation from the cases studied at lower loading rates. Therefore, the method and device developed for measuring the dynamic fracture-initiation toughness under impulsive loadings was considered suitable for such a purpose

Impact and fracture resistance of an experimental acrylic polymer with elastomer in different proportions

The purpose of this study was to evaluate the impact and fracture resistance of acrylic resins: a heat-polymerized resin, a high-impact resin and an experimental polymethyl methacrylate with elastomer in different proportions (10, 20, 40 and 60%). 120 specimens were fabricated and submitted to conventional heat-polymerization. For impact test, a Charpy-type impact tester was used. Fracture resistance was assessed with a 3-point bending test by using a mechanical testing machine. Ten specimens were used for each test. Fracture (MPa) and impact resistance values (J.m-1) were submitted to ANOVA - Bonferroni's test - 5% significance level. Materials with higher amount of elastomer had statistically significant differences regarding to impact resistance (p < 0.05). Fracture resistance was superior (p < 0.01) for high-resistance acrylic resin. The increase in elastomer concentration added to polymethyl methacrylate raised the impact resistance and decreased the fracture resistance. Processing the material by injection decreased its resistance to impact and fracture.

Residual stresses in TiN, DLC and MoS(2) coated surfaces with regard to their tribological fracture behaviour

Thin hard coatings on components and tools are used increasingly due to the rapid development in deposition techniques, tribological performance and application skills. The residual stresses in a coated surface are crucial for its tribological performance. Compressive residual stresses in PVD deposited TiN and DLC coatings were measured to be in the range of 0.03-4 GPa on steel substrate and 0.1-1.3 GPa on silicon. MoS(2) coatings had tensional stresses in the range of 0.8-1.3 on steel and 0.16 GPa compressive stresses on silicon. The fracture pattern of coatings deposited on steel substrate were analysed both in bend testing and scratch testing. A micro-scale finite element method (FEM) modelling and stress simulation of a 2 mu m TiN-coated steel surface was carried out and showed a reduction of the generated tensile buckling stresses in front of the sliding tip when compressive residual stresses of 1 GPa were included in the model. However, this reduction is not similarly observed in the scratch groove behind the tip, possibly due to sliding contact-induced stress relaxation. Scratch and bending tests allowed calculation of the fracture toughness of the three coated surfaces, based on both empirical crack pattern observations and FEM stress calculation, which resulted in highest values for TiN coating followed by MoS(2) and DLC coatings, being K(C) = 4-11, about 2, and 1-2 MPa M(1/2), respectively. Higher compressive residual stresses in the coating and higher elastic modulus of the coating correlated to increased fracture toughness of the coated surface. (C) 2009 Elsevier B.V. All rights reserved.

Three-dimensional analysis of fracture, corrosion and wear surfaces

A brief look at the history of fractography has shown a recent trend in the quantification of topographic parameters through the use of three-dimensional reconstruction techniques, which associate SEM stereoscopy and stereophotogrammetry software, allowing the calculation of the elevation measurement at numerous points of the topography due to the parallax that takes place during the tilting of the sample along the microscope eucentric plane. Several investigators have used reconstruction techniques to correlate some fractographic parameters, such as fractal dimension and fractured to projected area ratio, to the mechanical properties of materials, such as fracture toughness and tensile strength. So far, the search for a clear relationship between the fracture topography and mechanical properties has provided ambiguous results. The present work applied a surface metrology software to reconstruct three-dimensionally fracture surfaces (transgranular cleavage, intergranular and dimple fracture), corrosion pits and tribo-surfaces in order to explore the potential of this stereophotogrammetry technique. The existence of a variation in the calculated topographic parameters with the conditions of SEM image acquisition reinforces the importance of both good image acquisition and accurate calibration methods in order to validate this 3D reconstruction technique in metrological terms. Preliminary results did not indicate the existence of a clear relationship between either the true to project area ratio and CVN absorbed energy or the fractal dimension and CVN absorbed energy. It is likely that each fracture mechanism presents a proper relationship between the fractographic parameters and mechanical properties. (C) 2009 Elsevier Ltd. All rights reserved.

The effect of heat treatment on the toughness, hardness and microstructure of low carbon white cast irons

The effect of destabilisation and subcritical heat treatment on the impact toughness, hardness, and the amount and mechanical stability of retained austenite in a low carbon white cast iron have been investigated. The experimental results show that the impact energy constantly increases when the destabilisation temperature is raised from 950 degreesC to 1200 degreesC. Although the hardness decreases, the heat-treated hardness is still greater than the as-cast state. After destabilisation treatment at 1130 degreesC, tempering at 200 to 250 degreesC for 3 hours leads to the highest impact toughness, and secondary hardening was observed when tempering over 400 degreesC. The amount of retained austenite increased with the increase in the destabilisation temperature, and the treatment significantly improves the mechanical stability of the retained austenite compared with the as-cast state. Tempering below 400 degreesC does not affect the amount of retained austenite and its mechanical stability. But the amount of retained austenite is dramatically reduced when tempered above 400 degreesC. The relationship between the mechanical properties and the microstructure changes was discussed. (C) 2001 Kluwer Academic Publishers.

The work of fracture in uniaxial and biaxial oriented unplasticised polyvinylchloride pipes

In oriented unplasticised polyvinylchloride (uPVC) pipes, cracks propagate tangentially rather than through the wall as in conventional pipe. Notched impact, a modified peel test and the specific work of fracture approach have been used to measure fracture toughness of a conventionally extruded, a uniaxially oriented and a biaxially oriented uPVC pipe in different directions. The different failure mode for the oriented pipes was found to result from an order of magnitude increase in the fracture toughness for cracks propagating perpendicular to the orientation direction. Differences in the fracture toughness between the oriented pipes were also related to their molecular orientation. (C) 2002 Elsevier Science Ltd. All rights reserved.

Interlaminar fracture characterization of a carbon-epoxy composite in pure mode II

The interlaminar fracture toughness in pure mode II (GIIc) of a Carbon-Fibre Reinforced Plastic (CFRP) composite is characterized experimentally and numerically in this work, using the End-Notched Flexure (ENF) fracture characterization test. The value of GIIc was extracted by a new data reduction scheme avoiding the crack length measurement, named Compliance-Based Beam Method (CBBM). This method eliminates the crack measurement errors, which can be non-negligible, and reflect on the accuracy of the fracture energy calculations. Moreover, it accounts for the Fracture Process Zone (FPZ) effects. A numerical study using the Finite Element Method (FEM) and a triangular cohesive damage model, implemented within interface finite elements and based on the indirect use of Fracture Mechanics, was performed to evaluate the suitability of the CBBM to obtain GIIc. This was performed comparing the input values of GIIc in the numerical models with the ones resulting from the application of the CBBM to the numerical load-displacement (P-) curve. In this numerical study, the Compliance Calibration Method (CCM) was also used to extract GIIc, for comparison purposes.

Mode III interlaminar fracture of carbon/epoxy laminates using the edge crack torsion (ECT) test

The mode III interlaminar fracture of carbon/epoxy laminates was evaluated with the edge crack torsion (ECT) test. Three-dimensional finite element analyses were performed in order to select two specimen geometries and an experimental data reduction scheme. Test results showed considerable non-linearity before the maximum load point and a significant R-curve effect. These features prevented an accurate definition of the initiation point. Nevertheless, analyses of non-linearity zones showed two likely initiation points corresponding to GIIIc values between 850 and 1100 J/m2 for both specimen geometries. Although any of these values is realistic, the range is too broad, thus showing the limitations of the ECT test and the need for further research.