Interactions between iron, manganese, and the Al-Si eutectic in hypoeutectic Al-Si alloys

Sand-cast plates were used to determine the effect of iron and manganese concentrations on porosity levels in Al-9 pet Si-0.5 pet Mg alloys. Iron increased porosity levels. Manganese additions increased porosity levels in alloys with 0.1 pet Fe, but reduced porosity in alloys with 0.6 and I pet Fe. Thermal analysis and quenching were undertaken to determine the effect of iron and manganese on the solidification of the Al-Si eutectic. At high iron levels, the presence of large beta-Al5FeSi was found to reduce the number of eutectic nucleation events and increase the eutectic grain size. The preferential formation of alpha-Al15Mn3Si2 upon addition of manganese reversed these effects. It is proposed that this interaction is due to beta-Al5FeSi and the Al-Si eutectic having common nuclei. Porosity levels are proposed to be controlled by the eutectic grain size and the size of the iron-bearing intermetallic particles rather than the specific intermetallic phase that forms.

Recent advances in understanding the eutectic solidification in Al-Si foundry alloys

The formation of the Al-Si eutectic is generally the final stage of the solidification process of Al-Si foundry alloys. This means that it can be expected to have a significant impact on the feeding of a casting, and consequently the formation of casting defects, in particular porosity. Understanding and controlling the eutectic solidification process are therefore very important. This paper reviews the recent advances and unique techniques used in improving our understanding of both eutectic nucleation and growth. The role of different modifiers in controlling the eutectic solidification mechanisms is presented and the relationship between eutectic solidification mechanisms and porosity formation is outlined. This new approach to aluminium foundry alloy metallurgy is likely to form the basis for further optimisation of alloy performance and master alloys for the future.

The effect of ball milling on the melting behavior of Sn-Cu-Ag eutectic alloy

Sn-Ag-Cu (SAC) solder alloys are the best Pb free alternative for electronic industry. Since their introduction, efforts are made to improve their efficacies by tuning the processing and composition to achieve lower melting point and better wettability. Nanostructured alloys with large boundary content are known to depress the melting points of metals and alloys. In this article we explore this possibility by processing prealloyed SAC alloys close to SAC305 composition (Sn-3wt%Ag-0.5wt%Cu) by mechanical milling which results in the formation of nanostructured alloys. Pulverisette ball mill (P7) and Vibratory ball mills are used to carry out the milling of the powders at room temperature and at lower temperatures (-104 A degrees C), respectively. We report a relatively smaller depression of melting point ranging up to 5 A degrees C with respect to original alloys. The minimum grain sizes achieved and the depression of melting point are similar for both room temperature and low-temperature processed samples. An attempt has been made to rationalize the observations in terms of the basic processes occurring during the milling.

The nature of non-equilibrium solidification of undercooled Agsingle bondCu alloys in contact with primary copper dendrites

Liquids of silver-copper alloys with near eutectic compositions embedded in a copper matrix were undercooled. The structural and microstructural investigations of these alloys solidified from undercooled temperature indicated the absence of both the eutectic reaction and diffusionless transformation below the equal free energy curve (T0). Instead the liquid maintained local equilibrium with the copper dendrites continuously until it intersected the extended solidus of the silver rich solid solution.