Avaliação por microdureza Vickers da profundidade de polimerização de cimentos resinosos na cimentação de pinos de fibra de vidro empregando diferentes fontes de luz

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo da infiltração marginal em restaurações de resinas compostas para dentes posteriores: efeito de material, preparo cavitário e condicionamento do esmalte a nível cervical

Pós-graduação em Odontologia Restauradora - ICT

Comparative study on direct and indirect bracket bonding techniques regarding time length and bracket detachment

OBJECTIVE: The aim of this study was to assess the time spent for direct (DBB - direct bracket bonding) and indirect (IBB - indirect bracket bonding) bracket bonding techniques. The time length of laboratorial (IBB) and clinical steps (DBB and IBB) as well as the prevalence of loose bracket after a 24-week follow-up were evaluated. METHODS: Seventeen patients (7 men and 10 women) with a mean age of 21 years, requiring orthodontic treatment were selected for this study. A total of 304 brackets were used (151 DBB and 153 IBB). The same bracket type and bonding material were used in both groups. Data were submitted to statistical analysis by Wilcoxon non-parametric test at 5% level of significance. RESULTS: Considering the total time length, the IBB technique was more time-consuming than the DBB (p < 0.001). However, considering only the clinical phase, the IBB took less time than the DBB (p < 0.001). There was no significant difference (p = 0.910) for the time spent during laboratorial positioning of the brackets and clinical session for IBB in comparison to the clinical procedure for DBB. Additionally, no difference was found as for the prevalence of loose bracket between both groups. CONCLUSION: the IBB can be suggested as a valid clinical procedure since the clinical session was faster and the total time spent for laboratorial positioning of the brackets and clinical procedure was similar to that of DBB. In addition, both approaches resulted in similar frequency of loose bracket.

On the reactivity of Mo species for methane partial oxidation on Mo/HMCM-22 catalysts

By characterizing fresh and used Mo/HMCM-22 catalysts with ICP-AES, XRD, NH3-TPD technique, UV - Vis DRS and UV Raman spectroscopy, the reactivity of Mo species for methane partial oxidation into formaldehyde were directly studied with a new point of view. By comparing the fresh and used catalysts, it was found that the tetrahedral Mo species bonding chemically to the support surface were practically unchanged after the reaction, while the polymolybdate octahedral Mo species, which had a rather weak interaction with the MCM-22 zeolite, leached out during the reaction, especially when the Mo loading was high. Correspondingly, it was found from the time-on-stream reaction data that the HCHO yield remained unchanged, while COx decreased with the reaction time during the reaction. By combining the characterization results and the reaction data, it can be drawn that the isolated tetrahedral molybdenum oxo-species (T-d) is responsible for HCHO formation, while the octahedral polyoxomolybdate species (O-h) will lead to the total oxidation of methane.

Poly(epsilon-caprolactone)/poly(ethylene oxide) diblock copolymer .1. Isothermal crystallization and melting behavior

The isothermal crystallization and melting behavior of the poly(epsilon-caprolactone) (PCL)/poly(ethylene oxide)(PEO) diblock copolymer has been studied by WAXD, SAXS, and DSC methods. Only the PCL block is crystallizable; the PEO block of weight fraction 20% cannot crystallize, although its corresponding homopolymer has strong crystallizability. The long period, amorphous layer, and crystalline lamella of the PCL/PEO block copolymer all increase with the rise in the crystallization temperature, and the thickness of the amorphous layer is much larger than that of crystalline lamella due to the existence of the PEO block in the amorphous region. The isothermal crystallization of the PCL/PEO block copolymer is investigated by using the theory of Turnbull and Fischer. It is found that the amorphous PEO block has a great influence on the nucleation of PCL block crystallization, and the extent of this influence depends on crystallization conditions, especially temperature. The outstanding characteristics are the phenomenon of the double melting peaks in the melting process of the PCL/PEO block copolymer after isothermal crystallization at different temperatures and the transformation of melting peaks from double peaks to a single peak with variations in the crystallization condition. They are related mainly to the existence of the PEO block bonding chemically with the PCL block. In summing up results of investigations into the crystallization and melting behavior of the PCL/PEO block copolymer, it is interesting to notice that when the PCL/PEO block copolymer crystallizes at three different crystallization temperatures, i.e., below 0 degrees C, between 0 and 35 degrees C, and above 35 degrees C, the variation of peak melting temperature is similar to that of overall crystallization rates in the process of isothermal crystallization. The results can be elucidated by the effect of the PEO block on the crystallization of the PCL block, especially its nucleation. (C) 1996 John Wiley & Sons, Inc.

Quantification of all-ceramic crown margin surface profile from try-in to 1-week post-cementation

To use profilometry to assess the margin surface profile of all-ceramic crowns (ACC’s) at try-in and 1-week after cementation with dual-cured resin (DC, RelyX ARC, 3 M ESPE, St. Paul, MN, USA), self-adhesive dual-cured resin (SADC, RelyX Unicem, 3 M ESPE), light-cured resin (LC, RelyX Veneer, 3 M ESPE) or chemically cured resin-modified glass ionomer (RMGI, RelyX Luting Plus, 3 M ESPE) luting cement. Methods: Forty, sound, extracted, human, premolar teeth underwent a standardised preparation for ACC’s. IPS Empress (Ivoclar-Vivadent, Liechtenstein) crowns of standard dimensions were fabricated and 10 luted with each cement and stored in water for 7 days. Three groups of serial profiles were taken, the first of the tooth preparation, the second of the crown margins at try-in and lastly of the crown margins after cementation and 7 days water storage. Results: There were no significant differences in the crown margin surface profile between the four cement groups at try-in. The change in crown margin position between try-in and post-cementation was significantly greater for DC than for LC and RMGI. SADC was not significantly different to the other cements. There were no significant differences in the crown margin extensions between the four cement groups, however most of the IPS Empress ACC’s in this study were underextended but this was not statistically significant. Conclusions: IPS Empress ACC’s seated more fully with LC and RMGI than with DC cement

Multidisciplinary approach for the treatment of a complicated crown-root fracture in a young patient: A case report

Crown-root fractures in permanent teeth cause esthetic and functional problems. This paper reports the case of a complicated crown-root fracture in the maxillary right central inc sor of a young patient who was treated with a multidisciplinary approach in two phases. A modified Widman flap, root canal therapy, glass fiber post cementation, and adhesive tooth fragment reattachment were performed shortly after an accident. Satisfactory esthetic and functional outcomes were obtained. However, the patient did not attend follow-up visits and returned after 7 years. During this second phase, the clinical and radiographic examination showed stability and adaptation of the fragment and good periodontal health conditions, but crown darkening and a radiolucent image associated with the root apex of the fractured tooth were also observed. The periapical lesion was surgically removed by apicoectomy, and the esthetics were recovered with a direct composite res n veneer on the traumatized tooth. (Quintessence Int 2011;42:729-735)

BOND STRENGTH DURABILITY of SELF-ETCHING ADHESIVES and RESIN CEMENTS TO DENTIN

Objectives: To evaluate the microtensile bond strength (mu TBS) of one-(Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). Material and Methods: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n = 10). The restored teeth were stored in distilled water at 37 C for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm(2) cross-sectional area, which were subjected to mu TBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The mu TBS data in MPa were subjected to three-way analysis of variance and Tukey's test (alpha = 0.05). Results: The interaction effect for all three factors was statistically significant (three-way ANOVA, p < 0.001). All eight experimental means (MPa) were compared by the Tukey's test (p < 0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4 +/- 7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4 +/- 11.6); Xeno III/C&B/24 h (40.3 +/- 12.9); Xeno III/Variolink II/24 h (25.8 +/- 10.5); Tyrian-One Step Plus / C&B/90 d (22.1 +/- 12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2 +/- 14.2); Xeno III/C&B/90 d (27.0 +/- 13.5); Xeno III/Variolink II/90 d (33.0 +/- 8.9). Conclusions: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.

Comparative in vitro study of the shear bond strength of brackets bonded with restorative and orthodontic resins

The aim of this study was to evaluate the shear bond strength of brackets bonded with different restorative systems and compare it with that afforded by an established orthodontic bonding system. Seventy human bicuspids were used, divided into five different groups with 14 teeth each. Whereas a specific orthodontic bonding resin (Transbond (TM) XT) was used in the control group, the restorative systems Charisma, Tetric Ceram, TPH Spectrum and Z100 were used in the other four groups. Seven days after bonding the brackets to the samples, shear forces were applied under pressure in a universal testing machine. The data collected was evaluated using the ANOVA test and, when a difference was identified, the Tukey test was applied. A 5% level of significance was adopted. The mean results of the shear bond strength tests were as follows: Group 1 (Charisma), 14.98 MPa; Group 2 (Tetric Ceram), 15.16 MPa; Group 3 (TPH), 17.70 MPa; Group 4 (Z100), 13.91 MPa; and Group 5 or control group (Transbond (TM) XT), 17.15 MPa. No statistically significant difference was found among the groups. It was concluded that all tested resins have sufficient bond strength to be recommended for bonding orthodontic brackets.

Influência de diferentes agentes de fixação na resistência de união, por tração, de ligas metálicas fixadas à dentina.

They were casted pieces using three kinds of alloy (Ni-Cr, Ag-Sn and Cu-Al) with circular and smooth surface. They were cemented to human teeth, on occlusal surface, grounded at dentin level, through three different materials kind (zinc polycarboxylate cement, glassionomer cement and composite). After 24 hours storing, the samples were subjected to the tensile test. The results showed that the samples cemented with composite and the casts made with Ag-Sn alloy had higher bond strength.

Estudo comaprativo da resistência da união esmalt/resina/metal. Efeito de resinas de fixação, artifícios retentivos e ligas metálicas.

The purpose of this study was to compare the enamel/resin/metal bond tensile strength by using human canines, in which castings were bonded. These castings were obtained by Co-Cr or Ni-Cr alloys and showed four types of mechanisms of retention: 50 micrograms aluminum oxide abrasive, electrochemical etch, acrylic beads metal mesh. The castings were bonded utilizing Comspan Opaque and Panavia Ex. The specimens were subjected to tensile forces after 24 hours in an Instron machine. The castings subjected to 50 micrograms aluminum oxide abrasive and bonded utilizing Panavia EX showed the biggest bond tensile strength.

Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.

Water sorption, solubility, and bond strength of two autopolymerizing acrylic resins and one heat-polymerizing acrylic resin.

STATEMENT OF PROBLEM: Because water sorption of autopolymerizing acrylic reline resins is accompanied by volumetric change, it is a physical property of importance. As residual monomer leaches into the oral fluids and causes tissue irritation, low solubility of these resins is desired. Another requirement is a satisfactory bond between the autopolymerizing acrylic resins and the denture base acrylic resin. PURPOSE: This study compared the water sorption, solubility, and the transverse bond strength of 2 autopolymerizing acrylic resins (Duraliner II and Kooliner) and 1 heat-polymerizing acrylic resin (Lucitone 550). MATERIAL AND METHODS: The water sorption and solubility test was performed as per International Standards Organization Specification No. 1567 for denture base polymers. Bond strengths between the autopolymerizing acrylic resins and the heat-polymerizing acrylic resin were determine with a 3-point loading test made on specimens immersed in distilled water at 37 degrees C for 50 hours and for 30 days. Visual inspection determined whether failures were adhesive or cohesive. RESULTS: Duraliner II acrylic resin showed significantly lower water sorption than Kooliner and Lucitone 550 acrylic resins. No difference was noted in the solubility of all materials. Kooliner acrylic resin demonstrated significantly lower transverse bond strength to denture base acrylic resin and failed adhesively. The failures seen with Duraliner II acrylic resin were primarily cohesive in nature. CONCLUSIONS: Autopolymerizing acrylic reline resins met water sorption and solubility requirements. However, Kooliner acrylic resin demonstrated significantly lower bond strength to denture base acrylic resin.

Microleakage in primary teeth restored by conventional or bonded amalgam technique.

The aim of this in vitro study was to evaluate marginal leakage in class V restorations in primary teeth restored with amalgam, using three different techniques. Thirty maxillary anterior primary teeth, clinically sound and naturally exfoliated, were used. In group 1 (n = 10), two thin layers of a copal varnish (Cavitine) were applied. In group 2 (n = 10), Scotchbond Multi-Purpose Plus, a dual adhesive system, was used according to manufacturer instructions. In group 3 (n = 10), One-Step adhesive system in combination with a low-viscosity resin (Resinomer) were used according to manufacturer instructions. All samples were restored with a high-copper dental amalgam alloy (GS 80, SDI). After restoration, the samples were stored in normal saline at 37 degrees C for 72 h. The specimens were polished, thermocycled (500 cycles, 5 degrees and 55 degrees C, 30-s dwell time) and impermeabilized with fingernail polish to within 1.0 mm of the restoration margins. The teeth were then placed in 0.5% methylene blue for 4 h. Finally, the samples were sectioned and evaluated for marginal leakage. The Kruskal-Wallis test showed that the filled adhesive resin (group 3) had the least microleakage. There was no significant difference between groups 1 and 2.

Effect of 2% chlorhexidine on microtensile bond strength of composite to dentin

Purpose: To evaluate the effect of 2% chlorhexidine on the microtensile bond strength of composite resin to dentin treated with three dentin bonding systems. Materials and Methods: Flat dentinal surfaces were prepared in 24 extracted human third molars. Teeth were randomly divided into 8 distinct experimental groups according to the adhesive applied (Prime & Bond NT, Single Bond and Clearfil SE Bond), the application (yes/no) of chlorhexidine, and the time point at which it was applied (before or after acid etching the dentin). Composite resin blocks were built up over treated surfaces, and teeth were then stored in water at 37°C for 24 h. Samples were thermocycled, stored under the same conditions, and then vertically sectioned, thus obtaining specimens with 1.0 ± 0.1 mm2 cross-sectional area. Specimens were stressed in tension at 0.5 mm/min crosshead speed. Bond strength results were evaluated using a one-way ANOVA (p < 0.05). The modes of failures were verified using optical microscopy. Dentin disks were obtained from 3 additional teeth treated in the same manner for observation under SEM. The most representative samples of fractured specimens were also observed under SEM. Results: No statistically significant differences of bond strength values were found between any groups. Failures occurred mainly within the bond; exclusively adhesive fractures (adhesive-dentin) were not observed. Conclusion: The 2% chlorhexidine solution, applied before or after acid etching of the dentin, did not interfere with the microtensile bond strength of composite resin to the dentin treated with Prime & Bond NT, Single Bond, or Clearfil SE Bond bonding systems.