A Systematic Review of the Clinical Performance of Tooth-Retained and Implant-Retained Double Crown Prostheses with a Follow-Up of ≥3 Years

Purpose: The objective of this review was to systematically screen the literature for data related to the survival and complication rates observed with dental or implant double crown abutments and removable prostheses under functional loading for at least 3 years. Materials and Methods: A systematic review of the dental literature from January 1966 to December 2009 was performed in electronic databases (PubMed and Embase) as well as by an extensive hand search to investigate the clinical outcomes of double crown reconstructions. Results: From the total of 2412 titles retrieved from the search, 65 were selected for full-text review. Subsequently, 17 papers were included for data extraction. An estimation of the cumulative survival and complication rates was not feasible due to the lack of detailed information. Tooth survival rates for telescopic abutment teeth ranged from 82.5% to 96.5% after an observation period of 3.4 to 6 years, and for tooth-supported double crown retained dentures from 66.7% to 98.6% after an observation period of 6 to 10 years. The survival rates of implants were between 97.9% and 100% and for telescopic-retained removable dental prostheses with two mandibular implants, 100% after 3.0 and 10.4 years. The major biological complications affecting the tooth abutments were gingival inflammation, periodontal disease, and caries. The most frequent technical complications were loss of cementation and loss of facings. Conclusions: The main findings of this review are: (I) double crown tooth abutments and dentures demonstrated a wide range of survival rates. (II) Implant-supported mandibular overdentures demonstrated a favorable long-term prognosis. (III) A greater need for prosthetic maintenance is required for both tooth-supported and implant-supported reconstructions. (IV) Future areas of research would involve designing appropriate longitudinal studies for comparisons of survival and complication rates of different reconstruction designs.

Long-term outcomes of dental implants with a titanium plasma-sprayed surface: a 20-year prospective case series study in partially edentulous patients

BACKGROUND Long-term studies of ≥10 years are important milestones to get a better understanding of potential factors causing implant failures or complications. PURPOSE The present study investigated the long-term outcomes of titanium dental implants with a rough, microporous surface (titanium plasma sprayed [TPS]) and the associated biologic and technical complications in partially edentulous patients with fixed dental prostheses over a 20-year follow-up period. MATERIALS AND METHODS Sixty-seven patients, who received 95 implants in the 1980s, were examined with well-established clinical and radiographic parameters. Based on these findings, each implant was classified as either successful, surviving, or failed. RESULTS Ten implants in nine patients were lost during the observation period, resulting in an implant survival rate of 89.5%. Radiographically, 92% of the implants exhibited crestal bone loss below 1 mm between the 1- and 20-year follow-up examinations. Only 8% yielded peri-implant bone loss of >1 mm and none exhibited severe bone loss of more than 1.8 mm. During the observation period, 19 implants (20%) experienced a biologic complication with suppuration. Of these 19 implants, 13 implants (13.7%) had been treated and were successfully maintained over the 20-year follow-up period. Therefore, the 20-year implant success rate was 75.8 or 89.5% depending on the different success criteria. Technical complications were observed in 32%. CONCLUSION The present study is the first to report satisfactory success rates after 20 years of function of dental implants with a TPS surface in partially edentulous patients.

Technical complications and failures of zirconia-based prostheses supported by implants followed up to 7 years: a case series.

PURPOSE To evaluate technical complications and failures of zirconia-based fixed prostheses supported by implants. MATERIALS AND METHODS Consecutive patients received zirconia-based single crowns (SCs) and fixed dental prostheses (FDPs) on implants in a private clinical setting between 2005 and 2010. One dentist performed all surgical and prosthetic procedures, and one master technician performed and coordinated all laboratory procedures. One-piece computer-aided design/ computer-assisted manufacture technology was used to fabricate abutments and frameworks, which were directly connected at the implant level, where possible. All patients were involved in a recall maintenance program and were finally reviewed in 2012. Data on framework fractures, chipping of veneering ceramics, and other technical complications were recorded. The primary endpoint was failure of the prostheses, ie, the need for a complete remake. A life table analysis was calculated. RESULTS A total of 289 implants supported 193 zirconia-based prostheses (120 SCs and 73 FDPs) in 127 patients (51 men, 76 women; average age: 62.5 ± 13.4 years) who were reviewed in 2012. Twenty-five (13%) prostheses were cemented on 44 zirconia abutments and 168 (87%) prostheses were screw-retained directly at the implant level. Fracture of 3 frameworks (1 SC, 2 FDPs) was recorded, and significant chipping resulted in the remake of 3 prostheses (1 SC, 2 FDPs). The 7-year cumulative survival rate was 96.4% ± 1.99%. Minor complications comprised 5 loose screws (these were retightened), small chips associated with 3 prostheses (these were polished), and dislodgement of 3 prostheses (these were recemented). Overall, 176 prostheses remained free of technical problems. CONCLUSIONS Zirconia-based prostheses screwed directly to implants are clinically successful in the short and medium term.

Zirconia-Based Screw-Retained Prostheses Supported by Implants: A Retrospective Study on Technical Complications and Failures

BACKGROUND Little information is yet available on zirconia-based prostheses supported by implants. PURPOSE To evaluate technical problems and failures of implant-supported zirconia-based prostheses with exclusive screw-retention. MATERIAL AND METHODS Consecutive patients received screw-retained zirconia-based prostheses supported by implants and were followed over a time period of 5 years. The implant placement and prosthetic rehabilitation were performed in one clinical setting, and all patients participated in the maintenance program. The treatment comprised single crowns (SCs) and fixed dental prostheses (FDPs) of three to 12 units. Screw-retention of the CAD/CAM-fabricated SCs and FDPs was performed with direct connection at the implant level. The primary outcome was the complete failure of zirconia-based prostheses; outcome measures were fracture of the framework or extensive chipping resulting in the need for refabrication. A life table analysis was performed, the cumulative survival rate (CSR) calculated, and a Kaplan-Meier curve drawn. RESULTS Two hundred and ninety-four implants supported 156 zirconia-based prostheses in 95 patients (52 men, 43 women, average age 59.1 ± 11.7 years). Sixty-five SCs and 91 FDPs were identified, comprising a total of 441 units. Fractures of the zirconia framework and extensive chipping resulted in refabrication of nine prostheses. Nearly all the prostheses (94.2%) remained in situ during the observation period. The 5-year CSR was 90.5%, and 41 prostheses (14 SCs, 27 FDPs) comprising 113 units survived for an observation time of more than 5 years. Six SCs exhibited screw loosening, and polishing of minor chipping was required for five prostheses. CONCLUSIONS This study shows that zirconia-based implant-supported fixed prostheses exhibit satisfactory treatment outcomes and that screw-retention directly at the implant level is feasible.

Autopercepção da saúde bucal em idosos e fatores associados em Campinas, SP, 2008-2009

OBJETIVO: Descrever a autopercepção de saúde bucal em idosos e analisar fatores sociodemográficos e clínicos associados. MÉTODOS: Estudo transversal com 876 participantes em amostra representativa de idosos (65 anos ou mais) de Campinas, SP, em 2008-2009. Os exames odontológicos seguiram critérios padronizados pela Organização Mundial da Saúde para levantamentos epidemiológicos de saúde bucal. A autopercepção da saúde bucal foi avaliada pelo índice Geriatric Oral Health Assessment Index (GOHAI). Os indivíduos foram classificados segundo características sociodemográficas, odontológicas e prevalência de fragilidade biológica. O estudo de associações utilizou análise de regressão de Poisson; a análise considerou os pesos amostrais e a estrutura complexa da amostra por conglomerados. RESULTADOS: A média de idade dos indivíduos foi de 72,8 anos; 70,1% eram mulheres. A proporção de indivíduos com mais de 20 dentes presentes foi 17,2%; 38,2% usavam prótese dentária total em ambos os arcos; 8,5% necessitavam desse recurso em ao menos um arco dentário. Em média, o índice GOHAI foi elevado: 33,9 (máximo possível 36,0). Manter 20 dentes ou mais, usar prótese total nos dois arcos, não necessitar desse tratamento, não apresentar alterações de mucosa oral e não apresentar fragilidade biológica foram os fatores significantemente associados com melhor autopercepção de saúde bucal (p < 0,05). CONCLUSÕES: A avaliação de autopercepção em saúde bucal permitiu identificar os principais fatores associados a esse desfecho. Esse instrumento pode contribuir para o planejamento de serviços odontológicos, orientando estratégias de promoção em saúde voltadas à melhora da qualidade de vida das pessoas desse grupo etário.

Inflammatory Papillary Hyperplasia of the Palate: Quantitative Analysis of Candida albicans and its Negative Correlation with Microscopic and Demographic Aspects

Inflammatory papillary hyperplasia of the palate (IPHP) is a tissue-reactive overgrowth characterized by hyperemic mucosa with nodular or papillary appearance in the palate. The exact pathogenesis is still unclear. In this study, the presence of Candida albicans in the epithelial lining was evaluated using the indirect immunofluorescence staining technique. Strongly stained C albicans was observed only in the lesions of the IPHP group. Therefore, the detection of C albicans in almost all samples from IPHP tissue enabled a suggestion as to the microbial etiology of the disease, since the use of dental prostheses was reported. Int J Prosthodont 2011;24:235-237

Reliability and Failure Modes of Implant-Supported Y-TZP and MCR Three-Unit Bridges

Purpose: Chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (yttria-tetragonal zirconia polycrystals [Y-TZP]) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus palladium-silver alloy (PdAg) three-unit bridges. Materials and Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n = 21 each), were fabricated, veneered, cemented (n = 3 each), and Hertzian contact-tested to obtain ultimate failure load. In each framework group, 18 specimens were distributed across three step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (two-sided at 90% confidence intervals) for a ""mission"" of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft, Tucson, AZ, USA). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusions: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300 N. Failure modes differed between materials.

Fatigue life and failure modes of crowns systems with a modified framework design

Objectives: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. Methods: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n = 10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n = 10 each). Fatigue loading was delivered with a spherical steel indenter (3.18 mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300 N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. Results: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. Conclusions: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system. (C) 2010 Elsevier Ltd. All rights reserved.

Failure modes of Y-TZP crowns at different cusp inclines

Objectives To compare the reliability of the disto-facial (DF) and mesio-lingual (ML) cusps of an anatomically correct zirconia (Y-TZP) crown system The research hypotheses tested were (1) fatigue reliability and failure mode are similar for the ML and DF cusps, (2) failure mode of one cusp does not affect the failure of the other Methods The average dimensions of a mandibular first molar crown were imported into CAD software, a tooth preparation was modelled by 1 5 mm marginal high reduction of proximal walls and occlusal surface by 2 0 mm The CAD-based tooth preparation was milled and used as a die to fabricate crowns (n = 14) with porcelain veneer on a 0 5 mm Y-TZP core. Crowns were cemented on composite reproductions of the tooth preparation The crowns were step-stress mouth motion fatigued with sliding (0 7 mm) a tungsten-carbide indenter of 6 25 mm diameter down on the inclines of either the DF or ML cusps Use level probability Weibull curve with use stress of 200 N and the reliability for completion of a mission of 50,000 cycles at 200 N load were calculated Results Reliability for a 200 N at 50,000 cycles mission was not different between tested cusps SEM imaging showed large cohesive failures within the veneer for the ML and smaller for the DF Fractures originated from the contact area regardless of the cusp loaded Conclusion No significant difference on fatigue reliability was observed between the DF compared to the ML cusp Fracture of one cusp did not affect the other (c) 2010 Elsevier Ltd All rights reserved

Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.

Thermal/mechanical simulation and laboratory fatigue testing of an alternative yttria tetragonal zirconia polycrystal core-veneer all-ceramic layered crown design

This study evaluated the stress levels at the core layer and the veneer layer of zirconia crowns (comprising an alternative core design vs. a standard core design) under mechanical/thermal simulation, and subjected simulated models to laboratory mouth-motion fatigue. The dimensions of a mandibular first molar were imported into computer-aided design (CAD) software and a tooth preparation was modeled. A crown was designed using the space between the original tooth and the prepared tooth. The alternative core presented an additional lingual shoulder that lowered the veneer bulk of the cusps. Finite element analyses evaluated the residual maximum principal stresses fields at the core and veneer of both designs under loading and when cooled from 900 degrees C to 25 degrees C. Crowns were fabricated and mouth-motion fatigued, generating master Weibull curves and reliability data. Thermal modeling showed low residual stress fields throughout the bulk of the cusps for both groups. Mechanical simulation depicted a shift in stress levels to the core of the alternative design compared with the standard design. Significantly higher reliability was found for the alternative core. Regardless of the alternative configuration, thermal and mechanical computer simulations showed stress in the alternative core design comparable and higher to that of the standard configuration, respectively. Such a mechanical scenario probably led to the higher reliability of the alternative design under fatigue.

Reliability of Metalloceramic and Zirconia-based Ceramic Crowns

Despite the increasing utilization of all-ceramic crown systems, their mechanical performance relative to that of metal ceramic restorations (MCR) has yet to be determined. This investigation tested the hypothesis that MCR present higher reliability over two Y-TZP all-ceramic crown systems under mouth-motion fatigue conditions. A CAD-based tooth preparation with the average dimensions of a mandibular first molar was used as a master die to fabricate all restorations. One 0.5-mm Pd-Ag and two Y-TZP system cores were veneered with 1.5 mm porcelain. Crowns were cemented onto aged (60 days in water) composite (Z100, 3M/ESPE) reproductions of the die. Mouth-motion fatigue was performed, and use level probability Weibull curves were determined. Failure modes of all systems included chipping or fracture of the porcelain veneer initiating at the indentation site. Fatigue was an acceleration factor for all-ceramic systems, but not for the MCR system. The latter presented significantly higher reliability under mouth-motion cyclic mechanical testing.

Testing the retention of attachments for implant overdentures - validation of an original force measurement system

P>The aim of this study was to validate an original portable device to measure attachment retention of implant overdentures both in the lab and in clinical settings. The device was built with a digital force measurement gauge (Imada) secured to a vertical wheel stand associated with a customized support to hold and position the denture in adjustable angulations. Sixteen matrix and patrix cylindrical stud attachments (Locator (R)) were randomly assigned as in vitro test specimens. Attachment abutments were secured in an implant analogue hung to the digital force gauge or to the load cell of a traction machine used as the gold standard (Instron Universal Testing Machine). Matrices were secured in a denture duplicate attached to the customized support, permitting reproducibility of their position on both pulling devices. Attachment retention in the axial direction was evaluated by measuring maximum dislodging force or peak load during five consecutive linear dislodgments of each attachment on both devices. After a wear simulation, retention was measured again at several time periods. The peak load measurements with the customized Imada device were similar to those obtained with the gold standard Instron machine. These findings suggest that the proposed portable device can provide accurate information on the retentive properties of attachment systems for removable dental prostheses.

Estudo da zircônia reforçado com alumina

Ceramics materials have good properties including chemical stability, high hardness and wear resistance. Moreover, due to its fragility, can suffer failure under relatively low levels of tension. Actually zirconia is the material of choice in metal free dental prostheses used in dentistry due its inertia in physiological environment, good bending strength, hardness and fracture toughness. The alumina and mixed tungsten and titanium carbides additions, acting as reinforcement elements in the zirconia matrix, have as their main objective the improvement of mechanical properties of this material. In this work, samples of zirconia, zirconia with 30% wt of alumina and zirconia with 30% wt mixed carbides were analyzed. The samples were sintered by uniaxial hot pressing on 30 MPa pressure, for 1 hour in an argon atmosphere. They were physically characterized by porosity and density measurements, and mechanically by 3-points bending strength and Vickers microhardness. The X-ray diffraction was used for the phase identifications and microstructure was examined by scanning electron microscopy (SEM). The addition of mixed carbides as reinforcement elements in zirconia matrix provides improvements in all properties analyzed in this work. The alumina addition has dropped the zirconia strength, although it caused improvement in other properties

Species diversity of yeast in oral colonization of insulin-treated diabetes mellitus patients

The aim of this study was to investigate oral yeast colonization, antifungal susceptibility and strain diversity in insulin-dependent diabetes mellitus patients (175), as well as to evaluate the influence of dental prostheses. Oral rinse samples were cultured on selective media, in order to isolate, count and identify the yeasts recovered. More than half of the diabetic subjects (53%) carried significant amounts of Candida cells in the buccal cavity and these organisms were recovered at higher densities in diabetics wearing dentures. A total of 93 yeast strains were isolated from these patients, including: Candida spp. (n = 89); Pichia (n = 02); Trichosporon (n = 1), and Geotrichum (n = 1). C. albicans represented 56% of these strains, non-albicans Candida 39.8%, and other genera of yeast 4.3%. C. albicans was prevalent, followed by C. parapsilosis, C. tropicalis, C. glabrata, C. krusei, C. rugosa and C. guilliermondii. Agar disk-diffusion tests of the susceptibility of non-albicans Candida and other genera of yeast to fluconazole showed resistance in 21.9%, mainly in C. rugosa (100%), C. glabrata (57%) and C. krusei (50%). Local oral factors, such as the presence of dentures, in association with diabetes, seemed to have the effect of increasing the amount and variety of Candida species in the oral cavities, mainly those with lower drug susceptibilities.