The effects of manganese content and mould size on abrasion and slurry erosion behaviour of chromium-manganese iron systems investigated by positron lifetime spectroscopy

Abrasion and slurry erosion behaviour of chromium-manganese iron samples with chromium (Cr) in the range similar to 16-19% and manganese (Mn) at 5 and 10% levels have been characterized for hardness followed by microstructural examination using optical and scanning electron microscopy. Positron lifetime studies have been conducted to understand the defects/microporosity influence on the microstructure. The samples were heat treated and characterized to understand the structural transformations in the matrix. The data reveals that hardness decreased with increase in Mn content from 5 to 10% in the first instance and then increase in the section size in the other case, irrespective of the sample conditions. The abrasion and slurry erosion losses show increase with increase in the section size as well as with increase in Mn content. The positron results show that as hardness increases from as-cast to heat treated sample, the positron trapping rate and hence defect concentration showed opposite trend as expected. So a good correlation between defects concentration and the hardness has been observed. These findings also corroborate well with the microstructural features obtained from optical and scanning electron microscopy. (C) 2009 Elsevier B. V. All rights reserved.

Sticking and erosion at carbon-containing plasma-facing materials in fusion reactors

Controlled nuclear fusion is one of the most promising sources of energy for the future. Before this goal can be achieved, one must be able to control the enormous energy densities which are present in the core plasma in a fusion reactor. In order to be able to predict the evolution and thereby the lifetime of different plasma facing materials under reactor-relevant conditions, the interaction of atoms and molecules with plasma first wall surfaces have to be studied in detail. In this thesis, the fundamental sticking and erosion processes of carbon-based materials, the nature of hydrocarbon species released from plasma-facing surfaces, and the evolution of the components under cumulative bombardment by atoms and molecules have been investigated by means of molecular dynamics simulations using both analytic potentials and a semi-empirical tight-binding method. The sticking cross-section of CH3 radicals at unsaturated carbon sites at diamond (111) surfaces is observed to decrease with increasing angle of incidence, a dependence which can be described by a simple geometrical model. The simulations furthermore show the sticking cross-section of CH3 radicals to be strongly dependent on the local neighborhood of the unsaturated carbon site. The erosion of amorphous hydrogenated carbon surfaces by helium, neon, and argon ions in combination with hydrogen at energies ranging from 2 to 10 eV is studied using both non-cumulative and cumulative bombardment simulations. The results show no significant differences between sputtering yields obtained from bombardment simulations with different noble gas ions. The final simulation cells from the 5 and 10 eV ion bombardment simulations, however, show marked differences in surface morphology. In further simulations the behavior of amorphous hydrogenated carbon surfaces under bombardment with D^+, D^+2, and D^+3 ions in the energy range from 2 to 30 eV has been investigated. The total chemical sputtering yields indicate that molecular projectiles lead to larger sputtering yields than atomic projectiles. Finally, the effect of hydrogen ion bombardment of both crystalline and amorphous tungsten carbide surfaces is studied. Prolonged bombardment is found to lead to the formation of an amorphous tungsten carbide layer, regardless of the initial structure of the sample. In agreement with experiment, preferential sputtering of carbon is observed in both the cumulative and non-cumulative simulations

The effect of viscosity and surface tension on the Taylor instability of the surface of a cavitation bubble*

This paper is devoted to a consideration of the following problem: A spherical mass of fluid of density varrho1, viscosity μ1 and external radius R is surrounded by a fluid of density varrho2 and viscosity μ2.The fluids are immiscible and incompressible. The interface is accelerated radially by g1: to study the effect of viscosity and surface tension on the stability of the interface. By analyzing the problem in spherical harmonics the mathematical problem is reduced to one of solution of the characteristic determinant equation. The particular case of a cavity bubble, where the viscosity μ1 of the fluid inside the bubble is negligible in comparison with the viscosity μ2 of the fluid outside the bubble, is considered in some detail. It is shown that viscosity has a stabilizing role on the interface; and when g1 > T(n − 1) (n + 2)/R2(varrho2 − varrho1) the stabilizing role of both viscosity and surface tension is more pronounced than would result when either of them is taken individually.

Effect of soil tillage on erosion and nutrient transport in plough layer runoff

Yhteenveto: Viljelymenetelmien vaikutus eroosioon ja ravinteiden huuhtoutumiseen

Some observations of tip-vortex cavitation

Cavitation has been observed in the trailing vortex system of an elliptic planform hydrofoil. A complex dependence on Reynolds number and gas content is noted at inception. Some of the observations can be related to tension effects associated with the lack of sufficiently large-sized nuclei. Inception measurements are compared with estimates of pressure in the vortex obtained from LDV measurements of velocity within the vortex. It is concluded that a complete correlation is not possible without knowledge of the fluctuating levels of pressure in tip-vortex flows. When cavitation is fully developed, the observed tip-vortex trajectory shows a surprising lack of dependence on any of the physical parameters varied, such as angle of attack, Reynolds number, cavitation number, and dissolved gas content.

Chromium-manganese iron alloy system design cast in metal and sand moulds for erosion resistance: a positron lifetime study

Erosion characteristics of high chromium (Cr, 16-19%) alloy cast iron with 5% and 10% manganese (Mn) prepared in metal and sand moulds through induction melting are investigated using jet erosion test setup in both as-cast and heat-treated conditions. The samples were characterised for hardness and microstructural properties. A new and novel non-destructive evaluation technique namely positron lifetime spectroscopy has also been used for the first time to characterise the microstructure of the material in terms of defects and their concentration. We found that the hardness decreases irrespective of the sample condition when the mould type is changed from metal to sand, On the other hand, the erosion volume loss shows an increasing trend. Since the macroscopic properties have a bearing on the microstructure, good credence is obtained from the microstructural features as seen from light and scanning electron micrographs. Faster cooling in the metal mould yielded fine carbide precipitation on the surface. The defect size and their concentration derived from positron method are higher for sand mould compared to metal mould. Lower erosion loss corresponds to smaller size defects in metal mould are the results of quicker heat transfer in the metal mould compared to the sand mould. Heat treatment effects are clearly seen as the reduced concentration of defects and spherodisation of carbides points to this. The erosion loss with respect to the defects size and concentration correlate very well.

Studies on Cavitation Inception Process in Separated Flows

Studies related to cavitation inception process in separated flows are reported. Experimental observations of bubble appearance in grooves with laminar or turbulent boundary layer over them have clearly shown that gaseous diffusion process is significantly enhanced in turbulent flow. This process can lead to local nuclei size modification in environment similar to that of flow over a groove, like laminar separation "bubbles." Cavitation inception modeling including this aspect is carried out for predicting inception conditions associated with "bubble-ring" cavitation commonly observed on hemispherically nosed axisymmetric body. Qualitative dependence of predicted inception numbers with velocity is found to agree very well with experimental observations of Carroll (1981).