HYDROLYTIC DEGRADATION BEHAVIOR OF PLLA NANOCOMPOSITES REINFORCED WITH MODIFIED CELLULOSE NANOCRYSTALS

Bionanocomposites derived from poly(L-Lactide) (PLLA) were reinforced with chemically modified cellulose nanocrystals (m-CNCs). The effects of these modified cellulose nanoparticles on the mechanical and hydrolytic degradation behavior of polylactide were studied. The m-CNCs were prepared by a method in which hydrolysis of cellulose chains is performed simultaneously with the esterification of hydroxyl groups to produce modified nanocrystals with ester groups. FTIR, elemental analysis, TEM, XRD and contact angle measurements were used to confirm and characterize the chemical modifications of the m-CNCs. These bionanocomposites gave considerably better mechanical properties than neat PLLA based on an approximately 100% increase in tensile strength. Due to the hydrophobic properties of the esterified nanocrystals incorporated into a polymer matrix, it was also demonstrated that a small amount of m-CNCs could lead to a remarkable decrease in the hydrolytic degradation rate of the biopolymer. In addition, the m-CNCs considerably delay the degradation of the nanocomposite by providing a physical barrier that prevents the permeation of water, which thus hinders the overall absorption of water into the matrix. The results obtained in this study show the nanocrystals can be used to reinforce polylactides and fine-tune their degradation rates in moist or physiological environments.

Développement de méthodes analytiques de séparation des produits de digestion enzymatique des dérivés de cellulose

La cellulose et ses dérivés sont utilisés dans un vaste nombre d’applications incluant le domaine pharmaceutique pour la fabrication de médicaments en tant qu’excipient. Différents dérivés cellulosiques tels que le carboxyméthylcellulose (CMC) et l’hydroxyéthylcellulose (HEC) sont disponibles sur le commerce. Le degré de polymérisation et de modification diffèrent énormément d’un fournisseur à l’autre tout dépendamment de l’origine de la cellulose et de leur procédé de dérivation, leur conférant ainsi différentes propriétés physico-chimiques qui leurs sont propres, telles que la viscosité et la solubilité. Notre intérêt est de développer une méthode analytique permettant de distinguer la différence entre deux sources d’un produit CMC ou HEC. L’objectif spécifique de cette étude de maitrise était l’obtention d’un profil cartographique de ces biopolymères complexes et ce, par le développement d’une méthode de digestion enzymatique donnant les oligosaccharides de plus petites tailles et par la séparation de ces oligosaccharides par les méthodes chromatographiques simples. La digestion fut étudiée avec différents paramètres, tel que le milieu de l’hydrolyse, le pH, la température, le temps de digestion et le ratio substrat/enzyme. Une cellulase de Trichoderma reesei ATCC 26921 fut utilisée pour la digestion partielle de nos échantillons de cellulose. Les oligosaccharides ne possédant pas de groupements chromophores ou fluorophores, ils ne peuvent donc être détectés ni par absorbance UV-Vis, ni par fluorescence. Il a donc été question d’élaborer une méthode de marquage des oligosaccharides avec différents agents, tels que l’acide 8-aminopyrène-1,3,6-trisulfonique (APTS), le 3-acétylamino-6-aminoacridine (AA-Ac) et la phénylhydrazine (PHN). Enfin, l’utilisation de l’électrophorèse capillaire et la chromatographie liquide à haute performance a permis la séparation des produits de digestion enzymatique des dérivés de cellulose. Pour chacune de ces méthodes analytiques, plusieurs paramètres de séparation ont été étudiés.

Enzymatic hydrolysis of pretreated sugar cane bagasse using Penicillium funiculosum and Trichoderma harzianum cellulases

In this study, we investigated the enzymatic hydrolysis of pretreated sugarcane bagasse using eight different enzymatic blends obtained from concentrated crude enzyme extracts produced by Penicillium funiculosum and Trichoderma harzianum as well as from the extracts in combination with a commercial enzymatic cocktail. The influence of different levels of biomass delignification, degree of crystallinity of lignicellulose, composition of enzymatic activities and BSA on enzymatic hydrolysis yields (HYs) was evaluated. Our X-ray diffraction studies showed that crystallinity of lignocellulose is not a key determinant of its recalcitrance toward enzymatic hydrolysis. In fact, under the experimental conditions of our study, an increase in crystallinity of lignocellulosic samples resulted in increased glucose release by enzymatic hydrolysis. Furthermore, under the same conditions, the addition of BSA had no significant effect on enzymatic hydrolysis. The most efficient enzyme blends were obtained by mixing a commercial enzymatic cocktail with P. funiculosum or T. harzianum cellulase preparations (HYs above 97%) followed by the concentrated extract of P. funiculosum alone (HY= 88.5%). Increased hydrolytic efficiencies appeared to correlate with having an adequate level of both beta-glucosidase and xylanase activities in the blends. (C) 2011 Elsevier Ltd. All rights reserved.

Microwave-Assisted Derivatization of Cellulose in an Ionic Liquid: An Efficient, Expedient Synthesis of Simple and Mixed Carboxylic Esters

Microwave (MW)-assisted cellulose dissolution in ionic liquids (ILs) has routinely led either to incomplete biopolymer solubilization, or its degradation. We show that these problems can be avoided by use of low-energy MW heating, coupled with efficient stirring. Dissolution of microcrystalline cellulose in the IL 1-allyl-3-methylimidazolium chloride has been achieved without changing its degree of polymerization; regenerated cellulose showed pronounced changes in its index of crystallinity, surface area, and morphology. MW-assisted functionalization of MCC by ethanoic, propanoic, butanoic, pentanoic, and hexanoic anhydrides has been studied. Compared with conventional heating, MW irradiation has resulted in considerable decrease in dissolution and reaction times. The value of the degree of substitution (DS) was found to be DS(ethanoate) > DS(propanoate) > DS(butanoate). The values of DS(pentanoate) and DS(hexanoate) were found to be slightly higher than DS(ethanoate). This surprising dependence on the chain length of the acylating agent has been reported before, but not rationalized. On the basis of the rate constants and activation parameters of the hydrolysis of ethanoic, butanoic, and hexanoic anhydrides in aqueous acetonitrile (a model acyl transfer reaction), we suggest that this result may be attributed to the balance between two opposing effects, namely, steric crowding and (cooperative) hydrophobic interactions between the anhydride and the cellulosic surface, whose lipophilicity has increased, due to its partial acylation. Four ethanoate-based mixed esters were synthesized by the reaction with a mixture of the two anhydrides; the ethanoate moiety predominated in all products. The DS is reproducible and the IL is easily recycled. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 134-143, 2010

Extraction of cellulose whiskers from cassava bagasse and their applications as reinforcing agent in natural rubber

In this work cassava bagasse, a by-product of cassava starch industrialization was investigated as a new raw material to extract cellulose whiskers. This by-product is basically constituted of cellulose fibers (17.5 wt%) and residual starch (82 wt%). Therefore, this residue contains both natural fibers and a considerable quantity of starch and this composition suggests the possibility of using cassava bagasse to prepare both starch nanocrystals and cellulose whiskers. In this way, the preparation of cellulose whiskers was investigated employing conditions of sulfuric acid hydrolysis treatment found in the literature. The ensuing materials were characterized by transmission electron microscopy (TEM) and X-ray diffraction experiments. The results showed that high aspect ratio cellulose whiskers were successfully obtained. The reinforcing capability of cellulose whiskers extracted from cassava bagasse was investigated using natural rubber as matrix. High mechanical properties were observed from dynamic mechanical analysis. (C) 2010 Elsevier B.V. All rights reserved.

Cassava bagasse cellulose nanofibrils reinforced thermoplastic cassava starch

Cellulose cassava bagasse nanofibrils (CBN) were directly extracted from a by-product of the cassava starch (CS) industry, viz. the cassava bagasse (CB), The morphological structure of the ensuing nanoparticles was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), presence of other components such as sugars by high performance liquid chromatography (HPLC), thermogravimetric analysis (TGA), and X-ray diffraction (XRD) experiments. The resulting nanofibrils display a relatively low crystallinity and were found to be around 2-11 nm thick and 360-1700 nm long. These nanofibrils were used as reinforcing nanoparticles in a thermoplastic cassava starch matrix plasticized using either glycerol or a mixture of glycerol/sorbitol (1:1) as plasticizer. Nanocomposite films were prepared by a melting process. The reinforcing effect of the filler evaluated by dynamical mechanical tests (DMA) and tensile tests was found to depend on the nature of the plasticizer employed. Thus, for the glycerol-plasticized matrix-based composites, it was limited especially due to additional plasticization by sugars originating from starch hydrolysis during the acid extraction. This effect was evidenced by the reduction of glass vitreous temperature of starch after the incorporation of nanofibrils in TPSG and by the increase of elongation at break in tensile test. On the other hand, for glycerol/sorbitol plasticized nanocomposites the transcrystallization of amylopectin in nanofibrils surface hindered good performances of CBN as reinforcing agent for thermoplastic cassava starch. The incorporation of cassava bagasse cellulose nanofibrils in the thermoplastic starch matrices has resulted in a decrease of its hydrophilic character especially for glycerol plasticized sample. (C) 2009 Elsevier Ltd. All rights reserved.

Evaluation of the kinetics of xylose formation from dilute sulfuric acid hydrolysis of forest residues of Eucalyptus grandis

Dilute acid hydrolysis studies were performed on forest residues of Eucalyptus grandis, in a cylindrical reactor of stainless steel. The kinetics of this hydrolysis reaction was investigated employing 0.65% sulfuric acid, a residue/acid solution ratio of 1/9 (w/w), temperatures of 130, 140, 150, and 160 degrees C, and reaction times in the range 20-100 min. The results showed that, under the optimized conditions of acid hydrolysis employed in this study, the variables temperature and reaction time had a strong influence on hemicellulose removal and a small influence on the degree of lignin and cellulose removal. The highest xylose extraction yield was 87.6% attained at 160 degrees C, after 70 min reaction time, simultaneously with the formation of decomposition products, namely 2.8% acetic acid, 0.6% furfural, and 0.06% 5-hydroxymethylfurfural. A similar xylose extraction yield (82.8%) was observed at 150 degrees C after 100 min, with the formation of 3.2% acetic acid, 1.0% furfural, and 0.07% 5-hydroxymethylfurfural. The kinetic parameters determined at 130, 140, 150, and 160 degrees C for degradation of xylan present in the hemicellulose of the eucalyptus forest residue during the formation of xylose were the first-order reaction rate constants (k) for each temperature, 1.22 x 10(-4), 2.12 x 10(-4), 5.43 x 10(-4), and 9.05 x 10(-4) s(-1), respectively, and an activation energy (E-a) of 101.3 kJ mol(-1).

Cellulose nanowhiskers from coconut husk fibers: Effect of preparation conditions on their thermal and morphological behavior

Cellulose nanowhiskers were prepared by sulfuric acid hydrolysis from coconut husk fibers which had previously been submitted to a delignification process. The effects of preparation conditions on the thermal and morphological behavior of the nanocrystals were investigated. Cellulose nanowhisker suspensions were characterized by Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), thermogravimetric analysis (TGA) and X-ray diffraction. Results showed that it was possible to obtain ultrathin cellulose nanowhiskers with diameters as low as 5 nm and aspect ratio of up to 60. A possible correlation between preparation conditions and particle size was not observed. Higher residual lignin content was found to increase thermal stability indicating that by controlling reaction conditions one can tailor the thermal properties of the nanowhiskers. Published by Elsevier Ltd.

Synthesis and characterization of microcrystalline cellulose produced from bacterial cellulose

In this study, microcrystalline cellulose (MCC) was prepared from the acid hydrolysis of bacterial cellulose (BC) produced in culture medium of static Acetobacter xylinum. The MCC-BC produced an average particle size between 70 and 90 mu m and a degree of polymerization (DP) of 250. The characterization of samples was performed by thermogravimetric analysis, X-ray diffraction, and scanning electron microscopy (SEM). The MCC shows a lower thermal stability than the pristine cellulose, which was expected due to the decrease in the DP during the hydrolysis process. In addition, from X-ray diffractograms, we observed a change in the crystalline structure. The images of SEM for the BC and MCC show clear differences with modifications of BC fiber structure and production of particles with characteristics similar to commercial MCC.

ISOLATION AND IN-VITRO HYDROLYSIS OF GLOBULIN G1 FROM LENTILS (LENS-CULINARIS, MEDIK)

The major globulin fraction from lentil seeds was investigated with respect td in vitro hydrolysis by trypsin and chymotrypsin. Globulin was isolated by a NaCl-ascorbate extraction procedure and purified by DEAE-cellulose chromatography and gelfiltration chromatography on Sepharose CL-6B. The purity and identification of the protein were performed by PAGE. The native globulin, with a molecular weight of 375 kD, was resolved by SDS-PAGE into twelve polypeptides with molecular weights ranging from 61 to 14.5 kD. Native and heated globulin GI was hydrolyzed with trypsin and chymotrypsin. SDS-PAGE indicated that native globulin was more resistant to digestion than heated protein. Amino acid analysis of the major globulin revealed that glutamic acid was present in the largest concentration, followed by aspartic acid, arginine and leucine. As is also the case for other legumin-like globulins, lentil GI was deficient in sulfur-containing amino acids.

Role of polyethylene-graft-glycidyl methacrylate compatibilizer on the biodegradation of poly(epsilon-calprolactone)/cellulose acetate blends

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Conductive nanocomposites based on cellulose nanofibrils coated with polyaniline-DBSA via in situ polymerization

Cellulose nanofibrils (CNF) were extracted by acid hydrolysis from cotton microfibrils and nanocomposites with polyaniline doped with dodecyl benzenesulphonic acid (PANI-DBSA) were obtained by in situ polymerization of aniline onto CNF. The ratios between DBSA to aniline and aniline to oxidant were varied in situ and the nanocomposites characterized by four probe DC electrical conductivity, ultraviolet-visible-near infrared (UV-Vis - NIR) and Fourier-transform infrared (FTIR) spectroscopies and X-ray diffraction (XRD). FTIR and UV-Vis/NIR characterization confirmed the polymerization of PANI onto CNF surfaces. Electrical conductivity of about 10 -1 S/cm was achieved for the composites; conductivity was mostly independent of DBSA/aniline (between 2 and 4) and aniline/oxidant (between 1 and 5) molar ratios. X-ray patterns of the samples showed crystalline peaks characteristic of cellulose I for CNF samples, and a mixture of both characteristic peaks of PANI and CNF for the nanocomposites. Field emission scanning electron microscopy (FESEM) characterization corroborated the abovementioned results showing that PANI coated the surface of the nanofibrils. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Xylo-oligosaccharides from lignocellulosic materials: Chemical structure, health benefits and production by chemical and enzymatic hydrolysis

Currently, there is worldwide interest in the technological use of agro-industrial residues as a renewable source of food and biofuels. Lignocellulosic materials (LCMs) are a rich source of cellulose and hemicellulose. Hemicellulose is rich in xylan, a polysaccharide used to develop technology for producing alcohol, xylose, xylitol and xylo-oligosaccharides (XOSs). The XOSs are unusual oligosaccharides whose main constituent is xylose linked by β 1-4 bonds. The XOS applications described in this paper highlight that they are considered soluble dietary fibers that have prebiotic activity, favoring the improvement of bowel functions and immune function and having antimicrobial and other health benefits. These effects open a new perspective on potential applications for animal production and human consumption. The raw materials that are rich in hemicellulose include sugar cane bagasse, corncobs, rice husks, olive pits, barley straw, tobacco stalk, cotton stalk, sunflower stalk and wheat straw. The XOS-yielding treatments that have been studied include acid hydrolysis, alkaline hydrolysis, auto-hydrolysis and enzymatic hydrolysis, but the breaking of bonds present in these compounds is relatively difficult and costly, thus limiting the production of XOS. To obviate this limitation, a thorough evaluation of the most convenient methods and the opportunities for innovation in this area is needed. Another challenge is the screening and taxonomy of microorganisms that produce the xylanolytic complex and enzymes and reaction mechanisms involved. Among the standing out microorganisms involved in lignocellulose degradation are Trichoderma harzianum, Cellulosimicrobium cellulans, Penicillium janczewskii, Penicillium echinulatu, Trichoderma reesei and Aspergillus awamori. The enzyme complex predominantly comprises endoxylanase and enzymes that remove hemicellulose side groups such as the acetyl group. The complex has low β-xylosidase activities because β-xylosidase stimulates the production of xylose instead of XOS; xylose, in turn, inhibits the enzymes that produce XOS. The enzymatic conversion of xylan in XOS is the preferred route for the food industries because of problems associated with chemical technologies (e.g., acid hydrolysis) due to the release of toxic and undesired products, such as furfural. The improvement of the bioprocess for XOS production and its benefits for several applications are discussed in this study. © 2012 Elsevier Ltd.

Nanocomposite PAAm/methyl cellulose/montmorillonite hydrogel: Evidence of synergistic effects for the slow release of fertilizers

In this work, we synthesized a novel series of hydrogels composed of polyacrylamide (PAAm), methylcellulose (MC), and calcic montmorillonite (MMt) appropriate for the controlled release of fertilizers, where the components presented a synergistic effect, giving very high fertilizer loading in their structure. The synthesized hydrogel was characterized in relation to morphological, hydrophilic, spectroscopic, structural, thermal, and kinetic properties. After those characterizations, the application potential was verified through sorption and desorption studies of a nitrogenated fertilizer, urea (CO(NH2)2). The swelling degree results showed that the clay loading considerably reduces the water absorption capability; however, the hydrolysis process favored the urea adsorption in the hydrogel nanocomposites, increasing the load content according to the increase of the clay mass. The FTIR spectra indicated that there was incorporation of the clay with the polymeric matrix of the hydrogel and that incorporation increased the water absorption speed (indicated by the kinetic constant k). By an X-ray diffraction technique, good nanodispersion (intercalation) and exfoliation of the clay platelets in the hydrogel matrix were observed. Furthermore, the presence of the montmorillonite in the hydrogel caused the system to liberate the nutrient in a more controlled manner than that with the neat hydrogel in different pH ranges. In conclusion, excellent results were obtained for the controlled desorption of urea, highlighting the hydrolyzed hydrogels containing 50% calcic montmorillonite. This system presented the best desorption results, releasing larger amounts of nutrient and almost 200 times slower than pure urea, i.e., without hydrogel. The total values of nutrients present in the system show that this material is potentially viable for application in agriculture as a nutrient carrier vehicle. © 2013 American Chemical Society.

Pretreatment of sugarcane bagasse with microwaves irradiation and its effects on the structure and on enzymatic hydrolysis