Comparative analysis of the fit of 3-unit implant-supported frameworks cast in nickel-chromium and cobalt-chromium alloys and commercially pure titanium after casting, laser welding, and simulated porcelain firings

This study compared the vertical misfit of 3-unit implant-supported nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloy and commercially pure titanium (cpTi) frameworks after casting as 1 piece, after sectioning and laser welding, and after simulated porcelain firings. The results on the tightened side showed no statistically significant differences. On the opposite side, statistically significant differences were found for Co-Cr alloy (118.64 mu m [SD: 91.48] to 39.90 mu m [SD: 27.13]) and cpTi (118.56 mu m [51.35] to 27.87 mu m [12.71]) when comparing 1-piece to laser-welded frameworks. With both sides tightened, only Co-Cr alloy showed statistically significant differences after laser welding. Ni-Cr alloy showed the lowest misfit values, though the differences were not statistically significantly different. Simulated porcelain firings revealed no significant differences.

Solidification behaviour and microstructural development of ironbased alloys under conditions pertinent to strip casting - 200 series stainless steels

The castability and microstructures produced from strip casting simulations of three compositions in the 200 series stainless steels have been examined. The nucleation density was similar for all three compositions.The as-cast microstructure showed very fine austenite grains of 10–20 μm in width. Retained delta ferrite was observed in the inter-dendritic regions, and was likely to be stabilised by the segregation of Cr into these regions. An analysis of the crystallography expected of different solidification sequences is presented, but a strict adherence to the Kurdjumov-Sachs orientation relationship was not found in these samples.

Microstructure development and solute behaviour in Fe-C and Fe-C-V alloys during strip casting and secondary processing

 Strip casting is a rapid, environment friendly technology for manufacturing thin sheets of steel directly from molten metal. Research presented in this thesis examines the effect of atomic location, cluster size and composition on internal microstructure development during strip casting. Current research potentially leads to green manufacturing of steel.

Does the casting mode influence microstructure, fracture and properties of different metal ceramic alloys?

The aim of the present study was to evaluate the tensile strength, elongation, microhardness, microstructure and fracture pattern of various metal ceramic alloys cast under different casting conditions. Two Ni-Cr alloys, Co-Cr and Pd-Ag were used. The casting conditions were as follows: electromagnetic induction under argon atmosphere, vacuum, using blowtorch without atmosphere control. For each condition, 16 specimens, each measuring 25 mm long and 2.5 mm in diameter, were obtained. Ultimate tensile strength (UTS) and elongation (EL) tests were performed using a Kratos machine. Vickers Microhardness (VM), fracture mode and microstructure were analyzed by SEM. UTS, EL and VM data were statistically analyzed using ANOVA. For UTS, alloy composition had a direct influence on casting condition of alloys (Wiron 99 and Remanium CD), with higher values shown when cast with Flame/Air (p < 0.05). The factors "alloy" and "casting condition" influenced the EL and VM results, generally presenting opposite results, i.e., alloy with high elongation value had lower hardness (Wiron 99), and casting condition with the lowest EL values had the highest VM values (blowtorch). Both factors had significant influence on the properties evaluated, and prosthetic laboratories should select the appropriate casting method for each alloy composition to obtain the desired property.

Chemical composition modification of casting aluminium alloys for engine applications

The research activities were focused on evaluating the effect of Mo addition to mechanical properties and microstructure of A354 aluminium casting alloy. Samples, with increasing amount of Mo, were produced and heat treated. After heat treatment and exposition to high temperatures samples underwent microstructural and chemical analyses, hardness and tensile tests. The collected data led to the optimization of both casting parameters, for obtaining a homogeneous Mo distribution in the alloy, and heat treatment parameters, allowing the formation of Mo based strengthening precipitates stable at high temperature. Microstructural and chemical analyses highlighted how Mo addition in percentage superior to 0.1% wt. can modify the silicon eutectic morphology and hinder the formation of iron based β intermetallics. High temperature exposure curves, instead, showed that after long exposition hardness is slightly influenced by heat treatment while the effect of Mo addition superior to 0,3% is negligible. Tensile tests confirmed that the addition of 0.3%wt Mo induces an increase of about 10% of ultimate tensile strength after high temperature exposition (250°C for 100h) while heat treatments have slight influence on mechanical behaviour. These results could be exploited for developing innovative heat treatment sequence able to reduce residual stresses in castings produced with A354 modified with Mo.

Improved of Cr-Ni-Mo iron base alloys by vacuum melting and casting. Final report.

"Bureau of Ships, Department of the Navy. Contract no. NObs-77019, Index Number NS-013-119."

Dispersion strengthened copper-thorium boride and copper-alumina alloys produced by melting and casting /

Photocopy. U.S. Dept. of Commerce, Office of Technical Services. AD606806.

Investigation of nano-scale precipitation phenomena in Al-Fe and Al-Cu-(Fe) alloys processed via direct strip casting

The use of rapid solidification processes such as direct strip casting (DSC) is a good way to refine the Fe-intermetallics and decrease their detrimental effects. DSC creates out-ofequilibrium supersaturated microstructures. In this work, we explore the precipitation phenomena in direct strip cast Al-Fe and Al-Cu-Fe alloys and related corrosion and mechanical properties. The precipitates are characterised with differential scanning calorimetry and transmission electron microscopy. The corrosion performances are evaluated with immersion tests and weight loss measurements and the yield strength and ductility are estimated with tensile tests. A strong correlation between the microstructure and the bulk properties is revealed with a significant improvement of properties of DSC alloys.

Wrought aluminum-nickel alloys for high strength-high conductivity applications

Aluminum-Nickel alloys ranging from 0.06 pct to 6.1 pct (by wt) Ni have been developed for high strength-high conductivity applications. These alloys were produced by solidification in a permanent mold followed by homogenization, hot extrusion or hot rolling and cold drawing to wire form. This sequence of fabrication a) led to the production of fine fibrous dispersoids of NiAl3 as part of the Al-NiAl3 eutectic during the initial casting operation, b) permitted the retention of fine fibrous dispersiods of NiAl3 produced during casting without any significant coarsening during processing and c) led to uniform dispersion and general alignment of these fibrous dispersoids along a given direction in the product without any measurable fiber-matrix separation, extensive fiber-fragmentation or crack production in the matrix. These alloys can be processed to wire form as easily as aluminum and when processed by the above sequence, possess very attractive combination of high strength-high electrical conductivity. Tensile strengths range from 173 N/mm2 (at 0.6 pct Ni) to 241 N/mm2 (at 6.1 pct Ni) in combination with corresponding conductivity values between 62 pct IACS and 55.5 pct IACS. The wires also possess attractive yield strength; for instance, the 0.2 pct off-set strength of Al-6.1 pct Ni wire is 213 N/mm2. Using simple composite rules, the estimated strength and the conductivity of NiAl3 fibers were found to be 1380 N/mm2 and 18 pct IACS respectively, in these wires.

Interrupted creep behaviour of Mg alloys developed for powertrain applications

A conventional magnesium alloy, AZ91D, and two creep resistant magnesium alloys, developed for powertrain applications, MRI 153M and MRI 230D, are prepared by high pressure die casting. These alloys are tested for their creep behaviour in the continuous manner, as is the Current practice, and in the interrupted manner, which represents the real life Situation more closely. It is observed that the interrupted creep tests give rise to a primary creep appearing at the beginning of each cycle resulting in a higher average strain rate than that encountered in the continuous creep tests. Further, the shorter the cycle time, higher is the average strain rate in the interrupted creep tests. A higher average strain rate will give rise to a higher strain over the same period. This is attributed to the recovery taking place during the cooling and heating between two cycles. The effect of additional precipitation during interrupted creep tests depends on the nature of the precipitates. The additional precipitation of beta phase during the cooling and heating between two cycles increases the steady state strain rate in the AZ91D and MRI 153M alloys. whereas the additional precipitation of C36 phase during the cooling and heating between two cycles decreases the steady state strain rate in the MRI 230D alloy. (C) 2009 Elsevier B.V. All rights reserved.

Electron beam surface melting of model 1200 Al alloys

Electron beam surface melting has been used to characterise the phase content formed in a number of model 1200 series Al alloys with increasing solidification velocity in the range 2–50 mm s−1, typical of that experienced during continuous strip casting. Phases were extracted from the Al matrix and analysed by X-ray diffraction. A qualitative solidification microstructure selection map has been produced, showing that, for a given Fe content of 0.55 wt.%: with increasing solidification velocity the metastable aluminides FeAl6 and FeAlm displace equilibrium Fe4Al13 at Si contents 0.15 wt.%, and that α-AlFeSi is an equilibrium phase at a Si content ≥0.50 wt.%.

Microstructural and mechanical behavior study of suction cast Nb-Si binary alloys

The solidification pathways of Nb rich Nb-Si alloys when processed under non-equilibrium conditions require understanding. Continuing with our earlier work on alloying additions in single eutectic composition 1,2], we report a detailed characterization of the microstructures of Nb-Si binary alloys with wide composition range (10-25 at% Si). The alloys are processed using chilled copper mould suction casting. This has allowed us to correlate the evolution of microstructure and phases with different possible solidification pathways. Finally these are correlated with mechanical properties through studies on deformation using mechanical testing under indentation and compressive loads. It is shown that microstructure modification can significantly influence the plasticity of these alloys.