Hydroisomerization of long-chain alkane over Pt/SAPO-11 catalysts synthesized from nonaqueous media

SAPO-11 molecular sieves were synthesized from nonaqueous media. The effects of Si and Al sources as well as solvents on the catalytic performance of SAPO-11 were investigated by the hydroisomerization reaction of n-dodecane. The samples were characterized by XRD, XRF, N-2-adsorption, SEM, NH3-TPD, IR-NH3 and Si-29 CP MAS NMR. The SAPO-11 samples synthesized with tetraethoxysilane as the Si source showed higher Si incorporation contents than the SAPO molecular sieves prepared with polymeric Si sources (fumed silica and Si colloidal gel). The reaction results showed that Pt/SAPO-11 catalysts synthesized from ethylene glycol and glycerol media with the monomeric Si and Al sources (tetraethoxysilane, aluminum isopropoxide) exhibited higher catalytic activities than those catalysts with the polymeric Si or Al (pseudo-boehmite) sources, due to the larger external surface area and higher acidity of the former ones. Especially, the catalyst synthesized in an ethylene glycol medium possessed the highest catalytic activity. Over this catalyst, 88% conversion of n-dodecane was achieved at a low temperature of 250 degrees C.

Specific surface area and structures of aluminas from fibrillar pseudoboehmite

By heating powders of the aluminum monohydroxide fibrillar pseudoboehmite from 200 degrees C to 1400 degrees C several high surface area aluminas are prepared and characterized by X-ray diffraction and electron optical methods. Aqueous sols with pseudoboehmite fibrils of different lengths were dried by two methods: at room temperature and spray-dried. The following aluminas were obtained after treatment of the powders at increasing temperatures and having a range of specific surface areas: gamma-Al(2)O(3) (470 degrees C - 770 degrees C; 179 m(2)/g 497 m(2)/g); delta-Al(2)O(3) (770 degrees C - 930 degrees C; 156 m(2)/g - 230 m(2)/g); theta-Al(2)O(3) (930 degrees C - 1050 degrees C; 11 m(2)/g - 200 m(2)/g); alpha-Al(2)O(3) (1050 degrees C - 1400 degrees C; 2 m(2)/g - 17 m(2)/g). Spray-dried powders, fired at the same temperature than the ground powders, showed higher specific surface areas. The higher surface area alumina have values of the same order of magnitude of the commercial ""ad-cat"" aluminas.

Nanocomposites materials generated from a spray

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Aluminoxane-epoxi-siloxane hybrids waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The influence of aluminium on the overall properties of SnO2-based varistors

The influence of aluminium on the development of the microstructure and on the electrical behaviour of the SnO2 center dot Co3O4 center dot Nb2O5 typical varistor system was studied. Two sources of Al were used, alumina (Al2O3) and boehmite (AlO(OH)). The microstructural features were characterised with scanning (SEM) and transmission (TEM) electron microscopies. The different phases present in the studied samples were also studied with XRD, EDS and electron diffraction patterns of selected areas (SAED). Particles containing Sri, Co, Al, and O were unveiled with TEM. Impedance spectroscopy measurements and current density versus electric field characteristics revealed superior electrical properties for samples with AlO(OH). The higher non-linearity (alpha = 19) was achieved with the addition of 0.1% mol of boehmite. The influence of the secondary phases on the electrical properties is also addressed in this work.

Influence of pH and precipitation temperature on the structural characteristics of aluminium hydroxides prepared form nitrate aqueous solutions

Aluminium Hydroxides were precipitated from Aluminium Nitrate and Ammonium Hydroxide, at the temperatures 64 degrees C (hot) and 25 degrees C (cold), under the pH conditions 5, 7 and 9. The samples were characterized by X-Ray Diffraction (XRD) and Differential Thermal Analysis (DTA). The hydroxide precipitated at pH 9 and 64 degrees C is built up by pseudoboehmite and a minor share of others apparently amorphous hydroxides. The crystallinity of the hot yielded pseudoboehmite diminishes with the pH. The crystallite size was evaluated as about 40 Angstrom for the best crystallized sample. The cold precipitated product is apparently composed by amorphous or very poorly crystallized hydroxides. Upon heating, the cold precipitated hydroxides, and the low pH and hot precipitated hydroxide, release their structural water before the occurrence, about 430 degrees C, of the transition of the pseudoboehmite to gamma-alumina, and exhibit a shifting (towards low temperature side) and a broadening in the peak of the transition to alpha-alumina, which occurs at 1200 degrees C in the pseudoboehmite pattern. The yielded pseudo-boehmite peptized by HNO3, addition and gelified by evaporation in a critical concentration approximately 0.17 gcm(-3).

Luminescent nano-composites generated from a spray

The spray-pyrolysis (SP) synthesis technique has been employed to obtain SiO2:Eu3+ and gamma-AlOOH:Eu3+, It was possible to obtain sub-micrometric spherical particles of SiO2 with luminescent Eu3+ ions bonded to the silica surface or embedded in amorphous silica beads, by controlling the synthesis and annealing process. Boehmite y-AlOOH doped with Eu3+ nanoparticles were synthesized by SP at moderate temperature (200 degrees C) with Eu3+ ions bonded to the surface hydroxyls of the boehmite nanocrystals. Luminescent nanocomposites were obtained by controlled reaction of gamma-AlOOH:Eu3+ nanocrystals with ASN (asparagine). In these nano-composites, the Eu3+ are held at the surface of the boehmite nanocrystals and partially shielded from interactions with additional luminescence quenchers (hydroxyl groups, water molecules). (C) 2008 Elsevier B.V. All rights reserved.

Monolithic diphasic gels of mullite by sol-gel process under ultrasound stimulation

Diphasic gel in the mullite composition was prepared from a colloidal sol of boehmite mixed with a hydrolyzed tetraethoxisilane (TEOS) solution. The boehmite sol was obtained by peptization of a poorly crystallized or very small mean crystallite size (∼34 Å) precipitate, resulting from the reaction between solutions of aluminum sulfate and sodium hydroxide. Ultrasound was utilized in the processes of the TEOS hydrolysis and the boehmite peptization, and also for complete homogenization of the mixture to gel. The wet gel is almost clear and monolithic. The gel transparency is lost on drying, when syneresis has ended, so that the interlinked pore structure starts to empty and is recovered upon water re-absorption. Cracking closely accompanies this critical drying process. Differential thermal analysis (DTA) and X-ray diffraction (XRD) show that the solid structure of the gel is composed of an amorphous silica phase, as a matrix, and a colloidal sized crystalline phase of boehmite. Upon heat treatment, the boehmite phase within the gel closely follows the same transition sequence as in pure alumina shifted towards higher temperatures. Orthorhombic mullite formation was detected at 1300°C. © 1998 Elsevier Science B.V. All rights reserved.

Synthesis of high-surface-area gamma-Al2O3 from aluminum scrap and its use for the adsorption of metals: Pb(II), Cd(II) and Zn(II)

Several types of alumina were synthesized from sodium aluminate (NaAlO2) by precipitation with sulfuric acid (H2SO4) and subsequently calcination at 500 degrees C to obtain gamma-Al2O3. The precursor aluminate was derived from aluminum scrap. The various gamma-Al2O3 synthesized were characterized by Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), adsorption-desorption of N-2 (S-BET) and scanning electron microscopy (SEM). XRD revealed that distinct phases of Al2O3 were formed during thermal treatment. Moreover, it was observed that conditions of synthesis (pH, aging time and temperature) strongly affect the physicochemical properties of the alumina. A high-surface-area alumina (371 m(2) g(-1)) was synthesized under mild conditions, from inexpensive raw materials. These aluminas were tested for the adsorption of Cd(II), Zn(II) and Pb(II) from aqueous solution at toxic metal concentrations, and isotherms were determined. (C) 2012 Elsevier B.V. All rights reserved.

The influence of heat treatment on the phase relations in mineral growth systems

ABSTRACT Corundum is one of the most famous gems materials. Different heat treatment methods for enhancement purposes are commonly applied and accepted in the gem market. With this reason, the identification of the natural, unheated corundum is intensively investigated. In this study, aluminium hydroxide minerals and zircon are focused to observe the crystallization and phase change of these minerals during heat treatment procedures. Aluminium hydroxide minerals can be transformed to alumina with the corundum structure by heating. The reaction history of aluminium hydroxide minerals containing corundum was investigated comparing it with diaspore, boehmite, gibbsite and bayerite by TG and DTA methods. These hydroxide minerals were entirely transformed to corundum after heating at 600°C. Zircon inclusions in corundums from Ilakaka, Madagascar, were investigated for the influence of different heat-treatment temperatures on the recovery of their crystalline structure and on possible reactions within and with the host crystals. The host corundum was heated at 500, 800, 1000, 1200, 1400, 1600 and 1800°C. The crystallinity, the trapped pressure, and the decomposition of the zircon inclusions within the host corundum have been investigated by Raman spectroscopy. Radiation-damaged zircon inclusions may be used as an indicator for unheated Ilakaka corundum crystals. They are fully recrystallized after heating at 1000°C influencing the lowering of the 3 Raman band shift, the decreasing of FWHM of the 3 Raman band and the decreasing of the trapped pressure between the inclusion and the host corundum. Under microscopic observation, surface alterations of the inclusions can be firstly seen from transparent into frosted-like appearance at 1400°C. Then, between 1600°C and 1800 °C, the inclusion becomes partly or even completely molten. The decomposition of the zircon inclusion to m-ZrO2 and SiO2-glass phases begins at the rim of the inclusion after heating from 1200°C to 1600°C which can be detected by the surface change, the increase of the 3 Raman band position and the trapped pressure. At 1800°C, the zircon inclusions entirely melt transforming to solid phases during cooling like m-ZrO2 and SiO2-glass accompanied by an increase of pressure between the transformed inclusion and its host.