Obtenção da liga Ti-35Nb por metalurgia do pó para utilização em próteses ortopédicas

Pós-graduação em Engenharia Mecânica - FEG

A Quality Assessment of Titanium Castings Produced in an Experimental Short-Heating-Cycle Investment

The aim of this study was to evaluate the quality of casting produced in an experimental short-term heating-cycle investment. Thus, reaction layer and castability of titanium casting using an experimental spinel-based investment (VR) with short heating cycle were compared with the commercial short-heating-cycle spinel-based investment Trinell (TR), the silica-phosphate-based investment Rematitan Plus ( RP), and the conventional spinel-based investment Rematitan Ultra (RU). VR has polymeric fibers added to inorganic particles. Reaction layer assessments were carried out using Vickers hardness and elemental analysis using dispersive X-ray microanalysis (EDX). Mesh patterns were used for castability test, and powder characterization was made by scanning electron microscopy (SEM). Hardness evaluation showed no difference among the investments between 100 and 200 mu m. The most important contaminant element for VR, TR, and RU was oxygen. Higher levels of mold filling were found for TR, VR, and RU compared with that obtained with RP. The quality of castings, characterized by means of the assessments of reaction layer and castability, made from the VR was similar to the commercial investments TR and RU but superior to the RP.

Streptococcus Mutans Adhesion to Titanium After Brushing with Fluoride and Fluoride-Free Toothpaste Simulating 10 Years of Use

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloys in different storage environments

Statement of problem. Removable partial dentures are affected by fatigue because of the cyclic mechanism of the masticatory system ansi frequent insertion and removal. Titanium and its alloys have been used in the manufacture of denture frameworks; however, preventive agents with fluorides are thought to attack titanium alloy surfaces.Purpose. This study evaluated, compared, analyzed the corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloy in different storage environments.Material and methods. For each metal, 33 dumbbell rods, 2.3 mm in diameter at the central segment, were cast in the Rematitan system. Corrosion-fatigue strength test was carried out through a universal testing machine with a load 30% lon er than the 0.2% offset yield strength and a combined influence of different: environments: in air at room temperature, with synthetic saliva, and with fluoride synthetic saliva. After failure, the number of cycles were recorded, and fracture surfaces were examined with on SEM.Results. ANOVA and Tukey's multiple comparison rest indicated that Ti-6Al-4V alloy achieved 21,269 cycles (SD = 8,355) against 19,157 cycles (SD = 3,624) for the commercially purr Ti. There were no significant differences between either metal in the corrosion-fatigue life for dry specimens, but when the solutions were present, the fatigue life was significantly reduced, probably because of the product-ion of corrosion pits caused by superficial reactions.

Influence of heat treatment and mechanical cycling on hardness and fracture analysis of Ti35Nb5Zr casting alloy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fios ortodônticos superelásticos e sua aplicabilidade na clínica ortodôntica: revisão da literatura

During clinical routine, the orthodontist uses several materials, which include metallic alloys in the form of metallic wires. However, it is necessary that the professional has some knowledge of the properties of those wires. Different types of wires are commercially available: stainless steel wires, chrome-cobalt wires, nickel-titanium wires and beta-titanium wires. Among the nickel-titanium wires, there are three subdivisions: a conventional alloy and two superelastic alloys. The superelasticity, associated to the effect of form memory, is a property used in orthodontics to initiate the dental movement in the first phase of the orthodontic treatment. This property is considered to be biologically compatible with the effective dental movement. These wires are available at the market in different transformation temperatures, and they offer the best adaptation in the groove of the bracket, simplicity and a faster treatment. However, they present little formability, and they don’t accept solder. They are also more onerous than other wires. Moreover, the low rigidity of these wires doesn’t allow them to be used for the retraction of the anterior teeth or closing of spaces. Therefore, the coherent use of superelastic orthodontic wires is recommended, accompanied by a detailed diagnosis and planning, so the result will be an efficient orthodontic correction, accomplished in a shorter period of time.

Influences of the pH on the adsorption properties of an antimicrobial peptide on titanium surfaces

The adsorption behavior of the Tet-124 antimicrobial peptide and the Tet-124 peptide modified at the C- and N-terminus with the sequence glycine-3,4-dihydroxyphenylalanine-glycine (G-DOPA-G) on titanium surfaces was studied using quartz crystal micro balance with dissipation (QCM-D). At a low pH level (4.75) Tet-124 and Tet-124-G-DOPA-G form rigid layers. This is attributed to the electrostatic interactions of the positively charged lysine and arginine residues in the peptide sequence with the negatively charged titanium oxide layer. At an elevated pH level (6.9) Tet-124 shows a lower mass adsorption at the surface than Tet-124-G-DOPA-G. This is attributed to the interaction of the catechol due to the formation of complexes with the titanium oxide and titanium surface layer. The C terminal and N terminal modification with the sequence G-DOPA-G shows similar adsorption rate and mass adsorption coverage at saturation; however it is presented a more loosely layers on the G-DOPA-G-TeT-124. Fibroblast adhesion and the biocompatibility test of both the surfaces following modification with Tet-124-G-DOPA-G and the titanium alloy control showed similar results. In addition, no changes in the adhesion of E. coli bacteria due to the modification of the surface were detected.

Tool wear evaluations in friction stir processing of commercial titanium Ti–6Al–4V

This research addresses the application of friction stir welding (FWS) of titanium alloy Ti–6Al–4V. Friction stir welding is a recent process, developed in the 1990s for aluminum joining; this joining process is being increasingly applied in many industries from basic materials, such as steel alloys, to high performance alloys, such as titanium. It is a process in great development and has its economic advantages when compared to conventional welding. For high performance alloys such as titanium, a major problem to overcome is the construction of tools that can withstand the extreme process environment. In the literature, the possibilities approached are only few tungsten alloys. Early experiments with tools made of cemented carbide (WC) showed optimistic results consistent with the literature. It was initially thought that WC tools may be an option to the FSW process since it is possible to improve the wear resistance of the tool. The metallographic analysis of the welds did not show primary defects of voids (tunneling) or similar internal defects due to processing, only defects related to tool wear which can cause loss of weld quality. The severe tool wear caused loss of surface quality and inclusions of fragments inside the joining, which should be corrected or mitigated by means of coating techniques on tool, or the replacement of cemented carbide with tungsten alloys, as found in the literature.

Bone repair in mandibular body osteotomy after using 2.0 miniplate system - histological and histometric analysis in dogs

The objective of this study was to evaluate the bone repair along a mandibular body osteotomy after using a 2.0 miniplate system. Nine adult mongrel dogs were subjected to unilateral continuous defect through an osteotomy between the mandibular 3rd and 4th premolars. Two four-hole miniplates were placed in accordance with the Arbeitgeimeinschaft fur Osteosynthesefragen Manual. Miniplates adapted to the alveolar processes were fixed monocortically with 6.0-mm-length titanium alloy self-tapping screws, whereas miniplates placed near the mandible bases were fixed bicortically. At 2, 6 and 12 weeks, three dogs were sacrificed per period, and the osteotomy sites were removed, divided into three thirds (Tension Third, TT; Intermediary Third, IT; Compression Third, CT) and prepared for conventional and polarized light microscopy. At 6 weeks, while the CT repaired faster and showed bone union by woven bone formation, the TT and IT exhibited a ligament-like fibrous connective tissue inserted in, and connecting, newly formed woven bone overlying the parent lamellar bone edges. At 12 weeks, bone repair took place at all thirds. Histometrically, proportions of newly formed bone did not alter at TT, IT and CT, whereas significantly enhanced bone formation was observed for the 12-week group, irrespective of the third. The results demonstrated that although the method used to stabilize the mandibular osteotomy allowed bone repair to occur, differences in the dynamics of bone healing may take place along the osteotomy site, depending on the action of tension and compression forces generated by masticatory muscles.

Otimização dos parâmetros de processamento em Laser Melting

Dissertação de mestrado integrado em Engenharia Mecânica

Processamento e caracterização de compósitos de Ti-HAP para aplicações biomédicas

Dissertação de mestrado integrado em Engenharia de Materiais

Evaluation of monoenergetic imaging to reduce metallic instrumentation artifacts in computed tomography of the cervical spine.

OBJECT Monoenergetic imaging with dual-energy CT has been proposed to reduce metallic artifacts in comparison with conventional polychromatic CT. The purpose of this study is to systematically evaluate and define the optimal dual-energy CT imaging parameters for specific cervical spinal implant alloy compositions. METHODS Spinal fixation rods of cobalt-chromium or titanium alloy inserted into the cervical spine section of an Alderson Rando anthropomorphic phantom were imaged ex vivo with fast-kilovoltage switching CT at 80 and 140 peak kV. The collimation width and field of view were varied between 20 and 40 mm and medium to large, respectively. Extrapolated monoenergetic images were generated at 70, 90, 110, and 130 kiloelectron volts (keV). The standard deviation of voxel intensities along a circular line profile around the spine was used as an index of the magnitude of metallic artifact. RESULTS The metallic artifact was more conspicuous around the fixation rods made of cobalt-chromium than those of titanium alloy. The magnitude of metallic artifact seen with titanium fixation rods was minimized at monoenergies of 90 keV and higher, using a collimation width of 20 mm and large field of view. The magnitude of metallic artifact with cobalt-chromium fixation rods was minimized at monoenergies of 110 keV and higher; collimation width or field of view had no effect. CONCLUSIONS Optimization of acquisition settings used with monoenergetic CT studies might yield reduced metallic artifacts.

Estudo do biomaterial Ti-6Al-4V empregando-se técnicas eletroquímicas e XPS

The Ti-6Al-4V alloy used as biomaterial has been used over the last years. The literature shows controversies concerning the kind and the chemical composition of the film naturally and elctrochemically formed on the surface of the titanium alloy. The presente work studies the film composition before and after the electrochemical polarization tests using the x Ray photoelectron spectroscopy (XPS) technique. The results showed that the film naturally formed on the metallic surface is constituted of a variety of oxides which do not cover the whole surface of the metallic alloy and therefore, metallic Ti, Al and V can be found on the uncovered areas. The tests of XPS made after the polarization up to 4V (SCE) showed that the electrochemically formed film is constituted only of TiO2 and that the peak current observed around 1,5 V (SCE) is due to the oxidation of any kind of titanium oxide or the growth of the film.

Fractal analysis of eroded surfaces by digital image processing

Jet impingement erosion test rig has been used to erode titanium alloy specimens (Ti-4Al-4V). Eroded surface profiles have been obtained by vertical sectioning method for light microscopy observation. Mixed fractals have been measured from profile images by a digital image processing and analysis technique. The use of this technique allows glimpsing a quantitative correlation among material properties, fractal surface topography and erosion phenomena. (C) 2002 Elsevier B.V. B.V. All rights reserved.

An investigation on sliding wear behavior of PVD coatings

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)