Raman spectroscopic study of the antimony containing mineral partzite Cu2Sb2(O,OH)7

Raman spectroscopy of the mineral partzite Cu2Sb2(O,OH)7 complimented with infrared spectroscopy were studied and related to the structure of the mineral. The Raman spectrum shows some considerable complexity with a number of overlapping bands observed at 479, 520, 594, 607 and 620 cm-1 with additional low intensity bands found at 675, 730, 777 and 837 cm-1. Raman bands of partzite in the spectral region 590 to 675 cm-1 are attributable the ν1 symmetric stretching modes. The Raman bands at 479 and 520 cm-1 are assigned to the ν3 antisymmetric stretching modes. Raman bands at 1396 and 1455 cm-1 are attributed to SbOH deformation modes. A complex pattern resulting from the overlapping band of the water and OH units is found. Raman bands are observed at 3266, 3376, 3407, 3563, 3586 and 3622 cm-1. The first three bands are assigned to water stretching vibrations. The three higher wavenumber bands are assigned to the stretching vibrations of the OH units. It is proposed that based upon observation of the Raman spectra that water is involved in the structure of partzite. Thus the formula Cu2Sb2(O,OH)7 may be better written as Cu2Sb2(O,OH)7 •xH2O

Electron beam evaporation of tungsten oxide films for gas sensors

Pure and Iron incorporated nanostructured Tungsten Oxide (WO3) thin films were investigated for gas sensing applications using noise spectroscopy. The WO3 sensor was able to detect lower concentrations (1 ppm-10 ppm) of NH3, CO, CH4 and Acetaldehyde gases at operating temperatures between 100 degrees celcius to 250 degrees celcius. The iron doped Tungsten Oxide sensor (WO3:Fe) showed some response to Acetaldehyde gas at relatively higher operating temperature (250 degrees celcius) and gas concentration of 10 ppm. The sensitivity of the WO3 sensor towards NH3, CH4 and Acetaldehyde at lower operating temperatures (50 degrees celcius - 100 degrees celcius) was significant when the sensor was photo-activated using blue-light emitting diode (Blue-LED). From the results, photo-activated WO3 thin film that operates at room temperature appeared to be a promising gas sensor. The overall results indicated that the WO3 sensor exhibited reproducibility for the detection of various gases and the WO3:Fe indicated some response towards Acetaldehyde gas.

Mechanical properties of thin sol-gel films

This thesis presents a study of the mechanical properties of thin films. The main aim was to determine the properties of sol-gel derived coatings. These films are used in a range of different applications and are known to be quite porous. Very little work has been carried out in this area and in order to study the mechanical properties of sol-gel films, some of the work was carried out on magnetron sputtered metal coatings in order to validate the techniques developed in this work. The main part of the work has concentrated on the development of various bending techniques to study the elastic modulus of the thin films, including both a small scale three-point bending, as well as a novel bi-axial bending technique based on a disk resting on three supporting balls. The bending techniques involve a load being applied to the sample being tested and the bending response to this force being recorded. These experiments were carried out using an ultra micro indentation system with very sensitive force and depth recording capabilities. By analysing the result of these forces and deflections using existing theories of elasticity, the elastic modulus may be determined. In addition to the bi-axial bending study, a finite element analysis of the stress distribution in a disk during bending was carried out. The results from the bi-axial bending tests of the magnetron sputtered films was confirmed by ultra micro indentation tests, giving information of the hardness and elastic modulus of the films. It was found that while the three point bending method gave acceptable results for uncoated steel substrates, it was very susceptible to slight deformations of the substrate. Improvements were made by more careful preparation of the substrates in order to avoid deformation. However the technique still failed to give reasonable results for coated specimens. In contrast, biaxial bending gave very reliable results even for very thin films and this technique was also found to be useful for determination of the properties of sol-gel coatings. In addition, an ultra micro indentation study of the hardness and elastic modulus of sol-gel films was conducted. This study included conventionally fired films as well as films ion implanted in a range of doses. The indentation tests showed that for implantation of H⁺ ions at doses exceeding 3x10¹⁶ ions/cm², the mechanical properties closely resembled those of films that were conventionally fired to 450°C.

A Raman spectroscopic study of the antimony mineral klebelsbergite Sb4O4(OH)2(SO4)

Many minerals based upon antimonite and antimonate anions remain to be studied. Most of the bands occur in the low wavenumber region, making infrared spectroscopy difficult to use. This problem can be overcome by using Raman spectroscopy. Raman spectra of the mineral klebelsbergite Sb4O4(OH)2(SO4) were studied, and related to the structure of the mineral. Raman bands observed at 971 cm-1 and a series of overlapping bands are observed at 1029, 1074, 1089, 1139 and 1142 cm-1 are assigned to the SO42- ν1 symmetric and ν3 antisymmetric stretching modes. Two Raman bands are observed at 662 and 723 cm-1 and assigned to the SbO ν3 antisymmetric and ν1 symmetric stretching modes. The intense Raman bands at 581, 604 and 611 cm-1 are assigned to the ν4 SO42- bending modes. Two overlapping bands at 481 and 489 cm-1 are assigned to the ν2 SO42- bending mode. Low intensity bands at 410, 435 and 446 cm-1 may be attributed to OSbO bending modes. The Raman band at 3435 cm-1 is attributed to the OH stretching vibration of the OH units. Multiple Raman bands for both SO42- and SbO stretching vibrations support the concept of the non-equivalence of these units in the klebelsbergite structure. It is proposed that two sulphate anions are distorted to different extents in the klebelsbergite structure.

Sound in the Aboriginal Australian Films of Rolf de Heer

Anna Hickey-Mody and Melissa Iocca invented a new name for the cinema-goer at "Bad Boy Bubby" (1993) when they wrote: "In de Heer's film, the viewer is primarily a listener, or aurator, and secondly a spectator" and I have argued the label 'aurator' can also be used for the person experiencing "Ten Canoes" (2006). This Aboriginal Australian Dreamtime fable features dialogue recorded entirely in the Ganalbingu language of the Indigenous people it stars, and is a prime example of what I would suggest can be labeled 'The Aboriginal Australian Films of Rolf de Heer'. "The Tracker" (2002) and "Dr. Plonk" (2007) have also included depictions of Aboriginal Australians and each of the trio utilizes Cat Hope's "innovative sound ideas" to present what I argue is an aural auteur's signature revealing a post-colonial Australian world-view that privileges the justice system and eco-spirituality of Aboriginal Australians.