The effect of water inorganic matrix in ibuprofen adsorption onto activated carbon for water and wastewater treatment

Dissertação para obtenção do Grau de Mestre em Engenharia Química e Bioquímica

Adsorption equilibria of flue gas components on activated carbon

Dissertação para obtenção do Grau de Mestre em Engenharia Química e Bioquímica

Gold recovery from cyanideand chloride solution using activated carbon

Uusia keinoja kullan erottamiseksi malmista on etsitty viimeaikoina taloudellisista ja ympäristöllisistä syistä kautta maailman. Syanidointimenetelmä on hallinnut kullan talteenottoayli sata vuotta. Menetelmässä kulta liuotetaan laimeaan syanidiliuokseen, jostase otetaan talteen aktiivihiilen avulla. Syanidin käyttöä pyritään kuitenkin vähentämään sen myrkyllisyyden takia. Lisäksi nykyään louhitaan enenemässä määrin malmia, josta on hankala rikastaa kulta kustannustehokkaasti syanidia käyttäen. Kullan talteenottoa syanidi- ja kloridiliuoksesta on selvitetty kirjallisuuden avulla. Kullan kemiaan liuotuksen aikana on perehdytty ennen kullan talteenottoa aktiivihiilellä. Aktiivihiilen elinkaari kullan adsorbenttinaon käsitelty valmistuksesta hylkäämiseen mukaan lukien hiilen myrkyttyminen prosessissa ja regenerointi. Aktiivi-hiilen käyttäytyminen syanidi- ja kloridiliuoksessa on selvitetty erikseen. Kullan talteenottoa kuparipitoisista malmeista on käsitelty. Kullan talteenottoa kloridiliuoksesta aktiivihiiltä käyttäen on tutkittu kokeellisesti. Pääasialliset tutkimuskohteet ovat adsorption kinetiikka, kuparin vaikutus adsorptioon, aktiivihiilen vaikutus adsorptioonja adsorboituneiden metallien strippaus hiilestä selektiivisesti. Hapettavan stippauksen vaikutus kullan desorptioon hiilestä on tutkittu yksityiskohtaisesti. Kullan erotusmenetelmät kuparimalmista aktiivihiiltä käyttäen on selvitetty diplomityön tulosten pohjalta. Diplomityön keskeisten tulosten perusteella kulta ei välttämättä saostu aktiivihiilen pinnalle kloridiliuoksesta. Havainto varmistettiin ladattujen hiilipartikkelien pyyhkäisyelektronimikroskooppikuvista ja partikkeleille tehdyistä mikroanalyyseistä. Kullan pelkistyminen metalliseksi kullaksi aktiivihiilessä voitaneen välttää käyttämällä erittäin hapettavia olosuhteita. Aktiivihiili ilmeisesti hapettuu näissä olosuhteissa, mikä mahdollistaa kultakloridin adsorboitumisen hiileen.

Aluminium fouling and its impact on activated carbon based dioxin and furan removal in a wet scrubber at a co-incineration plant

Dioxins and furans, PCDD/Fs, are highly toxic substances formed in post combustion zones in furnaces. PCDD/F emissions are regulated by a waste incineration directive which relates also to co-incineration plants. Several observations of dioxin and furan enhancements in wet scrub- bers have been reported previously. This is thought to be due to the so-called "memory effect" which occurs when dioxins and furans absorb into plastic material in scrubbers and desorb when ambient circumstances alter significantly. At the co-incineration plant involved, dioxins and furans are controlled with a wet scrubber, the tower packing of which is made of plastic in which activated carbon particles are dispersed. This should avoid the memory effect and act as a dioxin and furan sink since dioxins and furans are absorbed irreversibly into the packing ma- terial. In this case, the tower packing in the scrubber is covered with a white layer that has been found to be mainly aluminium. The aim of this thesis was to determine the aluminium balance and the dioxin and furan behaviour in the scrubber and, thus, the impacts that the foul- ing has on dioxin and furan removal. The source of aluminium, reasons for fouling and further actions to minimize its impacts on dioxin and furan removal were also to be discovered. Measurements in various media around the scrubber and in fuels were made and a profile analysis of PCDD/F and mass balance calculations were carried out. PCDD/F content de- creased in the scrubber. The reduced PCDD/F was not discharged into scrubbing water. The removal mechanism seems to work in spite of the fouling, at least with low PCDD/F loads. Most of the PCDD/F in excess water originates from the Kymijoki River which is used as feeding water in the scrubber. Fouling turned out to consist mainly of aluminium hydroxides. Sludge combusted in the furnace was found to be a significant source of aluminium. Ways to minimize the fouling would be adjustment of pH to a proper lever, installation of a mechanical filter to catch the loose material from the scrubbing water and affecting the aluminium content of the sludge.

Removal of Pb(II) ions and malachite green dye from wastewater by activated carbon produced from lemon peel

In the present study, a high-surface area activated carbon was prepared by chemical activation of lemon peel with H3PO4 as the active agent. Then, the adsorption behavior of Malachite green dye and Pb(II) ions on the produced activated carbon was studied. Batch process was employed for sorption kinetics and equilibrium studies. Experimental data were fitted to various isotherm models. According to the Langmuir model, the maximum adsorption capacities of Malachite green dye and Pb(II) ions were found to be 66.67 and 90.91 mg g-1, respectively, at room temperature. Kinetic studies showed the adsorption process followed a pseudo second-order rate model. The sorption kinetics were controlled by intra-particle diffusion. The results indicated that the produced activated carbon can be economically and effectively used as an adsorbent for the removal of Malachite green dye and Pb(II) ions from wastewaters.

METHANE DRY REFORMING OVER Ni SUPPORTED ON PINE SAWDUST ACTIVATED CARBON: EFFECTS OF SUPPORT SURFACE PROPERTIES AND METAL LOADING

The influence of metal loading and support surface functional groups (SFG) on methane dry reforming (MDR) over Ni catalysts supported on pine-sawdust derived activated carbon were studied. Using pine sawdust as the catalyst support precursor, the smallest variety and lowest concentration of SFG led to best Ni dispersion and highest catalytic activity, which increased with Ni loading up to 3 Ni atoms nm-2. At higher Ni loading, the formation of large metal aggregates was observed, consistent with a lower "apparen" surface area and a decrease in catalytic activity. The H2/CO ratio rose with increasing reaction temperature, indicating that increasingly important side reactions were taking place in addition to MDR.

Immersion enthalpy variation of surface-modified mineral activated carbon in lead (II) aqueous solution adsorption: the relation between immersion enthalpy and adsorption capacity

An activated carbon was obtained by chemical activation with phosphoric acid, CM, from a mineral carbon. Afterwards, the carbon was modified with 2 and 5 molL-1, CMox2 and CMox5 nitric acid solutions to increase the surface acid group contents. Immersion enthalpy at pH 4 values and Pb2+ adsorption isotherms were determined by immersing activated carbons in aqueous solution. The surface area values of the adsorbents and total pore volume were approximately 560 m².g-1 and 0.36 cm³g-1, respectively. As regards chemical characteristics, activated carbons had higher acid sites content, 0.92-2.42 meq g-1, than basic sites, 0.63-0.12 meq g-1. pH values were between 7.4 and 4.5 at the point of zero charge, pH PZC. The adsorbed quantity of Pb2+ and the immersion enthalpy in solution of different pH values for CM activated carbon showed that the values are the highest for pH 4, 15.7 mgg-1 and 27.6 Jg-1 respectively. Pb2+ adsorption isotherms and immersion enthalpy were determined for modified activated carbons and the highest values were obtained for the activated carbon that showed the highest content of total acid sites on the surface.

Design of an adsorbent employing activated carbon fiber to remove lead

Zorflex® activated carbon fibers (ACF), reference FM100 198B, are used before and after an oxidizing procedure with H3PO4 to study the adsorption of Pb2+. The point of zero charge was determined for the modified and unmodified fiber giving values of 2.3 and 4.3, respectively. After oxidizing the ACF, the fiber showed to have a greater Pb2+ adsorption capacity in comparison with the unmodified fiber, which is related with the acid sites increase, where lead was mainly adsorbed. Determination of the BET area was carried out by nitrogen physisorption at 77K. ACFs presented superficial areas between 1000 and 1500 m²/g showing mostly, a microporous structure. The preliminary design of an adsorbent using the modified fiber is presented where the fiber superior physicochemical properties over the unmodified one are observed.

Synthesis and characterization of activated carbon fibers from Kevlar

Kevlar [poly (p-phenilylene terephtalamide)], was used as a precursor in the preparation of activated carbon fibers. For this intention, physical and chemical activations were carried out. Activated fibers were physically prepared from the carbonization of the Kevlar and its later activation with CO2 and steam of water, by the other hand; the chemically activated fibers were obtained by means of the impregnation of the material with phosphoric acid and their later carbonization. Different conditions were used and preliminary analyses of the precursor were taken into account (TGA-DTA / IR). The resulting fibers were characterized by N2 (77K) adsorption, infrared spectroscopy, SEM, and immersion calorimetry. Yields and Burn off were also evaluated. The results shows that if you want to synthesize activated carbon fibers from Kevlar strong conditions respect to the commonly used such as water steam, high phosphoric acid concentrations and methods of impregnation are the ones who allows the development of optimal surface areas and pore volumes.

Physicochemical and sensory changes in aged sugarcane spirit submitted to filtering with activated carbon filter

Sugarcane spirit is a drink considered as a national symbol of Brazil. It is produced by large producers and by about 30 thousand small and medium home-distilling producers dispersed throughout the country. The copper originating from the home-distillers can become a serious problem since at high concentrations in beverages it may cause serious human health problems. Therefore, the objective of this study was to investigate the influence of the activated carbon used in commercial filters on the physicochemical and sensory characteristics of aged sugarcane spirit. Analyses of copper, dry extract, alcoholic degree, higher alcohols, volatile acids, aldehydes, esters, furfural, and methanol were performed. The sensory evaluation was performed by seven selected trained judges, who analyzed the yellow color, woody aroma and flavor, and intensity of alcoholic aroma and flavor of the cane spirit before and after the filtration process. The sensory tests were carried out using a 9 cm non-structured intensity scale. A reduction was observed in all compounds analyzed physicochemically, except for the esters, which increased after filtration. This increase is probably due to the esterification of the alcohols and acids present. According to the sensory results obtained, a reduction was observed in the intensity of the yellow color, aroma, and wood flavor characteristics, the major characteristics of the aging process.

Influence of functional groups of activated carbon in the anchoring of iron particles by forced hydrolysis and its use to remove hexavalent chromiun from aqueous solutions.

Tesis (Master of Science with orientation in Sustainable Processes) UANL, 2014.

Artificial neural network modeling of phenol adsorption onto barley husks activated carbon in an airlift reactor.

Tesis (Doctor en Ciencias con Orientación en Procesos Sustentables) UANL, 2013.

Studies on Magnetic Iron Oxide Loaded Activated Carbon

The current water treatment technology is oriented towards the removal of contaminants, mostly organic compounds, by activated carbon. Activated carbons are classified as Granular Activated Carbons (GAC) and Powdered Activated Carbons (PAC) on the basis of the particle size of the carbon granules. Powdered carbons are generally less expensive than granular carbon, operating costs with powdered carbon could be lower. Though powdered activated carbon has many advantages over granular carbon, its application in large-scale separation process is limited by difficulty in recovery and regeneration. Deposition of magnetic iron oxide on carbon particles provides a convenient way of recovering the spent carbon from process water. The study deals with the preparation and physico-chemical characterization of magnetic iron oxide loaded activated carbons. The evaluation of absorption properties of magnetic iron oxide loaded activated carbon composites. The target molecules studied were phenol, p-nitro phenol and methylene blue. The feasibility of magnetic separation of iron oxide loaded activated carbons were studied and described in this thesis.

Imaging the structure of activated carbon using aberration corrected TEM

The precise atomic structure of activated carbon is unknown, despite its commercial importance. Here we show that the structure of a commercial activated carbon can be imaged directly using aberration corrected transmission electron microscopy. Images are presented both of the as-produced carbon and of the carbon following heat- treatment at 2000°C. In the 2000°C carbon clear evidence is found for the presence of pentagonal rings, suggesting that the carbons have a fullerene-related structure.