Effect of dentine surface treatment on leakage of root fillings with a glass ionomer sealer.

The purpose of this study was to observe the quality of seal of the glass ionomer cement, Ketac-Endo, after treatment of the root canal wall. The root canals of 140 extracted human teeth were prepared biomechanically. The root canals were treated with either EDTA or received an intracanal dressing of calcium hydroxide or camphorated paramonochlorphenol. The root canals were filled by the lateral condensation technique with gutta-percha points and the sealer Ketac-Endo, or zinc oxide-eugenol cement or Sealapex. The teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly. Sealapex exhibited significantly less leakage than Ketac-Endo or zinc oxide-eugenol cement (P<0.01). The use of EDTA and intermediary dressings reduced significantly (P<0.01) the leakage observed with the zinc oxide-eugenol sealer and Ketac-Endo.

Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.

Microleakage in primary teeth restored by conventional or bonded amalgam technique.

The aim of this in vitro study was to evaluate marginal leakage in class V restorations in primary teeth restored with amalgam, using three different techniques. Thirty maxillary anterior primary teeth, clinically sound and naturally exfoliated, were used. In group 1 (n = 10), two thin layers of a copal varnish (Cavitine) were applied. In group 2 (n = 10), Scotchbond Multi-Purpose Plus, a dual adhesive system, was used according to manufacturer instructions. In group 3 (n = 10), One-Step adhesive system in combination with a low-viscosity resin (Resinomer) were used according to manufacturer instructions. All samples were restored with a high-copper dental amalgam alloy (GS 80, SDI). After restoration, the samples were stored in normal saline at 37 degrees C for 72 h. The specimens were polished, thermocycled (500 cycles, 5 degrees and 55 degrees C, 30-s dwell time) and impermeabilized with fingernail polish to within 1.0 mm of the restoration margins. The teeth were then placed in 0.5% methylene blue for 4 h. Finally, the samples were sectioned and evaluated for marginal leakage. The Kruskal-Wallis test showed that the filled adhesive resin (group 3) had the least microleakage. There was no significant difference between groups 1 and 2.