Ultrasonic degradation of poly(methyl methacrylate-co-alkyl acrylate) copolymers

The copolymers, poly(methyl methacrylate-co-methyl acrylate) (PMMAMA), poly(methyl methacrylate-co-ethyl acrylate) (PMMAEA) and poly(methyl methacrylate-co-butyl acrylate) (PMMABA), of different compositions were synthesized and characterized. The effect of alkyl acrylate content, alkyl group substituents and solvents on the ultrasonic degradation of these copolymers was studied. A model based on continuous distribution kinetics was used to study the kinetics of degradation. The rate coefficients were obtained by fitting the experimental data with the model. The linear dependence of the rate coefficients on the logarithm of the vapor pressure of the solvent indicated that vapor pressure is the crucial parameter that controls the degradation process. The rate of degradation increases with an increase in the alkyl acrylate content. At any particular copolymer composition, the rate of degradation follows the order: PMMAMA > PMMAEA > PMMABA. It was observed that the degradation rate coefficient varies linearly with the mole percentage of the alkyl acrylate in the copolymer.

Mixed saturated-unsaturated alkyl-chain assemblies: Solid solutions of zinc stearate and zinc oleate

The linear saturated stearic acid and the bent mono-unsaturated oleic acid do not mix and form solid solutions. However, the zinc salts of these acids can. From X-ray diffraction and DSC measurements we show that the layered zinc stearate and zinc oleate salts form a homogeneous solid solution at all composition ratios. The solid solutions exhibit a single melting endotherm, with the melting temperature varying linearly with composition but with the enthalpy change showing a minimum. By monitoring features in the infrared spectra that are characteristic of the global conformation of the hydrocarbon chain, and hence can distinguish between stearate and oleate chains, it is shown that solid solution formation is realized by the introduction of gauche defects in a fraction of the stearate chains that are then no longer linear. This fraction increases with oleate concentration. It has also been possible from the spectroscopic measurements to establish a quantitative relation between molecular conformational order and the thermodynamic enthalpy of melting of the solid solutions.

Adsorption of anionic dyes on chitosan grafted poly(alkyl methacrylate)s

Chitosan grafted poly(alkyl methacrylate)s (namely chitosan grafted poly(methyl methacrylate) (ChgPMMA), chitosan grafted poly(ethyl methacrylate)(ChgPEMA), chitosan grafted poly(butyl methacrylate) (ChgPBMA) and chitosan grafted poly(hexyl methacrylate) (ChgPHMA)) were synthesized and characterized by using FT-IR and C-13 NMR techniques. The adsorption batch experiments on these grafted copolymers were conducted by using an anionic sulfonated dye. Orange-G. A pseudo-second-order kinetic model was used to determine the kinetics of adsorption. The effect of grafting, effect of process variables and the effect of different sulfonated anionic dyes (Orange-C, Congo Red, Remazol Brill Blue R and Methyl Blue) on the adsorption kinetics was determined. The Langmuir and Freundlich models were used to fit the adsorption isotherms and from the values of correlation coefficients (R-2), it was observed that the experimental data fits very well to the Langmuir model. The values of the maximum adsorption capacity of the adsorbents follow the order: ChgPMMA > ChgPEMA > ChgPBMA > ChgPHMA > chitosan. (C) 2010 Elsevier B.V. All rights reserved.

Heats of combustion of some symmetrical dialkyl ureas and their corresponding alkyl carbamates

The standard heats of combustion of the disubstituted ureas, N, N′-diheptyl urea, N, N′-dioctyl urea and N, N′-didecyl urea and the carbamates,n-heptyl ammoniumn-heptyl carbamate,n-octylammoniumn-octyl carbamate andn-decyl ammoniumn-decyl carbamate have been determined. The values found are 2353±1·3, 2658·4±1·1, 3268·5±1·7, 2349·8±1·6, 2654·4±1·2, 3264·6±1·8, K.cals. mole−1 respectively. The heats of formation of these compounds have been calculated.

Infrared spectra of substituted benzoyl chlorides and benzoyl bromides. Explanation of the anomalous carbonyl band-splittings

Infrared spectra of substituted benzoyl chlorides and benzoyl bromides have been studied. The extent of splitting of the carbonyl band in benzoyl chlorides varies with substitution. While benzoyl bromide shows the carbonyl band as a single peak, para-nitrobenzoyl bromide shows a doublet. The results are interpreted in terms of intramolecular vibration effects (Fermi resonance). The intense band in the 860–880 cm−1 region in benzoyl chloride and benzoyl bromide has been assigned to the Ph-C stretching vibration.

Ultrasonic degradation of poly (styrene-co-alkyl methacrylate) copolymers

The ultrasonic degradation of poly (styrene-co-methyl methacrylate) (SMMA), poly (styrene-co-ethyl methacrylate) (SEMA) and poly (styrene-co-butyl methacrylate) (SBMA) copolymers of different compositions was studied. The copolymers were synthesized and NMR spectroscopy was used to determine the composition, and the glass transition temperatures were determined by DSC. The reactivity ratios were determined by the Kelen-Tudos method and it indicated that the copolymers were random. The effect of solvent, temperature and copolymer composition on the ultrasonic degradation rate of these copolymers was investigated. A model based on continuous distribution kinetics was employed to study the degradation kinetics. The degradation rate coefficients of the copolymers decreased with an increase in the styrene content in the copolymer. At any particular copolymer composition the rate of degradation follows the order: SBMA >SEMA > SMMA. Thermogravimetric analysis (TGA) of the copolymers was carried in order to assess their thermal stability. The same order of degradation was observed for the thermal degradation of the copolymers as that observed for ultrasonic degradation. (C) 2010 Elsevier B.V. All rights reserved.

Syntheses based on cyclohexadienes. Part 2. Convenient synthesis of 6-alkylsalicylates, 6-alkyl 2,4-dihydroxybenzoate, and 2,5-dialkylresorcinols

A one pot synthesis of 6-alkylsalicylates and 6-alkyl-2,4- dihydroxybenzoates is described. Cycloaddition of 1-methoxycyclohexa-1,4- or 1,3-dienes with alkylpropiolic esters results in the regio-specific formation of 2-alkyl-6-methoxybenzoates. Thus, methyl 2-methoxy-6-methyl benzoate, methyl 2,4-dimethoxy-6-methylbenzoate, methyl 2,5-dimethoxy-6-methylbenzoate, methyl 2-methoxy-4,6-dimethylbenzoate, and ethyl 2-butyl-4,6-dimethoxybenzoate, have been prepared. By making use of this method, the synthesis of two dihydroisocoumarins namely (±)-mellein (12) and (±)-6-methoxy- mellein (14) is described. Employing a similar strategy, a novel route to 2,5-dialkylresorcinols has been developed. Stemphol (24b) and the antibiotic DB2073 (24d) have been synthesized.

Rare earth exchanged (Ce3+, La3+ and RE3+) H-Y zeolites as solid acid catalysts for the synthesis of linear alkyl benzenes

Rare earth exchanged H–Y zeolites were prepared by simple ion exchange methods at 353 K and have been characterized using different physicochemical techniques. A strong peak around 58 ppm in the 27Al{1H} MAS NMR spectra of these zeolites suggests a tetrahedral coordination for the framework aluminium. Small peak at or near 0 ppm is due to hexa-coordinated extra-framework aluminium and a shoulder peak near 30 ppm is a penta-coordinated aluminium species; [Al(OH)4]−. The vapor-phase benzene alkylation with 1-decene and 1-dodecene was investigated with these catalytic systems. Under the reaction conditions of 448 K, benzene/olefin molar ratio of 20 and time on stream 3 h, the most efficient catalyst was CeH–Y which showed more than 70% of olefin conversion with 48.5% 2-phenyldecane and 46.8%, 2-phenyldodecane selectivities with 1-decene and 1-dodecene respectively.

Role of hydroxyl group on the mesomorphism of alkyl glycosides:synthesis and thermal behavior of alkyl 6-deoxy-beta-D-glucopyranosides

A homologous series of alkyl 6-deoxy-beta-D-glucopyranoside amphiphiles was prepared,in an effort to identify the role of hydroxyl group in the mesomorphic behavior of alkyl glycosides. Synthesis was performed by a chlorination of the sugar moiety in alkyl-beta-D-glucopyranosides with methylsulfonyl chloride in DMF, followed by a metal mediated dehalogenation to secure alkyl 6-deoxy-beta-D-glucopyranosides, wherein the alkyl chain length varied from C-9 to C-16. The mesomorphic behavior of these 6-deoxy alkyl glycosides was assessed using polarizing optical microscopy, differential scanning calorimetry and X-ray diffraction method. Whereas the lower homologues exhibited a monotropic SmA phase till sub-ambient temperatures, the higher homologues formed a plastic phase. A partial interdigitized bilaye structure of SmA phase is inferred from experimental d-spacing and computationally derived lengths of the molecules. The results were compared with those of normal alkyl glucopyranosides, retained with hydroxyl groups at C-2-C-6 carbons, and alkyl 2-deoxy-glucopyranosides, devoid of a hydroxyl group at C-2 and the comparison showed important differences in the mesomorphic behavior.(C)2010 Elsevier Ireland Ltd. All rights reserved.

A Novel Synthetic Route For The Preparation Of Ammonium And Alkali-Metal Tetrafluoroborates And Alkyl Substituted Ammonium Tetrafluoroborates Using Pyridinium Tetrafluoroborate As The Precursor

Ammonium and alkali metal tetrafluoroborates have been prepared by the cation exchange reaction of pyridinium tetrafluoroborate with the corresponding hydroxides/halides. The reaction of pyridinium tetrafluoroborate with primary, secondary and tertiary alkyl amines at room temperature gives rise to mono-, di- and tri-alkylammonium tetrafluoroborates, respectively. The yields are good and the samples are of high purity. The products have been characterised by elemental analysis, IR and PMR spectroscopy. The spectral data for most of the compounds are reported for the first time.

Flame retardant polyphosphate esters: 2. Condensation polymers of bisphenol A with alkyl phosphorodichloridates: synthesis, characterization and thermal studies

Polyphosphate esters based on bisphenol A and alkyl phosphorodichloridates have been synthesized and characterized by i.r. and n.m.r. spectroscopy. The molecular weights were calculated from 31P n.m.r. The thermal stability of the polymers were analysed by thermogravimetry.

Structure-Reactivity Correlations of Benzoin Alkyl Ethers. Structures of 2-Methoxy-1,2-diphenylethanone (I) and 2-Isopropoxy-1,2-diphenylethanone (II)

(I): C15H1402, Mr---226.27, triclinic, Pi,a=8.441 (2), b= 10.276 (1), c= 15.342 (2)A, a=91.02 (2), ~ t= 79.26 (2), y= 105.88 (2) °, V=1256.8 (4)A 3, Z=4, D,,= 1.209 (flotation in KI),D x - 1.195 g cm -3, #(Mo, 2 = 0.7107/~) = 0.44 cm -~,F(000) = 480, T= 293 K, R -- 0.060 for 1793 significant reflections. (II): C~THlsO2, Mr= 254.83, orthorhombic, Pca21, a=8.476 (1); b= 16.098 (3), c=10.802(3)A, V=1473.9 (5) A s, Z=4, Dm=1.161 (flotation in KI), Dx= 1.148gem -3, /~(Mo, 2=0.7107 A) =0.41 cm -~, F(000) = 544, T= 293 K, R = 0.071 for 867 significant reflections. Both (I) and (II) crystallize in a cisoid conformation for the carbonyl group and alkoxy groups. Compounds (I) and (II) are photostable on irradiation in the solid state in spite of the favourable conformation of the functional groups for intramolecular H abstraction. Absence of photoreaction of (I)and (II) in the solid state is rationalized in the light of unfavourable intramolecular geometry.

Reactions of tetrahalogeno-o-benzoquinones—Part VII. Reaction of alkyl-2-naphthols with tetrachloro-o-benzoquinone

Reaction of 8-methyl-2-naphthol (4a) with the quinone3 gave a mixture of 8-methyl-2,2-(tetrachlorohenylenedioxy)naphthalen-1(2H)-one (1b) and 8-methyl-1,1-(tetrachloro-o-phenylenedioxy)naphthalen-2(1H)-one (2b) in almost equal amounts. Similarly, reaction of the naphthols (4b), (4d) and (4e) with3 gave the corresponding dienones (1c &2c), (1e &2e) and (1f &2f) in almost equal amounts. Reaction of 8-t-butyl-2-naphthol (4c) with3 gave exclusively 8-t-butyl-2,2-(tetrachloro--henylenedioxy)-naphthalen-1(2H)-one (1d). Oxidation of 3-t-butyl-2-naphthol (4f) with3 gave a mixture of 3-t-butyl-2,2-(tetrachloro-o-phenylendioxy) nephthalene-1(2H)-one(1g) and 3-t-butyl-1,1-(tetrachloro--phenylenedioxy)naphthelen-2 (1H)-one (2g) in the ratio 1∶6. Thus, onlyt-butyl group exherts pronounced steric influence on the rearrangement observed in the reaction of β-naphthol with the quinone3. Structures of all the compounds have been established by spectral data.

Supramolecular Chirality in Organogels: A Detailed Spectroscopic, Morphological, and Rheological Investigation of Gels (and Xerogels) Derived from Alkyl Pyrenyl Urethanes

This Article addresses the formation of chiral supramolecular structures in the organogels derived from chiral organogelator 1R (or 2R), and its mixtures with its enantiomer (1S) and achiral analogue 3 by extensive circular dichroism (CD) spectroscopic measurements. Morphological analysis by atomic force microscopy (AFM) and scanning electron microscopy (SEM) were complemented by the measurements of their bulk properties by thermal stability and rheological studies. Specific molecular recognition events (1/3 vs 2/3) and solvent effects (isooctane vs dodecane) were found to be critical in the formation of chiral aggregates. Theoretical studies were also carried out to understand the interactions responsible for the formation of the superstructures.