Synthesis and electrochemical properties of mesoporous nickel oxide

Mesoporous Ni(OH)(2) is synthesized using sodium dodecyl sulfate as a template and urea as a hydrolysis-controlling agent. Mesoporous NiO with a centralized pore-size distribution is obtained by calcining Ni(OH)(2) at different temperatures. The BET specific surface area reaches 477.7 m(2) g(-1) for NiO calcined at 250 degreesC. Structure characterizations indicate a good mesoporous structure for the nickel oxide samples. Cyclic voltammetry shows the NiO to have good capacitive behaviour due to its unique mesoporous structure when using a large amount of NiO to fabricate the electrode. Compared with NiO prepared by dip-coating and cathodic precipitation methods, mesoporous NiO with a controlled pore structure can be used in much larger amounts to fabricate electrodes and still maintain a high specific capacitance and good capacitive behaviour. (C) 2004 Elsevier B.V. All rights reserved.

Characterisation of xerogels derived from sucrose templated sol-gel synthesis

This work presents the results of the nanostructural characterisation of the effect of sucrose as a template added to a sol derived from a tetraethoxysilane acid catalysed process. By increasing the sucrose template ratio, N-2 adsorption isotherms showed that the xerogel samples changed from a micropore to a mesopore nanostructure as evidenced by the formation of hysteresis at 0.5 partial pressure. In turn, this led to a direct increase in surface areas, pore volumes and average pore sizes. Sucrose has two molecular components of the same molecular weight: D-fructose and D-glucose. D-fructose resulted in the formation of higher pore volumes and pore sizes, while D-glucose formed higher surface area xerogels. Depending of the template ratio employed in the xerogel synthesis, average pore radius ranged from 8.8 to 26 Angstrom, while surface areas increased by over two fold up to 750 m(2) . g(-1). However, pore volumes increased by as much as six fold, from 0.15 to almost 1 cm(3) . g(-1).

Molecular dynamics simulation of the structural and dynamic properties of dioctadecyldimethyl ammoniums in organoclays

The structural and dynamic properties of dioctadecyldimethylammoniums (DODDMA) intercalated into 2:1 layered clays are investigated using isothermal-isobaric (NPT) molecular dynamics (MD) simulation. The simulated results are in reasonably good agreement with the available experimental measurements, such as X-ray diffraction (XRD), atom force microscopy (AFM), Fourier transform infrared (FTIR), and nuclear magnetic resonance (NMR) spectroscopies. The nitrogen atoms are found to be located mainly within two layers close to the clay surface whereas methylene groups form a pseudoquadrilayer structure. The results of tilt angle and order parameter show that interior two-bond segments of alkyl chains prefer an arrangement parallel to the clay surface, whereas the segments toward end groups adopt a random orientation. In addition, the alkyl chains within the layer structure lie almost parallel to the clay surface whereas those out of the layer structure are essentially perpendicular to the surface. The trans conformations are predominant in all cases although extensive gauche conformations are observed, which is in agreement with previous simulations on n-butane. Moreover, an odd-even effect in conformation distributions is observed mainly along the chains close to the head and tail groups. The diffusion constants of both nitrogen atoms and methylene groups in these nanoconfined alkyl chains increase with the temperature and methelene position toward the tail groups.

A comparison of attitudes among purchasers of imported fruit in Guangzhou and Urumqi, China

Research on Chinese consumer behavior is dominated by studies of Chinese consumers as a whole, or studies of consumers in a single city or region. Comparative studies that take into account the cultural, economic and demographic differences between contrasting markets within China are poorly represented in the literature. The widening economic gap between rapidly developing coastal cities and less developed cities in more remote regions provides an opportunity for comparative consumer studies. In this research we compared the responses of buyers of imported fruit in two very different cites, Guangzhou (highly developed) and Urumqi (relatively undeveloped). Results revealed that buyers' beliefs and their evaluation of those beliefs towards the attributes of imported fruit were distinctly different. Factors such as the city's background, consumers' education level and the intended uses explained most of these differences. Results will help to broaden our understanding of Chinese consumer behavior and provide valuable information when formulating marketing strategies. (C) 2003 Elsevier Ltd. All rights reserved.

The fatty acid composition of muscle and adipose tissues from entire and castrated male Boer goats raised in Australia

The fatty acid composition of longissimus thoracis (LT) muscle and adipose tissues (subcutaneous and intermuscular fat) from castrated and entire male Boer goat bucks was investigated. Sixty Boer bucks in groups of between three and five animals were slaughtered at 5, 15, 30, 45, 60, 75, 90 and 105 kg live weight (5 and 15 kg animals were not castrated). The fatty acid composition of LT muscle from castrated and entire Boers was significantly affected by slaughter weight. The fatty acid content of LT muscle and subcutaneous and intermuscular fat from both castrated and entire Boer bucks was primarily composed of oleic acid followed by palmitic and stearic acid. Both oleic and palmitic acid increased with slaughter weight whereas stearic acid decreased. LT muscle from castrated Boer bucks contained higher amounts of desirable fatty acids. In contrast to slaughter weight, castration of Boer bucks resulted in only minor changes in fatty acid composition of adipose tissues. It can be concluded that slaughter weight plays a role in changing the fatty acid composition of LT muscle and adipose tissues from Boer bucks.

Repressor- and activator-type ethylene response factors functioning in jasmonate signaling and disease resistance identified via a genome-wide screen of Arabidopsis transcription factor gene expression

To identify transcription factors (TFs) involved in jasmonate (JA) signaling and plant defense, we screened 1,534 Arabidopsis (Arabidopsis thaliana) TFs by real-time quantitative reverse transcription-PCR for their altered transcript at 6 h following either methyl JA treatment or inoculation with the incompatible pathogen Alternaria brassicicola. We identified 134 TFs that showed a significant change in expression, including many APETALA2/ethylene response factor (AP2/ERF), MYB, WRKY, and NACTF genes with unknown functions. Twenty TF genes were induced by both the pathogen and methyl JA and these included 10 members of the AP2/ERF TF family, primarily from the B1a and B3 subclusters. Functional analysis of the B1a TF AtERF4 revealed that AtERF4 acts as a novel negative regulator of JA-responsive defense gene expression and resistance to the necrotrophic fungal pathogen Fusarium oxysporum and antagonizes JA inhibition of root elongation. In contrast, functional analysis of the B3 TF AtERF2 showed that AtERF2 is a positive regulator of JA-responsive defense genes and resistance to F. oxysporum and enhances JA inhibition of root elongation. Our results suggest that plants coordinately express multiple repressor-and activator-type AP2/ERFs during pathogen challenge to modulate defense gene expression and disease resistance.

Water and nutrient availabilities do not affect lignotuber growth and sprouting ability of three eucalypt species of south-eastern Queensland

Shoot biomass and lignotuber size of seedlings of three eucalypt species, Eucalyptus acmenoides Schauer, E. siderophloia Benth. and Corymbia variegata [syn. E. maculata (F. Muell.)K. D. Hill and L. A. S. Johnson], were measured for glasshouse-grown seedlings established under two water and nutrient regimes. Seedlings were subjected to shoot removal (clipping) at ages from 9 to 19 weeks, and transferred to the high water treatment for a further 8 weeks to assess shoot emergence from lignotubers. Seedling shoot biomass was greater in both the high than the low nutrient and water treatments, but lignotuber diameter was not affected significantly. C. variegata seedlings had the largest lignotuber diameters, followed by E. siderophloia and E. acmenoides, respectively. Although growth of shoots was influenced by nutrient availability, results suggest that species differences in the growth of lignotubers was less affected. It is suggested that lignotuber growth was strongly influenced by genotype. More than 70% of C. variegata seedlings clipped at 9 weeks sprouted, compared with only 5 and 10% of seedlings of E. siderophloia and E. acmenoides, respectively. All C. variegata seedlings sprouted after being clipped at 19 weeks, but < 80% of E. siderophloia and < 60% of E. acmenoides sprouted when clipped at the same age. It was concluded that seedlings forming part of the regeneration stratum in dry sclerophyll forests need to be protected from damage for at least 4 months (for C. variegata) or at least 6 months (for E. siderophloia and E. acmenoides) if they are to survive by sprouting from lignotubers.

The interlayer swelling and molecular packing in organoclays

Understanding the interlayer swelling and molecular packing in organoclays is important to the formation and design of polymer nanocomposites. This paper presents recent experimental and molecular simulation studies on a variety of organoclays that show a linear relationship between the increase of d-spacing and the mass ratio between organic and clay. A denser molecular packing is observed in organoclays containing surfactants with hydroxyl-ethyl units. Moreover, our simulation results show that the head (nitrogen) groups are essentially tethered to the clay surface while the long hydrocarbon chains tend to adopt a layering structure with disordered conformation, which contrasts with the previous assumptions of either the chains lying parallel to the clay surface or being tilted at rather precise angles. (c) 2005 Elsevier Inc. All rights reserved.

Synthesis and characterization of mesoporous nickel oxide and its application to electrochemical capacitor

Mesoporous Ni(OH)(2) was synthesized using cationic surfactant as template and urea as hydrolysis-controlling agent. Mesoporous NiO with centralized pore size distribution was obtained by calcining Ni(OH)(2) at different temperatures. The BET specific surface area reaches 477.7 m(2).g(-1) for NiO calcined at 523 K. Structure characterizations indicate the polycrystalline pore wall of mesoporous nickel oxide. The pore-formation mechanism is also deduced to be quasi-reverse micelle mechanism. Cyclic voltammetry shows the good capacitive behavior of these NiO samples due to its unique mesoporous structure when using large amount of NiO to fabricate electrode. Compared with NiO prepared by dip-coating and cathodic precipitation methods, this mesoporous NiO with controlled pore structure can be used in much larger amount to fabricate the electrode and still maintains high specific capacitance and good capacitive behavior.

Dissolution of porcine incisor pulps in sodium hypochlorite solutions of varying compositions and concentrations

Background: The solubility of dental pulp tissue in sodium hypochlorite has been extensively investigated but results have been inconsistent; due most likely to variations in experimental design, the volume and/or rate of replenishment of the solutions used and the nature of the tissues assessed. Traditionally, the sodium hypochlorite solutions used for endodontic irrigation in Australia have been either Milton or commercial bleach, with Milton being the most common. Recently, a range of Therapeutic Goods Administration (TGA) approved proprietary sodium hypochlorite solutions, which contain surfactant, has become available. Some domestic chlorine bleaches now also contain surfactants. The purpose of this study was to perform new solubility assessments, comparing Milton with new TGA approved products, Hypochlor 1% and Hypochlor 4% forte, and with a domestic bleach containing surfactant (White King). Methods: Ten randomly assigned pulp samples of porcine dental pulp of approximately equal dimensions were immersed in the above solutions, as well as representative concentrations of sodium hydroxide. Time to complete dissolution was measured and assessed statistically. Results: White King 4% showed the shortest dissolution time, closely followed by Hypochlor 4% forte. White King 1% and Hypochlor 1% each took around three times as long to completely dissolve the samples of pulp as their respective 4% concentrations, while Milton took nearly 10 times as long. The sodium hydroxide solutions showed no noticeable dissolution of the pulp samples. Conclusions: The composition and content of sodium hypochlorite solutions had a profound effect on the ability of these solutions to dissolve pulp tissue in vitro. Greater concentrations provided more rapid dissolution of tissue. One per cent solutions with added surfactant and which contained higher concentrations of sodium hydroxide were significantly more effective in dissolution of pulp tissue than Milton.

Structural evolution in a hydrothermal reaction between Nb2O5 and NaOH solution: From Nb2O5 grains to microporous Na2Nb2O6 center dot(2)/3H2O fibers and NaNbO3 cubes

Niobium pentoxide reacts actively with concentrate NaOH solution under hydrothermal conditions at as low as 120 degrees C. The reaction ruptures the corner-sharing of NbO7 decahedra and NbO6 octahedra in the reactant Nb2O5, yielding various niobates, and the structure and composition of the niobates depend on the reaction temperature and time. The morphological evolution of the solid products in the reaction at 180 degrees C is monitored via SEM: the fine Nb2O5 powder aggregates first to irregular bars, and then niobate fibers with an aspect ratio of hundreds form. The fibers are microporous molecular sieve with a monoclinic lattice, Na2Nb2O6 center dot(2)/3H2O. The fibers are a metastable intermediate of this reaction, and they completely convert to the final product NaNbO3 Cubes in the prolonged reaction of 1 h. This study demonstrates that by carefully optimizing the reaction condition, we can selectively fabricate niobate structures of high purity, including the delicate microporous fibers, through a direct reaction between concentrated NaOH solution and Nb2O5. This synthesis route is simple and suitable for the large-scale production of the fibers. The reaction first yields poorly crystallized niobates consisting of edge-sharing NbO6 octahedra, and then the microporous fibers crystallize and grow by assembling NbO6 octahedra or clusters of NbO6 octahedra and NaO6 units. Thus, the selection of the fibril or cubic product is achieved by control of reaction kinetics. Finally, niobates with different structures exhibit remarkable differences in light absorption and photoluminescence properties. Therefore, this study is of importance for developing new functional materials by the wet-chemistry process.