Magnetic and transport relaxation property of La0.85Sr0.15CoO3 single crystals

Here, we present a comprehensive investigation of the dc magnetization and magnetotransport studies on La0.85Sr0.15CoO3 single crystals grown by the optical float zone method. The spin freezing temperature in the ac susceptibility study shifts to lower value at higher dc field and this is well described by the de Almeida-Thouless line which is the characteristic of SG behavior. The Magnetotransport study shows that the sample exhibits a huge negative MR of similar to 70% at 10 K which monotonically decreases with the increase in temperature. Besides, the magnetization and the resistivity relaxation give strong indication that the MR scales with sample's magnetization. In essence, all the present experimental findings evidence the SG behavior of La0.85Sr0.15CoO3 single crystals.

Characterization and magnetic response of multiwall carbon nanotubes filled with iron nanoparticles of different aspect ratios

Three samples of multiwall carbon nanotubes (MWCNT) TF200, TF150 and TF100, where T and F stand for toluene and ferrocene respectively, and numeral denotes the amount (mg) of ferrocene] filled with iron-nanoparticles (Fe-NPs) of different aspect ratios are grown by chemical vapor deposition of toluene-ferrocene mixture. Energy dispersive X-ray analysis shows a systematic variation in the intensities of peak corresponding to Fe, indicating that Fe is present in different amounts in the three MWCNT samples. The lengths of Fe-NPs lie in the range of 200-250; 80-120; and 30-40 nm for TF200, TF150 and TF100, respectively, as estimated statistically from transmission electron microscopy micrographs. However, the diameter of the encapsulated Fe-NPs does not vary significantly for different samples and is 20-30 nm for all samples. Hysteresis loop measurements on these MWCNT samples were done at 10, 150 and 300 K up to an applied field of 1.5 T. At 10 K, values of coercivity are 2584, 2315, and 2251 Oe for TF200, TF150 and TF100 respectively. This is attributed to the strong shape anisotropy of the Fe-NPs and significant dipolar interactions between them. Further, M-H loops reveal that saturation magnetization of TF200 is almost four times that of TF100 at all temperatures.

Interplay of structural distortions, dielectric effects and magnetic order in multiferroic GdMnO3

Multiferroic materials are characterized by simultaneous magnetic and ferroelectric ordering making them good candidates for magneto-electrical applications. We conducted thermal expansion and magnetostriction measurements in magnetic fields up to 14 T on perovskitic GdMnO3 by highresolution capacitive dilatometry in an effort to determine all longitudinal and transversal components of the magnetostriction tensor. Below the ordering temperature T (N) = 42 K, i.e., within the different complex (incommensurate or complex) antiferromagnetic phases, lattice distortions of up to 100 ppm have been found. Although no change of the lattice symmetry occurs, the measurements reveal strong magneto-structural phenomena, especially in the incommensurate sinusoidal antiferromagnetic phase. A strong anisotropy of the magnetoelastic properties was found, in good agreement with the type and propagation vector of the magnetic structure. We demonstrate that our capacitive dilatometry can detect lattice expansion effects and changes of the dielectric permittivity simultaneously because the sample is housed inside the capacitor. A separation of both effects is possible by shielding the sample. Dielectric transitions could be detected by this method and compared to the critical values of H and T in the magnetic phase diagram. Dielectric changes measured at 1 kHz excitation frequency are detected in GdMnO3 at about 180 K, and between 10 K and 25 K in the canted antiferromagnetic structure which is characterized by a complex magnetic order on both the Gd- and Mn-sites.

New rock salt-related oxides Li3M2RuO6 (M=Co, Ni): Synthesis, structure, magnetism and electrochemistry

We describe the synthesis, crystal structure, magnetic and electrochemical characterization of new rock salt-related oxides of formula, Li3M2RuO6 (M=Co, Ni). The M=Co oxide adopts the LiCoO2 (R-3m) structure, where sheets of LiO6 and (Co-2/Ru)O-6 octahedra are alternately stacked along the c-direction. The M=Ni oxide also adopts a similar layered structure related to Li2TiO3, where partial mixing of Li and Ni/Ru atoms lowers the symmetry to monoclinic (C2/c). Magnetic susceptibility measurements reveal that in Li3Co2RuO6, the oxidation states of transition metal ions are Co3+ (S=0), Co2+ (S=1/2) and Ru4+ (S=1), all of them in low-spin configuration and at 10 K, the material orders antiferromagnetically. Analogous Li3Ni2RuO6 presents a ferrimagnetic behavior with a Curie temperature of 100 K. The differences in the magnetic behavior have been explained in terms of differences in the crystal structure. Electrochemical studies correlate well with both magnetic properties and crystal structure. Li-transition metal intermixing may be at the origin of the more impeded oxidation of Li3Ni2RuO6 when compared to Li3CO2RuO6. Interestingly high first charge capacities (between ca. 160 and 180 mAh g(-1)) corresponding to ca. 2/3 of theoretical capacity are reached albeit, in both cases, capacity retention and cyclability are not satisfactory enough to consider these materials as alternatives to LiCoO2. (C) 2013 Elsevier Inc. All rights reserved.

Characterization, charge transport and magnetic properties of multi-walled carbon nanotube-polyvinyl chloride nanocomposites

Multi-walled carbon nanotube (MWCNT)-polyvinyl chloride (PVC) nanocomposites, with MWCNT loading up to 44.4 weight percent (wt%), were prepared by the solvent mixing and casting method. Electron microscopy indicates high degree of dispersion of MWCNT in PVC matrix, achieved by ultrasonication without using any surfactants. Thermogravimetric analysis showed a significant monotonic enhancement in the thermal stability of nanocomposites by increasing the wt% of MWCNT. Electrical conductivity of nanocomposites followed the classical percolation theory and the conductivity prominently improved from 10(-7) to 9 S/cm as the MWCNT loading increased from 0.1 to 44.4 wt%. Low value of electrical percolation threshold similar to 0.2 wt% is achieved which is attributed to high aspect ratio and homogeneous dispersion of MWCNT in PVC. The analysis of the low temperature electrical resistivity data shows that sample of 1.9 wt% follows three dimensional variable range hopping model whereas higher wt% nanocomposite samples follow power law behavior. The magnetization versus applied field data for both bulk MWCNTs and nanocomposite of 44.4 wt% display ferromagnetic behavior with enhanced coercivities of 1.82 and 1.27 kOe at 10 K, respectively. The enhancement in coercivity is due to strong dipolar interaction and shape anisotropy of rod-shaped iron nanoparticles. (C) 2013 Elsevier B.V. All rights reserved.

Synthesis, structural and thermoluminescence properties of YAlO3:Dy3+ nanophosphors

Thermoluminescence properties of YAlO3:Dy3+ nanophosphor prepared by a low temperature solution combustion (SC) method using oxalyl dihydrazide as a fuel were studied and the results were compared to bulk phosphor prepared by solid state (SS) synthesis. Powder X-ray diffraction patterns confirm the orthorhombic phase of SC and SS methods. Rietveld refinement was used to estimate the cell parameters of undoped and Dy3+ doped YAlO3. Scanning electron micrographs reveal dumbbell shape particles. Electron paramagnetic resonance spectra of YAlO3:Dy3+ nanophosphors were studied at 293 K, 77 K and 10 K. Thermoluminescence responses of SC and SS prepared phosphor were studied using gamma irradiation in the dose range 0.1-6 kGy at a warming rate of 1 degrees C s (1) at room temperature (RT). The optimized concentrations of Dy3+ ions in YAlO3 was found to be 3 mol%. The trapping parameters (i. e. activation energy, frequency factor, order of kinetic) of all the individual peaks of the glow curves have been analysed by using Chen's method. The low fading and linear response in the wide range (0.1-1 kGy) suggests the possibility of usage of SC prepared phosphor in dosimeter applications. (C) 2013 Elsevier B. V. All rights reserved.

Large linear magnetoresistance in a GaAs/AlGaAs heterostructure

We report non-saturating linear magnetoresistance (MR) in a two-dimensional electron system (2DES) at a GaAs/AlGaAs heterointerface in the strongly insulating regime. We achieve this by driving the gate voltage below the pinch-off point of the device and operating it in the non-equilibrium regime with high source-drain bias. Remarkably, the magnitude of MR is as large as 500% per Tesla with respect to resistance at zero magnetic field, thus dwarfing most non-magnetic materials which exhibit this linearity. Its primary advantage over most other materials is that both linearity and the enormous magnitude are retained over a broad temperature range (0.3 K to 10 K), thus making it an attractive candidate for cryogenic sensor applications.

Orientation, Size, and Temperature Dependent Ductile Brittle Transition in NiAl Nanowire under Tensile Loading - A Molecular Dynamics Study

In the present paper, thermo-mechanical response of B2-NiAl nanowire along the < 100 >, < 110 >, and < 111 > orientations has been studied using molecular dynamics simulations. Nanowire with cross-sectional dimensions of similar to 20x20 angstrom(2), similar to 25x25 angstrom(2), and similar to 30x30 angstrom(2) and temperature range of 10 K-900 K has been considered. A Combined effect of size, orientation, and temperature on the stress-strain behavior under uniaxial tensile loading has been presented. It has been observed that < 111 > oriented NiAl nanowire that is energetically most stable gives highest yield stress which further reduces with < 110 > and < 100 > orientations. A remarkable ductile brittle transition (DBT) with an increase in temperature has also been reported for all the orientations considered in the present study. The DBT observed for the nanowire has also been compared with the reported DBT of bulk B2-NiAl obtained from experiments. Alternate technique has also been proposed to increase the toughness of a given material especially at lower temperature regions, i.e. below DBT.

Field dependent and disorder-induced nonlinear charge transport in electrochemically doped polypyrrole devices

Electric field activated charge transport is studied in the metal/polymer/metal device structure of electropolymerized polypyrrole down to 10 K with varying carrier density and disorder. Disorder induced nonlinear behaviour is observed in polypyrrole devices grown at room temperature which is correlated to delocalization of states. The slope parameter of currentvoltage characteristics (in log-log scale) increases as the temperature decreases, which indicates the onset of stronger field dependence. The field dependence of mobility becomes dominant as the carrier density decreases. The sharp dip in differential conductance indicates the localization of carriers at low temperatures which reduces the effective number of carriers involved in the transport.

Low temperature giant magnetocaloric effect in multiferroic GdMnO3 single crystals

Magnetocaloric (MC) properties of GdMnO3 single crystals are investigated using magnetic and magneto-thermal measurements. GdMnO3 exhibits a giant MC effect (isothermal change in magnetic entropy (-Delta S-M) similar to 31 J (kg K)(-1) at 7 K and adiabatic change in temperature similar to 10 K at 19 K for magnetic field variation 0-80 kOe). Complex interactions between 3d and 4f magnetic sublattices influence MC properties. The rare-earth antiferromagnetic ordering induces an inverse MC effect (positive Delta S-M) along `a' and `c' axes whereas it's not seen along the `b' axis, revealing complex anisotropic magnetic ordering. The antiferromagnetic ordering possibly changes to ferromagnetic ordering at higher fields.

Ferromagnetism and the effect of free charge carriers on electric polarization in the double perovskite Y2NiMnO6

The double perovskite Y2NiMnO6 displays ferromagnetic transition at T-c approximate to 81 K. The ferromagnetic order at low temperature is confirmed by the saturation value of magnetization (Ms) and also validated by the refined ordered magnetic moment values extracted from neutron powder diffraction data at 10 K. This way, the dominant Mn4+ and Ni2+ cationic ordering is confirmed. The cation-ordered P2(1)/n nuclear structure is revealed by neutron powder diffraction studies at 300 and 10 K. Analysis of the frequency-dependent dielectric constant and equivalent circuit analysis of impedance data take into account the bulk contribution to the total dielectric constant. This reveals an anomaly which coincides with the ferromagnetic transition temperature (T-c). Pyrocurrent measurements register a current flow with onset near T-c and a peak at 57 K that shifts with temperature ramp rate. The extrinsic nature of the observed pyrocurrent is established by employing a special protocol measurement. It is realized that the origin is due to reorientation of electric dipoles created by the free charge carriers and not by spontaneous electric polarization at variance with recently reported magnetism-driven ferroelectricity in this material.

Thermal, magnetic and electrical properties of Tb1-xDyxMnO3 multiferroics

A series of multiferroic materials with the compositional formula, Tb1 - xDyxMnO3 (where x=0, 0.1, 0.2, 0.3 and 0.4) were prepared by the sol gel method. After characterizing the samples structurally, a systematic investigation of specific heat, magnetization and dielectric properties over the temperature range, 4-300 K, was undertaken. Based on these studies, it was found that all the samples exhibit a transition at 40 K and the observed behavior may be attributed to the ordering of Mn3+ ions. Further, all the five samples are found to exhibit a ferroelectric transition in the temperature range 20-24 K. Finally, yet another transition was also exhibited by all the samples at temperatures below 10 K and is attributed to the antiferromagnetic (AF) ordering of rare-earth ionic moments. The magnetic entropy of all the samples was also computed with the help of their heat capacity data. (C) 2015 Elsevier B.V. All rights reserved.

Stabilization of Cu-7 clusters in azide networks: syntheses, structures and magnetic behaviour

Two new azide bridged copper(II) coordination polymer compounds, Cu-7(N-3)(14)(C3H10N2)(C4H13N3)]n (I) and Cu-7(N-3)(14)(C3H10N2)(C5H15N3)(2)](n) (II) where C3H10N2 = 1,2-diaminopropane (1,2-DAP); C4H13N3 = di-ethylenetriamine (DETA); C5H15N3 = N-2-aminoethyl-1,3-propanediamine (AEDAP)] were prepared by employing a room temperature diffusion technique involving three layers. Single crystal studies reveal that both compounds I and II, have similar connectivity forming Cu7 clusters through end-on (EO) bonding of the azide. The Cu-7 clusters are connected through end-to-end (EE) connectivity of the azides forming three-dimensional structures. Magnetic studies confirmed the ferromagnetic interactions within the Cu-7 units and revealed the occurrence of concomitant ferro- and antiferro-magnetic interactions between these clusters. As a result I behaves as a weak-ferromagnet with T-C = 10 K.

Fabrication and properties of TBCCO films via air-atomising spray deposition of thallium-free precursors

The high-field properties of polycrystalline superconducting TlBaCaCuO films fabricated by the incorporation of thallium vapour into air-atomised BaCaCuO precursors are described. Thick films with Tc values in the range 106-111 K have been prepared on polycrystalline yttria-stabilised zirconia substrates. The surface morphology, crystal structure and composition of the films are related to their high-field transport and magnetisation properties. Typical 10 mm × 9 mm films show Jc values > 1×104 A/cm2 at 77 K (0 T). The best film has a Jc=1.3×104 A/cm2 (Ic=3.6 A) at 77 K (0 T). Films prepared on 26 mm×9 mm substrates show typical large-area Jc values > 0.5×104 A/cm2 (77 K, 0 T). A square planar specimen of dimensions 4.3 mm ×4.3 mm exhibited magnetisation Jc values=1.2×105 A/cm2 at 4.2 K (0.1 T), 9.3×104 A/cm2 at 10 K (0.1 T), 3.3×104 A/ cm2 at 4 K (8 T), and 1.6×104 A/cm2 at 10 K (8 T). © 1994.

Electrical and field emission investigation of individual carbon nanotubes from plasma enhanced chemical vapour deposition

Plasma enhanced chemical vapour deposition (PECVD) is a controlled technique for the production of vertically aligned multiwall carbon nanotubes for field emission applications. In this paper, we investigate the electrical properties of individual carbon nanotubes which is important for designing field emission devices. PECVD nanotubes exhibit a room temperature resistance of 1-10 kΩ/μm length (resistivity 10-6 to 10-5 Ω m) and have a maximum current carrying capability of 0.2-2 mA (current density 107-108 A/cm2). The field emission characteristics show that the field enhancement of the structures is strongly related to the geometry (height/radius) of the structures and maximum emission currents of ∼ 10 μA were obtained. The failure of nanotubes under field emission is also discussed. © 2002 Elsevier Science B.V. All rights reserved.