Strength prediction of adhesively-bonded scarf repairs in composite structures under bending

This work reports on the experimental and numerical study of the bending behaviour of two-dimensional adhesively-bonded scarf repairs of carbon-epoxy laminates, bonded with the ductile adhesive Araldite 2015®. Scarf angles varying from 2 to 45º were tested. The experimental work performed was used to validate a numerical Finite Element analysis using ABAQUS® and a methodology developed by the authors to predict the strength of bonded assemblies. This methodology consists on replacing the adhesive layer by cohesive elements, including mixed-mode criteria to deal with the mixed-mode behaviour usually observed in structures. Trapezoidal laws in pure modes I and II were used to account for the ductility of the adhesive used. The cohesive laws in pure modes I and II were determined with Double Cantilever Beam and End-Notched Flexure tests, respectively, using an inverse method. Since in the experiments interlaminar and transverse intralaminar failures of the carbon-epoxy components also occurred in some regions, cohesive laws to simulate these failure modes were also obtained experimentally with a similar procedure. A good correlation with the experiments was found on the elastic stiffness, maximum load and failure mode of the repairs, showing that this methodology simulates accurately the mechanical behaviour of bonded assemblies.

Buckling strength of adhesively-bonded single and double-strap repairs on carbon-epoxy structures

This work reports on an experimental and finite element method (FEM) parametric study of adhesively-bonded single and double-strap repairs on carbon-epoxy structures under buckling unrestrained compression. The influence of the overlap length and patch thickness was evaluated. This loading gains a particular significance from the additional characteristic mechanisms of structures under compression, such as fibres microbuckling, for buckling restrained structures, or global buckling of the assembly, if no transverse restriction exists. The FEM analysis is based on the use of cohesive elements including mixed-mode criteria to simulate a cohesive fracture of the adhesive layer. Trapezoidal laws in pure modes I and II were used to account for the ductility of most structural adhesives. These laws were estimated for the adhesive used from double cantilever beam (DCB) and end-notched flexure (ENF) tests, respectively, using an inverse technique. The pure mode III cohesive law was equalled to the pure mode II one. Compression failure in the laminates was predicted using a stress-based criterion. The accurate FEM predictions open a good prospect for the reduction of the extensive experimentation in the design of carbon-epoxy repairs. Design principles were also established for these repairs under buckling.

Strength prediction and experimental validation of adhesive joints including polyethylene, carbon-epoxy and aluminium adherends

Polyolefins are especially difficult to bond due to their non-polar, non-porous and chemically inert surfaces. Acrylic adhesives used in industry are particularly suited to bond these materials, including many grades of polypropylene (PP) and polyethylene (PE), without special surface preparation. In this work, the tensile strength of single-lap PE and mixed joints bonded with an acrylic adhesive was investigated. The mixed joints included PE with aluminium (AL) or carbon fibre reinforced plastic (CFRP) substrates. The PE substrates were only cleaned with isopropanol, which assured cohesive failures. For the PE CFRP joints, three different surfaces preparations were employed for the CFRP substrates: cleaning with acetone, abrasion with 100 grit sand paper and peel-ply finishing. In the PE AL joints, the AL bonding surfaces were prepared by the following methods: cleaning with acetone, abrasion with 180 and 320 grit sand papers, grit blasting and chemical etching with chromic acid. After abrasion of the CFRP and AL substrates, the surfaces were always cleaned with acetone. The tensile strengths were compared with numerical results from ABAQUS® and a mixed mode (I+II) cohesive damage model. A good agreement was found between the experimental and numerical results, except for the PE AL joints, since the AL surface treatments were not found to be effective.

Shear modulus and strength of an acrylic adhesive by the notched plate shear method (Arcan) and the thick adherend shear test (TAST)

In this work, the shear modulus and strength of the acrylic adhesive 3M® DP 8005 was evaluated by two different methods: the Thick Adherend Shear Test (TAST) and the Notched Plate Shear Method (Arcan). However, TAST standards advise the use of a special extensometer attached to the specimen, which requires a very experienced technician. In the present study, the adhesive shear displacement for the TAST was measured using an optical technique, and also with a conventional inductive extensometer of 25 mm used for tensile tests. This allowed for an assessment of suitability of using a conventional extensometer to measure this parameter. Since the results obtained by the two techniques are identical, it can be concluded that using a conventional extensometer is a valid option to obtain the shear modulus for the particular adhesive used. In the Arcan tests, the adhesive shear displacement was only measured using the optical technique. This work also aimed the comparison of shear modulus and strength obtained by the TAST and Arcan test methods.

Strength improvement of adhesively-bonded joints using a reverse-bent geometry

Adhesive bonding of components has become more efficient in recent years due to the developments in adhesive technology, which has resulted in higher peel and shear strengths, and also in allowable ductility up to failure. As a result, fastening and riveting methods are being progressively replaced by adhesive bonding, allowing a big step towards stronger and lighter unions. However, single-lap bonded joints still generate substantial peel and shear stress concentrations at the overlap edges that can be harmful to the structure, especially when using brittle adhesives that do not allow plasticization in these regions. In this work, a numerical and experimental study is performed to evaluate the feasibility of bending the adherends at the ends of the overlap for the strength improvement of single-lap aluminium joints bonded with a brittle and a ductile adhesive. Different combinations of joint eccentricity were tested, including absence of eccentricity, allowing the optimization of the joint. A Finite Element stress and failure analysis in ABAQUS® was also carried out to provide a better understanding of the bent configuration. Results showed a major advantage of using the proposed modification for the brittle adhesive, but the joints with the ductile adhesive were not much affected by the bending technique.

Strength prediction of single- and double-lap joints by standard and extended finite element modelling

The structural integrity of multi-component structures is usually determined by the strength and durability of their unions. Adhesive bonding is often chosen over welding, riveting and bolting, due to the reduction of stress concentrations, reduced weight penalty and easy manufacturing, amongst other issues. In the past decades, the Finite Element Method (FEM) has been used for the simulation and strength prediction of bonded structures, by strength of materials or fracture mechanics-based criteria. Cohesive-zone models (CZMs) have already proved to be an effective tool in modelling damage growth, surpassing a few limitations of the aforementioned techniques. Despite this fact, they still suffer from the restriction of damage growth only at predefined growth paths. The eXtended Finite Element Method (XFEM) is a recent improvement of the FEM, developed to allow the growth of discontinuities within bulk solids along an arbitrary path, by enriching degrees of freedom with special displacement functions, thus overcoming the main restriction of CZMs. These two techniques were tested to simulate adhesively bonded single- and double-lap joints. The comparative evaluation of the two methods showed their capabilities and/or limitations for this specific purpose.

Effect of hole drilling at the overlap on the strength of single-lap joints

Bonded unions are gaining importance in many fields of manufacturing owing to a significant number of advantages to the traditional fastening, riveting, bolting and welding techniques. Between the available bonding configurations, the single-lap joint is the most commonly used and studied by the scientific community due to its simplicity, although it endures significant bending due to the non-collinear load path, which negatively affects its load bearing capabilities. The use of material or geometric changes in single-lap joints is widely documented in the literature to reduce this handicap, acting by reduction of peel and shear peak stresses at the damage initiation sites in structures or alterations of the failure mechanism emerging from local modifications. In this work, the effect of hole drilling at the overlap on the strength of single-lap joints was analyzed experimentally with two main purposes: (1) to check whether or not the anchorage effect of the adhesive within the holes is more preponderant than the stress concentrations near the holes, arising from the sharp edges, and modification of the joints straining behaviour (strength improvement or reduction, respectively) and (2) picturing a real scenario on which the components to be bonded are modified by some external factor (e.g. retrofitting of decaying/old-fashioned fastened unions). Tests were made with two adhesives (a brittle and a ductile one) varying the adherend thickness and the number, layout and diameter of the holes. Experimental testing showed that the joints strength never increases from the un-modified condition, showing a varying degree of weakening, depending on the selected adhesive and hole drilling configuration.

The effect of superplasticizers on the workability and compressive strength of concrete made with fine recycled concrete aggregates

The reuse of structural concrete elements to produce new concrete aggregates is accepted as an alternative to dumping them and is favourable to the sustainability of natural reserves. Even though the construction sector is familiar with the use of coarse recycled concrete aggregates, the recycled concrete fines are classified as less noble resources. This research sets out to limit the disadvantages associated with the performance of concrete containing fine recycled concrete aggregates through the use of superplasticisers. Two types of latest generation superplasticisers were used that differ in terms of water reduction capacity and robustness, and the workability, density and compressive strength of each of the compositions analysed were then compared: a reference concrete, with no plasticisers, and concrete mixes with the superplasticisers. For each concrete family mixes with 0%, 10%, 30%, 50% and 100% replacement ratios of fine natural aggregates (FNA) by fine recycled concrete aggregates (FRA) were analysed. Concrete with incorporation of recycled aggregates was found to have poorer relative performance. The mechanical performance of concrete with recycled aggregates and superplasticisers was generally superior to that of the reference concrete with no admixtures and of conventional concrete with lower performance superplasticisers.

Acute pulmonary histoplasmosis and first isolation of Histoplasma capsulatum from soil of Rio Grande do Sul, Brazil

A case of acute pulmonary histoplasmosis, where the clinical histoiy and epidemiological data led to the identification of H. capsulatum natural source, is described. Specimens of spleen and liver, obtained after intraperitonial inoculation in mice, grew H. capsulatum in culture from the soil of rural area of General Câmara, by the first time in Rio Grande do Sul.

Land use/ land cover change and its impact on soil erosion process in Begnas Tal Rupa Tal watershed using geospatial tools, Kaski district, Nepal

Dissertation submitted in partial fulfilment of the requirements for the Degree of Master of Science in Geospatial Technologies

On sampling collection procedure effectiveness for forest soil characterization

One of the most important measures to prevent wild forest fires is the use of prescribed and controlled burning actions as it reduce the fuel mass availability. The impact of these management activities on soil physical and chemical properties varies according to the type of both soil and vegetation. Decisions in forest management plans are often based on the results obtained from soil-monitoring campaigns. Those campaigns are often man-labor intensive and expensive. In this paper we have successfully used the multivariate statistical technique Robust Principal Analysis Compounds (ROBPCA) to investigate on the sampling procedure effectiveness for two different methodologies, in order to reflect on the possibility of simplifying and reduce the sampling collection process and its auxiliary laboratory analysis work towards a cost-effective and competent forest soil characterization.

Insignificant impact of prescribed fire on surface soil in a Pinus pinaster plantation, northern Portugal

Following a prescribed fire in a Pinus pinaster forest site located in the north-west Portugal, monitoring of any changes in selected soil characteristics and soil hydrology was undertaken to assess the effects of burning on the following: pH, electrical conductivity, water content, organic carbon and porosity. Thirty plots were established on a regular grid. At each sample plot before and after the fire, samples were collected (disturbed samples from depths of 0-1cm and 1-5cm; undisturbed core samples from 0-5cm). The results indicate that there was no measurable impact on the properties of the soil following this carefully conducted prescribed fire. The fire only affected the litter layer, as intended. Confirmation of this minimal impact on the soil was provided by regrowth of grasses and herbs already occurring two months after the fire. The implication is, therefore, that provided this wildfire-risk reduction strategy is carried out under existing strict guidelines, any impact on soil quality will be minimal.

Soil erosion after forest fires: evaluation of mitigation measures applied to drainage channels in the northwest of Portugal

The development and implementation of measures which promote the reduction of the impacts of forest fires on soils is imperative and should be part of any strategy for forest and soil preservation and recovery, especially considering the actual scenario of continuous growth in the number of fires and burnt area. Consequently, with the dendrocaustologic reality that has characterized the Portuguese mainland in recent decades, a research project promoted by the Center for the Study of Geography and Spatial Planning (CEGOT) was implemented with the objective of applying several erosion mitigation measures in a burned area of the Peneda-Geres National Park in NW Portugal. This paper therefore seeks to present the measures applied in the study area within the project Soil Protec, relating to triggered channel processes and the results of preliminary observations concerning the evaluation of the effectiveness of erosion mitigation measures implemented, as well as their cost/benefit ratio.

Fuzzy modelling of prescribed burning effects on soil physical properties

This paper presents the preliminary work of an approach where Fuzzy Boolean Nets (FBN) are being used to extract qualitative knowledge regarding the effect of prescribed fire burning on soil chemical physical properties. FBN were chosen due to the scarcity on available quantitative data.

Study on the changes of soil chemical characteristics as result of prescribed fire

Every year, particularly during the summer period, the Portuguese forests are devastated by forest fire that destroys their ecosystems. So in order to prevent these forest fires, public and private authorities frequently use methods for the reduction of combustible mass as the prescribed fire and the mechanical vegetation pruning. All of these methods of prevention of forest fires alter the vegetation layer and/or soil [1-2]. This work aimed the study of the variation of some chemical characteristics of soil that suffered prescribed fire. The studied an area was located in the Serra of Cabreira (Figure 1) with 54.6 ha. Twenty sampling points were randomly selected and samples were collected with a shovel before, just after the prescribed fire, and 125 and 196 days after that event. The parameters that were studied were: pH, soil moisture, organic matter and iron, magnesium and potassium total concentration. All the analysis followed International Standard Methodologies. This work allowed to conclude that: a) after the prescribed fire; i) the pH remained practically equal to the the initial value; ii) occurred a slight increase of the average of the organic matter contents and iron total contents; b) at the end of the sampling period compared to the initial values; i) the pH didn´t change significantly; ii) the average of the contents of organic matter decreased; and iii) the average of the total contents of Fe, Mg and K increased.