Influence of the solution pH on the morphological, structural and electrical properties of Bi3.50La0.50Ti3O12 thin films obtained by the polymeric precursor method

Lanthanum-doped Bi4Ti3O12 thin films (BLT) were deposited on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution. The spin-coated films were specular, crack-free and crystalline after annealing at 700 degrees C for 2 h. Crystallinity and morphological evaluation were examined by X ray diffraction (YRD) and atomic force microscopy (AFM). The stability of the formed complex is of extreme importance for the formation of the perovskite phase. Films obtained from acid pH solution present elongated grains around 200 ran in size, whereas films obtained from basic solution present a dense microstructure with spherical grains (100 nm). The dielectric and ferroelectric properties of the BLT films are strongly affected by the solution pH. The hysteresis loops are fully saturated with a remnant polarization and coercive voltage of P-r=20.2 mu C/cm(2) and V-c = 1.35 V and P-r= 15 mu C/cm(2) and V-c = 1.69 V for the films obtained from basic and acid solutions, respectively. (C) 2005 Elsevier B.V. All rights reserved.

Investigation of the electrical properties of SnO2 varistor system using impedance spectroscopy

The electrical properties of tin oxide varistors doped with CoO, Nb2O5 and Cr2O3, were investigated using the impedance spectroscopy technique with the temperature ranging from 25 to 400 degrees C. The impedance data, represented by means of Nyquist diagrams, show two time constants with different activation energies, one at low frequencies and the other at high frequencies. These activation energies were associated with the adsorption and reaction of O-2 species at the grain boundary interface. The Arrhenius plots show two slopes with a turnover at 200 degrees C for both the higher and lower frequency time constants. This behavior can be related with the decrease of minor charge carrier density. The barrier formation mechanism was associated with the presence of Cr-Sn at the surface, which promotes the adsorption of the O' and O species which are in turn proposed as being responsible for the barrier formation. (C) 1998 American Institute of Physics. [S0021-8979(98)04719-7]

THEORY OF ELECTRICAL CHARACTERISTICS OF A SCHOTTKY-BARRIER HAVING EXPONENTIALLY DISTRIBUTED IMPURITY STATES AND METAL-INSULATOR METAL STRUCTURES

The metal-insulator or metal-amorphous semiconductor blocking contact is still not well understood. Here, we discuss the steady state characteristics of a non-intimate metal-insulator Schottky barrier. We consider an exponential distribution (in energy) of impurity states in addition to impurity states at a single energy level within the depletion region. We present analytical expressions for the electrical potential, field, thickness of depletion region, capacitance, and charge accumulated in the depletion region. We also discuss ln I versus V(ap) data. Finally, we compare the characteristics in three cases: (i) impurity states at only a single energy level; (ii) uniform energy distribution of impurity states; and (iii) exponential energy distribution of impurity states.In general, the electrical characteristics of Schottky barriers and metal-insulator-metal structures with Schottky barriers depend strongly on the energy distribution of impurity states.

THEORY OF NON-STEADY-STATE ELECTRICAL CHARACTERISTICS OF METAL-INSULATOR-METAL STRUCTURES WITH SCHOTTKY BARRIERS AND UNIFORMLY DISTRIBUTED INTERFACE IMPURITY STATES

The metal-insulator (or amorphous semiconductor) blocking contact is still not well understood. In the present paper, we discuss the non steady state characteristics of Metal-lnsulator-Metal Structure with non-intimate blocking contacts (i.e. Metal-Oxide-Insulator-Metal Structure). We consider a uniform distribution (in energy) of impurity states in addition to impurity states at a single energy level within the depletion region. We discuss thermal as well as isothermal characteristics and present expressions for the temperature of maximum current (T-m) and a method to calculate the density of uniformly distributed impurity states. The variation of mobility with electrical field has also been considered. Finally we plot the theoretical curves under different conditions. The present results are closing into available experimental results.

Montmorillonite (MMT) effect on the structure of poly(oxyethylene) (PEO)-MMT nanocomposites and silica-PEO-MMT hybrid materials

In this work we report the effects of incorporation of variable amounts (0.5-25%w/w) of montmorillonite in poly(oxyethylene) based materials in order to decrease the polymer crystallinity. Two different classes of materials were studied: silica-poly(oxyethylene)-montmorillonite hybrids prepared by the sol-gel route and poly(oxyethylene)-montmorillonite nanocomposites prepared by mixing the dry clay or the clay aqueous suspension into the melt poly(oxyethylene). The effects of monternorillonite loading on the poly(oxyethylene) crystallization control and on the nanostructural features were investigated by X-ray powder diffraction, small-angle X-ray scattering and differential scanning calorimetry. Experimental results show that free montmorillonite layers coexist with open aggregates and tactoids in the poly(oxyethylene)-montmorillonite nanocomposites, with different features depending on the filler proportion and preparation route. The intercalation of polymer chains in montmorillonite galleries markedly hinders the crystallization of the poly(oxyethylene) matrix. For hybrids materials the silica phase favors the exfoliation of montmorillonite tactoids, so that samples are predominantly constituted by dispersed platelets. (c) 2006 Elsevier B.V. All rights reserved.

Effect of Ta2O5 doping on the electrical properties of 0.99SnO(2)center dot 0.01CoO ceramic

The effect of Ta2O5 doping in 0.99SnO(2). 0.01CoO on the microstructure and electrical properties of this ceramic were analyzed in this study. The grain size was found to decrease from 6.87 mu m to 5.68 mu m when the Ta2O5 concentration increased from 0.050 to 0.075 mol%. DC electrical characterization showed a dramatic increase in the current loss and decrease in the non-linear coefficient with the increase of the Ta2O5 concentration. The conduction mechanism is by thermionic emission and the potential barriers are of Schottky type, separated by a thin film. (C) 2000 Kluwer Academic Publishers.

Structural and electrical characterization of semiconducting barium-lead-titanate ceramics

BaTiO3 is usually doped to achieve the temperature stability required by device applications, as well as to obtain a large positive temperature coefficient anomaly of resistivity (PTCR). Uniform distribution of dopants among the submicron dielectric particles is the key for optimal control of grain size and microstructure to maintain a high reliability. The system Ba0.84Pb0.16TiO3 was synthesized from high purity BaCO3, TiO2, PbO oxide powders as raw materials. Sb2O3, MnSO4 and ZnO were used as dopants and Al2O3, TiO2 and SiO2 as grain growth controllers. Phase composition was analyzed by using XRD and the microstructure was investigated by SEM. EDS attached to SEM was used to analyze phase composition specially related to abnormal grain growth. Electrical resistivities were measured as a function of temperature and the PTCR effect characterized by an abrupt increase on resistivity.

Effect of Fe2O3 doping on the electrical properties of a SnO2 based varistor

The effect of Fe2O3 addition on the densification and electrical properties of the (0.9895 - x) SnO2 + 0.01CoO + 0.005Nb(2)O(5) + xFe(2)O(3) system, where x = 0.005 or 0.01, was considered in this study. The samples were sintered at 1300degreesC for 2 h. Microstructure analysis by scanning electron microscopy showed that the effect of Fe2O3 addition is to decrease the SnO2 grain size. J x E curves indicated that the system exhibit a varistor behavior and the effect of Fe2O3 is to increase both, the non-linear coefficient (alpha) and the breakdown voltage (E-r). Considering the Schottky thermionic emission model the potential height and width were estimated. Small amount addition of Fe2O3 to the basic system increases both the potential barrier height and width. (C) 2002 Kluwer Academic Publishers.

Effect of the heat flux direction on electrical properties of SrBi2Nb2O9 thin films crystallized using a microwave oven

Ferroelectric SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by spin coating onto Pt/Ti/SiO2/Si substrate and crystallized using a domestic microwave oven. It was studied the influence of the heat flux direction and the duration of the thermal treatment on the films crystallization. An element with high dielectric loss, a SiC susceptor, was used to absorb the microwave energy and transfers the heat to the film. Influence of the susceptor position to the sample crystallization was verified, the susceptor was, placed or below the substrate or above the film. The SBN perovskite phase was observed after a thermal treatment at 700 degreesC for 10 min when the susceptor was placed below the substrate and for 30 min when the susceptor was placed above the film. Electrical measurements revealed that the film crystallized at 700 degreesC for 10 min, with the susceptor placed below the film, presented dielectric constant, dielectric loss, remanent polarization and coercive field of, 67, 0.011, 4.2 muC/cm(2) and 27.5 kV/cm, respectively. When the films were crystallized at 700 degreesC for 30 min, with the susceptor placed above the film, the dielectric constant was 115 and the dissipation factor was around of 0.033, remanent polarization and coercive field were 10.8 muC/cm(2) and 170 kV/cm, respectively. (C) 2003 Elsevier B.V. All rights reserved.

Huge values of room-temperature dielectric constants in pellets of poly(3-methylthiophene)

Room temperature data of impedance and phase angle in pellets of electrochemically synthesized ClO4- doped poly(3-methylthiophene) (P3MT) were analyzed assuming the sample being represented by a parallel resistor-capacitor (RC) circuit or by a series RC circuit. The last assumption proved to be the correct one, and to confirm it we use the sample as the RC component of a resistor-capacitor-inductor series resonator. We discuss the possibility of this RC series behavior to be due to a charge-density wave characteristic also evidenced from the huge values of the low-frequency dielectric constant of the system.

The role of oxygen vacancies on the microstructure development and on the electrical properties of SnO2-based varistors

Variations on the microstructure development and on the electrical properties of SnO2-based varistors are discussed on the basis of the oxygen vacancies created or annihilated by the presence of different additives. Electron paramagnetic resonance (EPR) analysis of sintered samples evidenced a substantial increase in the paramagnetic oxygen vacancies concentration when Nb2O5 is added to the SnO2 center dot Co3O4 system. on the other hand, the observed diminution in the concentration of such species after the addition of Fe2O3 indicates solid solution formation. The quantification of paramagnetic oxygen vacancies allowed to confirm the proposed substitutions taking place in the lattice during sintering. These findings are supported by scanning electron microscopy, by density measurements and by current density versus electric field curves. The characterization of secondary phases through EDS assisted SEM and TEM is also reported in this work.

Synthesis and electrical characterization of tungsten doped Pb(Zr0.53Ti0.47)O-3 ceramics obtained from a hybrid process

Pure and W-doped PZT ceramics (PZT and PZTW) were prepared by a hybrid process consisting in the association of polymeric precursor and partial oxalate methods. The phase formation was investigated by simultaneous thermal analysis (TG/DSC) and X-ray diffraction (XRD). The effect of W doping PZT and their electrical properties was evaluated. Substitution of W by Ti leads to an increase of Curie temperature and broadening of dielectric constant. A typical hysteresis loop was observed at room temperature and the remnant polarization was increased with the content of W. (c) 2007 Elsevier B.V. All rights reserved.

Influence of ionic interactions on the photoinduced Birefringence of poly[1-[4-(3-carboxy-4 hydroxyphenylazo) benzene sulfonamido]-1 2-ethanediyl, sodium salt] films

Electrostatic interactions govern most properties of polyelectrolyte films, as in the photoinduced bire-fringence of azo-containing polymers. In this paper we report a systematic investigation of optical storage characteristics of cast and layer-by-layer (LbL) films of poly[1 -[4-(3-carboxy-4 hydroxypheny-lazo) benzene sulfonamido]-1,2-ethanediyl, sodium salt] (PAZO). Birefringence was photoinduced faster in PAZO cast films prepared at high pHs, with the characteristic writing times decreasing almost linearly with the pH in the range between 4 and 9. This was attributed to an increased free volume for the azochromophores with the enhanced electrostatic repulsion in PAZO charged to a greater extent. In contrast, in LbL films of PAZO alternated with poly(allylamine hydrochloride) (PAH), the electrostatic interactions between the oppositely charged polymers hampered photoisomerization and molecular rearrangement, thus leading to a slower writing kinetics for highly charged PAH or PAZO.

Voltammetric sensor for sodium nitroprusside determination in biological fluids using films of poly-L-lysine

Sodium nitroprusside (NP), a commercial vasodilator, can be pre-concentrated on vitreous carbon electrode modified by films of 97.5%: 2.5% Poly-L-lysine (PLL): glutaraldehyde (GA). This coating gives acceptable anion exchange properties whilst giving the required improvement of adhesion to the glassy carbon electrode surface. Linear response range and detection limit on nitroprusside in B-R buffer pH 4.0, were 1 x 10(-6) to 2 x 10-(5) mol L-1 and 1 x 10(-7) mol L-1, respectively. The repeatability of the proposed sensor, evaluated in term of relative standard deviation, was measured as 4.1% for 10 experiments. The voltammetric sensor was directly applied to determination of nitroprusside in human plasma and urine samples and the average recovery for these samples was around 95-97% without any pre treatment.

Electrical characterization of SnO2 : Sb ultrathin films obtained by controlled thickness deposition

A representative study is reported on the electrical properties of SnO2: Sb. ultrathin films (thickness of 40-70 nm) produced by a deposition method based on aqueous colloidal suspensions of 3-5 nm crystalline oxides. The results revealed the films' electrical behavior in a range of 10-300 K, showing a strong dependence on dopant incorporation, with minimum resistivity values in 10 mol % of Sb content. All the samples displayed semiconductor behavior, but the transport mechanism showed a strong dependence on thickness, making it difficult to fit it to well-known models. In thicker films, the mechanism proved to be an intermediary system, with thermally activated and hopping features. Electron hopping was estimated in the range of 0.4-1.9 nm, i.e., in the same order as the particle size. (c) 2007 American Institute of Physics.