Influence of alumina content on green machined electrical porcelain

The effect of alumina content on the mechanical strength of electrical porcelain manufactured by green machining of isostatically pressed blanks was examined with a view to attaining optimal mechanical properties at low sintering temperatures. Porcelain compositions were formulated with four different alumina contents, maintaining the same proportion of the other materials (kaolin, clay and feldspar). Test specimens were isostatically pressed at 70 MPa and machined at high speed into cylindrical test specimens using controlled machining parameters. These specimens were sintered at several temperatures to determine the optimal sintering temperature for each composition, after which their mechanical properties were analyzed by the flexural bend test. The results indicated a correlation between the alumina content and the sintering temperature, and between the flexural strength and its influence on the green machining conditions. An average tensile strength of 786 MPa was attained for the composition with an added content of 30 wt% of commercial alumina sintered at 1250 degrees C, pressed and machined under industrial conditions.

Experimental analysis of active-passive vibration control using viscoelastic materials and extension and shear piezoelectric actuators

Hybrid active-passive damping treatments combine the reliability, low cost and robustness of viscoelastic damping treatments and the high-performance, modal selective and adaptive piezoelectric active control. Numerous hybrid damping treatments have been reported in the literature. They differ mainly by the relative positions of viscoelastic treatments, sensors and piezoelectric actuators. In this work we present an experimental analysis of three active-passive damping design configurations applied to a cantilever beam. In particular, two design configurations based on the extension mode of piezoelectric actuators combined with viscoelastic constrained layer damping treatments and one design configuration with shear piezoelectric actuators embedded in a sandwich beam with viscoelastic core are analyzed. For comparison purposes, a purely active design configuration with an extension piezoelectric actuator bonded to an elastic beam is also analyzed. The active-passive damping performance of the four design configurations is compared. Results show that active-passive design configurations provide more reliable and wider-range damping performance than the purely active configuration.

Non-linear boundary element formulation with tangent operator to analyse crack propagation in quasi-brittle materials

This work deals with analysis of cracked structures using BEM. Two formulations to analyse the crack growth process in quasi-brittle materials are discussed. They are based on the dual formulation of BEM where two different integral equations are employed along the opposite sides of the crack surface. The first presented formulation uses the concept of constant operator, in which the corrections of the nonlinear process are made only by applying appropriate tractions along the crack surfaces. The second presented BEM formulation to analyse crack growth problems is an implicit technique based on the use of a consistent tangent operator. This formulation is accurate, stable and always requires much less iterations to reach the equilibrium within a given load increment in comparison with the classical approach. Comparison examples of classical problem of crack growth are shown to illustrate the performance of the two formulations. (C) 2009 Elsevier Ltd. All rights reserved.

Analytical formulae for electromechanical effective properties of 3-1 longitudinally porous piezoelectric materials

A unidirectional fiber composite is considered here, the fibers of which are empty cylindrical holes periodically distributed in a transversely isotropic piezoelectric matrix, The empty-fiber cross-section is circular and the periodicity is the same in two directions at an angle pi/2 or pi/3. Closed-form formulae for all electromechanical effective properties of these 3-1 longitudinally periodic porous piezoelectric materials are presented. The derivation of such expressions is based on the asymptotic homogenization method as a limit of the effective properties of two-phase transversely isotropic parallel fiber-reinforced composites when the fibers properties tend to zero. The plane effective coefficients satisfy the corresponding Schulgasser-Benveniste-Dvorak universal type of relations, A new relation among the antiplane effective constants from the solutions of two antiplane strains and potential local problems is found. This relation is valid for arbitrary shapes of the empty-fiber cross-sections. Based on such a relation, and using recent numerical results for isotropic conductive composites, the antiplane effective properties are computed for different geometrical shapes of the empty-fiber cross-section. Comparisons with other analytical and numerical theories are presented. (c) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

PERMEABILITY MEASUREMENTS OF BRAZILIAN PINUS ELLIOTTII

The liquid and gas phase permeability, of Brazilian Pinus elliotii was studied with a custom built gas and liquid flow rate analysis chamber. The longitudinal gas phase permeability is shown to be six times greater than the radial permeability. There is no statistically significant difference between the longitudinal permeability of water versus wood preservative. Scanning Electron Microscopy (SEM) images confirm that the reported permeability properties arc due to the wood itself rather than to blocked pores or other artifacts of the sample cutting process. Wood composition analysis shows that the samples of Pinus elliotii grown in Brazil are similar to other species of Pinus grown in tropical climates. Specifically, the Pinus elliotti in this study is composed of 17% extractives, 0,27% ashes, 21% hemicellulose, 45% cellulose and 30% lignin. Results arc discussed in the context of the continued search for effective wood preservatives for use in tropical climates.

Sorption aspects for unconsolidated materials of the Sao Carlos region (SP), Brazil

The transport of liquid and gaseous pollutants through porous geological media depends on the physical and chemical characteristics of the unconsolidated material, rocks and water associated with the characteristics of the pollutants. Of these characteristics, the sorption aspect is of fundamental importance and is a function of the mineral proportions, pH, Eh and void aspects encountered in the porous media. In the Sao Carlos region, located in the eastern-central part of the 9 ate of Sao Paulo, Brazil, there are basically two types of unconsolidated materials: the first is a residual from sandstones cemented with fines and the secondarily composed of claystones, siltstones and conglomerates from the Cretaceous Period that constitute the Itaqueri Formation; the second is a sandy sediment of the Tertiary Period. These geological conditions are found in areas where chemical products are disposed of characterized as either diffuse or point pollutions sources. Because of this situation, a study was developed to evaluate the sorption aspects of some inorganic cations that are frequently found in these sources, in varied concentrations. Taken into consideration were their physical/chemical properties, such as: specific weight, grain size, mineralogy, cationic exchange capacity, pH, hydraulic conductivity. Batch tests were run using solutions of KCl, ZnCl(2) and CuCl center dot H(2)O at three different pH values, and then with a combined solution (KCl + ZnCl(2) + CuCl center dot H(2)O), also at three different pH values.

Performance evaluation and phylogenetic characterization of anaerobic fluidized bed reactors using ground tire and pet as support materials for biohydrogen production

This study evaluated two different support materials (ground tire and polyethylene terephthalate [PET]) for biohydrogen production in an anaerobic fluidized bed reactor (AFBR) treating synthetic wastewater containing glucose (4000 mg L(-1)). The AFBR, which contained either ground tire (R1) or PET (R2) as support materials, were inoculated with thermally pretreated anaerobic sludge and operated at a temperature of 30 degrees C. The AFBR were operated with a range of hydraulic retention times (HRT) between 1 and 8 h. The reactor R1 operating with a HRT of 2 h showed better performance than reactor R2, reaching a maximum hydrogen yield of 2.25 mol H(2) mol(-1) glucose with 1.3 mg of biomass (as the total volatile solids) attached to each gram of ground tire. Subsequent 16S rRNA gene sequencing and phylogenetic analysis of particle samples revealed that reactor R1 favored the presence of hydrogen-producing bacteria such as Clostridium, Bacillus, and Enterobacter. (C) 2010 Elsevier Ltd. All rights reserved.

Anaerobic degradation of linear alkylbenzene sulfonate (LAS) in fluidized bed reactor by microbial consortia in different support materials

Four anaerobic fluidized bed reactors filled with activated carbon (R1), expanded clay (R2), glass beads (R3) and sand (R4) were tested for anaerobic degradation of LAS. All reactors were inoculated with sludge from a UASB reactor treating swine wastewater and were fed with a synthetic substrate supplemented with approximately 20 mg l(-1) of LAS, on average. To 560 mg l(-1) COD influent, the maximum COD and LAS removal efficiencies were mean values of 97 +/- 2% and 99 +/- 2%, respectively, to all reactors demonstrating the potential applicability of this reactor configuration for treating LAS. The reactors were kept at 30 degrees C and operated with a hydraulic retention time (HRT) of 18 h. The use of glass beads and sand appear attractive because they favor the development of biofilms capable of supporting LAS degradation. Subsequent 16S rRNA gene sequencing and phylogenetic analysis of samples from reactors R3 and R4 revealed that these reactors gave rise to broad microbial diversity, with microorganisms belonging to the phyla Bacteroidetes, Firmicutes, Actinobacteria and Proteobacteria, indicating the role of microbial consortia in degrading the surfactant LAS. (C) 2010 Elsevier Ltd. All rights reserved.

Performance evaluation of packing materials in the removal of hydrogen sulphide in gas-phase biofilters: Polyurethane foam, sugarcane bagasse, and coconut fibre

The main objective of this work was to investigate three packing materials (polyurethane foam, sugar-cane bagasse, and coconut fibre) for biofiltration of a gaseous mixture containing hydrogen sulphide (H(2)S). Mixed cultures were obtained from two sources, aerated submerged biofilters and activated sludge, and were utilised as inoculums. Biofilters reached 100% removal efficiency after two clays of operation. The empty bed residence time was 495 for each of the biofilters. The reactors were operated simultaneously, and the inlet concentrations of H(2)S varied between 184 and 644 ppmv during the long-term continuous operation of the biofilters (100 clays). Average removal efficiencies remained above 99.3%, taking into consideration the entire period of operation. Average elimination capacities reached by the biofilters packed with polyurethane foam, coconut fibre, and sugarcane bagasse were in the range of 17.8-66.6; 18.9-68.8, and 18.7-72.9g m(-3) h(-1), respectively. Finally, we concluded that the packing materials tested in this work are appropriate for the long-term biofiltration of hydrogen sulphide. (C) 2010 Elsevier B.V. All rights reserved.

Effects of bed materials on the performance of an anaerobic sequencing batch biofilm reactor treating domestic sewage

The objective of this study was to determine the best performance of an anaerobic sequencing batch biofilm reactor (AnSBBR) based on the use of four different bed materials as support for biomass immobilization. The bed materials utilized were Polyurethane foam (PU), vegetal carbon (VC), synthetic pumice (SP), and recycled low-density polyethylene (PE). The AnSBBR. with I total volume Of 7.2 L, was operated in 8-h batch cycles over 10 months, and fed with domestic sewage with an average influent chemical oxygen demand (COD) of 358 +/- 110 mg/L. The average effluent COD values were 121 +/- 31, 208 +/- 54, 233 +/- 52, and 227 +/- 51 mg/L. for PU, VC, SP, and PE, respectively. A modified first-order kinetic model was adjusted to temporal profiles of COD during a batch cycle, and the apparent kinetic constants were 0.52 +/- 0.05, 0.37 +/- 0.05, 0.80 +/- 0.04, and 0.30 +/- 0.021h(-1) for PU, VC, SP, and PE, respectively. Specific substrate utilization rates of 1.08, 0.11, and 0.86 mg COD/mg VS day were obtained for PU, VC, and PE, respectively. Although SP yielded the highest kinetic coefficient, PU was considered the best support, since SP presented loss of chemical constituents during the reactor`s operational phase. In addition, findings oil the microbial community were associated with the reactor`s performance data. Although PE did not show a satisfactory performance, an interesting microbial diversity was found oil its surface. Based oil the morphology and denaturing gradient gel electrophoresis (DGGE) results, PE showed the best capacity for promoting the attachment of methanogenic organisms, and is therefore a material that merits further analysis. PU was considered the Most suitable material showing the best performance in terms of efficiency of solids and COD removal. (C) 2007 Elsevier Ltd. All rights reserved.

Glass formation of alloys selected by lambda and electronegativity criteria in the Ti-Zr-Fe-Co system

This work evaluates the glass formation of selected alloys based on the Ti-Zr-Fe-Co system, assuming the synergy of two distinct criteria: minimum topological instability and average electronegativity plots. Combining the minimum topological instability and the average electronegativity values result in a plot in which the most probable good glass former compositions are identified Ti-Zr rich alloys with Fe and Co additions were produced, compared against the final plot, and the best glass forming alloy composition was found to be very close the theoretically predicted ones on the Ti-Zr rich side, for both Ti-Zr-Fe and Ti-Zr-Co systems. (C) 2009 Elsevier B V All rights reserved

Citric acid as anti-hydration additive for magnesia containing refractory castables

Magnesia hydration is a key concern in refractory castable processing. The volumetric expansion that follows this reaction can result in cracks or even explosion during the first heating-up. Citric acid (CA) and other chelants can significantly reduce MgO hydration rate in aqueous suspensions by forming an insoluble magnesium citrate protective coating on the magnesia particles` surface. In the present work, the performance of CA as an anti-hydration additive in refractory castables was evaluated by hydration tests, mechanical strength and apparent volumetric expansion (AVE) measurements and thermogravimetry. The results attained have shown that CA effectiveness depends strongly on the amount added and by the interaction with other raw materials in the composition, in particular calcium aluminate cement. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Production and characterization of boride layers on AISI D2 tool steel

AISI D2 is the most commonly used cold-work tool steel of its grade. It offers high hardenability, low distortion after quenching, high resistance to softening and good wear resistance. The use of appropriate hard coatings on this steel can further improve its wear resistance. Boronizing is a surface treatment of Boron diffusion into the substrate. In this work boride layers were formed on AISI D2 steel using borax baths containing iron-titanium and aluminium, at 800 degrees C and 1000 degrees C during 4 h. The borided treated steel was characterized by optical microscopy, Vickers microhardness, X-ray diffraction (XRD) and glow discharge optical spectroscopy (GDOS) to verify the effect of the bath compositions and treatment temperatures in the layer formation. Depending on the bath composition, Fe(2)B or FeB was the predominant phase in the boride layers. The layers exhibited ""saw-tooth"" morphology at the substrate interface; layer thicknesses varied from 60 to 120 mu m, and hardness in the range of 1596-1744 HV were obtained. (C) 2009 Elsevier Ltd. All rights reserved.

VEGETABLE OIL STRUCTURE AND ANTIOXIDANTS

Five vegetable oils: canola, soybean, corn, cottonseed and sunflower oils were characterized with respect to their composition by gas chromatography and viscosity. The compositions of the vegetable oils suggest that they exhibit substantially different propensity for oxidation following the order of: canola < corn < cottonseed < sunflower approximate to soybean. Viscosities at 40 degrees C and 100 degrees C and the viscosity index (VI) values were determined for the vegetable oils and two petroleum oil quenchants: Microtemp 157 (a conventional slow oil) and Microtemp 153B (an accelerated or fast oil). The kinematic viscosities of the different vegetable and petroleum oils at 40 degrees C were similar. The VI values for the different vegetable oils were very close and varied between 209-220 and were all much higher than the VI values obtained for Microtemp 157 (96) and Microtemp 153B (121). These data indicate that the viscosity variations of these vegetable oils are substantially less sensitive to temperature variation than are the parafinic oil based Microtemp 157 and Microtemp 153B. Although these data suggest that any of the vegetable oils evaluated could be blended with minimal impact on viscosity, the oxidative stability would surely be substantially impacted. Cooling curve analysis was performed on these vegetable oils at 60 degrees C under non-agitated conditions. These results were compared with cooling curves obtained for Microtemp 157, a conventional, unaccelerated petroleum oil, and Microtemp 153B, an accelerated petroleum oil under the same conditions. The results showed that cooling profiles of the different vegetable oils were similar as expected from the VI values. However, no boiling was observed wit any of the vegetable oils and heat transfer occurs only by convection since there is no full-film boiling and nucleate boiling process as typically observed for petroleum oil quenchants, including those of this study. Therefore, high-temperature cooling is considerable faster for vegetable oils as a class. The cooling properties obtained suggest that vegetable oils would be especially suitable fur quenching low-hardenability steels such as carbon steels.

Crystallisation behaviours of Al-based metallic glasses: Compositional and topological aspects

The different types of thermal crystallisation behaviours observed during continuous heating of M-based metallic glasses have been successfully associated with the topological instability. criterion, which is simply calculated from the alloy composition and metallic radii of the alloying elements and aluminium. In the present work, we report on new results evidencing the correlation between the values of X and the crystallisation behaviours in Al-based alloys of the Al-Ni-Ce system and we compare the glass-forming abilities of alloys designed with compositions corresponding to the same topological instability condition. The results are discussed in terms of compositional and topological aspects emphasizing the relevance of the different types of clusters in the amorphous phase in defining the stability of the glass and the types of thermal crystallisation. (C) 2008 Elsevier B.V. All rights reserved.