Effect of the Etching Duration and Ultrasonic Cleaning on Microtensile Bond Strength Between Feldspathic Ceramic and Resin Cement

This study assessed the effect of different etching durations of feldspathic ceramic with hydrofluoric acid (HF) and ultrasonic cleaning of the etched ceramic surface on the microtensile bond strength stability of resin to a feldspathic ceramic. The research hypotheses investigated were: (1) different etching times would not affect the adhesion resistance and (2) ultrasonic cleaning would improve the adhesion. Ceramic blocks (6 x 6 x 5 mm) (N = 48) were obtained. The cementations surfaces were duplicated in resin composite. The six study groups (n = 8) were: G1Etching with 10% aqueous HF (30 s) + silane; G 210% HF (1 min) + silane; G3-10% HF (2 min) + silane; G4-10% HF (30 s) + ultrasonic cleaning (4 min) in distilled water + silane; G5-10% HF (1 min) + ultrasonic cleaning + silane; G6-10% HF (2 min) ultrasonic cleaning + silane. The cemented blocks were sectioned into microbars for the microtensile test. The etching duration did not create significant difference among the groups (p = .156) but significant influence of ultrasonic cleaning was observed (p = .001) (Two-way ANOVA and Tukey's test, p > 0.05). All the groups after ultrasonic cleaning presented higher bond strength (19.38-20.08 MPa) when compared with the groups without ultrasonic cleaning (16.2117.75 MPa). The bond strength between feldspathic ceramic and resin cement was not affected by different etching durations using HF. Ultrasonic cleaning increased the bond strength between ceramic surface and resin cement, regardless of the etching duration.

Low-temperature degradation of a Y-TZP ceramic after surface treatments

The purpose of this study was to evaluate the influence of zirconia surface treatments on low-temperature degradation (LTD). Disc-shaped specimens were subjected to one of four surface treatments, denoted as C (controlno surface treatment), Si (air abrasion with 30 mu m silica-modified alumina particles), Al (air abrasion with 30 mu m alumina particles), and Gr (grinding with 120 grit diamond discs). Half of the samples were submitted to autoclave treatment for 12 h (127 degrees C, 1.5 bar). Samples were characterized by x-ray diffraction and profilometer analysis and were subjected to biaxial flexural strength test. All of the groups exhibited an increase in the amount of monoclinic phase (m-phase) after LTD. The tm transformation was remarkable for the specimens from the C group, which also exhibited a significant increase in strength. The Gr group also exhibited an increase in strength but lower initial roughness, which probably suppressed LTD on the zirconia surface. The specimens subjected to air abrasion exhibited higher initial amounts of m-phase and a small increase in m-phase after LTD; the strength was not affected in these groups. The effects of LTD were different with each surface treatment applied. Apparently, LTD may be suppressed by smoother surfaces or the presence of an initial amount of m-phase on zirconia surface. (c) 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 101B: 1387-1392, 2013.

Effects of thickness, processing technique, and cooling rate protocol on the flexural strength of a bilayer ceramic system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Uniaxially aligned ceramic nanofibers obtained by chemical mechanical processing

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of different methods of cooling-lubrication in cylindrical grinding of advanced ceramic dip

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Information flows and environments in business contexts: the meat sector case of Salmanca/Spain

Organizational environments are related to hierarchic levels existing in a determined organization, and they influence in the formal and informal flows origin and in their monitoring and/or extinction. Informational environments are a result of organizational environments, of which focus is information and knowledge. Information flows are a fundamental element to informational environments, in a way that there´s no informational environments if there´s no information flows. Informational flows are natural reflections from their environments, in terms of content and in the way they occur. This qualitative and quantitative research was developed in three stages, in a way to allow the comprehension of the phenomena related to information and knowledge environments and information flows that occur in the meat sector from the Province of Salamanca, Spain. We used Laurence Bardin´s ‘Analysis of Content’, more specifically the ‘Categorical Analysis’ technique to data analysis. As data collection procedure we accomplished a field research, applying a questionnaire as an intentional sample of the meat industries segment from the Province of Salamanca, Spain. From data tabulation and analysis, we infer that information environments and flows are relevant to these companies business development, as well as we emphasized the need of information and knowledge management deployment, in a way to insure organizational processes quality, industrial chain production and companies competition to conquer potential markets.

Análise do processo de reparo de defeitos ósseos críticos em calvária de ratos preenchidos com osso autógeno ou Bone Ceramic: um estudo histométrico e imunoistoquímico

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reassessment of the potential applications of Eu3+-doped Y2O3 photoluminescent material in ceramic powder form

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The fracture resistance of a CAD/CAM Resin Nano Ceramic (RNC) and a CAD ceramic at different thicknesses

Objective. This study aimed to investigate the influence of restoration thickness to the fracture resistance of adhesively bonded Lava (TM) Ultimate CAD/CAM, a Resin Nano Ceramic(RNC), and IPS e. max CAD ceramic.Methods. Polished Lava (TM) Ultimate CAD/CAM (Group L), sandblasted Lava (TM) Ultimate CAD/CAM (Group LS), and sandblasted IPS e.max CAD (Group ES) discs (n=8, phi=10 mm) with a thickness of respectively 0.5 mm, 1.0 mm, 1.5 mm, 2.0 mm, and 3.0 mm were cemented to corresponding epoxy supporting discs, achieving a final thickness of 3.5 mm. All the 120 specimens were loaded with a universal testing machine at a crosshead speed of 1 mm/min. The load (N) at failure was recorded as fracture resistance. The stress distribution for 0.5 mm restorative discs of each group was analyzed by Finite Element Analysis (FEA). The results of facture resistances were analyzed by one-way ANOVA and regression.Results. For the same thickness of testing discs, the fracture resistance of Group L was always significantly lower than the other two groups. The 0.5 mm discs in Group L resulted in the lowest value of 1028 (112) N. There was no significant difference between Group LS and Group ES when the restoration thickness ranged between 1.0 mm and 2.0 mm. There was a linear relation between fracture resistance and restoration thickness in Group L (R = 0.621, P < 0.001) and in Group ES (R = 0.854, P < 0.001). FEA showed a compressive permanent damage in all groups.Significance. The materials tested in this in vitro study with the thickness above 0.5 mm could afford the normal bite force. When Lava Ultimate CAD/CAM is used, sandblasting is suggested to get a better bonding. (C) 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of aging procedures on the topographic surface, structural stability, and mechanical strength of a ZrO2-based dental ceramic

Objective. To determine the effects of different aging methods on the degradation and flexural strength of yttria-stabilized tetragonal zirconia (Y-TZP)Methods. Sixty disc-shaped specimens (0, 12 mm; thickness, 1.6 mm) of zirconia (Vita InCeram 2000 YZ Cubes, VITA Zahnfabrik) were prepared (ISO 6872) and randomly divided into five groups, according to the aging procedures (n=10): (C) control; (M) mechanical cycling (15,000,000 cycles/3.8 Hz/200N); (T) thermal cycling (6,000 cycles/5-55 degrees C/30 s); (TM) thermomechanical cycling (1,200,000 cycles/3.8 Hz/200N with temperature range from 5 C to 55 C for 60s each); (AUT) 12h in autoclave at 134 degrees C/2 bars; and (STO) storage in distilled water (37 degrees C/400 days). After the aging procedures, the monoclinic phase percentages were evaluated by X-ray diffraction (XRD), and topographic surface analysis was performed by 3D profilometry. The specimens were then subjected to biaxial flexure testing (1 mm/min, load 100 kgf, in water). The biaxial flexural strength data (MPa) were analyzed by 1-way ANOVA and Tukey's test (alpha = 0.05). The data for monoclinic phase percentage and profilometry (Ra) were analyzed by Kruskal-Wallis and Dunn's tests.Results. ANOVA revealed that flexural strength was affected by the aging procedures (p = 0.002). The M (781.6 MPa) and TM (771.3 MPa) groups presented lower values of flexural strength than did C (955 MPa), AUT (955.8 MPa), T (960.8 MPa) and STO (910.4 MPa). The monoclinic phase percentage was significantly higher only for STO (12.22%) and AUT (29.97%) when compared with that of the control group (Kruskal-Wallis test, p = 0.004). In addition, the surface roughnesses were similar among the groups (p = 0.165).Signcance. Water storage for 400 days and autoclave aging procedures induced higher phase transformation from tetragonal to monoclinic; however, they did not affect the flexural strength of Y-TZP ceramic, which decreased only after mechanical and thermomechanical cycling. (C) 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of grinding with diamond-disc and -bur on the mechanical behavior of a Y-TZP ceramic

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Investigation of the dielectric relaxation processes in PbZr0.65Ti0.35O3-BaFe12O19 multiferroic ceramic composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The physicochemical characterization and in vivo response of micro/nanoporous bioactive ceramic particulate bone graft materials

In this study, the physicochemical characteristics of calcium phosphate based bioactive ceramics of different compositions and blends presenting similar micro/nanoporosity and micrometer scale surface texture were characterized and evaluated in an in vivo model. Prior to the animal experiment, the porosity, surface area, particle size distribution, phase quantification, and dissolution of the materials tested were evaluated. The bone regenerative properties of the materials were evaluated using a rabbit calvaria model. After 2, 4, and 8 weeks, the animals were sacrificed and all samples were subjected to histologic observation and histomorphometric analysis. The material characterization showed that all materials tested presented variation in particle size, porosity and composition with different degrees of HA/TCP/lower stoichiometry phase ratios. Histologically, the calvarial defects presented temporal bone filling suggesting that all material groups were biocompatible and osteoconductive. Among the different materials tested, there were significant differences found in the amount of bone formation as a function of time. At 8 weeks, the micro/nanoporous material presenting similar to 55,TCP:45%,HA composition ratio presented higher amounts of new bone regeneration relative to other blends and a decrease in the amount of soft tissue infiltration. (C) 2014 Elsevier B.V. All rights reserved.

INFLUENCE OF THE VENEER-FRAMEWORK INTERFACE ON THE MECHANICAL BEHAVIOR OF CERAMIC VENEERS: A NONLINEAR FINITE ELEMENT ANALYSIS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

EVALUATION OF ROUGHNESS, WETTABILITY, AND MORPHOLOGY OF AN YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTAL CERAMIC AFTER DIFFERENT AIRBORNE-PARTICLE ABRASION PROTOCOL

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)