Finite Element Analysis of Shear Versus Torsion Adhesive Strength Tests for Dental Resin Composites

Stress distributions in torsion and wire-loop shear tests were compared using three-dimensional (3-D) linear-elastic finite element method, in an attempt to predict the ideal conditions for testing adhesive strength of dental resin composites to dentin. The torsion test presented lower variability in stress concentration at the adhesive interface with changes in the proportion adhesive thickness/resin composite diameter, as well as lower variability with changes in the resin composite elastic modulus. Moreover, the torsion test eliminated variability from changes in loading distance, and reduced the cohesive fracture tendency in the dentin. The torsion test seems to be more appropriate than wire-loop shear test for testing the resin composite-tooth interface strength. (c) Koninklijke Brill NV, Leiden, 2009

An electron microscopic study of nickel sulfide inclusions in toughened glass

It has been known since the early sixties that nickel sulfide inclusions cause spontaneous fracture of toughened (thermally tempered) glass, but despite the considerable amount of work done on this problem in the last four decades, failures still occur in the field with regularity. In this study we have classified (by viewing through a 60x optical microscope) inclusions into two groups, which are classic and atypical nickel sulfides. The classics look like the nickel sulfide inclusions found at the initiation-of-fracture of windows that have broken spontaneously. We have compared the structure and composition of the atypical inclusions with the structure and composition of the classics. All of the classic and atypical nickel sulfide inclusions studied in this work were found to have a composition in the range of Ni52S48 to Ni48S52. Inclusions on the nickel rich side of stoichiometric NiS were found to be two-phase assemblies, and inclusions on the sulphur rich side of NiS were single phase. It had been proposed that the atypicals were passive, and of a different composition to the classics. However, we found that the difference between passive and dangerous nickel sulfide inclusions was not a difference in composition but rather a difference in the type of material in the internal pore space. The passive's had carbon char in their internal pore space, whereas the pore space of dangerous inclusions contained Na2O. The presence of Na2O and carbon char with the inclusions indicates that the formation of the inclusions results from a reaction of a nickel-rich phase with sodium sulphate and carbon. (C) 2001 Kluwer Academic Publishers.