Effects of plasticizing and crosslinking on the mechanical and barrier properties of coatings based on blends of starch and poly(vinyl alcohol)

In the last decades, intensive research has been carried out in order to replace oil-based polymers with bio-based polymers due to growing environmental concerns. So far, most of the barrier materials used in food packaging are petroleum-based materials. The purpose of the barrier is to protect the packaged food from oxygen, water vapour, water and fat. The mechanical and barrier properties of coatings based on starch-plasticizer and starch-poly(vinyl alcohol) (PVOH)-plasticizer blends have been studied in the work described in this thesis. The plasticizers used were glycerol, polyethylene glycol and citric acid. In a second step, polyethylene coatings were extruded onto paperboard pre-coated with a starch-PVOH-plasticizer blend. The addition of PVOH to the starch increased the flexibility of the film. Curing of the film led to a decrease in flexibility and an increase in tensile strength. The flexibility of the starch-PVOH films was increased more when glycerol or polyethylene glycol was added than citric acid. The storage modulus of the starch-PVOH films containing citric acid increased substantially at high temperature. It was seen that the addition of polyethylene glycol or citric acid to the starch-PVOH blend resulted in an enrichment of PVOH at the surface of the films. Tensile tests on the films indicated that citric acid acted as a compatibilizer and increased the compatibility of the starch and PVOH in the blend. The addition of citric acid to the coating recipe substantially decreased the water vapour transmission rate through the starch-PVOH coated paperboard, which indicated that citric acid acts as a cross-linker for starch and/or PVOH. The starch-PVOH coatings containing citric acid showed oxygen-barrier properties similar to those of pure PVOH or of a starch-PVOH blend without plasticizer when four coating layers were applied on a paperboard. The oxygen-barrier properties of coatings based on a starch-PVOH blend containing citric acid indicated a cross-linking and increase in compatibility of the starch-PVOH blends. Polyethylene extrusion coating on a pre-coated paperboard resulted in a clear reduction in the oxygen transmission rate for all the pre-coating formulations containing plasticizers. The addition of a plasticizer to the pre-coating reduced the adhesion of polyethylene to pre-coated board. Polyethylene extrusion coating gave a board with a lower oxygen transmission rate when the paperboard was pre-coated with a polyethylene-glycol-containing formulation than with a citric-acid-containing formulation. The addition of polyethylene glycol to pre-coatings indicated an increase in wetting of the pre-coated paperboard by the polyethylene melt, and this may have sealed the small defects in the pre-coating leading to low oxygen transmission rate. The increase in brittleness of starch-PVOH films containing citric acid at a high temperature seemed to have a dominating effect on the barrier properties developed by the extrusion coating process. 

Additive Manufacturing by LPBF and WAAM of metals: correlation between production process, microstructure and mechanical properties

In the most recent years, Additive Manufacturing (AM) has drawn the attention of both academic research and industry, as it might deeply change and improve several industrial sectors. From the material point of view, AM results in a peculiar microstructure that strictly depends on the conditions of the additive process and directly affects mechanical properties. The present PhD research project aimed at investigating the process-microstructure-properties relationship of additively manufactured metal components. Two technologies belonging to the AM family were considered: Laser-based Powder Bed Fusion (LPBF) and Wire-and-Arc Additive Manufacturing (WAAM). The experimental activity was carried out on different metals of industrial interest: a CoCrMo biomedical alloy and an AlSi7Mg0.6 alloy processed by LPBF, an AlMg4.5Mn alloy and an AISI 304L austenitic stainless steel processed by WAAM. In case of LPBF, great attention was paid to the influence that feedstock material and process parameters exert on hardness, morphological and microstructural features of the produced samples. The analyses, targeted at minimizing microstructural defects, lead to process optimization. For heat-treatable LPBF alloys, innovative post-process heat treatments, tailored on the peculiar hierarchical microstructure induced by LPBF, were developed and deeply investigated. Main mechanical properties of as-built and heat-treated alloys were assessed and they were well-correlated to the specific LPBF microstructure. Results showed that, if properly optimized, samples exhibit a good trade-off between strength and ductility yet in the as-built condition. However, tailored heat treatments succeeded in improving the overall performance of the LPBF alloys. Characterization of WAAM alloys, instead, evidenced the microstructural and mechanical anisotropy typical of AM metals. Experiments revealed also an outstanding anisotropy in the elastic modulus of the austenitic stainless-steel that, along with other mechanical properties, was explained on the basis of microstructural analyses.

Strength and ductility of corroded strands within the framework of safety assessment of existing bridges

Existing bridges built in the last 50 years face challenges due to states far different than those envisaged when they were designed, due to increased loads, ageing of materials, and poor maintenance. For post-tensioned bridges, the need emerged for reliable engineering tools for the evaluation of their capacity in case of steel corrosion due to lack of mortar injection. This can lead to sudden brittle collapses, highlighting the need for proper maintenance and monitoring. This thesis proposes a peak strength model for corroded strands, introducing a “group coefficient” that aims at considering corrosion variability in the wires constituting the strands. The application of the introduced model in a deterministic approach leads to the proposal of strength curves for corroded strands, which represent useful engineering tools for estimating their maximum strength considering both geometry of the corrosion and steel material parameters. Together with the proposed ultimate displacement curves, constitutive laws of the steel material reduced by the effects of corrosion can be obtained. The effects of corroded strands on post-tensioned beams can be evaluated through the reduced bending moment-curvature diagram accounting for these reduced stress-strain relationships. The application of the introduced model in a probabilistic approach allows to estimate peak strength probability functions and consecutive design-oriented safety factors to consider corrosion effects in safety assessment verifications. Both approaches consider two procedures that are based on the knowledge level of the corrosion in the strands. On the sidelines of this main research line, this thesis also presents a study of a seismic upgrading intervention of a case-study bridge through HDRB isolators providing a simplified procedure for the identification of the correct device. The study also investigates the effects due to the variability of the shear modulus of the rubber material of the HDRB isolators on the structural response of the isolated bridge.

Processos adaptativos do tecido muscular esqueletico e tecido conjuntivo : repercussões sobre a flexibilidade

Universidade Estadual de Campinas. Faculdade de Educação Física

Functionalized adamantane: Building blocks for nanostructure self-assembly

We report first-principles calculations on the electronic and structural properties of chemically functionalized adamantane molecules, either in isolated or crystalline forms. Boron and nitrogen functionalized molecules, aza-, tetra-aza-, bora-, and tetra-bora-adamantane, were found to be very stable in terms of energetics, consistent with available experimental data. Additionally, a hypothetical molecular crystal in a zincblende structure, involving the pair tetra-bora-adamantane and tetra-aza-adamantane, was investigated. This molecular crystal presented a direct and large electronic band gap and a bulk modulus of 20 GPa. The viability of using those functionalized molecules as fundamental building blocks for nanostructure self-assembly is discussed.

Avaliação tecnológica de painéis MDF de madeira de Eucalyptus grandis confeccionados em laboratório e em linha de produção industrial

MDF panels of Eucalyptus grandis wood fibers were made in either experimentally in a laboratory or on an industrial production line. In order to analyze the influence of the production condition, the anatomical, physical and mechanical properties of the panels were determined. The wood refining induced the transversal rupture of the transversal fiber wall. The MDF panels obtained from the industrial production line presented less swelling in thickness and absorption values and improved mechanical properties in the requirements of bending strength, module of elasticity and surface resistance. For laboratory MDF panels, it was possible to verify a statistically significant correlation between bending strength and module of elasticity, medium density and internal bond and swelling in thickness and absorption. This tendency was also true for the MDF panels obtained in real conditions of production, however without statistical significance. By comparing the quality properties of MDF panels produced in the laboratory with those obtained in real conditions of production, it was sought to standardize the established variables for obtaining panels on a small scale, as well to make possible the safe transfer and divulgation of information obtained in the laboratory.

Cellulose modified fibres in cement based composites

The objective of the present work is to evaluate the effect of surface modification of cellulose pulp fibres on the mechanical and microstructure of fibre-cement composites. Surface modification of the cellulose pulps was performed with Methacryloxypropyltri-methoxysilane (MPTS) and Aminopropyltri-ethoxysilane (APTS) in an attempt to improve their durability into fibre-cement composites. The surface modification showed significant influence on the microstructure of the composites on the fibre-matrix interface and in the mineralization of the fibre lumen as seen by scanning electron microscopy (SEM) with back-scattered electron (BSE) detector. Accelerated ageing cycles decreased modulus of rupture (MOR) and toughness (TE) of the composites. Composites reinforced with MPTS-modified fibres presented fibres free from cement hydration products, while APTS-modified fibres presented accelerated mineralization. Higher mineralization of the fibres led to higher embrittlement of the composite after accelerated ageing cycles. These observations are therefore very useful for understanding the mechanisms of degradation of fibre-cement composites. (C) 2009 Elsevier Ltd. All rights reserved.

Residual stresses in TiN, DLC and MoS(2) coated surfaces with regard to their tribological fracture behaviour

Thin hard coatings on components and tools are used increasingly due to the rapid development in deposition techniques, tribological performance and application skills. The residual stresses in a coated surface are crucial for its tribological performance. Compressive residual stresses in PVD deposited TiN and DLC coatings were measured to be in the range of 0.03-4 GPa on steel substrate and 0.1-1.3 GPa on silicon. MoS(2) coatings had tensional stresses in the range of 0.8-1.3 on steel and 0.16 GPa compressive stresses on silicon. The fracture pattern of coatings deposited on steel substrate were analysed both in bend testing and scratch testing. A micro-scale finite element method (FEM) modelling and stress simulation of a 2 mu m TiN-coated steel surface was carried out and showed a reduction of the generated tensile buckling stresses in front of the sliding tip when compressive residual stresses of 1 GPa were included in the model. However, this reduction is not similarly observed in the scratch groove behind the tip, possibly due to sliding contact-induced stress relaxation. Scratch and bending tests allowed calculation of the fracture toughness of the three coated surfaces, based on both empirical crack pattern observations and FEM stress calculation, which resulted in highest values for TiN coating followed by MoS(2) and DLC coatings, being K(C) = 4-11, about 2, and 1-2 MPa M(1/2), respectively. Higher compressive residual stresses in the coating and higher elastic modulus of the coating correlated to increased fracture toughness of the coated surface. (C) 2009 Elsevier B.V. All rights reserved.

Estudo de algumas propriedades mecânicas da madeira de um híbrido clonal de Eucalyptus urophylla X Eucalyptus grandis

A procura por madeiras oriundas de reflorestamentos destinadas à serraria é uma realidade já há muitos anos, principalmente aquelas das espécies do gênero Eucalyptus. Visando buscar novas informações importantes para esse mercado, este trabalho objetivou determinar algumas propriedades mecânicas da madeira de um híbrido clonal de Eucalyptus urophylla x Eucalyptus grandis de duas idades e provenientes de talhadia simples e de reforma. Os resultados indicaram que a madeira desse híbrido apresenta boas características tecnológicas, destacando-se a segunda tora (a partir de 3 m) com as melhores propriedades de flexão estática (Módulo de Elasticidade - MOE e Módulo de Ruptura - MOR) e Compressão Axial das fibras. As árvores de maior idade (166 meses) e que sofreram dois desbastes apresentaram as melhores propriedades de flexão estática e compressão axial.

Estudo da utilização de fibras em misturas betuminosas

A presente dissertação tem como objectivo principal aprofundar os conhecimentos sobre a incorporação de fibras em misturas betuminosas, em particular, sobre as misturas do tipo Stone Mastic Asphalt (SMA). Para este tipo de mistura betuminosa existe uma norma de produto europeia, a EN 13108-5:2006. Os ensaios tipo iniciais para efeitos de certificação CE das misturas estão contemplados na norma portuguesa NP EN 13108-20:2008, onde também são estipuladas as condições de ensaio. São descritos diversos tipos de fibras passíveis de serem utilizadas no fabrico da mistura betuminosa do tipo SMA, dando especial enfoque às misturas fabricadas com fibras celulósicas, uma vez que este tipo específico de mistura é frequentemente aplicado em camada de desgaste noutros países, com reconhecidas vantagens em termos de durabilidade e desempenho do pavimento. As misturas do tipo SMA são descritas, analisando-se métodos de formulação e métodos para a sua caracterização. Posteriormente, são apresentados e discutidos os trabalhos experimentais levados a cabo para um caso concreto. Os ensaios realizados permitiram caracterizar a mistura quanto à sensibilidade à água, ao seu módulo de rigidez e resistência à deformação permanente. Conclui-se que a mistura do tipo SMA com a incorporação de fibras analisada, apresenta bom comportamento à deformação permanente e boa resistência á acção da água, comparativamente às misturas betuminosas tradicionais aplicadas em camada de desgaste.

Heat transfer coefficients from Newtonian and non-Newtonian fluids flowing in laminar regime in a helical coil

This study aimed to carry out experimental work to obtain, for Newtonian and non-Newtonian fluids, heat transfer coefficients, at constant wall temperature as boundary condition, in fully developed laminar flow inside a helical coil. The Newtonian fluids studied were aqueous solutions of glycerol, 25%, 36%, 43%, 59% and 78% (w/w) and the non-Newtonian fluids aqueous solutions of carboxymethylcellulose (CMC), a polymer, with concentrations 0.1%, 0.2%, 0.3%, 0.4% and 0.6% (w/w) and aqueous solutions of xanthan gum (XG), another polymer, with concentrations 0.1% and 0.2% (w/w). According to the rheological study performed, the polymer solutions had shear thinning behavior and different values of elasticity. The helical coil used has internal diameter, curvature ratio, length and pitch, respectively: 0.004575 m, 0.0263, 5.0 m and 11.34 mm. The Nusselt numbers for the CMC solutions are, on average, slightly higher than those for Newtonian fluids, for identical Prandtl and generalized Dean numbers. As outcome, the viscous component of the shear thinning polymer tends to potentiate the mixing effect of the Dean cells. The Nusselt numbers of the XG solutions are significant lower than those of the Newtonian solutions, for identical Prandtl and generalized Dean numbers. Therefore, the elastic component of the polymer tends to diminish the mixing effect of the Dean cells. A global correlation, for Nusselt number as a function of Péclet, generalized Dean and Weissenberg numbers for all Newtonian and non-Newtonian solutions studied, is presented.

Strap repair optimization by using embedded patches

Adhesively-bonded techniques offer an attractive option for repair of aluminium structures, and currently there are three widely used configurations, i.e., single-strap (SS), double-strap (DS) and scarf repairs. SS and DS repairs are straightforward to execute but stresses in the adhesive layer peak at the ends of the overlap. DS repairs additionally require both sides of the damaged structures to be reachable for repair, which is often not possible. In these repair configurations, some limitations emerge such as the weight, aerodynamic performance and aesthetics. The scarf repair is more complex to fabricate but stresses are more uniform along the adhesive bondline. Few studies of SS and DS repairs with embedded patches, such that these are completely flush with the adherends, are available in the literature. Furthermore, no data is available about the effects of geometrical and material parameters (e.g. the Young’s modulus of adhesive, E) on the mechanical behaviour optimization of embedded repairs. For this purpose, in this work standard SS and DD repairs, and also with embedded patches in the adherends, were tested under tension to allow the geometry optimization, by varying the overlap length (LO), thus allowing the maximization of the repairs strength. The influence of the patch embedding technique, showing notorious advantages such as aerodynamic or aesthetics, was compared in strength with standard strap repairs, for the viability analysis of its implementation. As a result of this work, some conclusions were drawn for the design optimization of bonded repairs on aluminium structures.

Extended immersive learning environment: a hybrid remote/virtual laboratory

This paper presents a collaborative virtual learning environment, which includes technologies such as 3D virtual representations, learning and content management systems, remote experiments, and collaborative learning spaces, among others. It intends to facilitate the construction, management and sharing of knowledge among teachers and students, in a global perspective. The environment proposes the use of 3D social representations for accessing learning materials in a dynamic and interactive form, which is regarded to be closer to the physical reality experienced by teachers and students in a learning context. A first implementation of the proposed extended immersive learning environment, in the area of solid mechanics, is also described, including the access to theoretical contents and a remote experiment to determine the elastic modulus of a given object.These instructions give you basic guidelines for preparing camera-ready papers for conference proceedings. Use this document as a template if you are using Microsoft Word 6.0 or later. Otherwise, use this document as an instruction set. The electronic file of your paper will be formatted further. Define all symbols used in the abstract. Do not cite references in the abstract.

A bayesian approach for NDT data fusion: The Saint Torcato Church case study

This paper presents a methodology based on the Bayesian data fusion techniques applied to non-destructive and destructive tests for the structural assessment of historical constructions. The aim of the methodology is to reduce the uncertainties of the parameter estimation. The Young's modulus of granite stones was chosen as an example for the present paper. The methodology considers several levels of uncertainty since the parameters of interest are considered random variables with random moments. A new concept of Trust Factor was introduced to affect the uncertainty related to each test results, translated by their standard deviation, depending on the higher or lower reliability of each test to predict a certain parameter.

Novel anisotropic magnetoelectric effect on δ-FeO(OH)/P(VDF-TrFE) multiferroic composites

The last decade has witnessed an increased research effort on multi-phase magnetoelectric (ME) composites. In this scope, this paper presents the application of novel materials for the development of anisotropic magnetoelectric (ME) sensors based on δ-FeO(OH)/P(VDF-TrFE) composites. The composite is able to precisely determine the amplitude and direction of the magnetic field. A new ME effect is reported in this study, as it emerges from the magnetic rotation of the δ-FeO(OH) nanosheets inside the piezoelectric P(VDF-TrFE) polymer matrix. δ-FeO(OH)/P(VDF-TrFE) composites with 1, 5, 10 and 20 δ-FeO(OH) filler weigh percentage in three δ-FeO(OH) alignment states (random, transversal and longitudinal) have been developed. Results shown that the modulus of the piezoelectric response (10-24 pC.N-1) is stable at least up to three months, the shape and magnetization maximum value (3 emu.g-1) is dependent on δ-FeO(OH) content and the obtained ME voltage coefficient, with a maximum of ≈0.4 mV.cm-1.Oe-1, is dependent on the incident magnetic field direction and intensity. In this way, the produced materials are suitable for innovative anisotropic sensor and actuator applications.