Effect of selective cyclooxygenase-2 inhibition on the development of ligature-induced periodontitis in rats

Background: the purpose of this study was to evaluate the effect of a selective cyclooxygenase-2 inhibitor on the progression of alveolar bone loss in an experimental periodontitis model in rats.Methods: One hundred eighty (180) Wistar rats were separated into 3 experimental groups. Cotton ligatures were placed at the gingival margin level of lower right first molars. The rats were randomly assigned to one of the following groups that received: a daily oral dose of 10 mg/kg body weight of celecoxib (Ce1); 20 mg/kg body weight of celecoxib (Ce2); or 10 ml/kg of saline solution (C). Serum levels of celecoxib and white blood cell count were determined. Standardized digital radiographs were taken after sacrifice at 3, 5, 10, 18, and 30 days to measure the amount of bone loss around the mesial root surface of the first molar tooth in each rat.Results: Two-way analysis of variance (ANOVA) indicated that groups treated with celecoxib had significantly less bone loss compared to controls (P <0.0001) and that there was a significant interaction between treatment with celecoxib and time (P <0.03). Post-hoc comparisons showed that in both groups treated with celecoxib, the bone loss became significant only after 10 days of ligature placement, while in the control group it was already significant after 5 days. However, differences in mean bone loss between control and Ce1 were significant only at 18 days and, between control and Ce2, at 5 and 18 days. There was no significant difference in bone loss among experimental groups at the end of the experimental period.Conclusion: These data provide evidence that systemic therapy with celecoxib can modify the progression of experimentally induced periodontitis in rats.

Linear dimensional changes of denture base and hard chair-side reline resins after disinfection

Objectives: This study evaluated the effect of disinfection by immersion in sodium perborate (50 degrees C/10 min) or microwave irradiation (650 W/6 min) on the linear dimensional change (LDC) of four reline resins (Kooliner-K, New Truliner-N, Tokuso Rebase Fast-T, Ufi Gel Hard-U) and one heat-polymerizing denture base resin (Lucitone 550-L). Methods: Specimens (50.0 mm diameter, 0.5 mm thickness) were made using a split mold with reference points, and divided into two controls and four test groups (u = 8). The distances between the points were measured on the mold (baseline readings), and compared to those obtained from the specimens after: polymerization or immersion in water (37 degrees C) for 7 days (controls); 2 or 7 cycles of disinfection by immersion or microwave irradiation. Results: the two-way ANOVA and Tukey's test (alpha = 0.05) showed that microwave disinfection significantly increased the mean LDC of materials L (-1.43%), N (-1.27%) and K (-1.06%). Material N also exhibited a significant increase in LDC after two cycles of chemical disinfection (-0.73%). For U (-0.47%) and T (-0.21%) materials, no significant changes in LDC were found. Conclusions: Microwave disinfection increases the shrinkage of materials L, N, and K. The dimensional stability of resins U and T was not affected by the disinfection methods evaluated. (c) 2006 Wiley Periodicals, Inc.

The effect of disinfectant solutions on the hardness of acrylic resin denture teeth

This investigation studied the effects of disinfectant solutions on the hardness of acrylic resin denture teeth. The occlusal surfaces of 64 resin denture teeth were ground flat with abrasives up to 400-grit silicon carbide paper. Measurements were made after polishing and after the specimens were stored in water at 37 degreesC for 48 h. The specimens were then divided into four groups and immersed in chemical disinfectants (4% chlorhexidine; 1% sodium hypochlorite and sodium perborate) for 10 min. The disinfection methods were performed twice to simulate clinical conditions and hardness measurements were made. Specimens tested as controls were immersed in water during the same disinfection time. Eight specimens were produced for each group. After desinfection procedures, testing of hardness was also performed after the samples were stored at 37 degreesC for 7, 30, 60, 90 and 120 days. Data were analysed using two-way analysis of variance (anova) and Tukey's test at 95% confidence level. According to the results, no significant differences were found between materials and immersion solutions (P > 0.05). However, a continuous decrease in hardness was noticed after ageing (P < 0.05). It was conclude that the surfaces of both acrylic resin denture teeth softened upon immersion in water regardless the disinfecting solution.

Color stability of chemically activated reline resin after microwave disinfection: A 1-year clinical trial

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Shear Bond Strength of Different Repair Systems to Titanium After Water Aging

This study evaluated the shear bond strength (SBS) and stability of commercially pure titanium (CP Ti)/repair material interfaces promoted by different repair systems. One hundred CP Ti cast discs were divided into five repair system groups: 1) Epricord (EP); 2) Bistite 11 DC (BT); 3) Cojet (CJ); 4) Scotchbond Multi-Purpose Plus (SB) (control group); and 5) Cojet Sand plus Scotchbond Multi-Purpose Plus (CJSB). The specimens were stored in distilled water for 24 hours at 37 degrees C, thermal cycled (5000 cycles, 5 degrees-55 degrees C) and stored under the same conditions for either 24 hours or six months (n=10). SBS was tested and the data were analyzed by two-way analysis of variance (ANOVA) and Tukey test (alpha=.05). Failure mode was determined with a stereomicroscope (20x). The repair system, storage time, and their interaction significantly affected the SBS (p<0.001). At 24 hours, CJSB exhibited the highest SBS value, followed by CJ. At six months, these two groups had similar mean SBS (p>0.05) and higher means in comparison to the other groups. For both storage times, BT presented the lowest SBS, while the EP and SB groups did not differ significantly from one another (p>0.05). There were no significant differences in SBS between the storage times for the groups EP and CJ (p>0.05). The groups BT, SB, and CJSB showed 100% adhesive failure, irrespective of storage time. The CJSB group showed the highest SBS at both storage times. At six months, the CJ group exhibited a similar SBS mean value when compared to the CJSB group. Water storage adversely affected the groups BT, SB (control group), and CJSB. Considering SBS values, stability, and the failure mode simultaneously, the CJ group showed the best CP Ti repair performance.

Effect of thermocycling on the flexural and impact strength of urethane-based and high-impact denture base resins

Objective: Mechanical properties of the acrylic resins used for denture fabrication may be influenced by water and temperature. Thus, the aim of this study was to evaluate the effect of thermocycling on the flexural and impact strength of a high-impact (Lucitone 199) and a urethane-based denture material (Eclipse).Materials and methods: Flexural strength (64 x 10 x 3.3 mm) and impact strength (60 x 6 x 4 mm) specimens were made following the manufacturers' instructions and assigned to two groups (n = 10): control (C) - not thermocycled - and T - thermocycled (5000 cycles between 5 and 55 degrees C). Specimens were submitted to three-point bending and Charpy impact tests.Results: Flexural strength (MPa) and impact strength (kJ/m(2)) data were analysed with two-way ANOVA (p = 0.05). The flexural strength of material Eclipse (C, 136.5; T, 130.7) was significantly higher than that of resin Lucitone 550 (C, 99.4; T, 90.1). Material Eclipse exhibited significantly higher impact strength (C, 6.9; T, 5.3) than the resin Lucitone 550 (C, 3.5; T, 3.0). For both materials, a significant decrease in flexural and impact strengths was observed when the specimens were thermocycled.Conclusion: Flexural and impact strengths were higher for Eclipse than for Lucitone 550, in both groups. Thermocycling decreased the flexural and impact strengths of Eclipse and Lucitone 550.

Effect of water storage and heat treatment on the cytotoxicity of soft liners

Objective: To evaluate the effect of water storage time on the cytotoxicity of soft liners.Methods: Sample discs of soft liners Dentusoft, Dentuflex, Trusoft, Ufi-Gel-P and denture base acrylic resin Lucitone-550 were prepared and divided into four groups: GN: No treatment, G24: Stored in water at 37 degrees C for 24 h; G48: Stored in water at 37 degrees C for 48 h, GHW: Immersed in water at 55 degrees C for 10 min. To analyse the cytotoxic effect, three samples of each group were placed in tubes with Dubelcco's Modified Eagle Mediums and incubated at 37 degrees C for 24 h. During this period, the toxic substances were leached to the culture medium. The cytotoxicity was analysed quantitatively by the incorporation of radioactivity H-3-thymidine checking the number of viable cells (synthesis of DNA). The data were statistically analysed using two-way ANOVA and Tukey's honestly significant difference tests (alpha = 0.05).Results: Treatments did not reduce the cytotoxicity effect of the soft liners (p > 0.05). It was found that Ufi-Gel-P had a non-cytotoxic effect, Trusoft had a slightly cytotoxic effect, Dentuflex had a moderated cytotoxic effect, Dentusoft alternated between slightly and non-cytotoxic effect, and Lucitone-550 had non-cytotoxic effect when stored in water for 48 h.Conclusion: The effect of water storage and the heat treatment did not reduce the cytotoxicity of the soft liners.

Effect of long-term water immersion on the fracture toughness of denture base and reline resins

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efficacy of Air-abrasion Technique and Additional Surface Treatment at Titanium/Resin Cement Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Maxillary complete denture movement during chewing in mandibular removable partial denture wearers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling.Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05).Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps.Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

Effect of microwave disinfection on the surface roughness of three denture base resins after tooth brushing

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

IMPROVEMENT TO THE MARGINAL COPING FIT of COMMERCIALLY PURE TITANIUM CAST IN PHOSPHATE-BONDED INVESTMENT BY USING A SIMPLE PATTERN COATING TECHNIQUE

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of disinfection by microwave irradiation on the strength of intact and relined denture bases and the water sorption and solubility of denture base and reline materials

This study evaluated the influence of microwave disinfection on the strength of intact and relined denture bases. Water sorption and solubility were also evaluated. A heat-polymerized acrylic resin (Lucitone 550) was used to construct 4-mm-thick (n = 40) and 2-mm-thick (n = 160) denture bases. Denture bases (2mm) were relined with an autopolymerizing resin (Tokuso Rebase Fast, Ufi Gel Hard, Kooliner, or New Truliner). Specimens were divided into four groups (n = 10): without treatment, one or seven cycles of microwave disinfection (650 W for 6 min), and water storage at 37 degrees C for 7 days. Specimens were vertically loaded (5 mm/min) until failure. Disc-shaped specimens (50 min x 0.5 mm) were fabricated (n = 10) to evaluate water sorption and solubility. Data on maximum fracture load (N), deflection (%), and solubility (%) were analyzed by two-way analysis of variance and Student-Newman-Keuls tests (alpha = 0.05). One cycle of microwave disinfection decreased the deflection at fracture and fracture energy of Tokuso Rebase Fast and New Truliner specimens. The strength of denture bases microwaved daily for 7 days was similar to the strength of those immersed in water for 7 days. Microwave disinfection increased the water sorption of all materials and affected the solubility of the reline materials. (C) 2007 Wiley Periodicals, Inc.

Assessing the surface roughness of a posterior resin composite: effect of surface sealing

This study assessed the in vitro influence of surface sealing on the surface roughness of a posterior resin composite before and after tooth-brushing. Thirty. specimens (13 nun diameter x 1 mm high) were fabricated from Filtek-P60 resin composite and randomly assigned to three groups (n=10): a non-sealed control and two groups sealed with one of the tested materials-a surface-penetrating sealant (Protect-it!-PI) and a one bottle adhesive system (Single Bond-SB). The samples were subjected to a surface roughness reading to determine the initial roughness, then submitted to simulated toothbrushing with 35,600 cycles for 100 minutes. Specimens were then cleaned and a post-abrasion surface roughness reading accomplished. Means (pm), recorded before (B) and after (A) toothbrushing, and standard deviations were: Control-(B): 0.032 (+/-0.005), (A): 0.054 (+/-0.005); PI-(B): 0.034 (+/-0.005), (A): 0.060 (+/-0.034); SB (B): 0.031 (+/-0.004), (A): 0.047 (+/-0.007). Data were tabulated and submitted to two-way ANOVA. No statistically significant difference was observed when the control and experimental groups were compared. However, a significant difference (p<0.05) was found between the measurements performed before and after toothbrushing. Based on these results, it may be concluded that using either a surface penetrating sealant or a one bottle adhesive system did not provide the optimization of superficial integrity. The use of a dentifrice and toothbrush resulted in significant alterations to the surface smoothness of the resin composite.