A note on finite determinacy for corank 2 map germs from surfaces to 3-space

We study properties of finitely determined corank 2 quasihomogeneous map germs f: (C(2), 0) -> (C(3), 0). Examples and counter examples of such map germs are presented.

Observation in the MINOS far detector of the shadowing of cosmic rays by the sun and moon

The shadowing of cosmic ray primaries by the moon and sun was observed by the MINOS far detector at a depth of 2070 mwe using 83.54 million cosmic ray muons accumulated over 1857.91 live-days. The shadow of the moon was detected at the 5.6 sigma level and the shadow of the sun at the 3.8 sigma level using a log-likelihood search in celestial coordinates. The moon shadow was used to quantify the absolute astrophysical pointing of the detector to be 0.17 +/- 0.12 degrees. Hints of interplanetary magnetic field effects were observed in both the sun and moon shadow. Published by Elsevier B.V.

Sudden stratospheric warmings seen in MINOS deep underground muon data

The rate of high energy cosmic ray muons as measured underground is shown to be strongly correlated with upper-air temperatures during short-term atmospheric (10-day) events. The effects are seen by correlating data from the MINOS underground detector and temperatures from the European Centre for Medium Range Weather Forecasts during the winter periods from 2003-2007. This effect provides an independent technique for the measurement of meteorological conditions and presents a unique opportunity to measure both short and long-term changes in this important part of the atmosphere. Citation: Osprey, S., et al. (2009), Sudden stratospheric warmings seen in MINOS deep underground muon data, Geophys. Res. Lett., 36, L05809, doi: 10.1029/2008GL036359.

The magnetized steel and scintillator calorimeters of the MINOS experiment

The Main Injector Neutrino Oscillation Search (MINOS) experiment uses an accelerator-produced neutrino beam to perform precision measurements of the neutrino oscillation parameters in the ""atmospheric neutrino"" sector associated with muon neutrino disappearance. This long-baseline experiment measures neutrino interactions in Fermilab`s NuMI neutrino beam with a near detector at Fermilab and again 735 km downstream with a far detector in the Soudan Underground Laboratory in northern Minnesota. The two detectors are magnetized steel-scintillator tracking calorimeters. They are designed to be as similar as possible in order to ensure that differences in detector response have minimal impact on the comparisons of event rates, energy spectra and topologies that are essential to MINOS measurements of oscillation parameters. The design, construction, calibration and performance of the far and near detectors are described in this paper. (C) 2008 Elsevier B.V. All rights reserved.

High-resolution electrocardiography in dogs under doxorubicin-induced cardiomyopathy

Determinaram-se a ocorrência de potencial tardio em cães com cardiomiopatia induzida pela doxorrubicina e sua relação com o desenvolvimento de arritmias ventriculares ou morte súbita. Sete cães adultos, sem raça definida, de ambos os sexos foram utilizados. A cardiomiopatia foi induzida por infusão venosa lenta de doxorrubicina (30mg/m²) em intervalos de 21 dias, até uma dose total cumulativa de 240mg/m². Os animais foram monitorados ecocardiograficamente. Após a confirmação da cardiomiopatia, foi feito o registro da eletrocardiografia de alta resolução. Potenciais tardios foram observados em dois animais que morreram subitamente poucos dias após.

Standard electrocardiographic values in Holstein calves

Este artigo apresenta valores eletrocardiográficos de 25 bezerros da raça Holandesesa, utilizando-se as derivações bipolares de membro (I, II, III), unipolares aumentadas de membro (avL, avR e avF) e uma derivação bipolar de torax (V10). Dois grupos com animais de diferentes idades foram comparados (18 a 72 horas e 27 a 33 dias de idade). Conclui-se que não houve diferença significativa entre os grupos nas ondas P, Q, R, S e T, nos intervalos PR, QRS, QT e ST e no eixo cardíaco.

Macro- and microstructural organization of the rabbit's celiac-mesenteric ganglion complex (Oryctolagus cuniculus)

The macro- and microstructures of the rabbit celiac-mesenteric ganglion complex are described in 20 young animals. We found ten celiac ganglia, twenty-seven cranial mesenteric ganglia and eleven celiac-mesenteric ganglia. The celiac ganglia had a rectangular shape in nine cases (90%) and a circular one in one case (10%). The cranial mesenteric ganglia presented triangular (66.7%), rectangular (11.1%), L-shape (18.5%) and semilunar (3.7%) arrangements. The celiac-mesenteric ganglia were organized in three patterns: a single left celiac-mesenteric ganglion having a caudal portion (72.7%); celiac-mesenteric ganglia without a caudal portion (18.2%) and a single celiac-mesenteric ganglion with two portions: left and right (9.1%).The microstructure was investigated in nine celiac-mesenteric ganglia. The results showed that the celiac-mesenteric ganglion is actually a ganglion complex constituted of an agglomerate of ganglionic units separated by nerve fibers, capillaries and septa of connective tissue. Using the semi-thin section method we described the cellular organization of the celiac-mesenteric ganglion complex. Inside of each ganglionic unit, there were various cell types: principal ganglion neurons (PGN), glial cells (satellite cells) and SIF cells (small intensely fluorescent cells or small granular cells), which are the cytologic basis for each ganglionic unit of the rabbit's celiac-mesenteric ganglion complex.

Pyrolysis and combustion of pulp mill lime sludge

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of electroless nickel interlayer on the fatigue strength of chromium electroplated AISI 4340 steel

Deposition of wear-resistant hard chromium plating leads to a decrease in the fatigue strength of the base material. Despite the effective protection against wear and corrosion, fatigue life and environmental requirements result in pressure to identify alternatives or to improve conventional chromium electroplating mechanical characteristics. An interesting, environmentally safer and cleaner alternative for the replacement of hard chronic plating is tungsten carbide thermal spray coating, applied by high velocity oxyfuel (HVOF) process.To improve the fatigue strength of aeronautical steel chromium electroplated, shot peening is a successfully used method. Multiple lacer systems of coatings are considered to have larger resistance to crack propagation in comparison with simple layer.The aim of this study was to analyze the effect of nickel underplate on the fatigue strength of hard chromium plated AISI 4340 steel in two mechanical conditions: HRc 39 and HRc 52.Rotating bending fatigue tests results indicate that the clectroless nickel plating underlayer is responsible for the increase in fatigue strength of AISI 4340 steel chromium electroplated. This behavior may be attributed to the largest toughness/ductility and compressive residual stresses which, probably, arrested or delayed the inicrocrack propagation from the hard chromium external layer. The compressive residual stress field (CRSF) induced by the electroplating process was determined by X-ray diffraction method. The evolution of fatigue strength compressive residual stress field CRSF and crack sources are discussed and analyzed by SEM. (c) 2006 Elsevier Ltd. All rights reserved.

The effect of WC-17Co thermal spray coating by HVOF and hard chromium electroplating on the fatigue life and abrasive wear resistance of AISI 4340 high strength steel

One of the most interesting alternatives for replacement of hard chrome plating is tungsten carbide thermal spray coating applied by the high velocity oxy-fuel (HVOF) process which presents a safer, cleaner and less expensive alternative to chromium plating. The objective of this research is to compare the influence of the tungsten carbide-17cobalt (WC- 17Co) coating applied by high velocity oxy fuel (HVOF) process with that of hard-chromium electroplating on the fatigue strength and abrasive wear of AISI 4340 steel.

Effects of surface treatments on the fatigue strength of AISI 4340 aeronautical steel

Internal residual stresses significantly influence the fatigue strength of coated materials. It is well known that chromium plating is the most used electrodeposited coating for important industrial applications. However, pressure to identify alternatives or to improve the chromium electroplating process have increased in recent years, related to the reduction in fatigue strength of the base material and to environmental requirements. The high efficiency and fluoride free hard chromium electroplating there called accelerated) is an improvement to the conventional process. One environmentally safer and cleaner alternative to hard chromium plating is tungsten carbide thermal spray coating applied by the High Velocity Oxy-Fuel (HVOF) process. To increase the fatigue strength of chromium plated materials, coating thickness and microcracks density are important parameters to be controlled. Techniques as compressive residual stresses induced by shot peening and multilayers, are also used. The aim of this study was to analyse the effects on AISI 4340 steel, in the rotating bending fatigue behaviour, of the: tungsten carbide thermal spray coating applied by HP/HVOF process; chemical nickel underplate, and shot peening process applied before coating deposition, in comparison to hard chromium electroplatings. Rotating bending fatigue test results indicate better performance for the conventional hard chromium plating in relation to the accelerated hard chromium electroplating. Tungsten carbide thermal spray coating and accelerated hard chromium plate over nickel resulted in higher fatigue strength when compared to samples conventional or accelerated hard chromium plated. Shot peening showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel hard chromium electroplated. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel

It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good lubricity. Environmental requirements are an important point to be considered in the search for possible alternatives to hard chrome plating. Aircraft landing gear manufactures are considering WC thermal spray coating applied by the high-velocity oxygen-fuel (HVOF) process an alternative candidate, which shows performance at least comparable to results, obtained for hard chrome plating. The aim of this study is to compare the influence of WC-17Co and WC-10Co-4Cr coatings applied by HVOF process and hard chromium electroplating on the fatigue strength of AISI 4340 steel, with and without shot peening. S-N curves were obtained in axial fatigue test for base material, chromium plated and tungsten carbide coated specimens. Tungsten carbide thermal spray coating results in higher fatigue strength when compared to hard chromium electroplated. Shot peening prior to thermal spraying showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel. Experimental data showed higher axial fatigue and corrosion resistance in salt fog exposure for samples WC-10Co-4Cr HVOF coated when compared with WC-17Co. Fracture surface analysis by scanning electron microscopy (SEM) indicated the existence of a uniform coverage of nearly all substrates. (C) 2004 Elsevier B.V. All rights reserved.

The open-ended photothermal cell with LiTaO3 and its use in determining the photochemical loss

Comparative determinations of the noise equivalent power (NEP) of open-ended photothermal cells are performed using LiTaO3 and LiNbO3 crystals with and without indium tin oxide (ITO) transparent electrodes. Open-ended cells can be used for in vivo measurements, which are important when considering the achievability for continuous monitoring of a plant, verifying, for example, the effect of water stress or UV-B radiation on a leaf. We also show the results obtained with one of these cells in the determination of photochemical loss of plant leaves. (c) 2007 Elsevier B.V. All rights reserved.

Phototrophic growth of Rubrivivax gelatinosus in poultry slaughterhouse wastewater

Rubrivivax gelatinosus was grown in Pfennig's synthetic medium (PM) and in treated wastewater from poultry slaughterhouse (TW) to assess growth profiles for biomass production. Cultures inoculated at 1% (v/v) were grown under anaerobiosis at 30 +/- 2 degrees C and 1400 200 lux for 12 days. Regular absorbance curves for R. gelatinosus were found both on PM and TW. on PM, the highest dry weight of biomass, 0.39 g L-1. was achieved in the 216-h culture and the highest specific growth rate of 0.2960 h(-1) occurred in the 24-h culture. on TW, the highest biomass of 0.57 g L-1 was also obtained in the 216-h culture and the highest specific growth rate, 0.1970 h(-1), was achieved in the 48-h culture. For productivity and chemical oxygen demand investigations, the cultivation was accomplished in the TW under anaerobiosis at 32 +/- 2 degrees C and 4000 +/- 500 lux, for 10 days. Productivity was 0.085 g biomass (d.w.) L-1 day(-1), with a COD decrease of 91%. (c) 2007 Elsevier Ltd. All rights reserved.