Optical properties of red, green and blue emitting rare earth benzenetricarboxylate compounds

Red, blue and green emitting rare earth compounds (RE(3+) = Eu(3+), Gd(3+) and Tb(3+)) containing the benzenetricarboxylate ligands (BTC) [hemimellitic (EMA), trimellitic (TLA) and trimesic (TMA)] were synthesized and characterized by elemental analysis, complexometric titration, X-ray diffraction patterns, thermogravimetric analysis and infrared spectroscopy. The complexes presented the following formula: [RE(EMA)(H(2)O)(2)], [RE(TLA)(H(2)O)(4)] and [RE(TMA)(H(2)O)(G)], except for Tb-TMA compound, which was obtained only as anhydrous. Phosphorescence data of Gd(3+)-(BTC) complexes showed that the triplet states (T) of the BTC(3-) anions have energy higher than the main emitting states of the Eu(3+) ((5)D(0)) and Tb(3+) ((5)D(4)), indicating that BTC ligands can act as intramolecular energy donors for these metal ions. The high values of experimental intensity parameters (Omega(2)) of Eu(3+)-(BTC) complexes indicate that the europium ion is in a highly polarizable chemical environment. Based on the luminescence spectra, the energy transfer from the T state of BTC ligands to the excited (5)D(0) and (5)D(4) levels of the Eu(3+) and Tb(3+) ions is discussed. The emission quantum efficiencies (eta) of the (5)D(0) emitting level of the Eu(3+) ion have been also determined. In the case of the Tb(3+) ion, the photoluminescence data show the high emission intensity of the characteristic transitions (5)D(4) -> (7)F(J) (J=0-6), indicating that the BTC ligands are good sensitizers. The RE(3+)-(BTC) complexes act as efficient light conversion molecular devices (LCMDs) and can be used as tricolor luminescent materials. (C) 2009 Elsevier B.V. All rights reserved.

Electroluminescent devices based on rare-earth tetrakis beta-diketonate complexes

In this paper the synthesis, photo luminescence and electroluminescence investigation of the novel tetrakis beta-diketonate of rare-earth complexes such as M[Eu(dbM)(4)] and M[Tb(acac)(4)] with a variety of cationic ligands, M=Li(+), Na(+) and K(+) have been investigated. The emission spectra of the Eu(3+) and Tb(3+) complexes displayed characteristic narrow bands arising from intraconfigurational transitions of trivalent rare-earth ions and exhibited red color emission for the Eu(3+) ion ((5)D(0) -> F(J), J=0-6) and green for the Tb(3+) ion ((5)D(4) -> (7)F(J), J = 6-0). The lack of the broaden emission bands arising from the ligands suggests the efficient intramolecular energy transfer from the dbm and acac ligands to Eu(3+) and Tb(3+) ions, respectively. In accordance to the expected, the values of PL quantum efficiency (eta) of the emitting (5)D(0) state of the tetrakis(beta-diketonate) complexes of Eu(3+) were higher compared with those tris-complexes. Therefore, organic electroluminescent (EL) devices were fabricated with the structure as follows: indium tin oxide (ITO)/hole transport layer (HTL) NPB or MTCD/emitter layer M[RE(beta-diketonate)(4)] complexes)/Aluminum (Al). All the films were deposited by thermal evaporation carried out in a high vacuum environment system. The OLED light emission was independent of driving voltage, indicating that the combination of charge carriers generates excitons within the M[RE(beta-diketonate)(4)] layers, and the energy is efficiently transferred to RE(3+) ion. As a best result, a pure red and green electroluminescent emission was observed from the Eu(3+) and Tb(3+) devices, confirmed by (X,Y) color coordinates. (C) 2008 Elsevier B.V. All rights reserved.

The origin of "Rare Earth" texture development in extruded Mg-based alloys and its effect on tensile ductility

The extrusion behaviour, texture and tensile ductility of five binary Mg-based alloys have been examined and compared to pure Mg. The five alloying additions examined were Al, Sn, Ca, La and Gd. When these alloys are compared at equivalent grain size, the La- and Gd-containing alloys show the best ductilities. This has been attributed to a weaker extrusion texture. These two alloying additions, La and Gd, were found to also produce a new texture peak with View the MathML source parallel to the extrusion direction. This “rare earth texture” component was found to be suppressed at high extrusion temperatures. It is proposed that the View the MathML source texture component arises from oriented nucleation at shear bands.

Effect of microalloying with rare-earth elements on the texture of extruded magnesium-based alloys

A series of alloys have been produced with microalloying additions of rare-earth (RE) elements in the range of 0.1–0.4 wt.%. The alloys have been extruded to produce grain sizes of 23 ± 5 μm. The texture of the extruded alloys was measured, and it was found that the extrusion texture was weakened by the addition of RE elements. The samples with weakened extrusion textures exhibited an increase in the tensile elongation.

The corrosion inhibition mechanism of new rare earth cinnamate compounds — electrochemical studies

A combination of linear polarisation resistance (LPR) and cyclic potentiodynamic polarisation (CPP) measurements demonstrated that the lanthanum-4 hydroxy cinnamate compound could inhibit both the cathodic and anodic corrosion reactions on mild steel surfaces exposed to 0.01 M NaCl solutions. However, the dominating response was shown to vary with inhibitor concentration. At the concentrations for which the highest level of protection was achieved, both REM-4 hydroxy cinnamate (REM being lanthanum and mischmetal) displayed a strong anodic behaviour for mild steel and their inhibition performance, including their resistance against localised attack, improved with time.

Electrochemical impedance spectroscopy (EIS) measurements and modelling were carried out so as to propose a simple electrical model and correlate the extracted parameters to the inhibition mechanism put forward for REM-cinnamate based compounds. The results supported the high corrosion inhibition performance of the compounds as well as the build-up of a protective film with time. Based on a two-layer model the results suggested that the upper layer of the inhibitor film seemed to offer less resistance to the diffusion of electrochemically active species than the highly resistive inner layer at the film/metal interface.

Corrosion mitigation of mild steel by new rare earth cinnamate compounds

Corrosion rate measurements based on weight loss (i.e., mild steel immersed for seven days in 0.01 M NaCl) and linear polarization resistance (LPR) techniques have shown that even low concentrations (200 ppm) of cerium and lanthanum cinnamates are able to significantly inhibit corrosion. Of all the compounds investigated in this work Ce(4-methoxycinnamate)3· 2 H2O and La(4-methoxycinnamate)3· 2 H2O compounds exhibited the greatest inhibition and, in comparison with the component inhibitors, a synergy was clearly observed. The mechanism of corrosion inhibition was investigated using cyclic potentiodynamic polarization (CPP) measurements. The results suggest that La(4-nitrocinnamate)3· 2 H2O and Ce(4-methoxycinnamate)3· 2 H2O behave as mixed inhibitors and improve the resistance of steel against localized attack.

Synthesis and structural diversity of rare earth anthranilate complexes

Four structural classes have been established for rare earth anthranilates, which have been prepared from the lanthanoid chloride or triflate and anthranilic acid (anthH) followed by pH adjustment to 4. [La(anth)3]n is a polymeric complex with nine coordinate lanthanum and bridging tridentate (O,O,O′) anthranilate ligands, whereas [Nd(anth)3(H2O)3] · 3H2O is monomeric with nine coordinate neodymium and solely chelating (O,O) anthranilate groups. Both chelating (O,O) and bridging bidentate (O,O′) ligands are observed in dimeric [Er2(anth)6(H2O)4] · 2H2O, in which erbium is eight coordinate and the water ligands are in a trans arrangement. A polymer is observed for [Yb(anth)3(H2O)]n with solely bridging bidentate (O,O′) ligands and seven coordination for ytterbium. The NH2 groups of the anthranilate ligands are not coordinated to the metal but is unusually involved in hydrogen-bond networks with water molecules for Ln = Er, Yb.