Translucent tin dioxide ceramics obtained by natural sintering

Dense SnO2-based ceramics (relative density >95%) have been obtained by natural sintering at a moderate temperature (less than or equal to 1300 degrees C) with the help of a small amount of manganese, Further thermal treatments above 1500 degrees C result in grain growth and transport of manganese toward the sample surface. If the ceramic is embedded inside alumina powder, the diffusion of Mn out of the sample and into alumina during such heat treatments leads to a manganese-free body (<40 ppm) which is translucent. The transmission in the visible region depends on sample thickness; 61% was achieved for a 0.05 mm thick sample.

Comparison of polymers and ceramics in new and discarded electrical insulators: reuse and recycling possibilities

The expansion and maintenance of electricity distribution networks generates large amounts of waste, much of it in the form of discarded insulators that are not reused or recycled. This paper describes the results of tests on used and new ceramic and polymeric insulators to verify if their exposure to weathering justifies their replacement. In new and used ceramic insulators, properties such as contact angle, relative density, porosimetry, dilatometry and X-ray diffraction patterns showed no differences or the differences that were found could not be related to their use. The discarded ceramic material showed high thermal stability, an interesting characteristic for application as chamotte. It can also be reused to replace gravel used in substations. In polymeric insulators, thermogravimetry, differential scanning calorimetry and relative density test results suggest degradation of used material compared to new. This would justify their replacement and discard as waste, but they show little recycling potential.

Corrosion prevention for Al2O3/SiC/C/MgAl2O4 based ceramics by means of impregnation with cerium-carrying solution

A cerium-carrying solution was developed so as to aprtially fill the open porosity of Al2O3/SiC/C/MgAl2O4 based refractory lining microstructure used in torpedo ladles, thereby enhancing wear resistance. The protection mchanism was cleared up and introduced from the impregnation technique using a cerium-carrying solution.

Piezoresponse force microscopy behaviour of Bi4Ti3O12 ceramics with various excess bismuth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

White Light and Multicolor Emission Tuning in Triply Doped Yb3+/Tm3+/Er3+ Novel Fluoro-phosphate Transparent Glass-ceramics

New Yb3+, Er3+ and Tm3+ doped fluoro-phosphate glasses belonging to the system NaPO3–YF3–BaF2–CaF2 and containing up to 10 wt% of rare-earth ion fluorides were prepared and characterized by differential scanning calorimetry, absorption spectroscopy and up-conversion emission spectroscopy under excitation with a 975 nm laser diode. Transparent and homogeneous glass-ceramics have been reproducibly obtained with a view to manage the red, green and blue emission bands and generate white light. X-ray diffraction as well as electron microscopy techniques have confirmed the formation of fluorite-type cubic nanocrystals at the beginning of the crystallization process while complex nanocrystalline phases are formed after a longer heat-treatment. The prepared glass-ceramics exhibit high optical transparency even after 170 h of thermal treatment. An improvement of up-conversion emission intensity – from 10 to 160 times larger – was measured in the glass-ceramics when compared to the parent glass, suggesting an important incorporation of the rare-earth ions into the crystalline phase(s). The involved mechanisms and lifetime were described in detail as a function of heat-treatment time. Finally, a large range of designable color rendering (from orange to turquoise through white) can be observed in these materials by controlling the laser excitation power and the crystallization rate.

Effect of oxidizing and reducing atmospheres on Ba(Ti0.90 Zr0.10)O3:2V ceramics as characterized by piezoresponse force microscopy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dielectric response of tungsten modified Ba(Ti0.90Zr0.10)O3 ceramics obtained by mixed oxide method

The electrical response of Ba(Ti0.90Zr0.10)O3 (BZT) ceramics obtained by the mixed oxide method as a functionof tungsten content was investigated. According to X-ray diffraction analysis the single phase BZT1W (1wt.% W doped BZT) and BZT2W (2 wt.% W doped BZT) ceramics, crystallized in a perovskite structure, wereobtained. It is also shown that tungsten substituted ceramics can be sintered at a reduced temperature whencompared to the undoped BZT. Electron paramagnetic resonance (EPR) analyses reveals that substitution ofTi4+ by W6+ causes distortion in the crystal structure changing lattice parameter. Substitution of W6+ on B-siteof ABO3 perovskite BZT ceramics shifted the phase transition to lower temperatures up to a tungsten contentof 2 wt.% leading to a relaxor-like behaviour.Keywords: donor dopant; ceramics; dielectric response; mixed oxide method

Surface roughness analysis of dental ceramics treated with hydrofl uoric acid and aluminum oxide jet

The aim of this study was to evaluate the surface roughness of 5 indirect restorative materials treated with hydrofluoric acid to 10%, with aluminum oxide jet and a combination of both. The specimens was prepared with 10 mm in diameter and 2 mm thickness, divided into fi ve groups: (1) Ceromer (CeseadII-Kuraray), (2) Leucite crystals ceramics (IPS EmpressIIIvoclarforcasket), (3) glass ceramic with fluorapatite (IPS D. Sign-Ivoclar), (4) lithium disilicate ceramic (IPS Empress II-Ivoclar restorations), (5) ceramics (Cergogold-Degussa). For all groups were performed the controls, and the surfaces with the 3 types of treatment. For testing roughness used the rugosimeter Taylor/Hobson-Precision, model form tracerSV-C525 high sensitivity. After confi rmation of variance analysis with a signifi cance level of 1% (p < 0.01), there was equality between the average roughness of materials from groups 1, 3 and 5, and the group 2 was different from the others. It was also found that the ceramics of the group 5 behaved similar to group 4. However the lowest average roughness was observed in group 2 ceramic. In the evaluation between the types of treatment, the aluminum oxide jet and associations and blasting with hydrofl uoric acid were similar, and different isolated hydrofl uoric acid, and 3 types of treatment signifi cantly higher than the control group. All treatments promoted superfi cial alterations in all tested materials.

Characterization of aluminum hydroxide (Al(OH)(3)) for use as a porogenic agent in castable ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Neural tool condition estimation in the grinding of advanced ceramics

Ceramic parts are increasingly replacing metal parts due to their excellent physical, chemical and mechanical properties, however they also make them difficult to manufacture by traditional machining methods. The developments carried out in this work are used to estimate tool wear during the grinding of advanced ceramics. The learning process was fed with data collected from a surface grinding machine with tangential diamond wheel and alumina ceramic test specimens, in three cutting configurations: with depths of cut of 120 mu m, 70 mu m and 20 mu m. The grinding wheel speed was 35m/s and the table speed 2.3m/s. Four neural models were evaluated, namely: Multilayer Perceptron, Radial Basis Function, Generalized Regression Neural Networks and the Adaptive Neuro-Fuzzy Inference System. The models'performance evaluation routines were executed automatically, testing all the possible combinations of inputs, number of neurons, number of layers, and spreading. The computational results reveal that the neural models were highly successful in estimating tool wear, since the errors were lower than 4%.

Pigments based on Cr and Sb doped TiO2 prepared by microemulsion-mediated solvothermal synthesis for inkjet printing on ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Titanium K-edge XAS study on local structure of Pb1-xCaxTiO3 ferroelectric ceramics

In order to characterize the local structure of Pb1-xCaxTiO3 (PCT) samples, Ti K-edge XANES measurements were performed and showed that Ca incorporation to PbTiO3 structure leads to a decreasing of local distortion of Ti atoms in relation to oxygen atoms at the TiO6 octahedra. Moreover, according to EXAFS measurements, the local structure around Ti atoms exhibits tetragonal symmetry with P4mm space group for samples with x <= 0.475, whereas orthorhombic symmetry with Pbnm space group was observed for x equals to 0.50 and 0.55.

Properties of glass-ceramics obtained from crystallization of the SiO2-Al2O3-MgO-Li2O system with addition of ZrO2

This paper presents the study results with glass-ceramics obtained from base glass (MgO-Al2O3- SiO2-Li2O system) with addition of ZrO2 as nucleating agent. The glass was melted at 1650 degrees C for 3 h and at a heating rate of 10 degrees C/min. The molten glass was poured into a graphite mold to obtain monolithic samples and also in water in order to obtain particulate material. Such material was grinded and then pressed by both uniaxial and isostatic pressing methods before being sintered. Both the monolithic and pressed samples were performed under two different conditions of heat treatment so that their nucleation and crystallization occurred. In the first one, the samples were heated to 1100 degrees C with a heating rate of 10 degrees C/min. In the second one, there was an initial heating rate of 10 degrees C/min up to 780 degrees C, which was kept for 5 minutes. After that, the samples were heated to 1100 degrees C at a heating rate of 1 degrees C/min. Microhardness analyses showed that base glass presented values around 7.0 GPa. The glass-ceramics obtained from the powder sintering showed microhardness values lower than those obtained from monolithic samples. The highest hardness values were observed in the samples which were treated with two heating rates, whose values were around 9.2 +/- 0.5 GPa. Moreover, the glass-ceramics which were produced with an only heating rate, presented values around 7.1 +/- 0.2 GPa, very close to those observed in the base glass.

X-ray photoelectron spectroscopy study on sintered Pb1-xLaxTiO3 ferroelectric ceramics

The Pb1-xLaxTiO3 sintered ferroelectric ceramics with x equal to 0, 0.10, 0.15, 0.20, and 0.30 were studied by X-ray photoelectron spectroscopy (XPS). The binding energy of the Ti 2p lines is consistent with only one chemical state, Ti4+. on the other hand, in the case of Pb 4f and 0 Is XPS spectra, apart from the main peaks attributed to the lattice ions, minor peaks related to the surface states were also observed. The presence of Pb-0 state on the surface of all samples was due to the reduction of lead ions caused by the preferential removal of the oxygen ions after sputtering. The non observation of Ti3+ ions confirms that the mechanism of charge compensation that should occurs owing to the substitution of Ph2+ by La3+ is due to the preferential formation of Pb site vacancies, and not to a reduction from Ti4+ to Ti3+ states. Within the limits of the present experiment, there is no evidence of the existence of non-equivalent Pb, Ti, and La sites as the Pb1-xLaxTiO3 ceramic changes from a normal to a relaxor ferroelectric state. (c) 2006 Elsevier B.V. All rights reserved.

Raman and infrared investigations of glass and glass-ceramics with composition 2Na2O·1CaO·3SiO2

Precursor glass and glass-ceramics with molar composition 2Na2O·1CaO·3SiO2 are studied by infrared, conventional, and microprobe Raman techniques. The Gaussian deconvoluted Raman spectrum of the glass presents bands at 625 and 660 cm-1, attributed to bending vibrations of Si-O-Si bonds, and at 860, 920, 975, and 1030 cm-1, attributed to symmetric stretching vibrations of SiO4 tetrahedra with 4, 3, 2, and 1 nonbridging oxygens, respectively. The Raman microprobe spectrum of a highly crystallized sample presents two narrow and intense bands at about 590 and 980 cm-1, associated with vibrations of SiO4 tetrahedra with two nonbridging oxygens, in agreement with the predicted chain-like structure of crystalline metasilicates. Scanning electron microscopy shows that the crystals distributed in partially crystallized samples have a spherical shape, built up by radially oriented needle-like single crystals. The Raman microprobe spectra of these spherulites show that they still contain residual amorphous material. A comparison of Raman and infrared spectra of amorphous and highly crystallized samples is presented.