New Cu-Based Catalysts Supported on TiO2 Films for Ullmann SNAr-Type C-O Coupling Reactions

New routes for the preparation of highly active TiO2-supported Cu and CuZn catalysts have been developed for C-O coupling reactions. Slurries of a titania precursor were dip-coated onto glass beads to obtain either structured mesoporous or non-porous titania thin films. The Cu and CuZn nanoparticles, synthesized using a reduction by solvent method, were deposited onto calcined films to obtain a Cu loading of 2 wt%. The catalysts were characterized by inductively coupled plasma (ICP) spectroscopy, temperature-programmed oxidation/reduction (TPO/TPR) techniques, Cu-63 nuclear magnetic resonance (NMR) spectroscopy, X-ray diffraction (XRD), scanning and transmission electron microscopy (S/TEM-EDX) and X-ray photo-electron spectroscopy (XPS). The activity and stability of the catalysts obtained have been studied in the C-O Ullmann coupling of 4-chloropyridine and potassium phenolate. The titania-supported nanoparticles retained catalyst activity for up to 12 h. However, catalyst deactivation was observed for longer operation times due to oxidation of the Cu nanoparticles. The oxidation rate could be significantly reduced over the CuZn/TiO2 catalytic films due to the presence of Zn. The 4-phenoxypyridine yield was 64% on the Cu/nonporous TiO2 at 120 degrees C. The highest product yield of 84% was obtained on the Cu/mesoporous TiO2 at 140 degrees C, corresponding to an initial reaction rate of 104 mmol g(cat)(-1) s(-1). The activation energy on the Cu/mesoporous TiO2 catalyst was found to be (144 +/- 5) kJ mol(-1), which is close to the value obtained for the reaction over unsupported CuZn nanoparticles (123 +/- 3 kJ mol(-1)) and almost twice the value observed over the catalysts deposited onto the non-porous TiO2 support (75 +/- 2 kJ mol(-1)).

Effect of glass substrate and deposition technique on the properties of sol gel TiO2 thin films

Na+ ions have a detrimental effect on the photocatalytic activity of thin sot gel films deposited on soda lime glass due to their diffusion into the film during the calcination process. Given that the content of sodium in glass substrate might be the crucial parameter in determining the activity of a photocatalyst, the aim of the present work was the comparison of the photoinduced properties of a thin TiO2 film prepared on three different glass substrates namely on quartz (Q) glass, borosilicate (BS) glass and soda lime (SL) glass which have different sodium content. The prepared layers were characterised by X-ray diffraction and UV-vis spectroscopy. The diffusion of Na+ from the substrate into the layers was determined by Glow Discharge Atomic Emission Spectroscopy. The photocatalytic activities of the films were assessed using two model pollutant test systems (resazurin/resorufin ink and stearic acid film), which appeared to correlate reasonably well. It was observed that TiO2 layer on SL glass has a brookite crystalline structure while the TiO2 layer on BS and Q glass has an anatase crystalline structure. On the other hand, the photodegradation of the model dye on TiO2 films deposited on Q and BS glass is about an order higher than on SL glass. The low sodium content of BS glass makes it the most suitable substrate for the deposition of photoactive sol gel TiO2 films. (C) 2011 Elsevier B.V. All rights reserved.

A rapid method of assessing the photocatalytic activity of thin TiO2 films using an ink based on the redox dye 2,6-dichloroindophenol

An indicator ink based on the redox dye 2,6-dichloroindophenol ( DCIP) is described, which allows the rapid assessment of the activity of thin, commercial photocatalytic films, such as Activ. The ink works via a photoreductive mechanism, DCIP being reduced to dihydro-DCIP within ca. 7.5 minutes exposure to UVA irradiation of moderate intensity ( ca. 4.8mW cm(-2)). The kinetics of photoreduction are found to be independent of the level of dye present in the ink formulation, but are highly sensitive to the level of glycerol. This latter observation may be associated with a solvatochromic effect, whereby the microenvironment in which the dye finds itself and, as a consequence, its reactivity is altered significantly by small changes in the glycerol content. The kinetics of photoreduction also appear linearly dependent on the UVA light intensity with an observed quantum efficiency of ca. 1.8 x 10(-3). Copyright (C) 2008.

Photocatalytic oxidation of deposited sulfur and gaseous sulfur dioxide by TiO2 films

Thick (4 mu m) films of anatase titania are used to photocatalyze the removal of deposited films of amorphous sulfur, similar to 2.8 mu m, thick and under moderate illumination conditions (I = 5.6 mW cm(-2)) on the open bench the process is complete within similar to 8 or 18 h using UVC or UVA light, respectively. Using UVA light, 96% of the product of the photocatalytic removal of the film of sulfur is sulfur dioxide, SO2. The photonic efficiency of this process is similar to 0.16%, which is much higher (> 15 times) than that of the removal of soot by the same films, under similar experimental conditions. In contrast to the open bench work, in a closed system the photocatalytic activity of a titania film toward the removal of sulfur decreased with repeated use, due to the accumulation of sulfuric acid on its surface generated by the subsequent photocatalytic oxidation of the initial product, SO2. The H2SO4-inactivated films are regenerated by soaking in water. The problems of using titania films to remove SO2 from a gaseous environment are discussed briefly.

Photochemical reduction of oxygen adsorbed to nanocrystalline TiO2 films: A transient absorption and oxygen scavenging study of different TiO2 preparations

Transient absorption spectroscopy (TAS) has been used to study the interfacial electron-transfer reaction between photogenerated electrons in nanocrystalline titanium dioxide (TiO2) films and molecular oxygen. TiO2 films from three different starting materials (TiO2 anatase colloidal paste and commercial anatase/rutile powders Degussa TiO2 P25 and VP TiO2 P90) have been investigated in the presence of ethanol as a hole scavenger. Separate investigations on the photocatalytic oxygen consumption by the films have also been performed with an oxygen membrane polarographic detector. Results show that a correlation exists between the electron dynamics of oxygen consumption observed by TAS and the rate of oxygen consumption through the photocatalytic process. The highest activity and the fastest oxygen reduction dynamics were observed with films fabricated from anatase TiO2 colloidal paste. The use of TAS as a tool for the prediction of the photocatalytic activities of the materials is discussed. TAS studies indicate that the rate of reduction of molecular oxygen is limited by interfacial electron-transfer kinetics rather than by the electron trapping/detrapping dynamics within the TiO2 particles.

Characterization of novel Ag on TiO2 films for surface-enhanced Raman scattering

Novel Ag on TiO₂ films are generated by semiconductor photocatalysis and characterized by ultraviolet-visible (UV/Vis) spectroscopy, scanning electron microscopy (SEM), and atomic force microscopy (AFM), as well as assessed for surface-enhanced Raman scattering (SERS) activity. The nature and thickness of the photodeposited Ag, and thus the degree of SERS activity, is controlled by the time of exposure of the TiO₂ film to UV light. All such films exhibit the optical characteristics (λ_max ≅ 390 nm) of small (<20 nm) Ag particles, although this feature becomes less prominent as the film becomes thicker. The films comprise quite large (>40 nm) Ag islands that grow and merge with increasing levels of Ag photodeposition. Tested with a benzotriazole dye probe, the films are SERS active, exhibiting activity similar to that of 6-nm-thick vapordeposited films. The Ag/TiO₂ films exhibit a lower residual standard deviation (∼25%) compared with Ag vapor-deposited films (∼45%), which is, however, still unacceptable for quantitative work. The sample-to-sample variance could be reduced significantly (<7%) by spinning the film during the SERS measurement. The Ag/TiO₂ films are mechanically robust and resistant to removal and damage by scratching, unlike the Ag vapor-deposited films. The Ag/TiO₂ films also exhibit no obvious loss of SERS activity when stored in the dark under otherwise ambient conditions. The possible extension of this simple, effective method of producing Ag films for SERS, to metals other than Ag and to semiconductors other than TiO₂, is briefly discussed. 

The photo-oxidation of water by sodium persulfate, and other electron acceptors, sensitised by TiO2

A number of different electron acceptors are tested for efficacy in the oxidation of water to oxygen, photocatalysed by titanium dioxide. The highly UV-absorbing metal ion electron acceptors, Ce4+ and Fe3+, appear ineffective at high concentration (10(-2) M), due to UV-screening, but more effective at lower concentrations (10(-3) M). The metal-depositing electron acceptor, Ag+, is initially effective, but loses activity upon prolonged irradiation due to metal deposition which promotes electron-hole recombination as well as UV-screening the titania particles. Most striking of the electron acceptors tested is persulfate, particularly in alkaline solution (0.1 M NaOH). The kinetics of the photo-oxidation of water by persulfate, photocatalysed by titania are studied as a function of pH, [S2O82-] and incident light intensity (I). The initial rate of water oxidation increases with pH, is directly proportional to the concentration of persulfate present and depends upon I-0.6. The TiO2/alkaline persulfate photosystem is robust and shows very little evidence of photochemical wear upon repeated irradiation. The results of this work are discussed with regard to previous work in this area and current mechanistic thinking. The formal quantum efficiency of the TiO2/alkaline persulfate photosystem was estimated as ca. 2%. (C) 2004 Elsevier B.V. All rights reserved.

Photo-oxidation of water sensitized by TiO2 and WO3 in presence of different electron acceptors

The photo-oxidation of water is studied in presence of UV-light (lambda

The alteration of the structural properties and photocatalytic activity of TiO2 following exposure to non-linear irradiation sources

When TiO2 powder was irradiated with a laser light (>0.8 MW peak pulse power (PPP) at 355 nm) a visible change in its colour from white to dark blue was observed. The initial rate of change of the total colour difference was related to the laser light intensity and the longer the irradiation time the more substantial the colour change. The result of X-ray diffraction (XRD) studies showed that the crystal structure of the TiO2 developed a more rutile form after laser exposure. ESR studies indicated that the colour change was associated with the generation of Ti(III) species in the photocatalyst. Electron microscopic studies showed that more spherical shaped particles of TiO2 were observed after laser treatment although the average particle size remained largely unchanged. No significant changes in the band gap or the surface area of the laser modified TiO2 were observed. The laser modified photocatalyst showed no enhancement in activity for the destruction of methylene blue, rhodamine B and stearic acids, indicating that the rutile/anatase ratio is unimportant in the destruction of the test pollutants used in this work, via TiO2 photocatalysis

Novel TiO2 CVD films for semiconductor photocatalysis

A novel CVD film of titanium(IV) oxide has been prepared on glass, via the reaction of titanium(IV) chloride and ethyl acetate, using a CVD technique. The film is clear, very robust mechanically and comprised of a thin (24 nm) layer of nanocrystalline anatase titania that absorbs light of lambda

Anodic stripping voltammetry with photochemical preconcentration at nanocrystalline TiO2 films: Detection of Ag+ and Hg2+

Nanocrystalline TiO2 deposited on conducting glass plates is shown to be an excellent material for preconcentration of silver and mercury, via photochemical reaction, prior to their detection by anodic stripping voltammetry (ASV). During the first stage of growth in the photoreduction of silver or mercury, 3D nuclei are formed on the TiO2 film. As the deposition proceeds micrometer size agglomerates grow on the surface. The conical morphology of the silver nuclei grown on a (110) rutile single crystal in the initial stages of growth suggests that there is a preferential deposition of silver at the centre of the growing nuclei. When the nuclei size reach a critical value (ca. 400 nm diameter, 40 nm height) the morphology changes to a globular shape without any preferential site for deposition on the surface of the silver nucleus. It was observed that micromolar concentrations of silver or mercury can be detected by anodic stripping voltammetry and relatively large amounts of these metals (micrometer scale nuclei) can be loaded on the nanocrystalline TiO2 film surface. The latter opens the possibility of analytical applications of nanocrystalline TiO2 electrodes for the selective detection of silver or mercury via photochemical anodic stripping voltammetry.

Photobleaching of methylene blue sensitised by TiO2: an ambiguous system?

The photobleaching of methylene blue MB, sensitised by TiO2, in an aqueous solution is studied in the absence and presence of oxygen, in the absence of oxygen and in the presence of a sacrificial electron acceptor (SED), MB is photoreduced to its colourless leuco form, LMB, by the TiO2 photocatalyst. This same photoreduction process is observed even if an SED is not present, indicating that MB itself can act as an SED. The oxidation of LMB by oxygen to regenerate MB is significantly slower if the aqueous solution is acidified (0.01 mol dm(-3) HClO4) and, at low partial pressures, the rate of reaction depends directly upon the concentration of dissolved oxygen. The TiO2-sensitised photobleaching of MB is irreversible in an oxygen-saturated aqueous solution, as expected, since the bleaching was due to an oxidative process. However, in an acidified solution (0.01 mol dm(-3) HClO4), the photobleaching process, in an oxygen-saturated solution, generates LMB initially. The latter situation arises because, under acidic conditions, LMB reacts only very slowly with oxygen to form MB. The significance of these findings with respect to the popular use of photobleaching of MB as a demonstration of semiconductor photomineralisation is discussed. (C) 1999 Elsevier Science S.A. All rights reserved.

Modification and enhanced photocatalytic activity of TiO2 following exposure to non-linear irradiation sources

The effects of high power pulsed laser light on a TiO2 photocatalyst (powder and 0.1% (w/v) aqueous suspension) are reported. When this material was irradiated with a laser of power over 0.8 MW peak pulse power at 355 nm wavelength a visible change in colour from white to dark blue was observed. The initial rate of change of the total colour difference is related to the laser power; the stronger the laser power the darker the colour change. The result of X-ray diffraction studies indicates that the crystal structure of the TiO2 developed a more rutile form after laser exposure. Electron microscopic studies showed that spherical shaped particles of TiO2 were observed after laser treatment. Preliminary results show enhanced photocatalytic activity for the destruction of methylene blue. (C) 1999 Elsevier Science S.A. All rights reserved.

Photomineralisation of 4-chlorophenol sensitised by TiO2 thin films

The results of a study of the oxidative mineralisation of 4-CP by oxygen, sensitised by thin films of Degussa P25 TiO2, are reported. The films are used under conditions in which the kinetics of photomineralisation are independent of mass transfer effects and stable towards repeated irradiation. Using a TiO2 film, the process goes through the same mechanism as a TiO2 dispersion, generating the same intermediates, namely: 4-chlorocatechol and hydroquinone. The kinetics of photomineralisation show clear differences between a TiO2 film and a dispersion. With TiO2 films the initial rate of photomineralisation is strongly dependent upon photocatalyst loading, (units; g dm(-3)) reaching a distinct maximum, which appears to be associated with the formation of a monolayer of aggregated particles - the diameter of the aggregated particles is estimated as 0.44 mu m. A simple 2D model is presented to help illustrate the features of such a system. With TiO2 dispersions the rate usually reaches a plateau at ca. 0.5 g dm(-3) of TiO2. For TiO2 films the initial rate depends directly upon the incident light intensity, implying that the photocatalytically active particles are under low illumination conditions, partially shielded by the other particles making up each aggregated particle. In contrast, with TiO2 dispersions R-i depends upon I-0.64, implying that the different light intensities used spanned both the high (R(i)proportional to I-1/2) and low (R(i)proportional to I) intensity kinetic regions. The kinetics of photomineralisation of 4-CP, sensitised by TiO2 films obey the same Langmuir-Hinshelwood expressions as found in most semiconductor photocatalyst work conducted with TiO2 dispersions. However, in a study of the variation R-i as a function of [4-CP] and [O-2] the values for the maximum rates were larger, and those for the apparent Langmuir adsorption coefficients were smaller, than those found for TiO2 dispersions. (C) 1998 Elsevier Science S.A. All rights reserved.