Very thin yttrium barium copper oxide films made by coevaporation

Superconducting YBa2Cu3O7 thin films with various thicknesses from 100 Å to 5000 Å were deposited on (100) SrTiO3 substrates with std. BaF2 coevaporation process. The films had crit. temps. of up to 93 K. The best crit. currents were 1 × 106 A/cm2 at 77 K and 3 × 107 A/cm2 at 4.2 K. The crit. current was generally higher for thinner films. Two different etching methods were used to pattern the films for jc measurements: Ar ion etching and EDTA wet etching. The wet etching was found to work well for thicker films (>1000 Å). For the thinner films, the ion etching process was preferred because of the reduced film surface degrdn. [on SciFinder(R)]

Artificial grain boundary Josephson junctions : properties and applications

Engineered grain boundary Josephson junctions in YBaCuO were formed on bicrystal Y-ZrO2 substrates. Laser deposited films were patterned into micron size microbridges. The authors obsd. a pronounced correlation between superconducting transport properties of grain boundary junctions and the misorientation angle θ between the two halves of the bicrystal. The crit. Josephson current Ic decreased about four orders of magnitude as θ was increased from 0 to 45 degrees. Clear microwave and magnetic field responses were obsd. at 77 K. At this temp., crit. current times normal resistance products, IcRn, of up to 1 mV were measured for low angle grain boundaries, and Shapiro steps were obsd. up to that voltage. DC SQUIDs were fabricated, and best performance at 77 K was obtained for θ = 32° with a 4-μm strip width. To utilize the higher IcRn value of a lower θ, submicron junctions have to be developed. [on SciFinder(R)]

Continuous production of Bi-2212 thick film on silver tape

Bi-2212 thick film on silver tapes are seen as a simple and low cost alternative to high temperature superconducting wires produced by the Powder In Thbe (PIT) technique, particularly in react and wind applications. A rig for the continuous production of Bi-2212 tapes for use in react and wind component manufacture has been developed and commissioned. The rig consists of several sections, each fully automatic, for task specific duties in the production of HTS tape. The major sections are: tape coating, sintering and annealing. High temperature superconducting tapes with engineering critical current densities of 10 kA/cm2 (77 K, self field), and lengths of up to 100 m have been produced using the rig. Properties of the finished tape are discussed and results are presented for current density versus bend radius and applied strain. Depending on tape content and thickness, irreversible strain tirrm varies between 0.04 and 0.1 %. Cyclic bending tests when applied strain does not exceed Eirrm showed negligible reduction in J c along the length of the tape.

Effect of heat treatment and bend strain on the Jc of Ag-sheathed Bi-2212 tape

Bi-2212 tapes were fabricated using a powder-in-tube method and their superconducting properties were measured as a function of heat treatment. The tapes were heated to temperature, T1 (884-915 °C), and kept at that temperature for 20 min to induce partial (incongruent) melting. The samples were cooled to T2 with a ramp rate of 120 °C h-1 and then slowly cooled to T3 with a cooling rate, R2, and from T3 to T4 with a cooling rate, R3. The tapes were kept at the temperature T4 for P1 hours and then cooled to room temperature. Both R1 and R2 were chosen between 2 and 8 °C h-1. It was found that the structure and Jc of the tapes depend on the sintering conditions, i.e. T1-4, R1-3 and P1. The highest Jc of 5800 Å cm-2 was obtained at 77 K in a self-field with heat treatment where T1 = 894 and 899 °C, R1 = R2 = 5 °C h-1 and P1 = 6 h were employed. When 0.7% of bend strain, which is equivalent to a bend radius of 5 mm, was applied to the tape, 80% of the initial Jc was sustained.

Comparison of functionals for metal hexaboride band structure calculations

Density functional calculations of the electronic band structure for superconducting and semi-conducting metal hexaborides are compared using a consistent suite of assumptions and with emphasis on the physical implications of computed models. Spin polarization enhances mathematical accuracy of the functional approximations and adds significant physical meaning to model interpretation. For YB6 and LaB6, differences in alpha and beta projections occur near the Fermi energy. These differences are pronounced for superconducting hexaborides but do not occur for other metal hexaborides.

Electron-conduction mechanism and specific heat above transition temperature in LaFeAsO and BaFe2As2 superconductors

The ionization energy theory is used to calculate the evolution of the resistivity and specific heat curves with respect to different doping elements in the recently discovered superconducting pnictide materials. Electron-conduction mechanism in the pnictides above the structural transition temperature is explained unambiguously, which is also consistent with other strongly correlated materials, such as cuprates, manganites, titanates and magnetic semiconductors.

Phonon modes of MgB2 : Super-lattice structures and spectral response

Micrometre-sized MgB2 crystals of varying quality, synthesized at low temperature and autogeneous pressure, are compared using a combination of Raman and Infra-Red (IR) spectroscopy. These data, which include new peak positions in both spectroscopies for high quality MgB2, are interpreted using DFT calculations on phonon behaviour for symmetry-related structures. Raman and IR activity additional to that predicted by point group analyses of the P6/mmm symmetry are detected. These additional peaks, as well as the overall shapes of calculated phonon dispersion (PD) models are explained by assuming a double super-lattice, consistent with a lower symmetry structure for MgB2. A 2x super-lattice in the c-direction allows a simple correlation of the pair breaking energy and the superconducting gap by activation of corresponding acoustic frequencies. A consistent physical interpretation of these spectra is obtained when the position of a phonon anomaly defines a super-lattice modulation in the a-b plane.

Magnetic and morphological properties of ferrofluid-impregnated hydroxyapatite/collagen scaffolds

In this article we present the morphological and magnetic characterization of ferrofluid-impregnated biomimetic scaffolds made of hydroxyapatite and collagen used for bone reconstruction. We describe an innovative and simple impregnation process by which the ferrofluid is firmly adsorbed onto the hydroxyapatite/collagen scaffolds. The process confers sufficient magnetization to attract potential magnetic carriers, which may be used to transport bioactive agents that favour bone regeneration. The crystalline structure of the magnetite contained in the ferrofluid is preserved and its quantity, estimated from the weight gain due to the impregnation process, is consistent with that obtained from energy dispersive X-ray spectroscopy. The magnetization, measured with a superconducting quantum interference device, is uniform throughout the scaffolds, demonstrating the efficiency of the impregnation process. The field emission gun scanning electron microscopy characterization demonstrates that the process does not alter the morphology of the hydroxyapatite/collagen scaffolds, which is essential for the preservation of their bioactivity and consequently for their effectiveness in promoting bone formation.

Electronic Properties of the Vortex State in Cuprate Superconductors

The superconducting state of the cuprates in the presence of a magnetic field has been investigated very actively in the past few years through measurements of electrical and thermal transport, ac conductivity, specific heat, and other quantities. The observed behavior is not well understood; it probes the nature of quasiparticies, vortices, and their interactions in a superconductor with nodes in the pair amplitude. We summarize here experimental results and our attempts to understand the phenomena.

Superconductivity in the nonadiabatic limit

Isotope-shift exponent (cu) and the pressure coefficient of superconducting transition temperature (beta) have been studied in the nonadiabatic limit. We have considered the effect of nonadiabaticity in both within and beyond the Migdal-Eliashberg formalism. It reveals from our study that the pressure coefficient of superconducting transition is high for the low-T-c region and low for the high-T-c region and the minimum value of alpha is obtained where the transition temperature is maximum. Lowest value of isotope-shift exponent is obtained for small momentum exchange between the electrons and the bosonic field. Qualitative variation of beta with temperature is consistent with the experimental results of the hole doped superconductors for small momentum exchange.

Vortex dynamics at rf frequencies in Bi2Sr2CaCu2O8 single crystals

We have studied the low magnetic field high temperature region of the H-T phase diagram of Bi2Sr2CaCu2O8 single crystals using the technique of non-resonant rf response at a frequency of 20 MHz. With H(rf)parallel to a, H parallel to c, the isothermal magnetic field scans below T-c show that the frequency f(H) of the tank circuit decreases continuously with increase in H before saturating at H similar to H-D(T). Such a decrease in f(H) reflects increasing rf penetration into the weakly screened region between CuO bilayers. The saturation of f(H) at its lowest value for H similar to H-D(T) indicates complete rf penetration land hence the disappearance of field dependence) due to the vanishing of the screening rf currents I-rf(c) in those regions or equivalently when the phase coherence between adjacent superconducting layers vanishes. Therefore H,(T) represents the decoupling of the adjacent superconducting bilayers, and hence also a 3D to 2D decoupling transition of the vortex structure. Simultaneous monitoring of the field dependent rf power dissipation P(H) shows a maximum in dP/dH at H-D(T). The observed H-D(T) line in many crystals is in excellent agreement with the (l/t-1) behavior proposed for decoupling.

Towards rational synthesis of inorganic solids

There have been major advances in the past couple of years in the rational synthesis of inorganic solids: synthesis of mercury-based superconducting cuprates showing transition temperatures up to 150 K; ZrP2-xVxO7 solid solutions showing zero or negative thermal expansion; copper oxides possessing ladder structures such as La1-xSrxCuO2.5; synthesis of mesoporous oxide materials having adjustable pore size in the range 15-100 Angstrom; and synthesis of a molecular ferromagnet showing a critical temperature of 18.6 K. Despite great advances in probing the structures of solids and measurement of their physical properties, the design and synthesis of inorganic solids possessing desired structures and properties remain a challenge today. With the availability of a variety of mild chemistry-based approaches, kinetic control of synthetic pathways is becoming increasingly possible, which, it is hoped, will eventually make rational design of inorganic solids a reality.

Codoping Effect of Zn and Pr in YBa2Cu3O7-delta

In this paper we present the resistivity data for Pr and Zn codoped compound Y1-xPrxBa2[Cu1-yZny](3)O7-delta with 0 < y < 0.1 and x = 0.0, 0.1 and 0.2. The data is analysed in terms of the superconducting critical temperature T-c, residual resistivity rho(0) and the resistivity slope d rho/dT corresponding to the linear rho-T region. It is found that for x = 0.1 Pr has a minimal influence on the in-plane processes for Zn impurity alone affecting slightly T-c and rho(0). The slope dp/dT becomes larger for 0.03 < y < 0.06 leading to larger depining effect and hence slower fall of T, as a function of y. For x = 0.2 there is a drastic change, rho(0) becomes abnormally large, d rho/dT becomes negative implying absence of depinning and a totally pinned charge stripes. Superconductivity vanishes at y = 0.03. It is concluded that for x = 0.2 Pr converts the system from overdoped to underdoped region leading to the universal superconductor-insulator transition.

Systematic stability analysis of the renormalization group flow for the normal-superconductor-normal junction of Luttinger liquid wires

We study the renormalization group flows of the two terminal conductance of a superconducting junction of two Luttinger liquid wires. We compute the power laws associated with the renormalization group flow around the various fixed points of this system using the generators of the SU(4) group to generate the appropriate parametrization of an matrix representing small deviations from a given fixed point matrix [obtained earlier in S. Das, S. Rao, and A. Saha, Phys. Rev. B 77, 155418 (2008)], and we then perform a comprehensive stability analysis. In particular, for the nontrivial fixed point which has intermediate values of transmission, reflection, Andreev reflection, and crossed Andreev reflection, we show that there are eleven independent directions in which the system can be perturbed, which are relevant or irrelevant, and five directions which are marginal. We obtain power laws associated with these relevant and irrelevant perturbations. Unlike the case of the two-wire charge-conserving junction, here we show that there are power laws which are nonlinear functions of V(0) and V(2kF) [where V(k) represents the Fourier transform of the interelectron interaction potential at momentum k]. We also obtain the power law dependence of linear response conductance on voltage bias or temperature around this fixed point.

High-temperature superconductivity in La- and Lu-substituted YBa2,Cu3,O7, and related oxides

The perovskites, Y0.75La0.25Ba2Cu3O7 and Y0.75Lu0.25Ba2Cu3O7, show high-Tc superconductivity (with zero resistance at or above 80 K), just as the parent compound YBa2Cu3O7. The Lu-substituted oxide, with the smallest unit-cell parameters, shows the highest Tc besides exhibiting a 100% Meissner effect. Hc1, in these oxides is around 25 mT, but the Hc2, is large. The thermopower of YBa2Cu3O7 shows a sharp transition to zero at the superconducting transition, reinforcing the bulk nature of the superconductivity. Preliminary studies show that ErBa2Cu3O7 and Er0.5Y0.5Ba2Cu3O7 are both high-temperature superconductors with zero resistance in the 82-90 K range.